CN103437153B - Compound crystal variation modification method of ambari fiber - Google Patents
Compound crystal variation modification method of ambari fiber Download PDFInfo
- Publication number
- CN103437153B CN103437153B CN201310320270.6A CN201310320270A CN103437153B CN 103437153 B CN103437153 B CN 103437153B CN 201310320270 A CN201310320270 A CN 201310320270A CN 103437153 B CN103437153 B CN 103437153B
- Authority
- CN
- China
- Prior art keywords
- modification
- hemp fiber
- gombo hemp
- pressure
- compound crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a compound crystal variation modification method of ambari fiber. The compound crystal variation modification method comprises following steps: the ambari fiber is delivered into a sealed container; a modification medium is added; the pressure of the sealed container is increased to be as large as a modification pressure, and then is decreased instantaneously; the ambari fiber is subjected to vacuumization, high speed centrifugation spinning drafting and microwave radiation; and the modification medium is removed so as to obtain the compound crystal variation modified ambari fiber. Advantages of the compound crystal variation modification method are that, 1) after modification, fiber pores are enlarged, crystallinity is reduced, the ambari fiber is softened, and dimensional stability, softness and dyeing properties of the obtained products are improved; 2) instantaneous pressure release is employed, so that bulkiness and softness of the fiber are increased greatly; and fiber quality is further improved because of the combination of vacuumization, high speed centrifugation spinning drafting and microwave radiation, and modification efficiency is increased significantly.
Description
Technical field
The present invention relates to a kind of compound crystal variation modification method of gombo hemp fiber, a kind of by modification medium being boosted to modifier pressure, pressurize a period of time, then abrupt release pressure, then adopt vacuumize, high speed centrifugation rotates drawing-off and microwave combined effect remove the gombo hemp fiber composite brilliant change method of modifying of modification medium.
Background technology
Gombo hemp fiber is textile raw material important in natural fabric, is the sizable fiber of Young's modulus in natural fabric.It has the advantageous characteristic such as moisture absorption, ventilative, heat radiation, antibacterial, mildew-resistant, radiation proof, intensity are high, but also there is the defects such as hard, difficulty is spun, difficulty is knitted, difficulty contaminates, cause its wearability poor, not easily make high-end textile product, the overwhelming majority is low value-added product.
In order to change above-mentioned present situation, existing a variety of method of modifying, as physical modification method, chemical modification method and biological modified method.Physical modification method mainly comprises discharge technology modification, high steam dodges quick-fried modification, ultrasonic cavitation and microwave irradiation modification, liquefied ammonia are processing modified etc.Chemical modification method mainly comprises cellulose esters modification, cellulose ethers modification, graft modification with cellulose and cellulose crosslinked modification etc.Biological modified method mainly utilizes the process such as biology enzyme comes unstuck to fiber, polishing.
The method of modifying having formed now industrialization production both at home and abroad mainly contains the processing modified and alkali mercerized modification of liquefied ammonia.Liquid ammonia modified and alkali mercerized process has similar effect, as features such as natural crimp disappearance, cross section change circle, inner chamber diminish, but the residual alkali lye of alkali mercerized modification is not easily removed and fiber also can be caused to melt erosion and inhomogeneities, and topmost difference is that liquid ammonia modified effect is better than alkali mercerized modification.The domestic liquefied ammonia that utilizes is as modification medium, in the recycled fiber of conventional boosting-pressurize in closed container-again, the method for modification medium has certain effect to gombo hemp fiber, but the method is modification for once, swelling not thoroughly, degree of crystallinity reduce not obvious, dyeability do not have be improved significantly.
Summary of the invention
The object of this invention is to provide a kind of compound crystal variation modification method of gombo hemp fiber, a kind of by modification medium is pressurized to modifier pressure, and after pressurize a period of time, abrupt release pressure, then adopt vacuumize, high speed centrifugation rotates drawing-off and microwave combined effect and the gombo hemp fiber composite crystalline substance removing modification medium becomes method of modifying.
