CN102241936A - 一种耐高温隔热保温涂料 - Google Patents

一种耐高温隔热保温涂料 Download PDF

Info

Publication number
CN102241936A
CN102241936A CN2011101387785A CN201110138778A CN102241936A CN 102241936 A CN102241936 A CN 102241936A CN 2011101387785 A CN2011101387785 A CN 2011101387785A CN 201110138778 A CN201110138778 A CN 201110138778A CN 102241936 A CN102241936 A CN 102241936A
Authority
CN
China
Prior art keywords
weight parts
thermostable heat
isolating coating
coating according
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101387785A
Other languages
English (en)
Inventor
刘昆虎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KAIPING CITY PAINT CO Ltd ON SOLID EDGE
Original Assignee
KAIPING CITY PAINT CO Ltd ON SOLID EDGE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KAIPING CITY PAINT CO Ltd ON SOLID EDGE filed Critical KAIPING CITY PAINT CO Ltd ON SOLID EDGE
Priority to CN2011101387785A priority Critical patent/CN102241936A/zh
Publication of CN102241936A publication Critical patent/CN102241936A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温隔热保温涂料，含有硅丙乳液、氟硅橡胶、成膜助剂、分散剂、颜填料、水等组分。本发明的涂料具有优秀的耐高温特性，可使用在－80℃～1100℃的物体表面，而且隔热保温效果优秀，可以显著降低高温物体表面温度，并可减少热量损失30%以上，可用于各类高温管道、炉膛、窑炉的内外表面。

Description

一种耐高温隔热保温涂料
技术领域
本发明涉及一种涂料，具体涉及一种耐高温隔热保温涂料。
背景技术
热管道在蒸汽或液体输送的过程中会产生热量损耗，传统的方法是采取内衬岩棉外包铁皮的方法，此种方法的缺点是不能观察内包铁管的“跑、冒、滴、漏”。此外，管道的锈蚀容易造成安全上的隐患。
现有技术中的耐温涂料耐温范围通常最高到700~800℃，且耐温变性、防腐性差。因此，研究开发一种更加耐高温，且耐温变性好、防腐防水性能优秀的耐高温隔热保温涂料，具有非常重要的实践意义。
发明内容
为了克服现有技术的不足，本发明提供了一种耐高温隔热保温涂料。本发明的涂料可以耐受更大范围的高温，隔热保温性能优秀。
本发明所采取的技术方案如下：
一种耐高温隔热保温涂料，含有硅丙乳液10~40重量份、氟硅橡胶10~30重量份、成膜助剂2~8重量份、分散剂0.3~0.8重量份、颜填料40~90重量份、水20~40重量份。
进一步，所述耐高温隔热保温涂料还含有催干剂0.1~0.5重量份。
优选的，所述成膜助剂由丙二醇苯醚、醇酯十二中的任意一种或一种以上组成。
优选的，所述分散剂由六偏磷酸钠、聚丙烯酸钠盐中的任意一种或一种以上组成。
优选的，所述颜填料由硅藻土、钛白粉、白炭黑、硅酸钙中的任意一种或一种以上组成。
进一步优选的，所述催干剂为二月桂酸二丁基锡。
进一步优选的，所述钛白粉为耐高温型金红石型钛白粉。
进一步优选的，所述白炭黑为纳米级气相白炭黑。
本发明具有以下有益效果：
（1）本发明的耐高温隔热保温涂料具有优秀的耐高温特性，可使用在－80℃～1100℃的物体表面（比重是1800 Kg/m3）；
（2）隔热保温效果优秀，在1100℃的物体表面涂上8mm厚度的本发明的耐高温隔热保温涂料，物体的表面温度能降低到100℃以内，并可以有效减少热量损失30%以上；涂刷在炉膛、窑炉内壁会比任何材料表面更平整光滑，并具有火焰红外线反射功能，减少炉壁的散热，使炉膛的火焰温度明显提高；
（3）防水防腐性能优秀，且施工方便，清洁美观，可用于各类高温管道、炉膛、窑炉的内外表面。
具体实施方式
一种耐高温隔热保温涂料，含有硅丙乳液10~40重量份、氟硅橡胶10~30重量份、成膜助剂2~8重量份、分散剂0.3~0.8重量份、颜填料40~90重量份、水20~40重量份。
进一步，所述耐高温隔热保温涂料还含有催干剂0.1~0.5重量份。
优选的，所述成膜助剂由丙二醇苯醚、醇酯十二中的任意一种或一种以上组成。
优选的，所述分散剂由六偏磷酸钠、聚丙烯酸钠盐中的任意一种或一种以上组成。
优选的，所述颜填料由硅藻土、钛白粉、白炭黑、硅酸钙中的任意一种或一种以上组成。
进一步优选的，所述催干剂为二月桂酸二丁基锡。
进一步优选的，所述钛白粉为耐高温型金红石型钛白粉。
进一步优选的，所述白炭黑为纳米级气相白炭黑。
下面结合实施例对本发明作进一步的具体描述，但并不局限于此。
实施例1
本发明的一种耐高温隔热保温涂料的一个优选方案，含有硅丙乳液30重量份、 氟硅橡胶10重量份、醇酯十二4重量份、聚丙烯酸钠盐0.4重量份、二月硅酸二丁基锡0.3重量份、硅藻土20重量份、金红石型钛白粉15重量份、纳米气相白炭黑10重量份、硅酸钙20重量份、去离子水 20重量份。
实施例2
本发明的一种耐高温隔热保温涂料的一个优选方案，含有硅丙乳液10重量份、 氟硅橡胶30重量份、醇酯十二2重量份、聚丙烯酸钠盐0.3重量份、二月硅酸二丁基锡0.5重量份、硅藻土30重量份、金红石型钛白粉20重量份、纳米气相白炭黑15重量份、硅酸钙25重量份、去离子水 40重量份。
实施例3
本发明的一种耐高温隔热保温涂料的一个优选方案，含有硅丙乳液20重量份、 氟硅橡胶20重量份、醇酯十二2重量份、丙二醇苯醚6重量份、聚丙烯酸钠盐0.2重量份、六偏磷酸钠0.3重量份、二月硅酸二丁基锡0.2重量份、硅藻土40重量份、金红石型钛白粉20重量份、纳米气相白炭黑15重量份、硅酸钙15重量份、去离子水 20重量份。
实施例4
本发明的一种耐高温隔热保温涂料的一个优选方案，含有硅丙乳液35重量份、 氟硅橡胶15重量份、醇酯十二4重量份、丙二醇苯醚4重量份、六偏磷酸钠0.6重量份、二月硅酸二丁基锡0.1重量份、硅藻土20重量份、金红石型钛白粉20重量份、去离子水 30重量份。
实施例5
本发明的一种耐高温隔热保温涂料的一个优选方案，含有硅丙乳液40重量份、氟硅橡胶10重量份、醇酯十二8重量份、聚丙烯酸钠盐0.5重量份、二月硅酸二丁基锡0.3重量份、金红石型钛白粉20重量份、纳米气相白炭黑20重量份、硅酸钙15重量份、去离子水 20重量份。
实施例6
本发明的一种耐高温隔热保温涂料的一个优选方案，含有硅丙乳液30重量份、氟硅橡胶20重量份、丙二醇苯醚8重量份、聚丙烯酸钠盐0.6重量份、六偏磷酸钠0.2重量份、二月硅酸二丁基锡0.4重量份、纳米气相白炭黑20重量份、硅酸钙30重量份、去离子水 30重量份。
将上述1-6实施例的各组分经溶解、混合、改性、研磨、过滤后，得到本发明的耐高温隔热保温涂料。
隔热性能实验：
（1）将实施例1-6制备的耐高温隔热保温涂料在1100℃的物体表面涂上8mm厚，物体的表面温度就能降低到100℃以内；
（2）将实施例1-6制备的耐高温隔热保温涂料在炉膛窑炉内外表面涂上6mm厚，可以减少热量损失30%以上；
（3）在规格为1200cm×1200cm×1200cm，钢板厚度为1cm的封闭钢板箱箱体外表面涂刷10mm的耐高温隔热保温涂料，置于冷冻箱中冰冻至箱体内部温度为－30℃后，将箱体置于室温环境下，24小时箱体内的温度不高于0℃。

