CN103467849A - 抗菌防霉pp/pet包装材料及其制备方法 - Google Patents
抗菌防霉pp/pet包装材料及其制备方法 Download PDFInfo
- Publication number
- CN103467849A CN103467849A CN2013103919066A CN201310391906A CN103467849A CN 103467849 A CN103467849 A CN 103467849A CN 2013103919066 A CN2013103919066 A CN 2013103919066A CN 201310391906 A CN201310391906 A CN 201310391906A CN 103467849 A CN103467849 A CN 103467849A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- parts
- pet
- polypropylene
- mouldproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
抗菌防霉PP/PET包装材料及其制备方法,抗菌防霉PP/PET包装材料包括如下质量份数的原料:聚丙烯40-45份、聚对苯二甲酸乙二醇酯22-25份、灵香草粉末5-15份、纳米二氧化钛2-4份、马来酸酐接枝聚丙烯5-7份。本发明通过将纯植物灵香草粉末和纳米二氧化钛复配作为PP/PET包装材料的抗菌防霉剂,与聚丙烯、聚对苯二甲酸乙二醇酯、马来酸酐接枝聚丙烯共同作用,使本发明包装材料具有显著的抗菌防霉效果,安全无毒,可广泛应用于水果、蔬菜、肉类等食品领域的包装。
Description
技术领域
本发明属于高分子材料技术领域,具体涉及一种抗菌防霉PP/PET包装材料及其制备方法。
背景技术
PP,即聚丙烯,是由丙烯聚合而制得的一种热塑性树脂,是无毒、无臭、无味的乳白色高结晶的聚合物,是目前所有塑料中最轻的品种之一,水稳定性良好,具有优异的抗弯曲疲劳性,良好的耐热性、化学稳定性和电学性能,可直接用于食品包装领域。PET,聚对苯二甲酸乙二醇酯,具有优良的热变形温度和弯曲强度,质优价廉,无毒环保,亦可直接用于食品的包装。
目前有诸多有关改性PP/PET包装材料的报道,其中已有其抗菌防霉方面的改性,但是主要通过添加化学抗菌剂和防霉剂或银离子抗菌剂来达到抗菌防霉效果,抗菌效果不理想。
发明内容
本发明的目的在于克服现有技术的不足而提供一种抗菌防霉PP/PET包装材料及其制备方法,本发明成品抗菌防霉效果优异,对人体和环境友好。
本发明的技术方案:
抗菌防霉PP/PET包装材料,包括如下质量份数的原料:聚丙烯40-45份、聚对苯二甲酸乙二醇酯22-25份、灵香草粉末5-15份、纳米二氧化钛2-4份、马来酸酐接枝聚丙烯5-7份。
所述灵香草粉末经40℃真空干燥3h,粒径为500-1000目。
所述的抗菌防霉PP/PET包装材料,包括如下质量份数的原料:聚丙烯42份、聚对苯二甲酸乙二醇酯23份、灵香草粉末11份、纳米二氧化钛3份、马来酸酐接枝聚丙烯6份。
抗菌防霉PP/PET包装材料的制备方法:按照质量配比称取各原料,将灵香草粉末和纳米二氧化钛于35℃下在高速混合机中共混10-15min,后依次加入聚丙烯、聚对苯二甲酸乙二醇酯、马来酸酐接枝聚丙烯于30℃下混合15-20min,得共混物,将共混物出料至双螺杆挤出机中于170-180℃下挤出造粒,即得抗菌防霉PP/PET包装材料。
