CN103421985A - 一种无磁性、高强度的织构Cu基三元合金基带的制备方法 - Google Patents

一种无磁性、高强度的织构Cu基三元合金基带的制备方法 Download PDF

Info

Publication number
CN103421985A
CN103421985A CN201310412582XA CN201310412582A CN103421985A CN 103421985 A CN103421985 A CN 103421985A CN 201310412582X A CN201310412582X A CN 201310412582XA CN 201310412582 A CN201310412582 A CN 201310412582A CN 103421985 A CN103421985 A CN 103421985A
Authority
CN
China
Prior art keywords
base band
ternary alloy
alloy ingot
ingot casting
conducted
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310412582XA
Other languages
English (en)
Other versions
CN103421985B (zh
Inventor
刘志勇
张娜
宋桂林
杨炳方
常方高
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Normal University
Original Assignee
Henan Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henan Normal University filed Critical Henan Normal University
Priority to CN201310412582.XA priority Critical patent/CN103421985B/zh
Publication of CN103421985A publication Critical patent/CN103421985A/zh
Application granted granted Critical
Publication of CN103421985B publication Critical patent/CN103421985B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种无磁性、高强度的织构铜Cu基三元合金基带的制备方法，将铜Cu块及镍Ni块采用真空感应熔炼，获得CuNi二元合金铸锭，其中铜Cu的原子百分比为54%～60%，然后将Cu-Ni铸锭与矾V块置于电磁感应真空熔炼炉中熔炼获得Cu-Ni-V三元合金铸锭，矾V的原子百分含量为4%～9%；随后在850～950℃保温1～2h后热锻及热轧成坯锭，对热轧后的坯锭进行冷轧处理；最后将冷轧基带在Ar/H2混合气体保护下采用再结晶热处理，以10～15℃/min的升温速率升温至1000℃～1050℃保温30～60min。所得织构铜Cu基三元合金基带具有高的机械强度及锐利的立方织构，并且在液氮温区没有磁性。

