CN103409042A - 一种无溶剂环氧地坪漆及制造方法 - Google Patents
一种无溶剂环氧地坪漆及制造方法 Download PDFInfo
- Publication number
- CN103409042A CN103409042A CN2013102081314A CN201310208131A CN103409042A CN 103409042 A CN103409042 A CN 103409042A CN 2013102081314 A CN2013102081314 A CN 2013102081314A CN 201310208131 A CN201310208131 A CN 201310208131A CN 103409042 A CN103409042 A CN 103409042A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor paint
- solvent
- epoxy floor
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种无溶剂环氧地坪漆，由以下重量份数的原料组成：环氧树脂，85-100份；滑石粉，6-8份；活性稀释剂，11-15份；膨润土，0.8-1.2份；钛白粉，11-15份；硅微粉，115-125份；乙炔黑，0.07-0.085份；助剂：6-7份。本发明另公开了这种无溶剂环氧地坪漆的制造方法，将环氧树脂、滑石粉、活性稀释剂、膨润土、钛白粉、硅微粉、乙炔黑进行预混合之后，用高速分散机在2000转/分的转速下高速分散30分钟，而后用研磨机研磨分散，之后在其中搅拌加入助剂进行调色、调粘度，最后过滤其中的杂质得到成品。所述环氧地坪漆不含有挥发性有机溶剂，不会对人体健康造成伤害，由所述环氧地坪漆制成的地板，表面平整光洁，可满足较高的洁净度要求。
Description
技术领域
本发明涉及一种涂料，具体设计一种无溶剂环氧地坪漆及制造方法。
背景技术
现代工业技术的高度专业化、精度化给生产环境带来更高和多样化的要求。洁净化生产成为制造完善优质产品的必备条件，因此各种工业地坪的应用日益广泛。环氧地坪漆是一种高强度、耐磨损、美观的地板，具有无接缝、质地坚实、耐药品性佳、防腐、防尘、保养方便、维护费用低廉等优点，被广泛应用于电子厂、机械制造厂、食品厂、化工厂、停车场等表面涂装。但是，普通溶剂型环氧地坪漆在生产、施工和固化过程中会排放一定量的挥发性有机物，污染环境，损害人体健康，不符合环保理念。
发明内容
本发明主要解决的技术问题是提供一种无溶剂环氧地坪漆及制造方法，能够生产出无挥发性有机溶剂的、符合环保要求的环氧地坪漆。
为解决上述技术问题，本发明采用的一个技术方案是：
一种无溶剂环氧地坪漆，由以下重量份数的原料组成：环氧树脂，85-100份；滑石粉， 6-8份；活性稀释剂，11-15份；膨润土，0.8-1.2份；钛白粉，11-15份；硅微粉，115-125份；乙炔黑，0.07-0.085份；助剂： 6-7份。
在本发明一个较佳实施例中，所述的无溶剂环氧地坪漆，由以下重量份数的原料组成：环氧树脂，90份；滑石粉，7份；活性稀释剂，12.5份；膨润土，1份；钛白粉，12.5份；硅微粉，120.925份；乙炔黑，0.075份；助剂，6份。
在本发明一个较佳实施例中，所述的无溶剂环氧地坪漆中的环氧树脂为E-44环氧树脂。
在本发明一个较佳实施例中，所述的无溶剂环氧地坪漆中的活性稀释剂为环氧活性稀释剂SM-90。
在本发明一个较佳实施例中，所述的无溶剂环氧地坪漆中的的膨润土为801-B有机膨润土。
在本发明一个较佳实施例中，所述的无溶剂环氧地坪漆中的钛白粉为钛白粉R940。
本发明的另一目的是提供这种无溶剂环氧地坪漆的制造方法，将85-100份的环氧树脂、6-8份的滑石粉、11-15份的活性稀释剂、0.8-1.2份的膨润土、11-15份的钛白粉、115-125份的硅微粉、0.07-0.085份的乙炔黑进行预混合之后，用高速分散机在2000转/分的转速下高速分散30分钟，而后用研磨机研磨分散，之后在其中搅拌加入6-7份的助剂进行调色、调粘度，最后过滤其中的杂质得到成品。
