CN103469605A - 一种抗紫外线织物的生产方法 - Google Patents

一种抗紫外线织物的生产方法 Download PDF

Info

Publication number
CN103469605A
CN103469605A CN2013104198021A CN201310419802A CN103469605A CN 103469605 A CN103469605 A CN 103469605A CN 2013104198021 A CN2013104198021 A CN 2013104198021A CN 201310419802 A CN201310419802 A CN 201310419802A CN 103469605 A CN103469605 A CN 103469605A
Authority
CN
China
Prior art keywords
ultraviolet
fabric
production method
capsule
ultraviolet absorbent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013104198021A
Other languages
English (en)
Other versions
CN103469605B (zh
Inventor
王斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yangxin Fengyun Home Clothing Co ltd
Original Assignee
JURONG CITY HOUBAI TOWN YINGRUI PRINT WORKS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JURONG CITY HOUBAI TOWN YINGRUI PRINT WORKS filed Critical JURONG CITY HOUBAI TOWN YINGRUI PRINT WORKS
Priority to CN201310419802.1A priority Critical patent/CN103469605B/zh
Publication of CN103469605A publication Critical patent/CN103469605A/zh
Application granted granted Critical
Publication of CN103469605B publication Critical patent/CN103469605B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗紫外线织物的生产方法，包括：（1）以高分子聚合物为囊衣，将紫外线吸收剂包于所述的高分子聚合物的囊芯，所述的高分子聚合物和紫外线吸收剂的质量比为1∶2-3；（2）将步骤（1）制备的紫外线吸收剂胶囊通过粘合剂和交联剂固定在织物上，所述的紫外线吸收剂胶囊与织物的质量比为2-3:15。本发明通过将紫外线吸收剂制成维胶囊的方式将其固定在织物上，使得紫外线吸收剂与织物的结合度牢固可靠，其紫外线屏蔽率可达到89%以上，且微胶囊的形式能够缓释紫外线吸收剂，因此能够达到长期、长效防紫外线的目的。

