CN103539391B - A kind of waterproof thermal insulation mortar - Google Patents

A kind of waterproof thermal insulation mortar Download PDF

Info

Publication number
CN103539391B
CN103539391B CN201310422991.8A CN201310422991A CN103539391B CN 103539391 B CN103539391 B CN 103539391B CN 201310422991 A CN201310422991 A CN 201310422991A CN 103539391 B CN103539391 B CN 103539391B
Authority
CN
China
Prior art keywords
powder
modification
jade
rock wool
thermal insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310422991.8A
Other languages
Chinese (zh)
Other versions
CN103539391A (en
Inventor
汪宗来
杨晓峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHIZHOU CHONGYUAN ENERGY-SAVING BUILDING MATERIALS Co Ltd
Original Assignee
CHIZHOU CHONGYUAN ENERGY-SAVING BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHIZHOU CHONGYUAN ENERGY-SAVING BUILDING MATERIALS Co Ltd filed Critical CHIZHOU CHONGYUAN ENERGY-SAVING BUILDING MATERIALS Co Ltd
Priority to CN201310422991.8A priority Critical patent/CN103539391B/en
Publication of CN103539391A publication Critical patent/CN103539391A/en
Application granted granted Critical
Publication of CN103539391B publication Critical patent/CN103539391B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of waterproof thermal insulation mortar; it is obtained by the raw material of following weight parts: cement 400-500, rock wool tankage 40-50, glass bead 110-120, modification jade powder 18-22, ether of cellulose 1-2, redispersable latex powder 18-24, waste glass powder 8-10, sodium lignosulfonate 1-2, length are nylon fiber 3-5, calcium powder 3-5, the Sodium hexametaphosphate 99 1-2 of 3-6mm; sodium lauryl sulphate 1-2, coarse colza meal 1-2, suitable quantity of water.

Description

A kind of waterproof thermal insulation mortar
Technical field
The present invention relates to thermal insulation mortar field, is exactly a kind of waterproof thermal insulation mortar.
Background technology
Inorganic heat insulation mortar (glass bead Fireproof thermal insulation mortar; complex silicate aluminium thermal insulation mortar) be a kind of novel heat-preserving energy-saving mortar material whitewashed for buildings inner-outer wall; using inorganic glass bead (also known as closed-cell expanded perlite) as light skeletal, add the dry-mix be made up of gelling material, anticrack additive and other stopping composition etc.There is the feature such as excellent properties and cheap price that energy-conserving profit waste, heat insulating, fire prevention are antifreeze, ageing-resistant, have the market requirement widely.
Summary of the invention
The object of the present invention is to provide a kind of waterproof thermal insulation mortar
Above-mentioned purpose is realized by following scheme:
A kind of waterproof thermal insulation mortar, is characterized in that: it is obtained by the raw material of following weight parts:
Cement 400-500, rock wool tankage 40-50, glass bead 110-120, modification jade powder 18-22, ether of cellulose 1-2, redispersable latex powder 18-24, waste glass powder 8-10, sodium lignosulfonate 1-2, length are nylon fiber 3-5, calcium powder 3-5, the Sodium hexametaphosphate 99 1-2 of 3-6mm, sodium lauryl sulphate 1-2, coarse colza meal 1-2, suitable quantity of water;
Described modification jade powder is made up of the raw material of following weight part:
Jade 10-15, lazurite 5-10, diatomite 3-5, silicon carbide 2-4, dimethyl tin oxide 1.2-2.3, silane coupling agent KH5800.5-1.2, rapeseed cake 1-2, dioctyl maleate 1.2-2.3;
The preparation method of described modification jade powder is:
After jade, lazurite fragmentation, cross 200-400 mesh sieve, after taking-up, at 700-750 DEG C, calcine 4-5 hour, taking out, is soak 8-12 hour in the hydrogen peroxide of 1-3% in concentration, takes out, deionized water wash, dry, abrasive dust, then mix with other surplus stock, stir 5-10 minute under 500-600r/min after, be incubated 8-10 minute at 80-90 DEG C in kneader after, take out, to obtain final product.
Described a kind of waterproof thermal insulation mortar, is characterized in that:
Preparation method is:
(1) getting rock wool tankage is soak 10-15 hour in the hydrochloric acid soln of 10-15% in concentration, take out, deionized water wash, dries, abrasive dust, cross 200-300 mesh sieve, add the attapulgite, the chitosan of 1-2%, the benzene emulsion of 3-5% that are equivalent to its weight 1-2% again, after mixing, granulation, balling-up particle diameter, at 0.5-1mm, obtains modification rock wool tankage particle for subsequent use;
(2) modification rock wool tankage particle, cement, glass bead, waste glass powder are mixed by weight; 3-5 minute is stirred under 300-400 rev/min; take out; again with residue whole raw material blending after; 80-90 rev/min is at the uniform velocity stirred 20-30 minute; the material three-roll grinder grinding 1-2 hour that will be stirred again, after packaging and get final product.
Beneficial effect of the present invention is: the thermal insulation mortar that the present invention produces, and there will not be burning, ftractures and the problem such as to come off, and waterproof durable, and the life-span is long, and use rock wool tankage, economize on resources, turn waste into wealth.
Embodiment
A kind of waterproof thermal insulation mortar, it is obtained by the raw material of following weight Kg:
Cement 480, rock wool tankage 50, glass bead 120, modification jade powder 22, ether of cellulose 2, redispersable latex powder 18, waste glass powder 10, sodium lignosulfonate 2, length are nylon fiber 5, calcium powder 3, the Sodium hexametaphosphate 99 2 of 3-6mm, sodium lauryl sulphate 2, coarse colza meal 2, suitable quantity of water;
Described modification jade powder is made up of the raw material of following weight kg:
Jade 15, lazurite 10, diatomite 3, silicon carbide 4, dimethyl tin oxide 1.8, silane coupling agent KH5800.7, rapeseed cake 1, dioctyl maleate 1.8;
The preparation method of described modification jade powder is:
After jade, lazurite fragmentation, cross 400 mesh sieves, calcine 5 hours at 750 DEG C after taking-up, take out, be soak 12 hours in the hydrogen peroxide of 3% in concentration, take out, deionized water wash, dry, abrasive dust, then mix with other surplus stock, stir under 600r/min after 5 minutes, be incubated 10 minutes at 90 DEG C in kneader after, take out, to obtain final product.
Described a kind of waterproof thermal insulation mortar, preparation method is:
(1) getting rock wool tankage is soak 12 hours in the hydrochloric acid soln of 15% in concentration, take out, deionized water wash, dries, abrasive dust, cross 200 mesh sieves, add the attapulgite, the chitosan of 2%, the benzene emulsion of 5% that are equivalent to its weight 1% again, after mixing, granulation, balling-up particle diameter, at 0.5-1mm, obtains modification rock wool tankage particle for subsequent use;
(2) by the kg mixing by weight ratio of modification rock wool tankage particle, cement, glass bead, waste glass powder; stir 5 minutes under 400 revs/min; take out; again with residue whole raw material blending after; 90 revs/min are at the uniform velocity stirred 20 minutes; again the material three-roll grinder be stirred is ground 2 hours, after packaging and get final product.
Products obtained therefrom test result is as follows:

