CN103451568A - 高碳不锈钢叶轮轴不锈钢材料及其制造方法 - Google Patents

高碳不锈钢叶轮轴不锈钢材料及其制造方法 Download PDF

Info

Publication number
CN103451568A
CN103451568A CN2013103334372A CN201310333437A CN103451568A CN 103451568 A CN103451568 A CN 103451568A CN 2013103334372 A CN2013103334372 A CN 2013103334372A CN 201310333437 A CN201310333437 A CN 201310333437A CN 103451568 A CN103451568 A CN 103451568A
Authority
CN
China
Prior art keywords
stainless steel
slag
raw material
electroslag
carbon stainless
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103334372A
Other languages
English (en)
Inventor
何祥炎
许吉军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Sanlian Pump Industry Co Ltd
Original Assignee
Anhui Sanlian Pump Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Sanlian Pump Industry Co Ltd filed Critical Anhui Sanlian Pump Industry Co Ltd
Priority to CN2013103334372A priority Critical patent/CN103451568A/zh
Publication of CN103451568A publication Critical patent/CN103451568A/zh
Pending legal-status Critical Current

Abstract

一种高碳不锈钢叶轮轴不锈钢材料及其制造方法，其中含有下列重量百分比的元素成分：C0.3-0.4、Mn1.7-1.9、Ni1.0-1.2、Cr24.0-24.5、Mo8.0-8.4、W3.5-4.0、Cu1.5-1.7、Ba0.3-0.5、In1.2-1.4、Pd3.1-3.3、Si1.2-1.4、As0.3-0.5、S、P小于0.03、余量为铁。本发明的不锈钢既有高的强度、高的硬度及耐磨性，又有较强的耐腐蚀性能及淬透性。适合于水泵叶轮轴制造。

Description

高碳不锈钢叶轮轴不锈钢材料及其制造方法
技术领域
本发明属于冶金材料技术领域，具体是一种高碳不锈钢叶轮轴不锈钢材料及其制造方法。
背景技术
水泵是输送液体或使液体增压的机械。它将原动机的机械能或其他外部能量传送给液体，使液体能量增加，主要用来输送液体包括水、油、酸碱液、乳化液、悬乳液和液态金属等，也可输送液体、气体混合物以及含悬浮固体物的液体。水泵主要由泵壳、泵盖、泵轴、叶轮及密封系统组成。由于水泵的工作条件复恶劣杂、所以不同用途的水泵对部件的要求不同，包括有耐酸、耐碱、耐盐雾、耐热、耐高温等。因此，需要研究不同的不锈钢材料来满足现实的需要。
发明内容
本发明的目的是提供一种高碳不锈钢叶轮轴不锈钢材料及其制造方法。
本发明的技术方案如下：
一种高碳不锈钢叶轮轴不锈钢材料，其特征在于：其中含有下列重量百分比的元素成分：C0.3-0.4、Mn1.7-1.9、Ni1.0-1.2、Cr24.0-24.5、Mo8.0-8.4、W3.5-4.0、Cu1.5-1.7、Ba0.3-0.5、In1.2-1.4、Pd3.1-3.3、Si1.2-1.4、As0.3-0.5、S、P小于0.03、余量为铁。
所述的高碳不锈钢叶轮轴不锈钢材料的制造方法，包括熔炼、电渣重熔、锻造，其特征在于：
（1）、熔炼：按元素含量向真空感应炉中投放生铁、废钢及各元素原料，生铁、废钢二者的重量比为1：0.50-0.65，在1650-1680℃下熔炼熔化后，待熔化结束后，取样分析并调整，并脱氧造渣，待分析结果符合要求后，降低出钢温度至1530-1560℃，并浇注出钢至钢包，钢水浇注温度控制在1490-1520℃，得到电渣棒；
（2）、真空电弧重熔：先向电渣炉内加入电渣棒，装好结晶器，加好引弧剂，通电，引弧和加入熔渣，将熔渣熔化在电炉中，将电渣棒熔化，等结晶器钢液到设定区域后停电，自然冷却10-12小时后，脱模形成圆锭；
所述的熔渣由下列重量份的原料制成：
蛭石粉5-6、铝钒土3-4、叶腊石粉1-2、膨胀珍珠岩2-3、谷壳灰3-4、Bi2O32-3、二硼化钒4-5、硅烷偶联剂KH550 3-4；制备方法是将蛭石粉、铝钒土、叶腊石粉、膨胀珍珠岩在490-520℃下焙烧4-5小时，用12-15%氢氧化钠溶液洗涤，再用清水洗净，烘干，与其它原料混合，研磨成40-100μm的粉末即可；
（3）、锻造。
本发明的不锈钢既有高的强度、高的硬度及耐磨性，又有较强的耐腐蚀性能及淬透性。适合于水泵叶轮轴制造。
具体实施方式
一种高碳不锈钢叶轮轴不锈钢材料，其中含有下列重量百分比的元素成分：C0.3-0.4、Mn1.7-1.9、Ni1.0-1.2、Cr24.0-24.5、Mo8.0-8.4、W3.5-4.0、Cu1.5-1.7、Ba0.3-0.5、In1.2-1.4、Pd3.1-3.3、Si1.2-1.4、As0.3-0.5、S、P小于0.03、余量为铁。
所述的高碳不锈钢叶轮轴不锈钢材料的制造方法，包括熔炼、电渣重熔、锻造：
（1）、熔炼：按元素含量向真空感应炉中投放生铁、废钢及各元素原料，生铁、废钢二者的重量比为1：0.50-0.65，在1650-1680℃下熔炼熔化后，待熔化结束后，取样分析并调整，并脱氧造渣，待分析结果符合要求后，降低出钢温度至1530-1560℃，并浇注出钢至钢包，钢水浇注温度控制在1490-1520℃，得到电渣棒；
（2）、真空电弧重熔：先向电渣炉内加入电渣棒，装好结晶器，加好引弧剂，通电，引弧和加入熔渣，将熔渣熔化在电炉中，将电渣棒熔化，等结晶器钢液到设定区域后停电，自然冷却10-12小时后，脱模形成圆锭；
所述的熔渣由下列重量份（公斤）的原料制成：
蛭石粉6、铝钒土3、叶腊石粉2、膨胀珍珠岩2、谷壳灰4、Bi2O32、二硼化钒4、硅烷偶联剂KH550 3；制备方法是将蛭石粉、铝钒土、叶腊石粉、膨胀珍珠岩在490-520℃下焙烧4-5小时，用12-15%氢氧化钠溶液洗涤，再用清水洗净，烘干，与其它原料混合，研磨成40-100μm的粉末即可；
（3）、锻造：将钢锭加热至1050～1100℃，进行锻造开坯或锻造锻件，再将钢坯再加热至1050～1100℃，进行轧制，然后炉冷至450℃，空冷退火处理。
本发明熔渣的脱氧、脱硫、脱磷率在65-75%之间，去除不锈钢液中的夹杂物及使夹杂物变性效果好、净化钢液提高了钢的内部质量，铸件中的气孔度降低1-2度，得到有效的控制。
经检测，本发明不锈钢材料，其抗拉强度大于1290 MPa 、屈服强度≥1098Mpa；延伸率可以达到12％，硬度在59HRC 。另外，本发明的不锈钢材料耐热性能良好，而且其加工性能良好。进行盐雾试验（SWAAT 试验）。腐蚀试验时间设定为800 小时，材料表面没有无明显腐蚀坑。

