CN105801081A - Color petuntse fired at temperature not higher than 1,150 DEG C and preparation method thereof - Google Patents
Color petuntse fired at temperature not higher than 1,150 DEG C and preparation method thereof Download PDFInfo
- Publication number
- CN105801081A CN105801081A CN201610111074.1A CN201610111074A CN105801081A CN 105801081 A CN105801081 A CN 105801081A CN 201610111074 A CN201610111074 A CN 201610111074A CN 105801081 A CN105801081 A CN 105801081A
- Authority
- CN
- China
- Prior art keywords
- mud
- colored
- less
- porcelain
- mineralizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses color petuntse fired at a temperature not higher than 1,150 DEG C and a preparation method thereof. The color petuntse comprises the following components in parts by weight: 1-10 parts of synthetic mineralizer clinker, 80-100 parts of white petuntse and 0.1-10 parts of pigment, wherein the synthetic mineralizer clinker is prepared by mixing lithium chinastone and albite and calcining. According to the color petuntse and preparation method thereof disclosed by the invention, the firing temperature can be effectively reduced by 30-50 DEG C, the energy and cost are saved, the glaze surface of the product is smoother, and the color is brighter.
Description
Technical field
The present invention relates to porcelain mud technical field, be specifically related to a kind of colored porcelain mud that can burn till below 1150 DEG C and preparation method thereof.
Background technology
Application number is that the colored porcelain mud water-retaining property in 200810107321.6 patents of invention " a kind of chromatic ceramics and preparation method thereof ", associativity and anti-corrosive properties are all better, is rapidly fired to through 1150~1200 DEG C of oxidizing atmospheres, and combinations color and lustre is abundant, beautiful, good decorating effect.But, its firing temperature is still higher, it is impossible to reduce further, causes burning till energy consumption bigger.
Summary of the invention
In view of this, colored porcelain mud it is an object of the invention to propose a kind of less than 1150 DEG C colored porcelain mud burnt till and preparation method thereof, so that can burn till below 1150 DEG C.
Based on above-mentioned purpose, less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, by weight, including:
1~10 part of mineralizer grog of synthesis;
80~100 parts of porcelain mud of white;
0.1~10 part of colorant;
Wherein, described synthesis mineralizer grog is by by after lithium porcelain stone, albite mixing, making then through calcining.
In some embodiments of the invention, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 7 3~8 2.
In some embodiments of the invention, Li in described lithium porcelain stone2O content is 0.4~3%.
In some embodiments of the invention, the calcining heat of described synthesis mineralizer grog is 1050~1100 DEG C.
In some embodiments of the invention, described colored porcelain mud also includes:
Base substrate reinforcing agent 0.05~5.00 part;And/or
Preservative 0.05~0.5 part.
In some embodiments of the invention, described base substrate reinforcing agent at least one in organic base substrate reinforcing agent, inorganic base substrate reinforcing agent;
Described organic base substrate reinforcing agent at least one in sodium carboxymethyl cellulose, polysaccharide, polyvinyl butyral resin, methylcellulose;
Described inorganic base substrate reinforcing agent at least one in bentonite, ball clay, camwood knag;
Described preservative at least one in Bravo, match bacterium spirit, thiram, benzene isothiazolone and first Kui at tenth of the twelve Earthly Branches derivative formulations.
In some embodiments of the invention, described white porcelain mud drum is drawn together:
Kaolin 20.00~30.00 parts;
At least two in Anhydrite, quartz, Muscovitum, porcelain stone, wollastonite 60.00~70.00% parts.
The present invention also provides for a kind of method preparing above-mentioned less than the 1150 DEG C colored porcelain mud burnt till, and comprises the following steps:
By ball milling after white porcelain mud, synthesis mineralizer grog mixing, obtain white compound;
Colorant is mixed with partial white compound, until becoming the mill base that color and luster is homogeneous, then mixing with remaining white compound, base substrate reinforcing agent again, obtaining color slurry;
By color slurry filter-press dehydration, obtain colored mud cake;
Colour mud cake is inserted in vacuum deairing machine together with preservative slightly practice, concise, make colored porcelain mud.
In some embodiments of the invention, the moisture content of described colored mud cake is 25~30%.
