CN103450424A - 磷改性酚醛树脂及其制备方法 - Google Patents

磷改性酚醛树脂及其制备方法 Download PDF

Info

Publication number
CN103450424A
CN103450424A CN2013103190215A CN201310319021A CN103450424A CN 103450424 A CN103450424 A CN 103450424A CN 2013103190215 A CN2013103190215 A CN 2013103190215A CN 201310319021 A CN201310319021 A CN 201310319021A CN 103450424 A CN103450424 A CN 103450424A
Authority
CN
China
Prior art keywords
phenol
modified phenolic
phosphorus
reaction
phenolic resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103190215A
Other languages
English (en)
Inventor
关炽昌
刘涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI TENGXIAN TONGXUAN LIXIN CHEMICAL Co Ltd
Original Assignee
GUANGXI TENGXIAN TONGXUAN LIXIN CHEMICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI TENGXIAN TONGXUAN LIXIN CHEMICAL Co Ltd filed Critical GUANGXI TENGXIAN TONGXUAN LIXIN CHEMICAL Co Ltd
Priority to CN2013103190215A priority Critical patent/CN103450424A/zh
Publication of CN103450424A publication Critical patent/CN103450424A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新的化学结构式的磷改性酚醛树脂材料,同时公开此材料的制备方法:先将酚与甲醛在催化剂作用下缩聚成酚醛缩合中间体,然后再与一元醇、有机磷类杂环化合物在指定温度、时间和催化条件下进一步反应制成。本发明的磷改性酚醛树脂解决了以往完全依赖国外进口磷改性酚醛树脂的问题,提升了原有磷改性环氧树脂物耐热、粘接与剥离强度、良好的空间尺寸与优异的电性能与机械强度等物化性能指标,使该磷改性酚醛树脂应用于电子化学品领域的涂装性能更加优良。

Description

磷改性酚醛树脂及其制备方法
技术领域
本发明属于磷改性环氧树脂领域,具体涉及一种磷改性酚醛树脂及其制备方法。 
背景技术
目前,国内的磷改性树脂体系还仅局限于在磷改性环氧树脂体系,主要应用于以电子封塑涂料为主的涂装领域。近年来随着涂装领域的使用要求、应用性能的不断提升,对磷改性环氧树脂固化剂的物理、化学应用性能参数要求也随之提出了更高的要求,一般的磷改性环氧树脂已不能满足此电子涂装高端领域的应用要求,应市场的特殊需要,在美国于二十纪初,有些国际性的大化学公司开始为满足市场需要而探索将有机磷类杂环化合物如磷菲类、环状磷酸酯类原料应用于双酚A与甲醛改性树脂中,经几年与应用的结合探索,于近年研发生产出磷改性双酚A醛树脂,并将其成功应用于无卤阻燃电子领域。至此,随着我国涂装领域应用需求的日益提高,在此应用的高端领域就完全依赖此类磷改性酚醛树脂的进口,严重限制了我国涂装领域的发展,而且价格昂贵,各性能也有待提高。 
发明内容
本发明提供了一种新的磷改性酚醛树脂材料及其制备方法,解决了以往完全依赖国外进口磷改性酚醛树脂的问题。 
为了解决上述技术问题,本发明所采用的技术方案是: 
本发明的磷改性酚醛树脂的分子结构式为:
Figure DEST_PATH_763083DEST_PATH_IMAGE001
式中,-R1代表-C3H7、-C4H9、-C5H11;n取值0-3,-R2-代表
Figure 2013103190215100002DEST_PATH_DEST_PATH_IMAGE002
Figure DEST_PATH_90159DEST_PATH_IMAGE003
Figure 2013103190215100002DEST_PATH_DEST_PATH_IMAGE004
上述磷改性酚醛树脂的制备方法包括以下步骤:
A、将酚、甲醛和水加入反应容器中,用催化剂催化反应得到酚醛缩合体,反应温度为50℃~100℃,反应时间为1~5小时;所述酚与所述甲醛的摩尔比为1:2~3;所述催化剂占所述甲醛和所述酚的总质量的质量百分比为1%~5%;所述水占所述甲醛和所述酚的总质量的质量百分比为10%~15%; 
B、引入一元醇,用三氧化二铝和硫酸做催化剂进行以单边封端为主的醚化反应,反应温度为80℃~120℃,反应时间为4~6小时;所述酚与所述一元醇的摩尔比为1:2~5,所述三氧化二铝占所述酚的总质量的质量百分比为0.5%~1.5%,所述硫酸占所述酚的总质量的质量百分比为0.1%~0.8%;
C、引入9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物进行接枝反应得到本磷改性酚醛树脂,反应温度为100℃~160℃,反应时间9~11小时;所述9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物与所述酚的摩尔比为0.8~1.5:1;
其中,所述酚是对特辛基苯酚、壬基酚和双酚A三者的混合酚;
所述催化剂是酸性催化剂、碱性催化剂中的一种;
所述酸性催化剂是对甲苯磺酸、盐酸、硫酸、磷酸、草酸的一种;
所述碱性催化剂是氢氧化钠、氢氧化钾、氢氧化钙、三乙胺、氨水的一种;
所述一元醇是丁醇、丙醇、戊醇的一种。
由于采用上述技术方案,本发明具有如下有益效果: 
1、本发明解决了以往完全依赖国外进口磷改性酚醛树脂的问题,提升了原有磷改性环氧树脂物耐热、粘接与剥离强度、良好的空间尺寸与优异的电性能与机械强度等物化性能指标,使该磷改性酚醛树脂应用于电子化学品领域的涂装性能更加优良。
2、优化了传统纯酚醛树脂的生产条件,采用无溶剂的反应模式,减少环境污染。 
3、以对特辛基苯酚、壬基酚、双酚A为基体先制备出酚醛树脂,然后再将有机磷类杂环化合物如9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物和一元醇在设定的催化条件下进行羟甲基均匀封端,形成系列不同物化性能的磷改性酚醛树脂,其粘接性能、热稳定、耐老化、机械加工性、电气性能、成膜稳定性能等更加优良于进口的单一磷改性双酚A醛树脂产品。 
4、可根据不同厂家的电子涂装工艺要求,通过调整原料酚的配比、醇的种类等制定出更加适应不同使用要求的环氧固化剂磷改性酚醛树脂产品。 
具体实施方式
表1、表2、表3、表4为实施例1~实施例20中的反应原料组分及反应条件,其中实施例1~实施例20中所述的酚均为对特辛基苯酚、壬基酚、双酚A三者的混合酚。 
结合表1、表2、表3、表4给出的反应原料组分及反应条件按照下列制备步骤制备: 
A、分别取酚、甲醛和水加入到四口烧瓶中混合均匀,再加入催化剂混合均匀,将四口烧瓶放入电热套中加热进行缩合反应得到酚醛缩合体,降温后将其放出,分去残留水分; 
B、将步骤A得到的酚醛缩合体加回四口瓶中,加入一元醇混合均匀,再加入三氧化二铝和硫酸做催化剂,升温后保温回流脱水反应,对酚醛缩合体进行以单边封端为主的醚化反应;
C、向步骤B中加入9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物,升温后保温脱水接枝反应,将酚醛缩合体的另一边剩下的羟甲基封端接枝,得到本磷改性酚醛树脂。
根据表1、表2、表3、表4及上述制备步骤,实施例1~实施例20得到本磷改性酚醛树脂的化学结构式均匀为: 
Figure DEST_PATH_843351DEST_PATH_IMAGE001
式中,-R1代表-C3H7、-C4H9、-C5H11;n取值0-3,-R2-代表
Figure DEST_PATH_255878DEST_PATH_IMAGE005
Figure 2013103190215100002DEST_PATH_DEST_PATH_IMAGE006
Figure DEST_PATH_611773DEST_PATH_IMAGE004
本发明磷改性酚醛树脂可加入醚类溶剂,调整物料的流动性能、粘度、固含量及成膜速度,以便于包装、使用和施工。 
表1 
表2
Figure 2013103190215100002DEST_PATH_IMAGE002
表3
Figure 2013103190215100002DEST_PATH_IMAGE003
表4
表5、表6是在本发明磷改性酚醛树脂加入环氧类树脂后得到的固化剂进行的性能检测,并与国外两个公司产品的性能比较,结果如下: 
表5
Figure 2013103190215100002DEST_PATH_IMAGE005
表6
Figure 2013103190215100002DEST_PATH_IMAGE006

