CN103483881A - 一种耐拉伸耐磨的地坪材料 - Google Patents
一种耐拉伸耐磨的地坪材料 Download PDFInfo
- Publication number
- CN103483881A CN103483881A CN201310366702.7A CN201310366702A CN103483881A CN 103483881 A CN103483881 A CN 103483881A CN 201310366702 A CN201310366702 A CN 201310366702A CN 103483881 A CN103483881 A CN 103483881A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor material
- stretch
- wear
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种耐拉伸耐磨的地坪材料，地坪材料由以下成分按照重量比组成：丁酸缩水甘油酯21～24份、碳化硅粉15～16份、二氧化锰粉为11～12份、间苯二酚甲醛树脂为2～3份、碳酸二正丁酯4～6份、石油磺酸钠为6～8份、环辛四烯为1～2份。制备得到的地坪材料具有良好的耐拉伸和耐磨的性能。
Description
技术领域
本发明涉及一种地坪材料，特别是涉及一种耐拉伸耐磨的地坪材料。
背景技术
净化车间的地坪材料选择范围较广，可以结合净化车间的用途来选择对应的材料。在一些机械产品相关的净化车间中，对净化车间的地坪材料的耐磨性有很高的要求，具备了良好的耐磨性才能保证车间的长期稳定使用。此外，如果地坪材料还具有相应的耐拉伸性能，可以更加扩大净化车间地坪材料的应用空间。
发明内容
要解决的技术问题：在净化车间中，地坪材料耐拉伸和耐磨性能差的问题。
技术方案：本发明公开了一种耐拉伸耐磨的地坪材料，地坪材料由以下成分按照重量比组成：丁酸缩水甘油酯21～24份、碳化硅粉15～16份、二氧化锰粉为11～12份、间苯二酚甲醛树脂为2～3份、碳酸二正丁酯4～6份、石油磺酸钠为6～8份、环辛四烯为1～2份。本发明的地坪材料制备方法如下：取丁酸缩水甘油酯21～24kg、碳化硅粉15～16kg、二氧化锰粉为11～12kg、间苯二酚甲醛树脂为2～3kg、碳酸二正丁酯4～6kg、石油磺酸钠为6～8kg、环辛四烯为1～2kg。将搅拌容器温度调整为90℃，投入上述各成分，充分搅拌混匀，混匀后冷却，冷却至常温后得到耐拉伸耐磨地坪材料。
有益效果：制备得到的地坪材料具有良好的耐拉伸和耐磨的性能，地坪材料的拉伸强度可达35Mpa，地坪材料耐磨性能≤0.013g/cm2（750g，500r）。由于具备了良好的耐拉伸和耐磨效果，可以充分的应用在净化车间中。
具体实施方式
实施例1
取丁酸缩水甘油酯21kg、碳化硅粉16kg、二氧化锰粉为11kg、间苯二酚甲醛树脂为3kg、碳酸二正丁酯4kg、石油磺酸钠为6kg、环辛四烯为1kg。将搅拌容器温度调整为90℃，投入上述各成分，充分搅拌混匀，混匀后冷却，冷却至常温后得到耐拉伸耐磨地坪材料。
实施例2
制备方法同实施例1，本实施例中各成分含量为：丁酸缩水甘油酯23kg、碳化硅粉15kg、二氧化锰粉为12kg、间苯二酚甲醛树脂为2kg、碳酸二正丁酯5kg、石油磺酸钠为7kg、环辛四烯为2kg。
实施例3
制备方法同实施例1，本实施例中各成分含量为：丁酸缩水甘油酯24kg、碳化硅粉15kg、二氧化锰粉为11kg、间苯二酚甲醛树脂为3kg、碳酸二正丁酯6kg、石油磺酸钠为8kg、环辛四烯为1kg。
耐拉伸和耐磨性能测试
取实施例1、实施例2、实施例3的产品测定耐拉伸性能和耐磨性能，测试标准为GB/T
1040-1992和GB/T1768-1979。测试结果见下表。
从表中可以看出，制备得到的地坪材料具备了良好的耐拉伸和耐磨性能，可以广泛应用于净化车间中。
Claims (5)
1.一种耐拉伸耐磨的地坪材料，其特征在于地坪材料由以下成分按照重量比组成：丁酸缩水甘油酯21～24份、碳化硅粉15～16份、二氧化锰粉为11～12份、间苯二酚甲醛树脂为2～3份、碳酸二正丁酯4～6份、石油磺酸钠为6～8份、环辛四烯为1～2份。
2.根据权利要求1所述的一种耐拉伸耐磨的地坪材料，其特征在于地坪材料组成中丁酸缩水甘油酯为24份。
3.根据权利要求1所述的一种耐拉伸耐磨的地坪材料，其特征在于地坪材料组成中碳化硅为15份。
4.根据权利要求1所述的一种耐拉伸耐磨的地坪材料，其特征在于地坪材料组成中二氧化锰为12份。
5.根据权利要求1所述的一种耐拉伸耐磨的地坪材料，其特征在于地坪材料组成中间苯二酚甲醛树脂为3份。