CN103525269A - 一种低温固化重防腐粉末涂料 - Google Patents

一种低温固化重防腐粉末涂料 Download PDF

Info

Publication number
CN103525269A
CN103525269A CN201310438241.XA CN201310438241A CN103525269A CN 103525269 A CN103525269 A CN 103525269A CN 201310438241 A CN201310438241 A CN 201310438241A CN 103525269 A CN103525269 A CN 103525269A
Authority
CN
China
Prior art keywords
parts
low
powder
mentioned
mix
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310438241.XA
Other languages
English (en)
Inventor
钱广华
周进
金纬
孙拉拉
胡震
黄彪
孙成文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Raysee Photoelectricity Technology Corp Ltd
Original Assignee
Anhui Raysee Photoelectricity Technology Corp Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Raysee Photoelectricity Technology Corp Ltd filed Critical Anhui Raysee Photoelectricity Technology Corp Ltd
Priority to CN201310438241.XA priority Critical patent/CN103525269A/zh
Publication of CN103525269A publication Critical patent/CN103525269A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种低温固化重防腐粉末涂料，它是由下述重量份的原料组成的：热固性端羧基聚酯树脂40-50、双酚a环氧树脂10-20、异氰脲酸三缩水甘油酯4-10、大理石粉6-10、儿茶酚1.0-1.5、甘油三醋酸酯2.3-2.8、聚甲基丙烯酸酯2-3、乙撑双硬脂酰胺1-2、1,4-环己烷二甲醇1-2、陶瓷粉2-3、复合填料6-10；本发明的粉末涂料防腐性能优越，固化温度低，降低生产成本，施工简易快捷，不会造成环境污染和危害施工人员身体健康，并能有效提高涂装效率。

Description

一种低温固化重防腐粉末涂料
技术领域
    本发明主要涉及一种涂料，尤其涉及一种低温固化重防腐粉末涂料。
背景技术
随着近年来各种仪表尤其是精密仪表的出现和微电、弱电元器件、大规模集成电路的发展，也要求仪表的外壳要有可靠的静电保护和静电屏蔽功能，所涂涂料不仅要能吸收高频辐射和高能电磁波的能量，使内部脆弱的元件得到良好的保护，还要具有一定的抗冲击和耐腐蚀等性能，以保证仪表在不同环境下的使用需求。
发明内容
本发明目的就是为了提供一种低温固化重防腐粉末涂料。
本发明是通过以下技术方案实现的：
一种低温固化重防腐粉末涂料，其特征在于它是由下述重量份的原料组成的：
热固性端羧基聚酯树脂40-50、双酚a环氧树脂10-20、异氰脲酸三缩水甘油酯4-10、大理石粉6-10、儿茶酚1.0-1.5、甘油三醋酸酯2.3-2.8、聚甲基丙烯酸酯2-3、乙撑双硬脂酰胺1-2、1,4-环己烷二甲醇1-2、陶瓷粉2-3、复合填料6-10；
所述的复合填料是由下述重量份的原料组成的：
红土30-45、氟磷灰石5-10、萤石粉3-5、氢氧化铝3-4、二硼化钒1-2、2，6- 二叔丁基对甲酚1-2、聚乙二醇1000 2-3；
将上述红土、氟磷灰石、萤石粉混合，在600-700℃下煅烧3-4小时，出料冷却后与二硼化钒混合，充分球磨，得料a；将上述聚乙二醇1000加入到4-5倍水中，加热到30-40℃，充分搅拌，加入氢氧化铝,100-200转/分搅拌分散3-4分钟，加入6- 二叔丁基对甲酚，充分混合后与上述料a混合，球磨，烘干，过60-80目筛，即得所述复合填料。
一种低温固化重防腐粉末涂料的制备方法，包括以下步骤：
将上述各原料混合，通过挤出机中熔融挤出，然后压片破碎后，再经过微粉碎机粉碎、过筛，即得所述低温固化重防腐粉末涂料。
本发明的优点是：
    本发明的粉末涂料防腐性能优越，固化温度低，降低生产成本，施工简易快捷，不会造成环境污染和危害施工人员身体健康,并能有效提高涂装效率。
具体实施方式
实施例1，
一种低温固化重防腐粉末涂料，它是由下述重量份（公斤）的原料组成的：
热固性端羧基聚酯树脂50、双酚a环氧树脂20、异氰脲酸三缩水甘油酯4-10、大理石粉10、儿茶酚1.5、甘油三醋酸酯2.8、聚甲基丙烯酸酯2-3、乙撑双硬脂酰胺1、1,4-环己烷二甲醇1、陶瓷粉2、复合填料10；
所述的复合填料是由下述重量份的原料组成的：
红土45、氟磷灰石10、萤石粉5、氢氧化铝4、二硼化钒1、2，6- 二叔丁基对甲酚1、聚乙二醇1000 3；
将上述红土、氟磷灰石、萤石粉混合，在600℃下煅烧4小时，出料冷却后与二硼化钒混合，充分球磨，得料a；将上述聚乙二醇1000加入到5倍水中，加热到40℃，充分搅拌，加入氢氧化铝,200转/分搅拌分散3分钟，加入6- 二叔丁基对甲酚，充分混合后与上述料a混合，球磨，烘干，过80目筛，即得所述复合填料。
一种低温固化重防腐粉末涂料的制备方法，包括以下步骤：
将上述各原料混合，通过挤出机中熔融挤出，然后压片破碎后，再经过微粉碎机粉碎、过筛，即得所述低温固化重防腐粉末涂料。
性能测试：
抗冲击性：≥50kg/cm；
硬度≥2H。

Claims (2)

1.一种低温固化重防腐粉末涂料，其特征在于它是由下述重量份的原料组成的：
热固性端羧基聚酯树脂40-50、双酚a环氧树脂10-20、异氰脲酸三缩水甘油酯4-10、大理石粉6-10、儿茶酚1.0-1.5、甘油三醋酸酯2.3-2.8、聚甲基丙烯酸酯2-3、乙撑双硬脂酰胺1-2、1,4-环己烷二甲醇1-2、陶瓷粉2-3、复合填料6-10；
所述的复合填料是由下述重量份的原料组成的：
红土30-45、氟磷灰石5-10、萤石粉3-5、氢氧化铝3-4、二硼化钒1-2、2，6- 二叔丁基对甲酚1-2、聚乙二醇1000 2-3；
将上述红土、氟磷灰石、萤石粉混合，在600-700℃下煅烧3-4小时，出料冷却后与二硼化钒混合，充分球磨，得料a；将上述聚乙二醇1000加入到4-5倍水中，加热到30-40℃，充分搅拌，加入氢氧化铝,100-200转/分搅拌分散3-4分钟，加入6- 二叔丁基对甲酚，充分混合后与上述料a混合，球磨，烘干，过60-80目筛，即得所述复合填料。
2.一种如权利要求1所述的低温固化重防腐粉末涂料的制备方法，其特征在于包括以下步骤：
将上述各原料混合，通过挤出机中熔融挤出，然后压片破碎后，再经过微粉碎机粉碎、过筛，即得所述低温固化重防腐粉末涂料。
CN201310438241.XA 2013-09-24 2013-09-24 一种低温固化重防腐粉末涂料 Pending CN103525269A (zh)