Description

一种无磁性、高强度的织构Cu基三元合金基带的制备方法
技术领域
本发明涉及一种无磁性、高强度的强立方织构Cu基三元合金基带的制备方法，属于高温涂层导体织构金属基带制备技术领域。
背景技术
第二代钇系高温涂层超导带材由于比第一代铋系超导材料具有更优越的性能，因而有望在超导变压器、超导电机、超导限流器等领域实现规模化应用。在第二代高温涂层超导体的制备中，RABiTS技术即压延辅助双轴织构基带制备技术是一种常用的基带制备技术。作为涂层超导用的织构金属基带需要有强的立方织构来外延生长过渡层和超导层，而在超导带材连续沉积的过程中需要金属基带能够承受一定的应力，同时在涂层导体应用方面需要织构金属基带具有高的机械强度，因此为了满足涂层导体生产的需求并拓宽其应用范围需要金属基带具有强立方织构及更高的机械强度。尽管Ni-5at.%W合金基带已经商业化生产，但是由于其居里温度为330K，在液氮温区具有铁磁性，在输运交流电时会造成磁滞损耗，中国专利CN1408889A（公开日2003.4.9）公开了在Cu中加入重量百分含量小于40%的Ni元素，制备出无磁性的铜镍合金基带，但是由于无磁性二元CuNi合金基带的机械强度较低，不能满足涂层超导进一步广泛的应用；另外，中国专利CN101786352A（公开日2010.07.28）公开了一种层状的无磁性Cu基合金复合基带，该复合基带的机械强度与单层基带相比有明显的提高，但是其制备工艺复杂，成本较高，效率低，为了提高生产效率、节省成本，为产业化生产第二代涂层超导体用高性能织构金属基带奠定良好的基础，本发明的无磁性、高强度、强立方织构的Cu基三元合金基带具有重要的现实意义。
发明内容
本发明的目的是提供一种无磁性、高强度的立方织构铜Cu基合金基带的制备方法。本发明通过在利用熔炼方法制备的CuNi合金铸锭中再加入一定含量的矾V元素制备得到无磁性三元合金基带，提高基带的机械强度。
本发明所提供的一种无磁性、高强度、强立方织构的铜Cu基三元合金基带的制备方法，包括以下步骤：
步骤1：制备初始坯锭：
将纯度均为99.9%以上的铜Cu块及镍Ni块，按照铜Cu的原子百分含量在54%～60%之间进行配比，将配比后的混合材料置于电磁感应真空熔炼炉中熔炼，获得Cu-Ni二元合金铸锭，然后将Cu-Ni二元合金铸锭与纯度为99.95%以上的矾V块置于电磁感应真空熔炼炉中熔炼获得Cu-Ni-V三元合金铸锭，矾V的原子百分含量为4%～9%；随后将得到的Cu-Ni-V三元合金铸锭在850～950℃保温1～2h，然后进行热锻，热锻最后一道次之后将Cu-Ni-V三元合金铸锭放回热处理炉中保温30～60min，最后进行热轧处理，道次变形量为3%～10%，总变形量为30%～50%，得到初始坯锭；
步骤2：对初始坯锭进行冷轧：
对前述步骤1热轧后的初始坯锭进行道次变形量为10～15%、总变形量为99%的冷轧处理，获得厚度为50～60μm的合金基带；
步骤3：对前述冷轧后的合金基带进行再结晶退火：
将前述冷轧后的合金基带在Ar/H2的混合气体保护下进行再结晶热处理，其中氢气H2体积含量为4～5%，以10～15℃/min的升温速率升温至1000～1050℃使合金基带保温30～60min，最终得到具有双轴的织构铜Cu基三元合金基带。
本发明的核心技术是：将一次熔炼得到的Cu-Ni二元合金铸锭和一定量的矾V块再采用真空感应熔炼得到Cu-Ni-V三元合金铸锭。得到的Cu-Ni-V三元合金基带与传统的Cu-Ni二元合金基带相比提高了基带的机械强度，在Cu-Ni-V三元合金铸锭的制备过程中Cu-Ni合金铸锭采用了两次熔炼方法，可以使铸锭中的三种合金元素固溶均匀，更容易得到强立方织构，能满足高性能金属基带的要求。
附图说明
图1是实施例1中所得织构Cu基三元合金基带的（001）面和（111）面极图。
图2是实施例2中所得织构Cu基三元合金基带的（001）面和（111）面极图。
图3是实施例3中所得织构Cu基三元合金基带的（001）面和（111）面极图。
具体实施方式
实施例1
将纯度均为99.99%的铜Cu块及镍Ni块，按照铜镍原子百分比为55:45进行配比，将配比后的两种原材料置于电磁感应真空熔炼炉中熔炼，获得Cu-Ni二元合金铸锭，然后将Cu-Ni二元合金铸锭与纯度为99.95%的矾V块置于电磁感应真空熔炼炉中熔炼获得Cu-Ni-V三元合金铸锭，矾V的原子百分含量为4%；随后将得到的Cu-Ni-V三元合金铸锭在900℃保温1h后进行热锻，热锻完成的最后一道次之后放回热处理炉中保温30min，然后进行热轧处理，道次变形量为4%，总变形量为40%；将热轧后的坯锭进行道次变形量为10%、总变形量为99%的冷轧处理，获得厚度为50～60μm的合金基带；最后将冷轧基带在Ar/H2混合气体保护下进行再结晶热处理，其中H2体积含量为5%，以10℃/min的升温速率升温至1000℃保温40min，最终得到无磁性、高强度、强立方织构Cu基三元合金基带，该合金基带的屈服强度为240MPa，是商业化Ni5W合金基带的1.4倍。该合金基带的（001）面极图如图1所示。
实施例2
将纯度均为99.99%的铜Cu块及镍Ni块，按照铜镍原子百分比为57:43进行配比，将两种原材料置于电磁感应真空熔炼炉中熔炼，获得Cu-Ni二元合金铸锭，然后将Cu-Ni铸锭与纯度为99.95%的矾V块置于电磁感应真空熔炼炉中熔炼获得Cu-Ni-V三元合金铸锭，矾V的原子百分含量为7%；随后将得到的Cu-Ni-V三元合金铸锭在900℃保温1h后进行热锻，热锻完成的最后一道次之后放回热处理炉中保温30min，然后进行热轧处理，道次变形量为7%，总变形量为45%；将热轧后的坯锭进行道次变形量为12%、总变形量为99%的冷轧处理，获得厚度为50μm的合金基带；最后将冷轧基带在Ar/H2混合气体保护下进行再结晶热处理，其中H2体积含量为5%，以12℃/min的升温速率升温至1020℃保温40min，最终得到无磁性、高强度、强立方织构的Cu基三元合金基带，该合金基带的屈服强度为260MPa，是商业化Ni5W合金基带的1.5倍。该织构Cu基三元合金基带的（001）面极图如图2所示。
实施例3
将纯度均为99.99%的铜Cu块及镍Ni块，按照铜镍原子百分比为60:40进行配比，将两种原材料置于电磁感应真空熔炼炉中熔炼，获得Cu-Ni二元合金铸锭，然后将Cu-Ni铸锭与纯度为99.95%的V块置于电磁感应真空熔炼炉中熔炼获得Cu-Ni-V三元合金铸锭，矾V的原子百分含量为8%；随后将得到的三元合金铸锭在900℃保温1h后进行热锻，热锻完成的最后一道次之后放回热处理炉中保温30min，然后进行热轧处理，道次变形量为10%，总变形量为50%；将热轧后的坯锭进行道次变形量为15%、总变形量为99%的冷轧处理，获得厚度为60μm的合金基带；最后将冷轧基带在Ar/H2混合气体保护下进行再结晶热处理，其中H2体积含量为5%，以15℃/min的升温速率升温至1040℃保温40min，最终得到无磁性、高强度、强立方的织构Cu基三元合金基带，该合金基带的屈服强度为270MPa，是商业化Ni5W合金基带的1.6倍。该合金基带的（001）面极图如图3所示。

