CN103525225B - 一种抗高温氧化滑板润滑涂料 - Google Patents

一种抗高温氧化滑板润滑涂料 Download PDF

Info

Publication number
CN103525225B
CN103525225B CN201310419560.6A CN201310419560A CN103525225B CN 103525225 B CN103525225 B CN 103525225B CN 201310419560 A CN201310419560 A CN 201310419560A CN 103525225 B CN103525225 B CN 103525225B
Authority
CN
China
Prior art keywords
coating
sliding plate
oxidation resistant
add
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310419560.6A
Other languages
English (en)
Other versions
CN103525225A (zh
Inventor
任振州
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi Baofang Construction Engineering Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310419560.6A priority Critical patent/CN103525225B/zh
Publication of CN103525225A publication Critical patent/CN103525225A/zh
Application granted granted Critical
Publication of CN103525225B publication Critical patent/CN103525225B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗高温氧化滑板润滑涂料，它是由下述重量份的原料组成的：硅丙乳液10-20、聚乙烯醇6-10、二辛酯1-2、苯甲酸钠0.1-0.2、陶瓷纤维3-4、平均粒度为1-2μm的鳞片石墨20-30、N-(2,4,6-三氯苯基)马来酰亚胺1-2、四氯间苯二甲腈1-2、硅藻土1-2、氮化铝2-3、无水氯化钙1-2、粘结助剂10-12、去离子水75-90；本发明的涂料在常温下干燥速度快，润滑涂层致密均匀，外观平整光滑，而且在高温条件下，与滑板结合强度高，保持了良好的润滑性能，还可显著防止滑板中焦油的渗出，本发明涂料耐水、耐冲击、耐腐蚀性强，储存稳定性好。

Description

一种抗高温氧化滑板润滑涂料
技术领域
本发明主要涉及一种涂料，尤其涉及一种抗高温氧化滑板润滑涂料。
背景技术
涂料应该具有防腐、防水、防油、耐化学品、耐光、耐温等，物件暴露在大气之中，受到氧气、水分等的侵蚀，造成金属锈蚀、木材腐朽、水泥风化等破坏现象。在物件表面涂以涂料，形成一层保护膜，能够阻止或延迟这些破坏现象的发生和发展，使各种材料的使用寿命延长。所以，保护作用是涂料的一个主要作用，提高传统涂料的保护作用，才能进一步提高涂料的品质。
发明内容
本发明目的就是为了提供一种抗高温氧化滑板润滑涂料。
本发明是通过以下技术方案实现的：
一种抗高温氧化滑板润滑涂料，它是由下述重量份的原料组成的：
硅丙乳液10-20、聚乙烯醇6-10、二辛酯1-2、苯甲酸钠0.1-0.2、陶瓷纤维3-4、平均粒度为1-2μm的鳞片石墨20-30、N-(2,4,6-三氯苯基)马来酰亚胺1-2、四氯间苯二甲腈1-2、硅藻土1-2、氮化铝2-3、无水氯化钙1-2、粘结助剂10-12、去离子水75-90；
所述的粘结助剂是由下述重量份的原料组成的：
苯丙乳液60-70、黄蓍胶6-8、吡啶硫酮锌1-2、硅铝酸钠4-6、聚丙烯酸丁酯1-2、羟乙基纤维素2-4、2,6-二叔丁基对甲酚0.1-0.3、水适量；
将上述重量黄蓍胶的10-20%加入到10-15倍水中，加入羟乙基纤维素和2,6-二叔丁基对甲酚，在400-600转/分的速度下搅拌分散10-15分钟，升高温度为60-80℃，加入吡啶硫酮锌、硅铝酸钠、聚丙烯酸丁酯，充分混合后，加入剩余各原料，搅拌均匀后过80-100℃的蒸汽加热，使得体系固含量为60-65%，冷却至常温，即得所述粘结助剂。
一种抗高温氧化滑板润滑涂料的制备方法，包括以下步骤：
将上述聚乙烯醇加入到去离子水中，加热至90-100℃，搅拌溶解，降低温度为60-70℃，加入二辛酯、N-(2,4,6-三氯苯基)马来酰亚胺，充分混合后冷却至常温，加入剩余各原料，100-200转/分搅拌分散3-5分钟，放入球磨机中，球磨混合10-20小时，出料，即得所述抗高温氧化滑板润滑涂料。
本发明的优点是：
本发明的涂料在常温下干燥速度快，润滑涂层致密均匀，外观平整光滑，而且在高温条件下，与滑板结合强度高，保持了良好的润滑性能，还可显著防止滑板中焦油的渗出，本发明涂料耐水、耐冲击、耐腐蚀性强，储存稳定性好。
具体实施方式
实施例1
一种抗高温氧化滑板润滑涂料，它是由下述重量份（公斤）的原料组成的：
硅丙乳液20、聚乙烯醇10、二辛酯1-2、苯甲酸钠0.2、陶瓷纤维3、平均粒度为1-2μm的鳞片石墨30、N-(2,4,6-三氯苯基)马来酰亚胺1、四氯间苯二甲腈1、硅藻土1、氮化铝2、无水氯化钙1-2、粘结助剂12、去离子水90；
所述的粘结助剂是由下述重量份的原料组成的：
苯丙乳液70、黄蓍胶8、吡啶硫酮锌1、硅铝酸钠4、聚丙烯酸丁酯1、羟乙基纤维素2、2,6-二叔丁基对甲酚0.3、水适量；
将上述重量黄蓍胶的20%加入到15倍水中，加入羟乙基纤维素和2,6-二叔丁基对甲酚，在600转/分的速度下搅拌分散15分钟，升高温度为80℃，加入吡啶硫酮锌、硅铝酸钠、聚丙烯酸丁酯，充分混合后，加入剩余各原料，搅拌均匀后过100℃的蒸汽加热，使得体系固含量为65%，冷却至常温，即得所述粘结助剂。
一种抗高温氧化滑板润滑涂料的制备方法，包括以下步骤：
将上述聚乙烯醇加入到去离子水中，加热至100℃，搅拌溶解，降低温度为70℃，加入二辛酯、N-(2,4,6-三氯苯基)马来酰亚胺，充分混合后冷却至常温，加入剩余各原料，200转/分搅拌分散3分钟，放入球磨机中，球磨混合16小时，出料，即得所述抗高温氧化滑板润滑涂料。
性能测试：
涂料经2个半月的静置后，未发现明显沉淀，涂料均匀稳定。

