CN103509216A - 一种户外变压器用抗紫外线密封垫及其制备方法 - Google Patents

一种户外变压器用抗紫外线密封垫及其制备方法 Download PDF

Info

Publication number
CN103509216A
CN103509216A CN201310399747.4A CN201310399747A CN103509216A CN 103509216 A CN103509216 A CN 103509216A CN 201310399747 A CN201310399747 A CN 201310399747A CN 103509216 A CN103509216 A CN 103509216A
Authority
CN
China
Prior art keywords
parts
resistance
ultraviolet
sealing gasket
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310399747.4A
Other languages
English (en)
Inventor
周俊
徐淑平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI KELIN ELECTRONIC Co Ltd
Original Assignee
ANHUI KELIN ELECTRONIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI KELIN ELECTRONIC Co Ltd filed Critical ANHUI KELIN ELECTRONIC Co Ltd
Priority to CN201310399747.4A priority Critical patent/CN103509216A/zh
Publication of CN103509216A publication Critical patent/CN103509216A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种户外变压器用抗紫外线密封垫及其制备方法,其由以下重量份的原料制成:氯丁橡胶65-85、丁苯橡胶25-35、SEBS5-10、邻苯二甲酸二辛酯10-15、磷酸三苯甲酯8-12、30号机油10-15、氧化锌3-5、氧化镁2-4、硬脂酸1-2、炭黑N22020-30、不溶性硫磺2-3、二甲基丙烯酸二甘醇酯3-4、纳米氮化铝5-10、滑石粉10-15、纳米重晶石4-8、复合填料3-5、防老剂2641-2、防老剂MBZ0.5-1、促进剂DZ1-2、紫外线吸收剂UV-91-2。本发明密封垫耐紫外线光照老化性能优异,且具有良好的机械强度、压缩回弹性、耐酸碱、耐冲击、耐磨,耐油、耐热等性能,能抵抗日光下的紫外线的侵袭,使变压器密封垫不产生龟裂,确保有效的密封,使用寿命长。

Description

一种户外变压器用抗紫外线密封垫及其制备方法
技术领域
本发明涉及一种户外变压器用抗紫外线密封垫及其制备方法,属于密封材料技术领域。
背景技术
密封垫,是油浸式变压器的一个重要零件,起到密封,防止变压器漏油的作用。对于户外变压器由于长期受日光照射,日光中的紫外线会直接损害橡胶密封垫,加速其老化产生龟裂,造成变压器渗漏油,严重影响了变压器的使用寿命,给电力系统和用户造成巨大的经济损失。
发明内容
本发明的目的在提供一种户外变压器用抗紫外线密封垫及其制备方法,提高的橡胶密封垫的耐紫外老化性能。
本发明采用的技术方案如下:
一种户外变压器用抗紫外线密封垫,由以下重量份的原料制成:氯丁橡胶(CR121)65-85、丁苯橡胶(SBR1712)25-35、SEBS5-10、邻苯二甲酸二辛酯10-15、磷酸三苯甲酯8-12、30号机油10-15、氧化锌3-5、氧化镁2-4、硬脂酸1-2、炭黑N22020-30、不溶性硫磺2-3、二甲基丙烯酸二甘醇酯3-4、纳米氮化铝5-10、滑石粉10-15、纳米重晶石4-8、复合填料3-5、防老剂2641-2、防老剂MBZ0.5-1、促进剂DZ1-2、紫外线吸收剂UV-91-2;
所述复合填料的制备方法如下:a、按重量比3-5:2-3:1称取硅灰石、叶腊石、凹凸棒石混合均匀,490-520℃煅烧3-5h,冷却至常温后放入浓度为15-20%的盐酸溶液中浸泡2-3h,过滤,将上述矿石混合物用蒸馏水洗涤至中性,烘干,粉碎,过300-400目筛;b、过筛后的粉末中加入0.5-1%的异丙基二硬脂酰氧基铝酸酯、2-3%的玉石粉、1-2%的纳米硼化硅、3-5%的季戊四醇硬脂酸酯,1000-1500rpm高速研磨20-30min,再加入5-8%的腰果壳油、1-2%的聚四氟乙烯微粉、2-3%的树木灰烬,500-1000rpm高速搅拌10-15min即可。
户外变压器用抗紫外线密封垫的制备方法,包括以下步骤:
(1)将丁苯橡胶、SEBS、邻苯二甲酸二辛酯、磷酸三苯甲酯、氧化镁、炭黑N220、复合填料放入开炼机中,在辊温为40-50℃下混炼3-5min;然后加入氯丁橡胶、30号机油、氧化锌、硬脂酸、不溶性硫磺、二甲基丙烯酸二甘醇酯、纳米氮化铝、纳米重晶石,在辊温为75-85℃下混炼4-8min;辊温降至50-55℃时,再加入其余原料,混炼3-4min,混合均匀后薄通6-8次,冷却至常温并停放22-24h,出片;
(2)将片料置于模具中,用平板硫化机中在170-190℃下加压硫化5-10min,成型脱模后再于140-160℃下二次硫化2-4h,硫化完成后制品经检验合格、修整毛边后即为成品。
本发明的有益效果:
本发明密封垫耐紫外线光照老化性能优异,且具有良好的机械强度、压缩回弹性、耐酸碱、耐冲击、耐磨,耐油、耐热等性能,能抵抗日光下的紫外线的侵袭,使变压器密封垫不产生龟裂,确保有效的密封,使用寿命长。
具体实施方式
一种户外变压器用抗紫外线密封垫,由以下重量(kg)的原料制成:氯丁橡胶(CR121)70、丁苯橡胶(SBR1712)30、SEBS8、邻苯二甲酸二辛酯12、磷酸三苯甲酯10、30号机油15、氧化锌4、氧化镁3、硬脂酸1、炭黑N22025、不溶性硫磺2、二甲基丙烯酸二甘醇酯3、纳米氮化铝8、滑石粉10、纳米重晶石6、复合填料4、防老剂2642、防老剂MBZ0.5、促进剂DZ1.5、紫外线吸收剂UV-91;
所述复合填料的制备方法如下:a、按重量比4:3:1称取硅灰石、叶腊石、凹凸棒石混合均匀,515℃煅烧4h,冷却至常温后放入浓度为16%的盐酸溶液中浸泡3h,过滤,将上述矿石混合物用蒸馏水洗涤至中性,烘干,粉碎,过300目筛;b、过筛后的粉末中加入相当于粉末重量0.8%的异丙基二硬脂酰氧基铝酸酯、2%的玉石粉、1.5%的纳米硼化硅、4%的季戊四醇硬脂酸酯,1500rpm高速研磨20min,再加入6%的腰果壳油、1.5%的聚四氟乙烯微粉、2%的树木灰烬,1000rpm高速搅拌10min即可。
户外变压器用抗紫外线密封垫的制备方法,包括以下步骤:
(1)将丁苯橡胶、SEBS、邻苯二甲酸二辛酯、磷酸三苯甲酯、氧化镁、炭黑N220、复合填料放入开炼机中,在辊温为50℃下混炼3min;然后加入氯丁橡胶、30号机油、氧化锌、硬脂酸、不溶性硫磺、二甲基丙烯酸二甘醇酯、纳米氮化铝、纳米重晶石,在辊温为80℃下混炼6min;辊温降至55℃时,再加入其余原料,混炼3min,混合均匀后薄通8次,冷却至常温并停放24h,出片;
(2)将片料置于模具中,用平板硫化机中在185℃下加压硫化7min,成型脱模后再于150℃下二次硫化3h,硫化完成后制品经检验合格、修整毛边后即为成品。
本实施例制得的密封垫物理性能如下:
Figure BDA0000377525370000031