Claims (1)

1.一种无磁性、高强度的织构铜Cu基三元合金基带的制备方法，包括以下步骤：步骤1：制备初始坯锭：
将纯度为99.9%以上的铜Cu块及镍Ni块，按照铜Cu的原子百分含量在54%～60%之间进行配比，将配比后的混合材料置于电磁感应真空熔炼炉中熔炼，获得Cu-Ni二元合金铸锭，然后将所述Cu-Ni二元合金铸锭与纯度为99.95%以上的矾V块置于电磁感应真空熔炼炉中熔炼获得Cu-Ni-V三元合金铸锭，矾V的原子百分含量为4%～9%；随后将得到的所述Cu-Ni-V三元合金铸锭在850～950℃保温1～2h，然后进行热锻，热锻最后一道次之后将所述Cu-Ni-V三元合金铸锭放回热处理炉中保温30～60min，最后进行热轧处理，道次变形量为3%～10%，总变形量为30%～50%，得到所述初始坯锭；
步骤2：对所述初始坯锭进行冷轧：
对前述步骤1热轧后的初始坯锭进行道次变形量为10～15%、总变形量为99%的冷轧处理，获得厚度为50～60μm的合金基带；
步骤3：对前述冷轧后的合金基带进行再结晶退火：
将前述冷轧后的合金基带在Ar/H2的混合气体保护下进行再结晶热处理，其中氢气H2体积含量为4～5%，以10～15℃/min的升温速率升温至1000～1050℃使所述合金基带保温30～60min，最终得到具有双轴的所述织构铜Cu基三元合金基带。
CN201310412582.XA 2013-09-11 2013-09-11 一种无磁性、高强度的织构Cu基三元合金基带的制备方法 Expired - Fee Related CN103421985B (zh)