CN103468163B - 一种含有改性阻燃剂的阻燃热熔胶 - Google Patents

一种含有改性阻燃剂的阻燃热熔胶 Download PDF

Info

Publication number
CN103468163B
CN103468163B CN201310349546.3A CN201310349546A CN103468163B CN 103468163 B CN103468163 B CN 103468163B CN 201310349546 A CN201310349546 A CN 201310349546A CN 103468163 B CN103468163 B CN 103468163B
Authority
CN
China
Prior art keywords
flame
retardant
magnesium hydroxide
weight
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310349546.3A
Other languages
English (en)
Other versions
CN103468163A (zh
Inventor
张洪滨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Lianbang Silicone Technology Co., Ltd.
Original Assignee
BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU HONGAN PRECISION MACHINERY Co Ltd filed Critical BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority to CN201310349546.3A priority Critical patent/CN103468163B/zh
Publication of CN103468163A publication Critical patent/CN103468163A/zh
Application granted granted Critical
Publication of CN103468163B publication Critical patent/CN103468163B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有改性阻燃剂的阻燃热熔胶，其是由下述重量份的原料制得:改性淀粉2-4，台湾台聚UE630？EVA70-80、2-硫醇基苯骈咪唑1-2、锡酸锌0.1-0.2、异氰酸酯0.1-0.2、苯并三氮唑0.1-0.2、苯二甲酸二丁酯0.3-0.5、交联剂TAC1-2，三盐基硫酸铅2-4，玫瑰精油0.1-0.2、改性氢氧化镁2-4、C5石油树脂16-20，柠檬酸三乙酯1-2，抗氧剂168？0.1-0.2。

Description

一种含有改性阻燃剂的阻燃热熔胶
技术领域
本发明涉及热熔胶领域，确切地说是一种含有改性阻燃剂的阻燃热熔胶。
背景技术
热熔胶粘合是利用热熔胶机通过热力把热熔胶熔解，熔胶后的胶成为一种液体，通过热熔胶机的热熔胶管和热熔胶枪，送到被粘合物表面，热熔胶冷却后即完成了粘合。
发明内容
本发明的目的在于提供一种含有改性阻燃剂的阻燃热熔胶。
上述目的通过以下方案实现：
一种含有改性阻燃剂的阻燃热熔胶，其是由下述重量份的原料制得:改性淀粉2-4，台湾台聚UE630EVA70-80、2-硫醇基苯骈咪唑1-2、锡酸锌0.1-0.2、异氰酸酯0.1-0.2、苯并三氮唑0.1-0.2、苯二甲酸二丁酯0.3-0.5、交联剂TAC1-2，三盐基硫酸铅2-4，玫瑰精油0.1-0.2、改性氢氧化镁2-4、C5石油树脂16-20，柠檬酸三乙酯1-2，抗氧剂1680.1-0.2。
所述的一种含有改性阻燃剂的阻燃热熔胶，
制备方法包括以下步骤：
(1)所述的改性淀粉的制备方法为：按重量份取淀粉，再加入相当于淀粉重量1-2％的己二酸酯，1.3-1.5％的柠檬酸三乙酯，0.6-0.8％平平加，以及适量去离子水，于100-200转/分下于40-45℃下搅拌反应10-15分钟后，取出，干燥，即得；
(2)所述的改性氢氧化镁的制备方法为：按重量份取氢氧化镁，再加入相当于氢氧化镁重量1-2％的己二酸酯，0.1-0.2％的碳化铝，0.2-0.4％的竹炭粉，以及适量去离子水，于400-600转/分下搅拌反应20-35分钟后，取出，干燥，即得；
(3)捏合机预加热至壁温180-200℃，然后按重量份加入台湾台聚UE630EVA、2-硫醇基苯骈咪唑、锡酸锌、异氰酸酯、苯并三氮唑、苯二甲酸二丁酯、交联剂TAC捏合20-30min，再加入改性氢氧化镁、C5石油树脂，于150-170℃捏合10-20分钟后，加入剩余原料，捏合10-20分钟，取出冷却即得。
本发明的有益效果为：本发明添加了改性氢氧化镁作为阻燃剂，氢氧化镁通过改性包覆，增加了其阻燃性能，是的本发明阻燃性能优异，改性淀粉增加了本发明的粘结强度。
具体实施方式
一种含有改性阻燃剂的阻燃热熔胶，其是由下述重量份(kg)的原料制得:改性淀粉4，台湾台聚UE630EVA80、2-硫醇基苯骈咪唑2、锡酸锌0.2、异氰酸酯0.2、苯并三氮唑0.2、苯二甲酸二丁酯0.5、交联剂TAC2，三盐基硫酸铅4，玫瑰精油0.2、改性氢氧化镁4、C5石油树脂20，柠檬酸三乙酯2，抗氧剂1680.2。
所述的一种含有改性阻燃剂的阻燃热熔胶，
制备方法包括以下步骤：
(1)所述的改性淀粉的制备方法为：按重量份取淀粉，再加入相当于淀粉重量1.4％的己二酸酯，1.4％的柠檬酸三乙酯，0.8％平平加，以及适量去离子水，于200转/分下于45℃下搅拌反应15分钟后，取出，干燥，即得；
(2)所述的改性氢氧化镁的制备方法为：按重量份取氢氧化镁，再加入相当于氢氧化镁重量1％的己二酸酯，0.2％的碳化铝，0.4％的竹炭粉，以及适量去离子水，于600转/分下搅拌反应35分钟后，取出，干燥，即得；
(3)捏合机预加热至壁温180℃，然后按重量份加入台湾台聚UE630EVA、2-硫醇基苯骈咪唑、锡酸锌、异氰酸酯、苯并三氮唑、苯二甲酸二丁酯、交联剂TAC捏合30min，再加入改性氢氧化镁、C5石油树脂，于170℃捏合10分钟后，加入剩余原料，捏合15分钟，取出冷却即得。
本实施例的粘结剂的表观粘度为4800MPa.s，剥离强度54N/2.5cm，初粘力达到5号钢球，开放时间38s，24小时热稳定性状稳定。

