CN103397252B - 高磁导率软磁合金 - Google Patents

高磁导率软磁合金 Download PDF

Info

Publication number
CN103397252B
CN103397252B CN201310342326.8A CN201310342326A CN103397252B CN 103397252 B CN103397252 B CN 103397252B CN 201310342326 A CN201310342326 A CN 201310342326A CN 103397252 B CN103397252 B CN 103397252B
Authority
CN
China
Prior art keywords
soft magnetic
magnetic permeability
magnetic
alloy
permeability soft
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310342326.8A
Other languages
English (en)
Other versions
CN103397252A (zh
Inventor
朱正良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuzhou Yuanyang Magnetic Material Co., Ltd.
Original Assignee
CHANGSHU ORIENT SPECIAL METALLIC MATERIAL FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU ORIENT SPECIAL METALLIC MATERIAL FACTORY filed Critical CHANGSHU ORIENT SPECIAL METALLIC MATERIAL FACTORY
Priority to CN201310342326.8A priority Critical patent/CN103397252B/zh
Publication of CN103397252A publication Critical patent/CN103397252A/zh
Application granted granted Critical
Publication of CN103397252B publication Critical patent/CN103397252B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高磁导率软磁合金,包括按质量百分比组成的下列成分:Ni:22%-25%,Zn:18%-20%,Mn:15%-18%,Al:8%-10%,Co:3%-5%,Si:0.5%-0.8%,B:0.1%-0.3%,Ti:0.02%-0.03%,Cd:0.01%-0.02%,Tb:0.01%-0.02%,Dy:0.005%-0.01%,Nd:0.005%-0.008%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。通过上述方式,本发明能够使材料性能达到一个很好的平衡。

