CN103351153A - Natural texture brick and production method thereof - Google Patents
Natural texture brick and production method thereof Download PDFInfo
- Publication number
- CN103351153A CN103351153A CN201310336225XA CN201310336225A CN103351153A CN 103351153 A CN103351153 A CN 103351153A CN 201310336225X A CN201310336225X A CN 201310336225XA CN 201310336225 A CN201310336225 A CN 201310336225A CN 103351153 A CN103351153 A CN 103351153A
- Authority
- CN
- China
- Prior art keywords
- major ingredient
- colorant
- weight percent
- percent meter
- water ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a natural texture brick and a production method thereof, and aims to effectively solve the problems of production trouble, high cost and less variety of the existing texture brick. The natural texture brick is prepared from the following materials in percentage by weight: 60-98% of a main ingredient and 2-40% of a pigment. A processing method comprises the following steps of: adding a diluting agent which respectively accounts for 0.2wt% of the main ingredient and the pigment and sodium humate which respectively accounts for 0.4wt% of the main ingredient and the pigment into the main ingredient and the pigment, performing ball milling to prepare slurry, drying to prepare powder, putting the main ingredient into a main bin and putting the pigment into a high-temperature pigment bin; then adding water into the main ingredient, stirring for aging, putting the aged main ingredient and the pigment into an extruding machine, performing screw extrusion on the main ingredient and the pigment through the extruding machine to perform forming, and drying the main ingredient and the pigment in a drying kiln for 1-5 hours at a temperature of lower than 200 DEG C; calcining in a kiln: putting a dried blank of which the water content is less than 1.5% into a natural gas calcining kiln, and calcining at 1100-1250 DEG C under an oxidation atmosphere to obtain a semifinished product; edging and polishing: performing edging and polishing treatments on the calcined product. According to the production method, two or more types of materials with color contrasts and water contrasts are directly added into the extruding machine from a feed port of the extruding machine, and whole-body texture bricks with different surface shapes are prepared according to proportions and types of the added materials.
Description
Technical field
The present invention relates to the brick body, particularly a kind of native texture brick and production method thereof.
Background technology
Along with people's living standard improves constantly, requirement to wood grain tile product and stone material is also more and more higher, existing wood grain tile technology be by two or more shrink consistent with water ratio and material with colour contrast through vacuum chamber continuous or intersection blanking make, the method can only make wood grain tile, and want two or more machines just can make, the brick body kind of production is few, and cost is high, equipment is complicated, applies difficulty.
Summary of the invention
For above-mentioned situation, for overcoming the defective of prior art, the present invention's purpose just provides a kind of native texture brick and production method thereof, can effectively solve existing texture brick production trouble, cost height and the few problem of kind.
The technical scheme of its solution is, the present invention is made by major ingredient 60-98% and the colorant 2-40% of weight percent meter, the water ratio of major ingredient is 12%～25%, the water ratio of colorant is 1%～3%, and said major ingredient is by weight percent meter: plasticity material 15%～80%, poor material 10%～65% and beramic color 1～20% are made; Said colorant is red iron oxide, cobalt blue, the beramic colors such as melanochrome, can directly be red soil also, plaster etc., can also directly be beramic color (can directly from the market enough), working method is: major ingredient and colorant add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant enters the high temperature decorating colour storehouse; Dried major ingredient adds the water that accounts for major ingredient weight percent meter 10%～23% and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative native texture brick after edging, the polished finish.
Said major ingredient is comprised of kaolin 20%～40%, alkali stone 30%～50% and the feldspar 10%～50% of weight percent meter.
Said thinner is tripoly phosphate sodium STPP.
The present invention has broken through from vacuum chamber and has intersected continuously the method for blanking, directly adding two or more color from the forcing machine opening for feed has contrast and moisture that the material of contrast is also arranged, according to the ratio that adds pan feeding and kind, can make the different planar entire body texture bricks such as imitative wood grain, imitative sandstone.
Embodiment
Below in conjunction with embodiment content of the present invention is described in further detail.
Below provide the basis of embodiment, major ingredient is by kaolin 20%～40%, alkali stone 30%～50%, and feldspar 10%～50% forms; Colorant is comprised of following three schemes: (1), beramic color (called after colorant 1); (2), look soil (called after colorant 2); (3), have a beramic color (called after beramic color) that contrast is arranged with major ingredient, therefore beramic color need not carry out ball milling and drying operation because of can be from market directly enough, directly advances forcing machine and mixes with major ingredient.
Embodiment 1
The present invention is made by major ingredient 70% and the colorant 1 30% of weight percent meter, the water ratio of major ingredient is 12%～25%, the water ratio of colorant is 1%～3%, working method is: major ingredient and colorant add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant enters the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative wood grain face brick after edging, the polished finish.
Embodiment 2
The present invention is made by major ingredient 50% and the colorant 1 50% of weight percent meter, the water ratio of major ingredient is 12%～25%, the water ratio of colorant is 1%～3%, working method is: major ingredient and colorant add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant enters the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative sandstone face brick after edging, the polished finish.
Embodiment 3
The present invention is by major ingredient 55% and the colorant 1 20% of weight percent meter, colorant 2 20% and beramic color 5% are made, working method is: major ingredient and colorant 1, colorant 2 adds respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, colorant 1, the water ratio of colorant 2 is 1-3%, major ingredient enters the major ingredient storehouse, and colorant 1 and colorant 2 enter the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant 1, colorant 2 and beramic color advance the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative stone face brick after edging, the polished finish.