The compound crystal variation modification method of a kind of gombo hemp fiber of the present invention, that gombo hemp fiber is placed in closed container, be filled with modification medium, boost to modifier pressure, then abrupt release pressure, adopt again vacuumize, high speed centrifugation rotates drawing-off and microwave combined effect and removes modification medium, namely obtain composite crystal and become modification gombo hemp fiber.Its principle is: gombo hemp fiber is placed in closed container, and this closed container can movable sealing under under high pressure movable sealing and negative pressure, and zero leakage.By pressure balance topping up and non-equilibrium speed governing topping up, adjustable be filled with modification medium in closed container flow, time and temperature, thus the rate of change of the regulation and control pressure of modification, two-phase interface and above-mentioned parameter, and then the technological parameter such as the permeability of regulation and control liquid medium, infiltration rate and evaporation rate; Regulate the intermittent time of topping up and the dwell time of modifier pressure simultaneously; Above-mentioned technique can make the diffusion coefficient of modification medium improve, modification medium penetrates in fibr tissue preferably, hydrogen bond network between reconstruct cellulosic molecule, change the microstructure of fiber, aggravation cellulose macromolecule sub-chain motion, make, between cellulosic molecule, swelling action occurs, hole increases, degree of crystallinity reduces, and achieves the once regulation and control of fibrous crystal lattice structure.Again by high speed overflow, a large amount of liquid modified medium in abrupt release closed container, huge pressure reduction is produced instantaneously with outside in fibr tissue inside, form high speed quick-fried swollen, the diffusion coefficient of modification medium significantly improved, the hydrogen bond network between Perfect Reconstruction cellulosic molecule, between cellulosic molecule, swelling action is more thorough, hole increases obviously, and degree of crystallinity significantly reduces, and achieves the secondary regulation and control of fibrous crystal lattice structure.Last employing again vacuumizes, high speed centrifugation rotates drawing-off, microwave combined effect, improve mercerization effect, degree of crystallinity also decreases, the third time achieving fibrous crystal lattice structure regulates and controls and removes the modification medium in gombo hemp fiber simultaneously, significantly improve modification efficiency, namely complete described composite crystal and become modification.For the fiber of different-stiffness, different constituent, regulate the relevant parameter of fibrous crystal lattice structure three regulation and control, described composite crystal can be realized and become modification.Composite crystal becomes modified gombo hemp fiber, and to have softness excellent, wrinkle resistant nonshrink, durable fluffy, significantly improves the spinning of fiber, knits, metachromia energy, becomes remarkable natural fabric and newly spin material.
As preferred technical scheme:
The compound crystal variation modification method of a kind of gombo hemp fiber as above, the length of described gombo hemp fiber is 100 ~ 500mm, and fineness is 2.5 ~ 6tex.
The compound crystal variation modification method of a kind of gombo hemp fiber as above, by three regulation and control of fibrous crystal lattice structure, make swelling action between cellulosic molecule more thorough, hole obviously increases, degree of crystallinity obviously reduces, and dye-uptake improves, and COLOR FASTNESS improves, mercerising degree improves, and namely the finally de-liquid of employing high speed centrifugation rotation, heating using microwave and the modification medium vacuumized in parallel method of evaporating removal gombo hemp fiber complete described composite crystal and become modification.Compound crystal variation modification method described in employing, composite crystal can be made to become the microcosmic lattice of modification gombo hemp fiber compared with the microcosmic lattice of described gombo hemp fiber, and hole increases 10% ~ 20%, and degree of crystallinity reduces 15% ~ 32%; Described composite crystal becomes modification gombo hemp fiber compared with described gombo hemp fiber, and dye-uptake improves 30% ~ 50%, and COLOR FASTNESS improves 16% ~ 30%, and modification efficiency improves 15% ~ 30%.
The compound crystal variation modification method of a kind of gombo hemp fiber as above, modification medium is liquefied ammonia; Modification medium need possess following three point patterns: 1) have excellent diffusivity; 2) form a large amount of hydrogen bonds between energy and cellulose, the hydrogen bond network between reconstruct cellulosic molecule, improves cellulosic swelling behavior; 3) be easy to phase transformation regulation and control, be convenient to modification medium evaporation and reclaim.And liquefied ammonia has, and molecular weight is little, viscosity is little, surface tension is little, be easy to the special physical property such as phase transformation, these special natures make liquefied ammonia meet above-mentioned three features.
The compound crystal variation modification method of a kind of gombo hemp fiber as above, modifier pressure abrupt release, produces high pressure instantaneously poor, significantly can improve the diffusion coefficient of modification medium, gombo hemp fiber is produced fully swelling, is the critical process process that composite crystal becomes modification.To different gombo hemp fibers, the modifier pressure of requirement is different, and the speed of earth pressure release is different, and the pressure differential produced instantaneously is different, under the prerequisite not improving modifier pressure, obtain release pressure high as far as possible poor, modifier pressure should be made to drop to negative pressure.To gombo hemp fiber, modifier pressure needs to be more than or equal to 5MPa, can reach 9MPa.Therefore described modifier pressure should be 5 ~ 9MPa.
