CN103468376A - 一种高效节能环保拉丝液 - Google Patents
一种高效节能环保拉丝液 Download PDFInfo
- Publication number
- CN103468376A CN103468376A CN2013103723883A CN201310372388A CN103468376A CN 103468376 A CN103468376 A CN 103468376A CN 2013103723883 A CN2013103723883 A CN 2013103723883A CN 201310372388 A CN201310372388 A CN 201310372388A CN 103468376 A CN103468376 A CN 103468376A
- Authority
- CN
- China
- Prior art keywords
- parts
- rev
- sodium
- minute
- stirring reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种高效节能环保拉丝液,由下列重量份的原料制成:去离子水1000、油酸3-4、硬脂酸2-3、失水山梨醇单油酸酯1-2、苯甲酸钠1-2、植酸1-2、硫酸铜1-2、氧化锌1-2、硫脲2-3、偏硼酸钠1-2、椰油酸单乙醇酰胺1-2、叔丁基过氧化氢1-2、改性氮化铝粉末2-3。
Description
技术领域
本发明涉及拉丝技术领域,是一种高效节能环保拉丝液及其制备方法。
背景技术
现有拉丝工艺中多采用润滑油作为拉丝介质,拉拔出的导线表面圆润、细腻、光滑、透亮、无杂物滞留,断丝率降低,产品质量大大提高。但是润滑油散热慢,损毁模具,影响产品质量,同时高温易引燃油品或使油品蒸发冒烟导致现场环境恶化。
发明内容
本发明的目的是提供一种高效节能环保拉丝液,具有稳定性高、传热速度快的特点。
本发明的技术方案如下:
一种高效节能环保拉丝液,其特征在于:由下列重量份的原料制成:去离子水1000、油酸3-4、硬脂酸2-3、失水山梨醇单油酸酯1-2、苯甲酸钠1-2、植酸1-2、硫酸铜1-2、氧化锌1-2、硫脲2-3、偏硼酸钠1-2、椰油酸单乙醇酰胺1-2、叔丁基过氧化氢1-2、改性氮化铝粉末2-3;
改性氮化铝粉末由下列重量份的原料制成:
三聚磷酸钠2.3-2.5、壳聚糖1.8-2.8、过硫酸钠1.0-1.2、1-羟乙基-2-油基咪唑啉2.0-2.3、纳米氮化铝3.4-3.8、冬青油2.1-3.2、癸二酸二辛酯0.1-0.2,纳米碳0.5-0.8、十二烷基苯磺酸钠0.4-0.7、硅烷偶联剂KH580 1.2-1.3、羟甲基脲2.0-2.3、聚乙烯吡咯烷酮2.1-2.5、水50;
所述的改性氮化铝粉末的制备方法如下:将壳聚糖、1-羟乙基-2-油基咪唑啉溶解于水中,再加入过硫酸钠,50-60℃下600-800转/分搅拌反应20-30分钟,再加入冬青油、十二烷基苯磺酸钠,300-500转/分搅拌30-45分钟,然后,加入其它剩余原料,升温至70-80℃,500-700转/分搅拌反应40-50分钟,烘干,磨粉即得。
所述的高效节能环保拉丝液,其特征在于,制备方法包括以下步骤:
先将油酸、偏硼酸钠加入水中,加热至40-50℃,300-500转/分搅拌反应20-30分钟,然后,再加入改性氮化铝粉末、硫脲,于500-700转/分下搅拌10-15分钟后,滴加叔丁基过氧化氢,搅拌反应20-30分钟,再加入其余原料,升温至60-70℃,700-800转/分继续搅拌反应1-2小时,即得。
本发明的有益效果为:
本发明高效节能、有环保作用、产品无毒、无害。
具体实施方式
一种高效节能环保拉丝液,由下列重量份(KG)的原料制成:去离子水1000、油酸3.4、硬脂酸3、失水山梨醇单油酸酯1.2、苯甲酸钠2、植酸2、硫酸铜1、氧化锌1.4、硫脲3、偏硼酸钠1、椰油酸单乙醇酰胺2、叔丁基过氧化氢1、改性氮化铝粉末3;
改性氮化铝粉末由下列重量份的原料制成:
三聚磷酸钠2.3、壳聚糖2.5、过硫酸钠1.2、1-羟乙基-2-油基咪唑啉2.3、纳米氮化铝3.6、冬青油2.8、癸二酸二辛酯0.2,纳米碳0.8、十二烷基苯磺酸钠0.7、硅烷偶联剂KH580 1.3、羟甲基脲2.3、聚乙烯吡咯烷酮2.5、水50;
所述的改性氮化铝粉末的制备方法如下:将壳聚糖、1-羟乙基-2-油基咪唑啉溶解于水中,再加入过硫酸钠,60℃下800转/分搅拌反应30分钟,再加入冬青油、十二烷基苯磺酸钠,300转/分搅拌45分钟,然后,加入其它剩余原料,升温至80℃,600转/分搅拌反应50分钟,烘干,磨粉即得。
所述的高效节能环保拉丝液,制备方法包括以下步骤:
先将油酸、偏硼酸钠加入水中,加热至45℃,500转/分搅拌反应30分钟,然后,再加入改性氮化铝粉末、硫脲,于700转/分下搅拌15分钟后,滴加叔丁基过氧化氢,搅拌反应28分钟,再加入其余原料,升温至65℃,800转/分继续搅拌反应1.5小时,即得。
使用本实施例拉丝液,最高拉丝速度可达20m/sec。生产出的铜丝工序间防锈时间在7天以上;集中油池换油周期为3 年,单机油池换油周期为9个月,减少了废液处理和排放,保护了环境。
Claims (2)
1.一种高效节能环保拉丝液,其特征在于:由下列重量份的原料制成:去离子水1000、油酸3-4、硬脂酸2-3、失水山梨醇单油酸酯1-2、苯甲酸钠1-2、植酸1-2、硫酸铜1-2、氧化锌1-2、硫脲2-3、偏硼酸钠1-2、椰油酸单乙醇酰胺1-2、叔丁基过氧化氢1-2、改性氮化铝粉末2-3;
改性氮化铝粉末由下列重量份的原料制成:
三聚磷酸钠2.3-2.5、壳聚糖1.8-2.8、过硫酸钠1.0-1.2、1-羟乙基-2-油基咪唑啉2.0-2.3、纳米氮化铝3.4-3.8、冬青油2.1-3.2、癸二酸二辛酯0.1-0.2,纳米碳0.5-0.8、十二烷基苯磺酸钠0.4-0.7、硅烷偶联剂KH580 1.2-1.3、羟甲基脲2.0-2.3、聚乙烯吡咯烷酮2.1-2.5、水50;
所述的改性氮化铝粉末的制备方法如下:将壳聚糖、1-羟乙基-2-油基咪唑啉溶解于水中,再加入过硫酸钠,50-60℃下600-800转/分搅拌反应20-30分钟,再加入冬青油、十二烷基苯磺酸钠,300-500转/分搅拌30-45分钟,然后,加入其它剩余原料,升温至70-80℃,500-700转/分搅拌反应40-50分钟,烘干,磨粉即得。
2.根据权利要求1所述的高效节能环保拉丝液,其特征在于,制备方法包括以下步骤:
先将油酸、偏硼酸钠加入水中,加热至40-50℃,300-500转/分搅拌反应20-30分钟,然后,再加入改性氮化铝粉末、硫脲,于500-700转/分下搅拌10-15分钟后,滴加叔丁基过氧化氢,搅拌反应20-30分钟,再加入其余原料,升温至60-70℃,700-800转/分继续搅拌反应1-2小时,即得。