Claims (2)

1.一种抗高温氧化滑板润滑涂料，其特征在于它是由下述重量份的原料组成的：
硅丙乳液10-20、聚乙烯醇6-10、二辛酯1-2、苯甲酸钠0.1-0.2、陶瓷纤维3-4、平均粒度为1-2μm的鳞片石墨20-30、N-(2,4,6-三氯苯基)马来酰亚胺1-2、四氯间苯二甲腈1-2、硅藻土1-2、氮化铝2-3、无水氯化钙1-2、粘结助剂10-12、去离子水75-90；
所述的粘结助剂是由下述重量份的原料组成的：
苯丙乳液60-70、黄蓍胶6-8、吡啶硫酮锌1-2、硅铝酸钠4-6、聚丙烯酸丁酯1-2、羟乙基纤维素2-4、2,6-二叔丁基对甲酚0.1-0.3、水适量；
将上述重量黄蓍胶的10-20%加入到10-15倍水中，加入羟乙基纤维素和2,6-二叔丁基对甲酚，在400-600转/分的速度下搅拌分散10-15分钟，升高温度至60-80℃，加入吡啶硫酮锌、硅铝酸钠、聚丙烯酸丁酯，充分混合后，加入剩余各原料，搅拌均匀后过80-100℃的蒸汽加热，使得体系固含量为60-65%，冷却至常温，即得所述粘结助剂。
2.一种如权利要求1所述的抗高温氧化滑板润滑涂料的制备方法，其特征在于包括以下步骤：
将上述聚乙烯醇加入到去离子水中，加热至90-100℃，搅拌溶解，降低温度至60-70℃，加入二辛酯、N-(2,4,6-三氯苯基)马来酰亚胺，充分混合后冷却至常温，加入剩余各原料，100-200转/分搅拌分散3-5分钟，放入球磨机中，球磨混合10-20小时，出料，即得所述抗高温氧化滑板润滑涂料。
CN201310419560.6A 2013-09-13 2013-09-13 一种抗高温氧化滑板润滑涂料 Active CN103525225B (zh)