CN103497456A - 改性pvdc膜材料及其制备方法 - Google Patents
改性pvdc膜材料及其制备方法 Download PDFInfo
- Publication number
- CN103497456A CN103497456A CN201310391978.0A CN201310391978A CN103497456A CN 103497456 A CN103497456 A CN 103497456A CN 201310391978 A CN201310391978 A CN 201310391978A CN 103497456 A CN103497456 A CN 103497456A
- Authority
- CN
- China
- Prior art keywords
- parts
- nisin
- edta
- polypropylene
- film material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
改性PVDC膜材料及其制备方法，改性PVDC膜材料包括如下质量份数的原料：聚偏二氯乙烯60-70份、聚丙烯20-28份、nisin5-8份、乙二胺四乙酸0.5-1份、马来酸酐接枝聚乙烯5-10份。本发明将nisin和EDTA复配作为抗菌剂，与聚偏二氯乙烯、聚丙烯、马来酸酐接枝聚乙烯共同作用，制备出具有优异阻隔性和抗菌性的改性PVDC保鲜膜，48h后检测，其抗菌性可达100%，氧气透过率可达0.7%，水蒸气透过率可达0.1%，特别适合肉类熟食的长时间保鲜。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种改性PVDC膜材料及其制备方法。
背景技术
PVDC是以偏二氯乙烯为主要成分的共聚物，具有优异的耐燃性、耐腐蚀性和阻隔性，被广泛应用于食品药品包装领域，但是纯PVDC不易加工成型，且其抗菌性能仍有待改善。PP，即聚丙烯，是由丙烯聚合而制得的一种热塑性树脂，是无毒、无臭、无味的乳白色高结晶的聚合物，是目前所有塑料中最轻的品种之一，水稳定性良好，具有优异的抗弯曲疲劳性，良好的耐热性、化学稳定性和电学性能，可直接用于食品包装领域。
目前将nisin与EDTA复配作为抗菌剂应用于PVDC膜领域的报道甚少。
发明内容
本发明的目的在于克服现有技术的不足而提供一种改性PVDC膜材料及其制备方法，本发明成品具有优异的阻隔性和抗菌性，且对人体和环境友好，特别适用于肉类熟食的保鲜。
本发明的技术方案：
改性PVDC膜材料，包括如下质量份数的原料：聚偏二氯乙烯60-70份、聚丙烯20-28份、nisin 5-8份、乙二胺四乙酸0.5-1份、马来酸酐接枝聚乙烯5-10份。
所述的改性PVDC膜材料，包括如下质量份数的原料：聚偏二氯乙烯66份、聚丙烯25份、nisin 6份、乙二胺四乙酸0.8份、马来酸酐接枝聚乙烯7份。
改性PVDC膜材料的制备方法：将nisin和乙二胺四乙酸粉碎至1000目，置于高速混合机中混合10-20min，依次加入聚偏二氯乙烯、聚丙烯、马来酸酐接枝聚乙烯，于45-50℃下混合20-30min，后经挤出成型即可得改性PVDC膜材料。
有益效果：本发明将nisin和EDTA复配作为抗菌剂，与聚偏二氯乙烯、聚丙烯、马来酸酐接枝聚乙烯共同作用，制备出具有优异阻隔性和抗菌性的改性PVDC保鲜膜，48h后检测，其抗菌性可达100%，氧气透过率可达0.7%，水蒸气透过率可达0.1%，特别适合肉类熟食的长时间保鲜。
具体实施方式
本发明所述nisin购自兰州伟日生物工程有限公司。
下面结合实施例对本发明作进一步的详细描述。
实施例1
改性PVDC膜材料，包括如下质量份数的原料：聚偏二氯乙烯60份、聚丙烯20份、nisin 5份、乙二胺四乙酸0.5份、马来酸酐接枝聚乙烯5份。
本实施例制备方法：将nisin和乙二胺四乙酸粉碎至1000目，置于高速混合机中混合10min，依次加入聚偏二氯乙烯、聚丙烯、马来酸酐接枝聚乙烯，于45℃下混合20min，后经挤出成型即可得改性PVDC膜材料。
实施例2
改性PVDC膜材料，包括如下质量份数的原料：聚偏二氯乙烯70份、聚丙烯28份、nisin 8份、乙二胺四乙酸1份、马来酸酐接枝聚乙烯10份。
本实施例制备方法：将nisin和乙二胺四乙酸粉碎至1000目，置于高速混合机中混合20min，依次加入聚偏二氯乙烯、聚丙烯、马来酸酐接枝聚乙烯，于50℃下混合30min，后经挤出成型即可得改性PVDC膜材料。
实施例3
改性PVDC膜材料，包括如下质量份数的原料：聚偏二氯乙烯66份、聚丙烯25份、nisin 6份、乙二胺四乙酸0.8份、马来酸酐接枝聚乙烯7份。
本实施例制备方法：将nisin和乙二胺四乙酸粉碎至1000目，置于高速混合机中混合15min，依次加入聚偏二氯乙烯、聚丙烯、马来酸酐接枝聚乙烯，于45℃下混合30min，后经挤出成型即可得改性PVDC膜材料。
将实施例1-3所得材料进行性能测试，水蒸气透过率：40℃，相对湿度100%RH；氧气透过率测：25℃，80%RH，48h后测试结果见下表1。
表1 测试数据
| 实施例1 | 实施例2 | 实施例3 | |
| 抗菌率，% | 100 | 100 | 100 |
| 水蒸气透过率，% | 0.11 | 0.1 | 0.14 |
| 氧气透过率，% | 0．9 | 0.7 | 0.8 |
由上表可见本发明成品具有良好的抗菌性和阻隔性，适用于食品的长期保鲜。
Claims (3)
1.改性PVDC膜材料，其特征在于，包括如下质量份数的原料：聚偏二氯乙烯60-70份、聚丙烯20-28份、nisin 5-8份、乙二胺四乙酸0.5-1份、马来酸酐接枝聚乙烯5-10份。
2.根据权利要求1所述的改性PVDC膜材料，其特征在于，包括如下质量份数的原料：聚偏二氯乙烯66份、聚丙烯25份、nisin 6份、乙二胺四乙酸0.8份、马来酸酐接枝聚乙烯7份。
3.如权利要求1所述的改性PVDC膜材料的制备方法，其特征在于，包括以下步骤：将nisin和乙二胺四乙酸粉碎至1000目，置于高速混合机中混合10-20min，依次加入聚偏二氯乙烯、聚丙烯、马来酸酐接枝聚乙烯，于45-50℃下混合20-30min，后经挤出成型即可得改性PVDC膜材料。