CN103496937A - 一种高强度导电混凝土 - Google Patents

一种高强度导电混凝土 Download PDF

Info

Publication number
CN103496937A
CN103496937A CN201310449632.1A CN201310449632A CN103496937A CN 103496937 A CN103496937 A CN 103496937A CN 201310449632 A CN201310449632 A CN 201310449632A CN 103496937 A CN103496937 A CN 103496937A
Authority
CN
China
Prior art keywords
conductive concrete
strength conductive
parts
concrete
strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310449632.1A
Other languages
English (en)
Inventor
黄国平
郭钢岭
谭文斌
徐海彬
徐文龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhangjiagang Shanmu New Material Technology Development Co Ltd
Original Assignee
Zhangjiagang Shanmu New Material Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhangjiagang Shanmu New Material Technology Development Co Ltd filed Critical Zhangjiagang Shanmu New Material Technology Development Co Ltd
Priority to CN201310449632.1A priority Critical patent/CN103496937A/zh
Publication of CN103496937A publication Critical patent/CN103496937A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度导电混凝土，其特征在于，所述高强度导电混凝土采用以下材料，按如下重量配比配置而成：胶凝材料20-40份；碳纳米管10-50份；丙烯乳酸液15-30份；炭黑2-20份；聚合物纤维2-3份。采用本方案使得混凝土在干燥条件下的电阻率可小于1.64Ω?m，抗折强度可达到9.0MPa，抗压强度可达到45MPa。

Description

一种高强度导电混凝土
技术领域
本发明涉及建筑材料领域，特别涉及一种高强度导电混凝土。
背景技术
普通的混凝土的电阻率较高，属于电的不良导体。而导电混凝土时再普通的混凝土中添加一定含量的导电组份材料，由胶凝材料、导电材料、介电骨料和水等组份，按一定的配比混合凝结而成。导电混凝土即具备结构材料的特点，又具有导电性和机敏特性，其在电工、工业防静电、建筑采暖等接地工程中有着非常重要的作用。
目前，用于配制导电混凝土的导电介质一般都有如下几类：石墨、钢渣、钢纤维、碳质骨科等，长期以来，导电混凝土的导电性能都是以牺牲其强度为代价来实现的。
发明内容
本发明目的是：提出一种高强度的导电混凝土，该导电混凝土不仅具备良好的导电性能，同时还具备良好的机械性能。
本发明解决其技术问题所采用的技术方案是：
一种高强度导电混凝土，其原料按重量份的配比如下：
胶凝材料 20-40份；
碳纳米管 10-50份；
丙烯乳酸液 15-30份；
炭黑 2-20份；
聚合物纤维 2-3份。
进一步，所述炭黑采用微米级炭黑。
进一步，所述碳纳米管的直径为50-80nm。
进一步，所述碳纳米管的长度为3-6nm。
进一步，所述胶凝材料采用以下原料按重量配比制成：水泥60-80份；粉煤灰10-30份；硅灰5-10份；微细石灰粉3-8份。
进一步，所述聚合物纤维采用以下原料按重量配比制成：聚乙烯醇纤维70-90份；聚丙烯纤维10-30份。
作为优选方案，所述碳纳米管为50份。
作为优选方案，所述丙烯乳酸液为20份。
本发明的有益效果是：采用本方案使得混凝土在干燥条件下的电阻率可小于1.64Ω•m，抗折强度可达到9.0MPa，抗压强度可达到45MPa。
具体实施方式
以下为本发明的较佳实施例。
实施例1：
一种高强度导电混凝土，其原料按重量份的配比如下：
胶凝材料 20份；
碳纳米管 50份；
丙烯乳酸液 20份；
炭黑 7份；
聚合物纤维 3份。
高强度导电混凝土制备方法如下：
将50份的碳纳米管、20份的丙烯乳酸液、7份炭黑和3份聚合物纤维3份混合，将其放置告诉搅拌机中充分搅拌，混合均匀后放入真空干燥箱，120℃干燥48小时，研磨成粉，最后再加入20份的胶凝材料以300r/min的转速搅拌20分钟，浇铸成膜，在标准养护条件下养护30天得到高强度导电混凝土。

Claims (8)

1.一种高强度导电混凝土，其特征在于，所述高强度导电混凝土采用以下材料，按如下重量配比配置而成：
胶凝材料 20-40份；
碳纳米管 10-50份；
丙烯乳酸液 15-30份；
炭黑 2-20份；
聚合物纤维 2-3份。
2.如权利要求1所述的一种高强度导电混凝土，其特征在于，所述炭黑采用微米级炭黑。
3.如权利要求2所述的一种高强度导电混凝土，其特征在于，所述碳纳米管的直径为50-80nm。
4.如权利要求3所述的一种高强度导电混凝土，其特征在于，所述碳纳米管的长度为3-6nm。
5.如权利要求1所述的一种高强度导电混凝土，其特征在于，所述胶凝材料采用以下原料按重量配比制成：水泥60-80份；粉煤灰10-30份；硅灰5-10份；微细石灰粉3-8份。
6.如权利要求1所述的一种高强度导电混凝土，其特征在于，所述聚合物纤维采用以下原料按重量配比制成：聚乙烯醇纤维70-90份；聚丙烯纤维10-30份。
7.如权利要求1所述的一种高强度导电混凝土，其特征在于，所述碳纳米管为50份。
8.如权利要求1所述的一种高强度导电混凝土，其特征在于，所述丙烯乳酸液为20份。
CN201310449632.1A 2013-09-29 2013-09-29 一种高强度导电混凝土 Pending CN103496937A (zh)