Claims (2)

1.一种磷改性酚醛树脂,其特征在于包括以下化学结构:
Figure 2013103190215100001DEST_PATH_DEST_PATH_IMAGE001
式中,-R1代表-C3H7、-C4H9、-C5H11;n取值0-3,-R2-代表
Figure DEST_PATH_750013DEST_PATH_IMAGE002
Figure 2013103190215100001DEST_PATH_DEST_PATH_IMAGE003
2.一种磷改性酚醛树脂的制备方法,其特征在于:
所述磷改性酚醛树脂的化学结构式为:
Figure DEST_PATH_670881DEST_PATH_IMAGE001
式中,-R1代表-C3H7、-C4H9、-C5H11;n取值0-3,-R2-代表
Figure DEST_PATH_143451DEST_PATH_IMAGE002
Figure DEST_PATH_584796DEST_PATH_IMAGE003
Figure DEST_PATH_510027DEST_PATH_IMAGE004
所述磷改性酚醛树脂的制备包括如下步骤:
A、将酚、甲醛和水加入反应容器中,用催化剂催化反应得到酚醛缩合体,反应温度为50℃~100℃,反应时间为1~5小时;所述酚与所述甲醛的摩尔比为1:2~3;所述催化剂占所述甲醛和所述酚的总质量的质量百分比为1%~5%;所述水占所述甲醛和所述酚的总质量的质量百分比为10%~15%; 
B、引入一元醇,用三氧化二铝和硫酸做催化剂进行以单边封端为主的醚化反应,反应温度为80℃~120℃,反应时间为4~6小时;所述酚与所述一元醇的摩尔比为1:2~5,所述三氧化二铝占所述酚的总质量的质量百分比为0.5%~1.5%,所述硫酸占所述酚的总质量的质量百分比为0.1%~0.8%;
C、引入9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物进行接枝反应得到本磷改性酚醛树脂,反应温度为100℃~160℃,反应时间9~11小时;所述9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物与所述酚的摩尔比为0.8~1.5:1;
其中,所述酚是对特辛基苯酚、壬基酚和双酚A三者的混合酚;
所述催化剂是酸性催化剂、碱性催化剂中的一种;
所述酸性催化剂是对甲苯磺酸、盐酸、硫酸、磷酸、草酸的一种;
所述碱性催化剂是氢氧化钠、氢氧化钾、氢氧化钙、三乙胺、氨水的一种;
所述一元醇是丁醇、丙醇、戊醇的一种。
CN2013103190215A 2013-07-27 2013-07-27 磷改性酚醛树脂及其制备方法 Pending CN103450424A (zh)