CN103496903A - Thermal mortar - Google Patents
Thermal mortar Download PDFInfo
- Publication number
- CN103496903A CN103496903A CN201310439067.0A CN201310439067A CN103496903A CN 103496903 A CN103496903 A CN 103496903A CN 201310439067 A CN201310439067 A CN 201310439067A CN 103496903 A CN103496903 A CN 103496903A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- raw material
- coal ash
- stirred
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses thermal mortar, which is prepared from the following raw materials in parts by weight: 350-380 parts of cement, 17-19 parts of calcined desulfurized gypsum powder, 6-8 parts of sisal fiber powder, 60-70 parts of vitrified microsphere aggregate, 18-22 parts of redispersible latex powder, 4-6 parts of wood fiber, 1-2 parts of calcium sulphate retarder, 2-4 parts of white alum, 1-2 parts of sodium tripolyphosphate, 10-16 parts of modified fly ash, 1.7-3.2 parts of sodium lignin sulfonate, and 1-2 parts of carboxymethylcellulose.
Description
Technical field
The present invention relates to the thermal insulation mortar field, is exactly a kind of thermal insulation mortar.
Background technology
Inorganic heat insulation mortar (glass bead fireproof heat insulating mortar; complex silicate aluminium thermal insulation mortar) be a kind of mortar material of the novel heat-preserving energy-saving for external rendering in buildings; using inorganic glass bead (claiming again closed-cell expanded perlite) as light skeletal, add the dry-mix formed by gelling material, anticrack additive and other stopping composition etc.There are antifreeze, the ageing-resistant excellent properties of energy-conserving profit waste, heat insulating, fire prevention and the cheap characteristics such as price, the market requirement is widely arranged.
Summary of the invention
The object of the present invention is to provide a kind of thermal insulation mortar.
Above-mentioned purpose realizes by following scheme:
A kind of thermal insulation mortar is characterized in that: it is that raw material by following weight parts makes:
Cement 350-380, calcining desulfurization gypsum powder 17-19, sisal fibers powder 6-8, glass bead aggregate 60-70, redispersable latex powder 18-22, wood fibre 4-6, calcium sulphate retarder 1-2, alum 2-4, tripoly phosphate sodium STPP 1-2, modified coal ash 10-16, sodium lignosulfonate 1.7-3.2, carboxymethyl cellulose 1-2;
Described modified coal ash is made by the raw material of following weight part:
Flyash 20-30, Pericarppium arachidis hypogaeae 4-6, aluminum oxide 1.5-2.5, rapeseed meal 10-12, clorafin 1-2, epoxy soybean oil 1-2, dioctyl maleate 1.2-2.3, aluminium hydroxide 8-10;
The preparation method of described modified coal ash is:
After flyash, Pericarppium arachidis hypogaeae are stirred, calcining 4-5 hour under 600-650 ℃, then, take out, soak 5-8 hour in the acetic acid solution that is 5-8% in concentration, then, after mixing with aluminium hydroxide, rapeseed meal, aluminum oxide, add in suitable quantity of water and grind, adding 10-15% hydrochloric acid soln tune PH is 4.4-5.2, ground slurry is to the 400-500 order, and the repeated hydrogenation sodium oxide is adjusted to neutrality, drying, the gained powder is mixed with other remaining component, ground and mixed evenly and get final product again.
Described a kind of thermal insulation mortar is characterized in that:
The preparation method is:
To calcine desulfurization gypsum powder, cement, redispersable latex powder, calcium sulphate retarder mixes by weight, stir 5-8 minute under 300-400 rev/min, take out, again with the residue whole raw material blendings after, 100-200 rev/min is at the uniform velocity stirred 10-20 minute, again the material three-roll grinder that is stirred is ground to 2-3 hour, after packing and get final product.
Beneficial effect of the present invention is: high insulating effect of the present invention, and preparation technology is simple, and ultimate compression strength is high.
Embodiment
A kind of thermal insulation mortar, it is that raw material by following weight kg makes:
Cement 380, calcining desulfurization gypsum powder 19, sisal fibers powder 8, glass bead aggregate 70, redispersable latex powder 22, wood fibre 6, calcium sulphate retarder 1, alum 2, tripoly phosphate sodium STPP 2, modified coal ash 16,
Sodium lignosulfonate 1.8, carboxymethyl cellulose 2;
Described modified coal ash is made by the raw material of following weight kg:
Flyash 28, Pericarppium arachidis hypogaeae 5, aluminum oxide 1.8, rapeseed meal 12, clorafin 2, epoxy soybean oil 1, dioctyl maleate 2.3, aluminium hydroxide 10;
The preparation method of described modified coal ash is:
After flyash, Pericarppium arachidis hypogaeae are stirred, under 650 ℃, calcining is 4 hours, then, take out, soak 8 hours in the acetic acid solution that is 8% in concentration, then, after mixing with aluminium hydroxide, rapeseed meal, aluminum oxide, add in suitable quantity of water and grind, adding 10% hydrochloric acid soln tune PH is 4.8, after ground slurry to 500 order, the repeated hydrogenation sodium oxide is adjusted to neutrality, drying, the gained powder is mixed with other remaining component, ground and mixed evenly and get final product again.
Described a kind of thermal insulation mortar,
The preparation method is:
To calcine desulfurization gypsum powder, cement, redispersable latex powder, calcium sulphate retarder by weight kg mix, under 400 rev/mins, stir 8 minutes, take out, again with the residue whole raw material blendings after, 200 rev/mins are at the uniform velocity stirred 15 minutes, again the material three-roll grinder that is stirred is ground 3 hours, after packing and get final product.
The products obtained therefrom test result is as follows:
Claims (2)
1. a thermal insulation mortar is characterized in that: it is that raw material by following weight parts makes:
Cement 350-380, calcining desulfurization gypsum powder 17-19, sisal fibers powder 6-8, glass bead aggregate 60-70, redispersable latex powder 18-22, wood fibre 4-6, calcium sulphate retarder 1-2, alum 2-4, tripoly phosphate sodium STPP 1-2, modified coal ash 10-16, sodium lignosulfonate 1.7-3.2, carboxymethyl cellulose 1-2;
Described modified coal ash is made by the raw material of following weight part:
Flyash 20-30, Pericarppium arachidis hypogaeae 4-6, aluminum oxide 1.5-2.5, rapeseed meal 10-12, clorafin 1-2, epoxy soybean oil 1-2, dioctyl maleate 1.2-2.3, aluminium hydroxide 8-10;
The preparation method of described modified coal ash is:
After flyash, Pericarppium arachidis hypogaeae are stirred, calcining 4-5 hour under 600-650 ℃, then, take out, soak 5-8 hour in the acetic acid solution that is 5-8% in concentration, then, after mixing with aluminium hydroxide, rapeseed meal, aluminum oxide, add in suitable quantity of water and grind, adding 10-15% hydrochloric acid soln tune PH is 4.4-5.2, ground slurry is to the 400-500 order, and the repeated hydrogenation sodium oxide is adjusted to neutrality, drying, the gained powder is mixed with other remaining component, ground and mixed evenly and get final product again.
2. a kind of thermal insulation mortar according to claim 1 is characterized in that:
The preparation method is:
To calcine desulfurization gypsum powder, cement, redispersable latex powder, calcium sulphate retarder mixes by weight, stir 5-8 minute under 300-400 rev/min, take out, again with the residue whole raw material blendings after, 100-200 rev/min is at the uniform velocity stirred 10-20 minute, again the material three-roll grinder that is stirred is ground to 2-3 hour, after packing and get final product.