Description

一种抗紫外线织物的生产方法
技术领域
本发明涉及一种纤维织物的生产方法，尤其是涉及一种抗紫外线织物的生产方法，属于纺织工艺技术领域。
背景技术
纺织行业是中国的传统行业，在市场竞争日益激烈的情况下，纺织品的不断创新成为企业长久生存的关键因素，目前，纺织品的技术创新主要集中在新材料和功能性纺织品，尤其是纺织品的保健功能。
而我们知道，目前的纤维织物做成的衣服，均没有抗紫外线功能，在夏季，强烈的紫外线会对人体产生很大的伤害，因此，非常需要一种具有抗紫外线功能的衣物。
发明内容
为解决现有技术的不足，本发明的目的在于提供一种抗紫外线效果好、且兼具吸附功能的抗紫外线织物的生产方法。
为达到上述目的，本发明是通过以下的技术方案来实现的：
一种抗紫外线织物的生产方法，其特征在于，包括以下步骤：
（1）制备紫外线吸收剂胶囊：以高分子聚合物为囊衣，将紫外线吸收剂包于所述的高分子聚合物的囊芯，所述的高分子聚合物和紫外线吸收剂的质量比为1：2-3；
（2）制备抗紫外线织物：将步骤（1）制备的紫外线吸收剂胶囊通过粘合剂和交联剂固定在织物上，得到抗紫外线织物，所述的紫外线吸收剂胶囊与织物的质量比为2-3:15。
进一步，步骤（1）中所述的高分子聚合物为苯乙烯或丙烯酸酯。
且所述的紫外线吸收剂为纳米二氧化钛或纳米氧化锌。
其中，所述的纳米二氧化钛的粒径为0.05-0.08μm。而所述的纳米氧化锌的粒径为0.005-0.01μm。
更近一步，所述的粘合剂为丙烯酸酯粘合剂，其粘合效果好，粘合速度快，不需要另外浸胶，只需要涂刮在织物上，操作简单方便，且所述的粘合剂的加入量为织物质量的8-10%。
此外，所述的交联剂为乙二醛，且所述的交联剂的加入量为织物质量的6-8%。
本发明的有益效果是：本发明通过将紫外线吸收剂制成维胶囊的方式将其固定在织物上，使得紫外线吸收剂与织物的结合度牢固可靠，其紫外线屏蔽率可达到89%以上，且微胶囊的形式能够缓释紫外线吸收剂，因此能够达到长期、长效防紫外线的目的。
具体实施方式
以下结合具体实施例对本发明作具体的介绍。
本实施方式的实施例中所采用的纳米二氧化钛的粒径为0.05-0.08μm，纳米氧化锌的粒径为0.005-0.01μm，且所述的纤维的主体为粘胶纤维。
实施例1：
抗紫外线织物的生产方法，包括以下步骤：
（1）制备紫外线吸收剂胶囊：以高分子聚合物苯乙烯为囊衣，将紫外线吸收剂纳米二氧化钛包于所述的苯乙烯的囊芯，所述的苯乙烯和纳米二氧化钛的质量比为1：2；
（2）制备抗紫外线织物：将步骤（1）制备的紫外线吸收剂胶囊通过丙烯酸酯粘合剂和乙二醛交联剂固定在织物上，得到抗紫外线织物，所述的紫外线吸收剂胶囊与织物的质量比为2:15，其中，所述的丙烯酸酯粘合剂的加入量为织物质量的8%，而所述的乙二醛交联剂的加入量为织物质量的6%。
实施例2：
抗紫外线织物的生产方法，包括以下步骤：
（1）制备紫外线吸收剂胶囊：以高分子聚合物丙烯酸酯为囊衣，将紫外线吸收剂纳米氧化锌包于所述的丙烯酸酯的囊芯，所述的丙烯酸酯和纳米氧化锌的质量比为1：3；
（2）制备抗紫外线织物：将步骤（1）制备的紫外线吸收剂胶囊通过丙烯酸酯粘合剂和乙二醛交联剂固定在织物上，得到抗紫外线织物，所述的紫外线吸收剂胶囊与织物的质量比为3:15，其中，所述的丙烯酸酯粘合剂的加入量为织物质量的10%，而所述的乙二醛交联剂的加入量为织物质量的8%。
实施例3：
抗紫外线织物的生产方法，包括以下步骤：
（1）制备紫外线吸收剂胶囊：以高分子聚合物丙烯酸酯为囊衣，将紫外线吸收剂纳米二氧化钛包于所述的丙烯酸酯的囊芯，所述的丙烯酸酯和纳米二氧化钛的质量比为1：3；
（2）制备抗紫外线织物：将步骤（1）制备的紫外线吸收剂胶囊通过丙烯酸酯粘合剂和乙二醛交联剂固定在织物上，得到抗紫外线织物，所述的紫外线吸收剂胶囊与织物的质量比为3:15，其中，所述的丙烯酸酯粘合剂的加入量为织物质量的9%，而所述的乙二醛交联剂的加入量为织物质量的7%。
本发明按照上述实施例进行了说明，应当理解，上述实施例不以任何形式限定本发明，凡采用等同替换或等效变换方式所获得的技术方案，均落在本发明的保护范围之内。

Claims (7)

1.一种抗紫外线织物的生产方法，其特征在于，包括以下步骤：
（1）制备紫外线吸收剂胶囊：以高分子聚合物为囊衣，将紫外线吸收剂包于所述的高分子聚合物的囊芯，所述的高分子聚合物和紫外线吸收剂的质量比为1：2-3；
（2）制备抗紫外线织物：将步骤（1）制备的紫外线吸收剂胶囊通过粘合剂和交联剂固定在织物上，得到抗紫外线织物，所述的紫外线吸收剂胶囊与织物的质量比为2-3:15。
2.根据权利要求1所述的一种抗紫外线织物的生产方法，其特征在于，步骤（1）中所述的高分子聚合物为苯乙烯或丙烯酸酯。
3.根据权利要求1所述的一种抗紫外线织物的生产方法，其特征在于，所述的紫外线吸收剂为纳米二氧化钛或纳米氧化锌。
4.根据权利要求3所述的一种抗紫外线织物的生产方法，其特征在于，所述的纳米二氧化钛的粒径为0.05-0.08μm。
5.根据权利要求3所述的一种抗紫外线织物的生产方法，其特征在于，所述的纳米氧化锌的粒径为0.005-0.01μm。
6.根据权利要求1所述的一种抗紫外线织物的生产方法，其特征在于，所述的粘合剂为丙烯酸酯粘合剂，且所述的粘合剂的加入量为织物质量的8-10%。
7.根据权利要求1所述的一种抗紫外线织物的生产方法，其特征在于，所述的交联剂为乙二醛，且所述的交联剂的加入量为织物质量的6-8%。
CN201310419802.1A 2013-09-13 2013-09-13 一种抗紫外线织物的生产方法 Active CN103469605B (zh)