Poor for obtaining high as far as possible release pressure, modifier pressure should be made to drop to negative pressure, therefore the abrupt release of modifier pressure, require modifier pressure drop to instantaneously modifier pressure 1% and below.
The compound crystal variation modification method of a kind of gombo hemp fiber as above, in order to specification technological standards, described pressure refers to absolute pressure.
The crystalline substance of a kind of gombo hemp fiber as above becomes method of modifying, obtain excellent swelling effect, require that the time that pressure drops to 1% of modifier pressure from modifier pressure is less than or equal to 1.2 seconds, be advisable at 0.3 second ~ 1.2 seconds, therefore the moment of described release pressure is 0.3 second ~ 1.2 seconds, and the rate of pressure reduction of corresponding described release pressure is 5MPa/s ~ 30MPa/s.
The compound crystal variation modification method of a kind of gombo hemp fiber as above, for obtaining the good diffusivity of modification medium and best modified effect, and modifying process energy ezpenditure is minimum, need to regulate and control the flow of ammoniacal liquor in filling process, time and temperature, reach the object of regulation and control pressure, and then regulation and control medium permeability, infiltration rate, evaporation rate, evaporation rate and phase transition process.And boost process is one of most important influence factor, different boost process need be adopted to different fibers, a large number of experiments show that: gombo hemp fiber is applicable to boosting by the combination of parabola boosting and gap boosting, and rate of pressure rise k all meets relational expression
wherein t is pressure rising time, k
0for initial boost speed.To gombo hemp fiber, initial boost speed k
0be not less than 0.5MPa/min, can reach 2.5MPa/min, therefore described parabola initial boost speed is within the scope of 0.5MPa/min ~ 2.5MPa/min; During the boosting of gap, off time is not less than 5min, and off time is 5min ~ 20min, and each intermittently pressure rising time is 3min-5min.Interval initial boost speed k
0be not less than 0.5MPa/min, can 2.5MPa/min be reached, gap initial boost speed k
0for within the scope of 0.5MPa/min ~ 2.5MPa/min.
The compound crystal variation modification method of a kind of gombo hemp fiber as above, in modifying process, after boosting, pressurize a period of time is to make modification medium penetrate in structure of fibrous tissue more fully, better completes the hydrogen bond network reconstruct between cellulosic molecule.It is all necessary that this process becomes modification to the composite crystal of all fibres.To gombo hemp fiber, more than pressurize 5min after boosting, the dwell time is advisable at 5 ~ 30min, and therefore after described boosting, the dwell time is 5 ~ 30min.
The compound crystal variation modification method of a kind of gombo hemp fiber as above, removes modification medium while the third time lattice regulation and control of gombo hemp fiber.
Third time as above lattice be regulated to vacuumize, high speed centrifugation rotates drawing-off and microwave combined effect concurrent running or alternate run.Be evacuated to negative pressure and following; High speed centrifugation rotary speed to 350 ~ 800rpm, rotational time can reach 10min, radial drawing-off to 2 ~ 5mm; In heating using microwave, single modification still power is between 1kW ~ 20kW.Remove while the lattice regulation and control of described third time modification medium for vacuumizing, high speed centrifugation rotates de-liquid and heating using microwave concurrent running or alternate run.
Beneficial effect:
The present invention adopts the advantage of above technical scheme as follows:
1. the present invention reaches modification object by changing crystal structure.Modified fiber overcomes its native defect, and hole increases, degree of crystallinity reduces, fiber softening, improves the DIMENSIONAL STABILITY of product, flexibility, level-dyeing property and dyeability etc.
2. the present invention adopts the method for abrupt release pressure, makes the maximum swelling sudden strain of a muscle of modified fiber quick-fried, and softness is excellent, wrinkle resistant nonshrink, durable fluffy, significantly improves the spinning of fiber, knits, metachromia energy, becomes remarkable and newly spins material.
3. provide a kind of anhydrous, almost without dielectric loss, pollution-free, zero-emission, energy-conservation, efficient gombo hemp method for modifying fibers.
Detailed description of the invention
Below in conjunction with detailed description of the invention, set forth the present invention further.Should be understood that these embodiments are only not used in for illustration of the present invention to limit the scope of the invention.In addition should be understood that those skilled in the art can make various changes or modifications the present invention, and these equivalent form of values fall within the application's appended claims limited range equally after the content of having read the present invention's instruction.