Claims (2)

1.一种高碳不锈钢叶轮轴不锈钢材料，其特征在于：其中含有下列重量百分比的元素成分：C0.3-0.4、Mn1.7-1.9、Ni1.0-1.2、Cr24.0-24.5、Mo8.0-8.4、W3.5-4.0、Cu1.5-1.7、Ba0.3-0.5、In1.2-1.4、Pd3.1-3.3、Si1.2-1.4、As0.3-0.5、S、P小于0.03、余量为铁。
2.根据权利要求1所述的高碳不锈钢叶轮轴不锈钢材料的制造方法，包括熔炼、电渣重熔、锻造，其特征在于：
（1）、熔炼：按元素含量向真空感应炉中投放生铁、废钢及各元素原料，生铁、废钢二者的重量比为1：0.50-0.65，在1650-1680℃下熔炼熔化后，待熔化结束后，取样分析并调整，并脱氧造渣，待分析结果符合要求后，降低出钢温度至1530-1560℃，并浇注出钢至钢包，钢水浇注温度控制在1490-1520℃，得到电渣棒；
（2）、真空电弧重熔：先向电渣炉内加入电渣棒，装好结晶器，加好引弧剂，通电，引弧和加入熔渣，将熔渣熔化在电炉中，将电渣棒熔化，等结晶器钢液到设定区域后停电，自然冷却10-12小时后，脱模形成圆锭；
所述的熔渣由下列重量份的原料制成：
蛭石粉5-6、铝钒土3-4、叶腊石粉1-2、膨胀珍珠岩2-3、谷壳灰3-4、Bi2O32-3、二硼化钒4-5、硅烷偶联剂KH550 3-4；制备方法是将蛭石粉、铝钒土、叶腊石粉、膨胀珍珠岩在490-520℃下焙烧4-5小时，用12-15%氢氧化钠溶液洗涤，再用清水洗净，烘干，与其它原料混合，研磨成40-100μm的粉末即可；
（3）、锻造。
CN2013103334372A 2013-08-02 2013-08-02 高碳不锈钢叶轮轴不锈钢材料及其制造方法 Pending CN103451568A (zh)