Embodiment 4
The present invention is made by major ingredient 60% and colorant 2 38%, the beramic color 2% of weight percent meter, working method is: major ingredient and colorant 2 add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant 2 is 1-3%, major ingredient enters the major ingredient storehouse, and colorant 2 enters the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant 2 and beramic color advance the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative stone face brick after edging, the polished finish.
Embodiment 5
The present invention is made by major ingredient 98% and the beramic color 2% of weight percent meter, working method is: major ingredient adds 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, major ingredient enters the major ingredient storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, beramic color advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative wood grain face brick after edging, the polished finish.
Embodiment 6
The present invention is made by major ingredient 70% and the colorant 2 30% of weight percent meter, the water ratio of major ingredient is 12%～25%, the water ratio of colorant is 1%～3%, working method is: major ingredient and colorant add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant enters the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative wood grain face brick after edging, the polished finish.
As can be seen from the above-described embodiment,
1, the different texture bricks that can obtain different-effect of ratio row by the material that adds;
2, follow one or more colorant to add the stone material surface that major ingredient can obtain different texture by beramic color.
The present invention adds one or more colorant by a kind of major ingredient, utilize the major ingredient water ratio high, the characteristics that the colorant water ratio is low, in the spiral squeezing process, the characteristics that are difficult to mix according to colorant and major ingredient, produce the ceramic tile of different texture, it is consistent and intersect continuously blanking through vacuum chamber and can only extrude the shortcoming of wood grain tile to have solved two kinds of water ratio, is the innovation on the texture brick.
Claims (7)
1. a native texture brick and production method thereof, major ingredient 60-98% and colorant 2-40% by weight percent meter make, the water ratio of major ingredient is 12%～25%, the water ratio of colorant is 1%～3%, and said major ingredient is by weight percent meter: plasticity material 15%～80%, poor material 10%～65% and beramic color 1～20% are made; Said colorant is red iron oxide, cobalt blue, melanochrome, can directly be red soil, plaster etc., can also directly be beramic color, working method is: major ingredient and colorant add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant enters the high temperature decorating colour storehouse; Dried major ingredient adds the water that accounts for major ingredient weight percent meter 10%～23% and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative native texture brick after edging, the polished finish;
Said major ingredient is comprised of kaolin 20%～40%, alkali stone 30%～50% and the feldspar 10%～50% of weight percent meter;
Said thinner is tripoly phosphate sodium STPP.
2. native texture brick according to claim 1 and production method thereof, it is characterized in that, major ingredient 70% and colorant 1 30% by weight percent meter are made, the water ratio of major ingredient is 12%～25%, the water ratio of colorant is 1%～3%, working method is: major ingredient and colorant add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant enters the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative wood grain face brick after edging, the polished finish.
3. native texture brick according to claim 1 and production method thereof, it is characterized in that, major ingredient 50% and colorant 1 50% by weight percent meter are made, the water ratio of major ingredient is 12%～25%, the water ratio of colorant is 1%～3%, working method is: major ingredient and colorant add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant enters the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative sandstone face brick after edging, the polished finish.
4. native texture brick according to claim 1 and production method thereof, it is characterized in that, major ingredient 55% and colorant 1 20% by weight percent meter, colorant 2 20% and beramic color 5% are made, working method is: major ingredient and colorant 1, colorant 2 adds respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, colorant 1, the water ratio of colorant 2 is 1-3%, major ingredient enters the major ingredient storehouse, and colorant 1 and colorant 2 enter the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant 1, colorant 2 and beramic color advance the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative stone face brick after edging, the polished finish.
5. native texture brick according to claim 1 and production method thereof, it is characterized in that, major ingredient 60% and colorant 2 38% by weight percent meter, beramic color 2% is made, working method is: major ingredient and colorant 2 add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant 2 is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant 2 enters the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant 2 and beramic color advance the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative stone face brick after edging, the polished finish.
6. native texture brick according to claim 1 and production method thereof, it is characterized in that, major ingredient 98% and beramic color 2% by weight percent meter are made, working method is: major ingredient adds 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, and major ingredient enters the major ingredient storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, beramic color advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative wood grain face brick after edging, the polished finish.
7. native texture brick according to claim 1 and production method thereof, it is characterized in that, major ingredient 70% and colorant 2 30% by weight percent meter are made, the water ratio of major ingredient is 12%～25%, the water ratio of colorant is 1%～3%, working method is: major ingredient and colorant add respectively 0.2% the thinner that accounts for its weight percent meter and the sodium humate of weight percent meter 0.4%, in expecting: ball: the weight percent meter of water=1:2:0.5 ratio ball milling in ball mill, ball milling 5～16 hours, make the mud that fineness is 50-80 μ m, the dry powder process of spray-dried tower, the water ratio that makes major ingredient is 12-25%, the water ratio of colorant is 1-3%, and major ingredient enters the major ingredient storehouse, and colorant enters the high temperature decorating colour storehouse; Dried major ingredient adds 10%～23% the water that accounts for the major ingredient weight percent meter and stirs old, descended old 48-72 hour at 25 ℃, with old good major ingredient by advancing the forcing machine opening for feed, colorant advances the forcing machine opening for feed through the colorant bucket, major ingredient and colorant advance forcing machine through screw extrusion molding, enter dry kiln below 200 ℃ dry 1-5 hour; Entering klining becomes: water ratio after the drying is entered Sweet natural gas calcining kiln oxidizing atmosphere under 1100 ℃～1250 ℃ temperature less than 1.5% base substrate burn till, firing period is 1～5 hour, obtains work in-process; Edging polishing: the product that bakes is carried out getting final product to get imitative wood grain face brick after edging, the polished finish.