CN103381428A - 一种7003铝合金型材的成型工艺 - Google Patents

一种7003铝合金型材的成型工艺 Download PDF

Info

Publication number
CN103381428A
CN103381428A CN2013103378366A CN201310337836A CN103381428A CN 103381428 A CN103381428 A CN 103381428A CN 2013103378366 A CN2013103378366 A CN 2013103378366A CN 201310337836 A CN201310337836 A CN 201310337836A CN 103381428 A CN103381428 A CN 103381428A
Authority
CN
China
Prior art keywords
mould
aluminium
extruding
aluminium bar
warmed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103378366A
Other languages
English (en)
Inventor
黄高勇
胡小平
李永坤
陈国华
吕德忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Ruijin Copper-Aluminium Section Bar Co Ltd
Original Assignee
Zhejiang Ruijin Copper-Aluminium Section Bar Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Ruijin Copper-Aluminium Section Bar Co Ltd filed Critical Zhejiang Ruijin Copper-Aluminium Section Bar Co Ltd
Priority to CN2013103378366A priority Critical patent/CN103381428A/zh
Publication of CN103381428A publication Critical patent/CN103381428A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铝7003铝合金型材的成型工艺，包括以下步骤：（1）铝棒加温，将平面模铝棒加温到430℃±15℃，保温1-2小时，所述的平面模铝棒为7003型铝棒（2）模具加温（3）盛锭筒加温（4）挤压成型等。本发明具有铝型材成品率高，且加工效果高的优点。

Description

一种7003铝合金型材的成型工艺
技术领域
 本发明涉及材料的成型工艺，具体是指一种7003铝合金型材的成型工艺。 
背景技术
7003铝合金，较市面上普通6系列的铝合金，强度更高，更轻便，是一种航空铝材，但是由于其强度较高，传统的成型加工较为困难，其加工工艺一般就是铝棒通过热熔、挤压、从而得到不同截面形状的铝材料。这种传统的工艺方法存在铝型材成型稳定性不佳的问题。 
发明内容
本发明的目的是为了克服现有技术存在的缺点和不足，而提供一种铝型材成型稳定和生产效率高的7003铝合金型材的成型工艺。 
为实现上述目的，本发明的技术方案是包括以下步骤： 
（1）铝棒加温，将平面模铝棒加温到430℃±15℃，保温1-2小时，所述的平面模铝棒为7003型铝棒；
（2）模具加温，平面模模具加温到450℃±15℃，保温1-2.5小时；
（3）盛锭筒加温，将盛锭筒加温到430℃±10℃，保温8-12小时；
    （4）将铝棒和模具装载入挤压机中，型材挤出控制以200mm～500mm/分的速度，以在线水冷淬火方式冷却至80℃/分以下；其中挤压机的挤压时压力控制为150±20kg/m2；
    （5）挤压出料温度，挤压出料口与水冷装置之间的温度500℃±10℃；
    （6）挤压压余厚度，每根铝棒挤完的压余长度25mm±5mm；
（7）拉直，切割获得成品。
    本发明人在经过实际研究后，发现铝型材的出现瑕疵可能性最大的时间段为从模具挤出后阶段，传统的铝型材加工工艺在此阶段一般都是自然冷却，导致铝型材出现较大的形变，导致废品，通过本设置，控制型材挤出速度和挤压压力，在水冷状态下，实现了非常好的定型效果，铝型材的废品率大为降低，因此本发明工艺具有铝型材成型稳定，且挤压成型，加工效果高。 
    综上所述本发明具有铝型材成品率高，且加工效果高的优点。 
    下面结合具体实施方式对本发明做进一步介绍。 
具体实施方式
下面通过实施例对本发明进行具体的描述，只用于对本发明进行进一步说明，不能理解为对本发明保护范围的限定，该领域的技术工程师可根据上述发明的内容对本发明作出一些非本质的改进和调整。 
实施例1
（1）铝棒加温，将平面模铝棒加温到435℃，保温1.5小时；本实施例该平面模铝棒为7003型铝棒；
（2）模具加温，平面模模具加温到450℃，保温1.5小时；
（3）盛锭筒加温，将盛锭筒加温到430℃，保温9小时；
   （4）将铝棒和模具装载入挤压机中，型材挤出控制以300mm/分的速度，以在线水冷淬火方式冷却至80℃/分以下；其中挤压机的挤压时压力控制为150kg/m2；
    （5）挤压出料温度，挤压出料口与水冷装置之间的温度500℃；
    （6）挤压压余厚度，每根铝棒挤完的压余长度25mm；
（7）拉直，切割获得成品。
实施例2
（1）铝棒加温，将平面模铝棒加温到440℃，保温1.8小时；本实施例该平面模铝棒为7003型铝棒；
（2）模具加温，平面模模具加温到460℃，保温2小时；
（3）盛锭筒加温，将盛锭筒加温到435℃，保温10小时；
    （4）将铝棒和模具装载入挤压机中，型材挤出控制以400mm/分的速度，以在线水冷淬火方式冷却至80℃/分以下；其中挤压机的挤压时压力控制为160kg/m2；
    （5）挤压出料温度，挤压出料口与水冷装置之间的温度505℃；
    （6）挤压压余厚度，每根铝棒挤完的压余长度28mm；
（7）拉直，切割获得成品。
实施例3
（1）铝棒加温，将平面模铝棒加温到445℃，保温2小时；本实施例该平面模铝棒为7003型铝棒；
（2）模具加温，平面模模具加温到465℃，保温2.5小时；
（3）盛锭筒加温，将盛锭筒加温到440℃，保温11小时；
    （4）将铝棒和模具装载入挤压机中，型材挤出控制以450mm/分的速度，以在线水冷淬火方式冷却至80℃/分以下；其中挤压机的挤压时压力控制为170kg/m2；
    （5）挤压出料温度，挤压出料口与水冷装置之间的温度510℃；
    （6）挤压压余厚度，每根铝棒挤完的压余长度30mm；
    （7）拉直，切割获得成品。

Claims (1)

1.一种7003铝合金型材的成型工艺，其特征在于包括以下步骤：
（1）铝棒加温，将平面模铝棒加温到430℃±15℃，保温1-2小时，所述的平面模铝棒为7003型铝棒；
（2）模具加温，平面模模具加温到450℃±15℃，保温1-2.5小时；
（3）盛锭筒加温，将盛锭筒加温到430℃±10℃，保温8-12小时；
（4）将铝棒和模具装载入挤压机中，型材挤出控制以200mm～500mm/分的速度，以在线水冷淬火方式冷却至80℃/分以下；其中挤压机的挤压时压力控制为150±20kg/m2；
（5）挤压出料温度，挤压出料口与水冷装置之间的温度500℃±10℃；
（6）挤压压余厚度，每根铝棒挤完的压余长度25mm±5mm；
（7）拉直，切割获得成品。
CN2013103378366A 2013-08-06 2013-08-06 一种7003铝合金型材的成型工艺 Pending CN103381428A (zh)