Embodiment 1
The gombo hemp fiber that length is 100mm by a compound crystal variation modification method for gombo hemp fiber, fineness is 2.5tex is placed in closed container, is filled with liquefied ammonia, and the mode that boost in boosting and gap parabolically combines boosting, and rate of pressure rise k all meets relational expression
during parabola boosting, initial boost speed k
0for 0.5MPa/min, boost to modifier pressure 2Mpa; Again by the mode of gap boosting, initial boost speed k
0for 0.5MPa/min, off time is 5min, and each interval pressure rising time is 3min, to modifier pressure 5MPa, pressurize 5min, then in 1.2 seconds with the rate of pressure reduction abrupt release of 5MPa/s to 0.005Mpa.Finally adopt high speed centrifugation to rotate de-liquid, heating using microwave and vacuumize the modification medium in parallel method of evaporating removal material, namely obtaining composite crystal and become modification gombo hemp fiber.Wherein high speed centrifugation rotary speed is to 350rpm, and rotational time can reach 10min, and radial drawing-off is to 2mm; In heating using microwave, single modification still power is 1kW; Be evacuated to negative pressure and following.Described composite crystal becomes the microcosmic lattice of modification gombo hemp fiber compared with the microcosmic lattice of described gombo hemp fiber, and hole increases 10%, and degree of crystallinity reduces 15%; Described composite crystal becomes modification gombo hemp fiber compared with described gombo hemp fiber, and dye-uptake improves 30%, and COLOR FASTNESS improves 16%, and modification efficiency improves 15%.
Embodiment 2
The gombo hemp fiber that length is 300mm by a compound crystal variation modification method for gombo hemp fiber, fineness is 4tex is placed in closed container, is filled with liquefied ammonia, and the mode that boost in boosting and gap parabolically combines boosting, and rate of pressure rise k all meets relational expression
during parabola boosting, initial boost speed k
0for 0.8MPa/min, boost to modifier pressure 2Mpa; Again by the mode of gap boosting, initial boost speed k
0for 1MPa/min, off time is 6min, and each interval pressure rising time is 4min, to modifier pressure 6MPa, pressurize 10min, then in 1 second with the rate of pressure reduction abrupt release of 6MPa/s to 0.006Mpa.Finally adopt high speed centrifugation to rotate de-liquid, heating using microwave and vacuumize the modification medium in parallel method of evaporating removal material, namely obtaining composite crystal and become modification gombo hemp fiber.Wherein high speed centrifugation rotary speed is to 350rpm, and rotational time can reach 10min, and radial drawing-off is to 3mm; In heating using microwave, single modification still power is 5kW; Be evacuated to negative pressure and following.Described composite crystal becomes the microcosmic lattice of modification gombo hemp fiber compared with the microcosmic lattice of described gombo hemp fiber, and hole increases 17%, and degree of crystallinity reduces 22%; Described composite crystal becomes modification gombo hemp fiber compared with described gombo hemp fiber, and dye-uptake improves 38%, and COLOR FASTNESS improves 22%, and modification efficiency improves 16%.
Embodiment 3
The gombo hemp fiber that length is 450mm by a compound crystal variation modification method for gombo hemp fiber, fineness is 5tex is placed in closed container, is filled with liquefied ammonia, and the mode that boost in boosting and gap parabolically combines boosting, and rate of pressure rise k all meets relational expression
during parabola boosting, initial boost speed k
0for 1MPa/min, boost to modifier pressure 3Mpa; Again by the mode of gap boosting, initial boost speed k
0for 1.5MPa/min, off time is 5min, and each interval pressure rising time is 4min, to modifier pressure 8MPa, pressurize 5min, then in 0.5 second with the rate of pressure reduction abrupt release of 16MPa/s to 0.008Mpa.Finally adopt high speed centrifugation to rotate de-liquid, heating using microwave and vacuumize the modification medium in parallel method of evaporating removal material, namely obtaining composite crystal and become modification gombo hemp fiber.Wherein high speed centrifugation rotary speed is to 400rpm, and rotational time can reach 10min, and radial drawing-off is to 4mm; In heating using microwave, single modification still power is 15kW; Be evacuated to negative pressure and following.Described composite crystal becomes the microcosmic lattice of modification gombo hemp fiber compared with the microcosmic lattice of described gombo hemp fiber, and hole increases 19%, and degree of crystallinity reduces 22%; Described composite crystal becomes modification gombo hemp fiber compared with described gombo hemp fiber, and dye-uptake improves 34%, and COLOR FASTNESS improves 24%, and modification efficiency improves 15%.