在本发明一个较佳实施例中，将90份的环氧树脂、7份的滑石粉、12.5份的活性稀释剂、1份的膨润土、12.5份的钛白粉、120.925份的硅微粉、0.075份的乙炔黑进行预混合之后，用高速分散机在2000转/分的转速下高速分散30分钟，而后用研磨机研磨分散，之后在其中搅拌加入6份的助剂进行调色、调粘度，最后过滤其中的杂质得到成品。
本发明的有益效果是：
本发明无溶剂环氧地坪漆，由以下原料组成：环氧树脂、滑石粉、活性稀释剂、膨润土、钛白粉、硅微粉、乙炔黑和助剂。本发明与普通溶剂型环氧地坪漆相比，不含挥发性有机溶剂，避免了火灾事故的发生，施工毒性小，完全固化后无毒无味，不会对人体健康产生伤害，符合环保；由所述无溶剂环氧地坪漆制成的地板，表面平整光洁，可以满足较高的洁净度要求，与基层的粘结强度高，易清洗，不集聚灰尘、细菌，固体份高，一次成膜厚，且强度高、耐磨损、抗渗透、耐腐蚀，容易维修保养。本发明制造方法简单，易操作，无需特殊设备就可实现。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1：将90份的E-44环氧树脂、7份的滑石粉、12.5份的环氧活性稀释剂SM-90、1份的801-B有机膨润土、12.5份的钛白粉R940、120.925份的硅微粉、0.075份的乙炔黑进行预混合之后，用高速分散机在2000转/分的转速下高速分散30分钟，而后用研磨机研磨分散，之后在其中搅拌加入6份由分散剂、消泡剂组成的助剂进行调色、调粘度，最后过滤其中的杂质得到成品。
实施例2：将90份的E-44环氧树脂、8份的滑石粉、13份的环氧活性稀释剂SM-90、0.9份的801-B有机膨润土、11份的钛白粉R940、122.02份的硅微粉、0.08份的乙炔黑进行预混合之后，用高速分散机在2000转/分的转速下高速分散30分钟，而后用研磨机研磨分散，之后在其中搅拌加入5份由分散剂、消泡剂组成的助剂进行调色、调粘度，最后过滤其中的杂质得到成品。
实验重要指标结果见下表。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (8)
1.一种无溶剂环氧地坪漆，其特征在于，由以下重量份数的原料组成：
环氧树脂，85-100份；
滑石粉， 6-8份；
活性稀释剂，11-15份；
膨润土，0.8-1.2份；
钛白粉，11-15份；
硅微粉，115-125份；
乙炔黑，0.07-0.085份；
助剂： 6-7份。
2.根据权利要求1所述的无溶剂环氧地坪漆，其特征在于，由以下重量份数的原料组成：
环氧树脂，90份；
滑石粉，7份；
活性稀释剂，12.5份；
膨润土，1份；
钛白粉，12.5份；
硅微粉，120.925份；
乙炔黑，0.075份；
助剂，6份。
3.根据权利要求1或2所述的无溶剂环氧地坪漆，其特征在于，所述的环氧树脂为E-44环氧树脂。
4.根据权利要求1或2所述的无溶剂环氧地坪漆，其特征在于，所述的活性稀释剂为环氧活性稀释剂SM-90。
5.根据权利要求1或2所述的无溶剂环氧地坪漆，其特征在于，所述的膨润土为801-B有机膨润土。
6.根据权利要求1或2所述的无溶剂环氧地坪漆，其特征在于，所述的钛白粉为钛白粉R940。
7.一种无溶剂环氧地坪漆的制造方法，其特征是，将85-100份的环氧树脂、6-8份的滑石粉、11-15份的活性稀释剂、0.8-1.2份的膨润土、11-15份的钛白粉、115-125份的硅微粉、0.07-0.085份的乙炔黑进行预混合之后，用高速分散机在2000转/分的转速下高速分散30分钟，而后用研磨机研磨分散，之后在其中搅拌加入6-7份的助剂进行调色、调粘度，最后过滤其中的杂质得到成品。
8.根据权利要求7所述的无溶剂环氧地坪漆的制造方法，其特征是，将90份的环氧树脂、7份的滑石粉、12.5份的活性稀释剂、1份的膨润土、12.5份的钛白粉、120.925份的硅微粉、0.075份的乙炔黑进行预混合之后，用高速分散机在2000转/分的转速下高速分散30分钟，而后用研磨机研磨分散，之后在其中搅拌加入6份的助剂进行调色、调粘度，最后过滤其中的杂质得到成品。