Claims (1)

1. a waterproof thermal insulation mortar, it is characterized in that: it is obtained by the raw material of following weight parts: cement 400-500, rock wool tankage 40-50, glass bead 110-120, modification jade powder 18-22, ether of cellulose 1-2, redispersable latex powder 18-24, waste glass powder 8-10, sodium lignosulfonate 1-2, length are nylon fiber 3-5, calcium powder 3-5, the Sodium hexametaphosphate 99 1-2 of 3-6mm, sodium lauryl sulphate 1-2, coarse colza meal 1-2, suitable quantity of water; Described modification jade powder is made up of the raw material of following weight part: jade 10-15, lazurite 5-10, diatomite 3-5, silicon carbide 2-4, dimethyl tin oxide 1.2-2.3, silane coupling agent KH5800.5-1.2, rapeseed cake 1-2, dioctyl maleate 1.2-2.3; The preparation method of described modification jade powder is: after jade, lazurite fragmentation, crosses 200-400 mesh sieve, calcines 4-5 hour after taking-up at 700-750 DEG C, taking out, is soak 8-12 hour in the hydrogen peroxide of 1-3% in concentration, takes out, deionized water wash, dry, abrasive dust, then mix with other surplus stock, stir 5-10 minute under 500-600r/min after, be incubated 8-10 minute at 80-90 DEG C in kneader after, take out, to obtain final product;
Described a kind of waterproof thermal insulation mortar, preparation method is: (1) gets rock wool tankage is soak 10-15 hour in the hydrochloric acid soln of 10-15% in concentration, takes out, deionized water wash, dry, abrasive dust, crosses 200-300 mesh sieve, then adds the attapulgite, the chitosan of 1-2%, the benzene emulsion of 3-5% that are equivalent to its weight 1-2%, after mixing, granulation, balling-up particle diameter, at 0.5-1mm, obtains modification rock wool tankage particle for subsequent use; (2) modification rock wool tankage particle, cement, glass bead, waste glass powder are mixed by weight; 3-5 minute is stirred under 300-400 rev/min; take out; again with residue whole raw material blending after; 80-90 rev/min is at the uniform velocity stirred 20-30 minute; the material three-roll grinder grinding 1-2 hour that will be stirred again, after packaging and get final product.
CN201310422991.8A 2013-09-16 2013-09-16 A kind of waterproof thermal insulation mortar Expired - Fee Related CN103539391B (en)