Embodiment 4
The gombo hemp fiber that length is 500mm by a compound crystal variation modification method for gombo hemp fiber, fineness is 6tex is placed in closed container, is filled with liquefied ammonia, and the mode that boost in boosting and gap parabolically combines boosting, and rate of pressure rise k all meets relational expression
during parabola boosting, initial boost speed k
0for 2.5MPa/min, boost to modifier pressure 5Mpa; Again by the mode of gap boosting, initial boost speed k
0for 2.5MPa/min, off time is 20min, and each interval pressure rising time is 5min, to modifier pressure 9MPa, pressurize 30min, then in 0.3 second with the rate of pressure reduction abrupt release of 30MPa/s to 0.009Mpa.Finally adopt high speed centrifugation to rotate de-liquid, heating using microwave and vacuumize the modification medium in parallel method of evaporating removal material, namely obtaining composite crystal and become modification gombo hemp fiber.Wherein high speed centrifugation rotary speed is to 800rpm, and rotational time can reach 10min, and radial drawing-off is to 5mm; In heating using microwave, single modification still power is 20kW; Be evacuated to negative pressure and following.Described composite crystal becomes the microcosmic lattice of modification gombo hemp fiber compared with the microcosmic lattice of described gombo hemp fiber, and hole increases 20%, and degree of crystallinity reduces 32%; Described composite crystal becomes modification gombo hemp fiber compared with described gombo hemp fiber, and dye-uptake improves 50%, and COLOR FASTNESS improves 30%, and modification efficiency improves 30%.
Claims (10)
1. the compound crystal variation modification method of a gombo hemp fiber, it is characterized in that: gombo hemp fiber is placed in closed container, be filled with modification medium, boost to modifier pressure, then abrupt release pressure, adopt again vacuumize, high speed centrifugation rotates drawing-off and microwave combined effect and removes modification medium, namely obtain composite crystal and become modification gombo hemp fiber.
2. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 1, is characterized in that, the length of described gombo hemp fiber is 100 ~ 500mm, and fineness is 2.5 ~ 6tex.
3. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 1, it is characterized in that, described composite crystal becomes the microcosmic lattice of modification gombo hemp fiber compared with the microcosmic lattice of described gombo hemp fiber, and hole increases 10% ~ 20%, and degree of crystallinity reduces 15% ~ 32%; Described composite crystal becomes modification gombo hemp fiber compared with described gombo hemp fiber, and dye-uptake improves 30% ~ 50%, and COLOR FASTNESS improves 16% ~ 30%, and modification efficiency improves 15% ~ 30%.
4. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 1, is characterized in that, described modification medium is liquefied ammonia.
5. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 1, is characterized in that, described modifier pressure P is 5 ~ 9MPa, described abrupt release pressure be finger pressure drop to instantaneously described modifier pressure 1% and following.
6. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 5, is characterized in that, described pressure is absolute pressure.
7. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 1 or 5, is characterized in that, describedly refers to 0.3 second ~ 1.2 seconds instantaneously, and the rate of pressure reduction of described release pressure is 5MPa/s ~ 30MPa/s.
8. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 1, is characterized in that, described boosting is the combination of parabola boosting and gap boosting, and rate of pressure rise k all meets relational expression
wherein t is pressure rising time, k
0for initial boost speed; During parabola boosting, initial boost speed k
0within the scope of 0.5MPa/min ~ 2.5MPa/min; During the boosting of gap, off time is 5min ~ 20min, and each intermittently pressure rising time is 3 ~ 5min, initial boost speed k
0within the scope of 0.5MPa/min ~ 2.5MPa/min.
9. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 1, is characterized in that, keep 5min ~ 30min after boosting.
10. the compound crystal variation modification method of a kind of gombo hemp fiber according to claim 1, it is characterized in that, describedly to vacuumize, high speed centrifugation rotates drawing-off and microwave combinedly act as: vacuumize until negative pressure and following, high speed centrifugation rotary speed to 350 ~ 800rpm, radial drawing-off to 2 ~ 5mm, microwave, to vacuumize and high speed centrifugation rotates drawing-off synergy, concurrent running or alternate run, remove the modification medium in gombo hemp fiber.