CN104058688B - 一种高粉煤灰掺量i型无机建筑保温砂浆 - Google Patents

一种高粉煤灰掺量i型无机建筑保温砂浆 Download PDF

Info

Publication number
CN104058688B
CN104058688B CN201410307196.9A CN201410307196A CN104058688B CN 104058688 B CN104058688 B CN 104058688B CN 201410307196 A CN201410307196 A CN 201410307196A CN 104058688 B CN104058688 B CN 104058688B
Authority
CN
China
Prior art keywords
mortar
parts
fly ash
type
high doping
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410307196.9A
Other languages
English (en)
Other versions
CN104058688A (zh
Inventor
丰曙霞
陈广立
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHENZHEN GANGCHUANG BUILDING MATERIAL CO Ltd
Original Assignee
Shandong Yingcai University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Yingcai University filed Critical Shandong Yingcai University
Priority to CN201410307196.9A priority Critical patent/CN104058688B/zh
Publication of CN104058688A publication Critical patent/CN104058688A/zh
Application granted granted Critical
Publication of CN104058688B publication Critical patent/CN104058688B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于建筑材料技术领域，具体涉及一种高粉煤灰掺量I型无机建筑保温砂浆。该高粉煤灰掺量I型无机建筑保温砂浆，其原料组成按质量配比为：P.O425水泥45-55份，二级粉煤灰45-55份，硫酸钠2.5-3.5份，灰钙粉10-15份，玻化微珠85-95份，羟丙基甲基纤维素醚0.2-0.4份，VAE可再分散性乳胶粉1-3份，聚丙烯纤维0.1-0.3份，松香类引气剂0.2-0.4份。其有益效果是：用粉煤灰取代45-55％的水泥，采用灰钙粉及硫酸钠激发粉煤灰活性，提高保温砂浆的力学性能；加入适量纤维素醚和可再分散乳胶粉改善砂浆的工作性能和粘结性能；提高其抗开裂性能；并降低其干密度及导热系数，提高保温隔热性能。

Description

一种高粉煤灰掺量I型无机建筑保温砂浆
技术领域
本发明属于建筑材料技术领域，具体涉及一种高粉煤灰掺量I型无机建筑保温砂浆。
背景技术
作为无机保温砂浆的典型代表，玻化微珠保温砂浆在围护结构内外保温上的应用迅速增加，其研制技术已受到广泛关注。相较于有机保温砂浆，玻化微珠无机保温砂浆在工作性、防火性、耐久性等方面有明显优势，但自重较大、保温隔热性能较差。由于玻化微珠骨料自身性能特点，现有技术制备的保温砂浆各项性能仅达到II型建筑保温砂浆标准，无法满足I型建筑保温砂浆技术标准中对于密度和导热系数的要求。相关研究结果表明，粉煤灰代替部分水泥用于无机保温砂浆中，可改善工作性、降低砂浆干密度、提高保温隔热性能，但对保温砂浆强度有不利影响。有研究者以砂浆抗压强度、粉煤灰单位强度因子为指标，研究了砂浆体系中粉煤灰的最佳掺量范围，认为粉煤灰在干混砂浆中的最佳掺量范围为20％-30％。
综上所述，出于对强度的考虑，粉煤灰在玻化微珠保温砂浆中的掺量一般不高于30％，大大限制了粉煤灰的利用率；同时由于骨料的自身特点，国内制备的玻化微珠无机保温砂浆均为II型建筑保温砂浆，干密度和导热系数较高，降低了无机保温砂浆的节能效果，限制了其应用。
发明内容
本发明为了弥补现有技术的缺陷，提供了一种各项性能均符合国家标准GBT20473-2006要求的粉煤灰掺量45％以上的I型无机建筑保温砂浆，以粉煤灰替代45％-55％水泥制备玻化微珠无机保温砂浆，解决无机保温砂浆的干密度和导热系数较高以及大掺量粉煤灰时保温砂浆力学性能不达标的问题。
本发明是通过如下技术方案实现的：
一种高粉煤灰掺量I型无机建筑保温砂浆，其原料组成按质量配比为：P.O425水泥45-55份，二级粉煤灰45-55份，硫酸钠2.5-3.5份，灰钙粉10-15份，玻化微珠85-95份，羟丙基甲基纤维素醚0.2-0.4份，VAE可再分散性乳胶粉1-3份，聚丙烯纤维0.1-0.3份，松香类引气剂0.2-0.4份。
本发明的有益效果是：1、用粉煤灰取代45-55％的水泥，采用灰钙粉及硫酸钠激发粉煤灰活性，提高保温砂浆的力学性能；2、以玻化微珠作为骨料制备无机保温砂浆，加入适量纤维素醚和可再分散乳胶粉改善砂浆的工作性能和粘结性能；3、加入适量聚丙烯纤维降低无机保温砂浆线性收缩率，提高其抗开裂性能；4、加入适量适量引气剂改善无机保温砂浆的工作性，并降低其干密度及导热系数，提高保温隔热性能，且各项性能优异：干密度250-270kg/m3，抗压强度0.30-0.40MPa，导热系数0.058-0.062W/(m·K)，线收缩率0.25％-0.28％。
具体实施方式
以下给出本发明的具体实施例，用来对本发明的构成进行进一步说明。
实施例1
本实施例的高粉煤灰掺量I型无机建筑保温砂浆，其原料组成按质量配比为：P.0425水泥45份，二级粉煤灰45份，硫酸钠2.5份，灰钙粉10份，玻化微珠85份，羟丙基甲基纤维素醚0.2份，VAE可再分散性乳胶粉1份，聚丙烯纤维0.1份，松香类引气剂0.2份。
实施例2
本实施例的高粉煤灰掺量I型无机建筑保温砂浆，其原料组成按质量配比为：P.0425水泥50份，二级粉煤灰50份，硫酸钠3份，灰钙粉13份，玻化微珠90份，羟丙基甲基纤维素醚0.3份，VAE可再分散性乳胶粉2份，聚丙烯纤维0.2份，松香类引气剂0.3份。
实施例3
本实施例的高粉煤灰掺量I型无机建筑保温砂浆，其原料组成按质量配比为：P.O425水泥55份，二级粉煤灰55份，硫酸钠3.5份，灰钙粉15份，玻化微珠95份，羟丙基甲基纤维素醚0.4份，VAE可再分散性乳胶粉3份，聚丙烯纤维0.3份，松香类引气剂0.4份。
随机选取上述实施例得到的高粉煤灰掺量I型无机建筑保温砂浆的原料组成质量配比进行正交试验性能测试，具体测试结果如以下表1和表2所示：
表1：
表2：
测试结果
本发明不局限于上述实施方式，任何人应得知在本发明的启示下作出的与本发明具有相同或相近的技术方案，均落入本发明的保护范围之内。
本发明未详细描述的技术均为公知技术。

Claims (1)

1.一种高粉煤灰掺量I型无机建筑保温砂浆，其特征在于，其原料组成按质量配比为：P.O425水泥55份，二级粉煤灰55份，硫酸钠3.5份，灰钙粉15份，玻化微珠95份，羟丙基甲基纤维素醚0.4份，VAE可再分散性乳胶粉2份，聚丙烯纤维0.2份，松香类引气剂0.4份。
CN201410307196.9A 2014-07-01 2014-07-01 一种高粉煤灰掺量i型无机建筑保温砂浆 Active CN104058688B (zh)