Description

高磁导率软磁合金
技术领域
本发明涉及金属材料领域,特别是涉及一种高磁导率软磁合金。
背景技术
软磁材料是指具有低的矫顽力,高的磁导率的磁性材料,在交流磁化状态下应用要求具有低的功率损耗。软磁材料在外磁场作用下迅速被磁化,去掉外磁场后,磁性消失。  
磁导率是软磁材料的基本参数之一,一般将磁导率大于5000的软磁材料称为高磁导率材料。现今的高磁导率软磁合金材料以铁镍系合金为主,其镍含量为30%~90%,是通过合金化元素配比和适当工艺,可控制磁性能,获得高导磁、恒导磁、矩磁等的软磁材料。其塑性高,对应力较敏感,可用作脉冲变压器材料、电感铁芯和功能磁性材料。
但是,高磁导率材料除了应具有高的起始磁导率外,还应有高的居里温度、高的温度稳定性、低的磁导率减落系数、低的比损耗系数及宽的频带等,而现今的铁镍系合金往往在追求高磁导率的同时忽略了这部分要求,无法在提高磁导率的同时兼顾其它参数,使材料性能达到一个很好的平衡。
发明内容
本发明主要解决的技术问题是:针对现有技术的不足,提供一种高磁导率软磁合金,能够在保证合金材料具有高的磁导率的同时,还具有高的居里温度、高的温度稳定性、低的磁导率减落系数、低的比损耗系数及宽的频带等,使材料性能达到一个很好的平衡。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种高磁导率软磁合金,所述高磁导率软磁合金包括按质量百分比组成的下列成分:Ni:22%-25%,Zn:18%-20%,Mn:15%-18%,Al:8%-10%,Co:3%-5%,Si:0.5%-0.8%,B:0.1%-0.3%,Ti:0.02%-0.03%,Cd:0.01%-0.02%,Tb:0.01%-0.02%,Dy:0.005%-0.01%,Nd:0.005%-0.008%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
在本发明一个较佳实施例中,所述高磁导率软磁合金包括按质量百分比组成的下列成分:Ni:22.38%,Zn:19.25%,Mn:16.43%,Al:8.92%,Co:4.85%,Si:0.62%,B:0.17%,Ti:0.03%,Cd:0.016%,Tb:0.015%,Dy:0.007%,Nd:0.005%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
在本发明一个较佳实施例中,所述高磁导率软磁合金包括按质量百分比组成的下列成分:Ni:24.16%,Zn:18.31%,Mn:17.05%,Al:9.12%,Co:3.67%,Si:0.73%,B:0.22%,Ti:0.021%,Cd:0.02%,Tb:0.02%,Dy:0.01%,Nd:0.006%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
本发明的有益效果是:各元素通过合理优化匹配,以及稀土元素的选配和适量添加,能够在保证合金材料具有高的磁导率的同时,还具有高的居里温度、高的温度稳定性、低的磁导率减落系数、低的比损耗系数及宽的频带等,使材料性能达到一个很好的平衡。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括:
一种高磁导率软磁合金,所述高磁导率软磁合金包括按质量百分比组成的下列成分:Ni:22%-25%,Zn:18%-20%,Mn:15%-18%,Al:8%-10%,Co:3%-5%,Si:0.5%-0.8%,B:0.1%-0.3%,Ti:0.02%-0.03%,Cd:0.01%-0.02%,Tb:0.01%-0.02%,Dy:0.005%-0.01%,Nd:0.005%-0.008%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
实施例一:
一种高磁导率软磁合金,包括按质量百分比组成的下列成分:Ni:22.38%,Zn:19.25%,Mn:16.43%,Al:8.92%,Co:4.85%,Si:0.62%,B:0.17%,Ti:0.03%,Cd:0.016%,Tb:0.015%,Dy:0.007%,Nd:0.005%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
实施例二:
一种高磁导率软磁合金,包括按质量百分比组成的下列成分:Ni:24.16%,Zn:18.31%,Mn:17.05%,Al:9.12%,Co:3.67%,Si:0.73%,B:0.22%,Ti:0.021%,Cd:0.02%,Tb:0.02%,Dy:0.01%,Nd:0.006%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
本发明揭示了一种高磁导率软磁合金,通过各元素的合理优化匹配,以及稀土元素的选配和适量添加,能够在保证合金材料具有高的磁导率的同时,还具有高的居里温度、高的温度稳定性、低的磁导率减落系数、低的比损耗系数及宽的频带等,使材料性能达到一个很好的平衡。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。

Claims (3)

1.一种高磁导率软磁合金,其特征在于,所述高磁导率软磁合金包括按质量百分比组成的下列成分:Ni:22%-25%,Zn:18%-20%,Mn:15%-18%,Al:8%-10%,Co:3%-5%,Si:0.5%-0.8%,B:0.1%-0.3%,Ti:0.02%-0.03%,Cd:0.01%-0.02%,Tb:0.01%-0.02%,Dy:0.005%-0.01%,Nd:0.005%-0.008%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
2.根据权利要求1所述的高磁导率软磁合金,其特征在于,所述高磁导率软磁合金包括按质量百分比组成的下列成分:Ni:22.38%,Zn:19.25%,Mn:16.43%,Al:8.92%,Co:4.85%,Si:0.62%,B:0.17%,Ti:0.03%,Cd:0.016%,Tb:0.015%,Dy:0.007%,Nd:0.005%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
3.根据权利要求1所述的高磁导率软磁合金,其特征在于,所述高磁导率软磁合金包括按质量百分比组成的下列成分:Ni:24.16%,Zn:18.31%,Mn:17.05%,Al:9.12%,Co:3.67%,Si:0.73%,B:0.22%,Ti:0.021%,Cd:0.02%,Tb:0.02%,Dy:0.01%,Nd:0.006%,S:≤0.01%,P:≤0.01%,C:≤0.015%,其余为Fe和不可避免的杂质。
CN201310342326.8A 2013-08-08 2013-08-08 高磁导率软磁合金 Active CN103397252B (zh)