In some embodiments of the invention, by the white compound mixing of colorant and 3~8%, until becoming the mill base that color and luster is homogeneous, then mixing with remaining white compound, base substrate reinforcing agent again, obtaining color slurry.
From the above it can be seen that colored porcelain mud provided by the invention and preparation method thereof can reduce firing temperature 30~50 DEG C further, it is possible to being effectively reduced firing temperature, both saved the energy and cost, goods glaze paint can be made again smoother, color and luster is more gorgeous.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearly understand, below in conjunction with specific embodiment, the present invention is described in more detail.
Embodiment 1
Less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, including following raw material and weight portion thereof:
Wherein, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 73, and makes through 1080 DEG C of calcinings.In the present embodiment, Li in described lithium porcelain stone2O content is 0.8%.
The preparation method of described less than the 1150 DEG C colored porcelain mud burnt till comprises the following steps:
1) after lithium porcelain stone, albite being mixed, then it is placed under 1080 DEG C of conditions and calcines makes synthesis mineralizer grog;
2) by ball milling after Kaolin, quartz, porcelain stone, Anhydrite, synthesis mineralizer grog mix homogeneously, obtaining white compound, the fineness of this white compound was 180 mesh sieves, tailed over 0.8%;
3) blue is first mixed with the white compound of about 5%, until becoming the mill base that color and luster is homogeneous, then putting in stock tank together with remaining white compound, bentonite again, being uniformly mixed and obtain color slurry, then color slurry is crossed 180 mesh sieves;
4) by color slurry filter-press dehydration, the colored mud cake that moisture content is 27% is obtained;
5) colour mud cake is inserted in vacuum deairing machine together with Bravo, slightly practice, concise, make plastic colored porcelain mud.
Embodiment 2
Less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, including following raw material and weight portion thereof:
Wherein, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 7.5 2.5, and makes through 1100 DEG C of calcinings.In the present embodiment, Li in described lithium porcelain stone2O content is 1.5%.
The preparation method of described less than the 1150 DEG C colored porcelain mud burnt till comprises the following steps:
1) after lithium porcelain stone, albite being mixed, then it is placed under 1100 DEG C of conditions and calcines makes synthesis mineralizer grog;
2) by ball milling after Kaolin, quartz, porcelain stone, Anhydrite, wollastonite, synthesis mineralizer grog mix homogeneously, obtaining white compound, the fineness of this white compound was 180 mesh sieves, tailed over 1.0%;
3) green material is first mixed with the white compound of about 6%, until becoming the mill base that color and luster is homogeneous, then put in stock tank together with remaining white compound, ball clay, sodium carboxymethyl cellulose again, be uniformly mixed and obtain color slurry, then color slurry is crossed 180 mesh sieves;
4) by color slurry filter-press dehydration, the colored mud cake that moisture content is 28.5% is obtained;
5) colour mud cake is inserted in vacuum deairing machine together with match bacterium spirit, slightly practice, concise, make plastic colored porcelain mud.
Embodiment 3
Less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, including following raw material and weight portion thereof:
Wherein, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 82, and makes through 1075 DEG C of calcinings.In the present embodiment, Li in described lithium porcelain stone2O content is 2.3%.
The preparation method of described less than the 1150 DEG C colored porcelain mud burnt till comprises the following steps:
1) after lithium porcelain stone, albite being mixed, then it is placed under 1075 DEG C of conditions and calcines makes synthesis mineralizer grog;
2) by ball milling after Kaolin, quartz, porcelain stone, Anhydrite, wollastonite, synthesis mineralizer grog mix homogeneously, obtaining white compound, the fineness of this white compound was 180 mesh sieves, tailed over 0.7%;
3) yellow material is first mixed with the white compound of about 7.5%, until becoming the mill base that color and luster is homogeneous, then put in stock tank together with remaining white compound, sodium carboxymethyl cellulose, polysaccharide again, be uniformly mixed and obtain color slurry, then color slurry is crossed 180 mesh sieves;
4) by color slurry filter-press dehydration, the colored mud cake that moisture content is 25.5% is obtained;
5) colour mud cake is inserted in vacuum deairing machine together with Bravo, thiram, slightly practice, concise, make plastic colored porcelain mud.