Claims (2)

1.一种户外变压器用抗紫外线密封垫,其特征在于,由以下重量份的原料制成:氯丁橡胶(CR121)65-85、丁苯橡胶(SBR1712)25-35、SEBS 5-10、邻苯二甲酸二辛酯10-15、磷酸三苯甲酯 8-12、30号机油10-15、氧化锌3-5、氧化镁2-4、硬脂酸1-2、炭黑N220 20-30、不溶性硫磺 2-3、二甲基丙烯酸二甘醇酯3-4、纳米氮化铝 5-10、滑石粉 10-15、纳米重晶石4-8、复合填料 3-5、防老剂264 1-2、防老剂MBZ 0.5-1、促进剂DZ 1-2、紫外线吸收剂UV-9 1-2;
所述复合填料的制备方法如下:a、按重量比3-5:2-3:1称取硅灰石、叶腊石、凹凸棒石混合均匀,490-520℃煅烧3-5h,冷却至常温后放入浓度为15-20%的盐酸溶液中浸泡2-3h,过滤,将上述矿石混合物用蒸馏水洗涤至中性,烘干,粉碎,过300-400目筛;b、过筛后的粉末中加入0.5-1%的异丙基二硬脂酰氧基铝酸酯、2-3%的玉石粉、1-2%的纳米硼化硅、3-5%的季戊四醇硬脂酸酯,1000-1500rpm高速研磨20-30min,再加入5-8%的腰果壳油、1-2%的聚四氟乙烯微粉、2-3%的树木灰烬,500-1000rpm高速搅拌10-15min即可。
2.如权利要求1所述的户外变压器用抗紫外线密封垫的制备方法,其特征在于包括以下步骤:
将丁苯橡胶、SEBS、邻苯二甲酸二辛酯、磷酸三苯甲酯、氧化镁、炭黑N220、复合填料放入开炼机中,在辊温为40-50℃下混炼3-5min;然后加入氯丁橡胶、30号机油、氧化锌、硬脂酸、不溶性硫磺、二甲基丙烯酸二甘醇酯、纳米氮化铝、纳米重晶石,在辊温为75-85℃下混炼4-8min;辊温降至50-55℃时,再加入其余原料,混炼3-4min,混合均匀后薄通6-8次,冷却至常温并停放22-24h,出片;
(2)将片料置于模具中,用平板硫化机中在170-190℃下加压硫化5-10min,成型脱模后再于140-160℃下二次硫化2-4h,硫化完成后制品经检验合格、修整毛边后即为成品。
CN201310399747.4A 2013-09-05 2013-09-05 一种户外变压器用抗紫外线密封垫及其制备方法 Pending CN103509216A (zh)