Claims (1)

1.一种含有改性阻燃剂的阻燃热熔胶，其特征在于：其是由下述重量份的原料制得:改性淀粉2-4，台湾台聚UE630EVA70-80、2-硫醇基苯骈咪唑1-2、锡酸锌0.1-0.2、异氰酸酯0.1-0.2、苯并三氮唑0.1-0.2、苯二甲酸二丁酯0.3-0.5、交联剂TAC1-2，三盐基硫酸铅2-4，玫瑰精油0.1-0.2、改性氢氧化镁2-4、C5石油树脂16-20，柠檬酸三乙酯1-2，抗氧剂1680.1-0.2；
　所述的一种含有改性阻燃剂的阻燃热熔胶制备方法包括以下步骤：
（1）所述的改性淀粉的制备方法为：按重量份取淀粉，再加入相当于淀粉重量1-2%的己二酸酯，1.3-1.5%的柠檬酸三乙酯，0.6-0.8%平平加，以及适量去离子水，于100-200转/分下于40-45℃下搅拌反应10-15分钟后，取出，干燥，即得；
（2）所述的改性氢氧化镁的制备方法为：按重量份取氢氧化镁，再加入相当于氢氧化镁重量1-2%的己二酸酯，0.1-0.2%的碳化铝，0.2-0.4%的竹炭粉，以及适量去离子水，于400-600转/分下搅拌反应20-35分钟后，取出，干燥，即得；
（3）捏合机预加热至壁温180-200℃，然后按重量份加入台湾台聚UE630EVA、2-硫醇基苯骈咪唑、锡酸锌、异氰酸酯、苯并三氮唑、苯二甲酸二丁酯、交联剂TAC捏合20-30min，再加入改性氢氧化镁、C5石油树脂，于150-170℃捏合10-20分钟后，加入剩余原料，捏合10-20分钟，取出冷却即得。
CN201310349546.3A 2013-08-13 2013-08-13 一种含有改性阻燃剂的阻燃热熔胶 Expired - Fee Related CN103468163B (zh)