有益效果:本发明通过将纯植物灵香草粉末和纳米二氧化钛复配作为PP/PET包装材料的抗菌防霉剂,与聚丙烯、聚对苯二甲酸乙二醇酯、马来酸酐接枝聚丙烯共同作用,使本发明包装材料具有显著的抗菌防霉效果,安全无毒,可广泛应用于水果、蔬菜、肉类等食品领域的包装。
具体实施方式
下面结合实施例对本发明作进一步的详细描述。
实施例1
抗菌防霉PP/PET包装材料,包括如下质量份数的原料:聚丙烯40份、聚对苯二甲酸乙二醇酯22份、灵香草粉末5份、纳米二氧化钛2份、马来酸酐接枝聚丙烯5份。
将灵香草粉碎,取500-700目之间的粉末,粉末经40℃真空干燥3h。
本实施例制备方法:按照质量配比称取各原料,将灵香草粉末和纳米二氧化钛于35℃下在高速混合机中共混10min,后依次加入聚丙烯、聚对苯二甲酸乙二醇酯、马来酸酐接枝聚丙烯于30℃下混合15min,得共混物,将共混物出料至双螺杆挤出机中于170℃下挤出造粒,即得抗菌防霉PP/PET包装材料。
实施例2
抗菌防霉PP/PET包装材料,包括如下质量份数的原料:聚丙烯45份、聚对苯二甲酸乙二醇酯25份、灵香草粉末15份、纳米二氧化钛4份、马来酸酐接枝聚丙烯7份。
将灵香草粉碎,取700-1000目之间的粉末,将粉末经40℃真空干燥3h。
本实施例制备方法:按照质量配比称取各原料,将灵香草粉末和纳米二氧化钛于35℃下在高速混合机中共混15min,后依次加入聚丙烯、聚对苯二甲酸乙二醇酯、马来酸酐接枝聚丙烯于30℃下混合20min,得共混物,将共混物出料至双螺杆挤出机中于180℃下挤出造粒,即得抗菌防霉PP/PET包装材料。
实施例3
抗菌防霉PP/PET包装材料,包括如下质量份数的原料:聚丙烯42份、聚对苯二甲酸乙二醇酯23份、灵香草粉末11份、纳米二氧化钛3份、马来酸酐接枝聚丙烯6份。
将灵香草粉碎,取粒径为500目的粉末,将粉末经40℃真空干燥3h。
本实施例制备方法:按照质量配比称取各原料,将灵香草粉末和纳米二氧化钛于35℃下在高速混合机中共混15min,后依次加入聚丙烯、聚对苯二甲酸乙二醇酯、马来酸酐接枝聚丙烯于30℃下混合20min,得共混物,将共混物出料至双螺杆挤出机中于180℃下挤出造粒,即得抗菌防霉PP/PET包装材料。
将实施例1-3所得材料进行性能测试,测试结果见下表1。
表1 测试数据
实施例1 | 实施例2 | 实施例3 | |
抗菌率,% | 99.99 | 100 | 100 |
抗霉菌率,% | 98.95 | 100 | 99.86 |
冲击强度,MPa | 42.6 | 50.5 | 48.6 |
由上表可见本发明成品具有良好的抗菌性和防霉性,且冲击强度较好。
Claims (4)
1.抗菌防霉PP/PET包装材料,其特征在于,包括如下质量份数的原料:聚丙烯40-45份、聚对苯二甲酸乙二醇酯22-25份、灵香草粉末5-15份、纳米二氧化钛2-4份、马来酸酐接枝聚丙烯5-7份。
2.根据权利要求1所述的抗菌防霉PP/PET包装材料,其特征在于,所述灵香草粉末经40℃真空干燥3h,粒径为500-1000目。
3.根据权利要求1所述的抗菌防霉PP/PET包装材料,其特征在于,包括如下质量份数的原料:聚丙烯42份、聚对苯二甲酸乙二醇酯23份、灵香草粉末11份、纳米二氧化钛3份、马来酸酐接枝聚丙烯6份。
4.如权利要求1所述的抗菌防霉PP/PET包装材料的制备方法,其特征在于,包括以下步骤:按照质量配比称取各原料,将灵香草粉末和纳米二氧化钛于35℃下在高速混合机中共混10-15min,后依次加入聚丙烯、聚对苯二甲酸乙二醇酯、马来酸酐接枝聚丙烯于30℃下混合15-20min,得共混物,将共混物出料至双螺杆挤出机中于170-180℃下挤出造粒,即得抗菌防霉PP/PET包装材料。