Claims (8)

1.一种耐高温隔热保温涂料，其特征在于：含有硅丙乳液10~40重量份、氟硅橡胶10~30重量份、成膜助剂2~8重量份、分散剂0.3~0.8重量份、颜填料40~90重量份、水20~40重量份。
2.根据权利要求1所述的一种耐高温隔热保温涂料，其特征在于：还含有催干剂0.1~0.5重量份。
3.根据权利要求1所述的一种耐高温隔热保温涂料，其特征在于：所述成膜助剂由丙二醇苯醚、醇酯十二中的任意一种或一种以上组成。
4.根据权利要求1所述的一种耐高温隔热保温涂料，其特征在于：所述分散剂由六偏磷酸钠、聚丙烯酸钠盐中的任意一种或一种以上组成。
5.根据权利要求1所述的一种耐高温隔热保温涂料，其特征在于：所述颜填料由硅藻土、钛白粉、白炭黑、硅酸钙中的任意一种或一种以上组成。
6.根据权利要求2所述的一种耐高温隔热保温涂料，其特征在于：所述催干剂为二月桂酸二丁基锡。
7.根据权利要求5所述的一种耐高温隔热保温涂料，其特征在于：所述钛白粉为耐高温型金红石型钛白粉。
8.根据权利要求5所述的一种耐高温隔热保温涂料，其特征在于：所述白炭黑为纳米级气相白炭黑。
CN2011101387785A 2011-05-26 2011-05-26 一种耐高温隔热保温涂料 Pending CN102241936A (zh)