Embodiment 4
Less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, including following raw material and weight portion thereof:
Wherein, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 7.8 2.2, and makes through 1090 DEG C of calcinings.In the present embodiment, Li in described lithium porcelain stone2O content is 0.8%.
The preparation method of described less than the 1150 DEG C colored porcelain mud burnt till comprises the following steps:
1) after lithium porcelain stone, albite being mixed, then it is placed under 1090 DEG C of conditions and calcines makes synthesis mineralizer grog;
2) by ball milling after Kaolin, quartz, porcelain stone, Anhydrite, wollastonite, synthesis mineralizer grog mix homogeneously, obtaining white compound, the fineness of this white compound was 180 mesh sieves, tailed over 0.5%;
3) Red pigment is first mixed with the white compound of about 7.5%, until becoming the mill base that color and luster is homogeneous, then put in stock tank together with remaining white compound, camwood knag, ball clay again, be uniformly mixed and obtain color slurry, then color slurry is crossed 180 mesh sieves;
4) by color slurry filter-press dehydration, the colored mud cake that moisture content is 28% is obtained;
5) colour mud cake is inserted in vacuum deairing machine together with Bravo, benzene isothiazolone, slightly practice, concise, make plastic colored porcelain mud.
Embodiment 5
Less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, including following raw material and weight portion thereof:
Wherein, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 7.2 2.8, and makes through 1050 DEG C of calcinings.In the present embodiment, Li in described lithium porcelain stone2O content is 3%.
The preparation method of described less than the 1150 DEG C colored porcelain mud burnt till comprises the following steps:
1) after lithium porcelain stone, albite being mixed, then it is placed under 1050 DEG C of conditions and calcines makes synthesis mineralizer grog;
2) by ball milling after Kaolin, quartz, Anhydrite, wollastonite, synthesis mineralizer grog mix homogeneously, obtaining white compound, the fineness of this white compound was 180 mesh sieves, tailed over 0.85%;
3) black material is first mixed with the white compound of about 3%, until becoming the mill base that color and luster is homogeneous, then put in stock tank together with remaining white compound, sodium carboxymethyl cellulose, methylcellulose again, be uniformly mixed and obtain color slurry, then color slurry is crossed 180 mesh sieves;
4) by color slurry filter-press dehydration, the colored mud cake that moisture content is 26% is obtained;
5) colour mud cake is inserted in vacuum deairing machine together with first Kui at tenth of the twelve Earthly Branches derivative formulations, slightly practice, concise, make plastic colored porcelain mud.
Embodiment 6
Less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, including following raw material and weight portion thereof:
Wherein, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 7.6 2.4, and makes through 1055 DEG C of calcinings.In the present embodiment, Li in described lithium porcelain stone2O content is 0.4%.
The preparation method of described less than the 1150 DEG C colored porcelain mud burnt till comprises the following steps:
1) after lithium porcelain stone, albite being mixed, then it is placed under 1055 DEG C of conditions and calcines makes synthesis mineralizer grog;
2) by ball milling after Kaolin, porcelain stone, wollastonite, synthesis mineralizer grog mix homogeneously, obtaining white compound, the fineness of this white compound was 180 mesh sieves, tailed over 0.82%;
3) green material is first mixed with the white compound of about 8%, until becoming the mill base that color and luster is homogeneous, then putting in stock tank together with remaining white compound, polysaccharide again, being uniformly mixed and obtain color slurry, then color slurry is crossed 180 mesh sieves;
4) by color slurry filter-press dehydration, the colored mud cake that moisture content is 28% is obtained;
5) colour mud cake is inserted in vacuum deairing machine together with thiram, slightly practice, concise, make plastic colored porcelain mud.
Embodiment 7
Less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, including following raw material and weight portion thereof:
Wherein, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 7.7 2.3, and makes through 1068 DEG C of calcinings.In the present embodiment, Li in described lithium porcelain stone2O content is 1.4%.
The preparation method of described less than the 1150 DEG C colored porcelain mud burnt till comprises the following steps:
1) after lithium porcelain stone, albite being mixed, then it is placed under 1068 DEG C of conditions and calcines makes synthesis mineralizer grog;
2) by ball milling after Kaolin, porcelain stone, wollastonite, Anhydrite, synthesis mineralizer grog mix homogeneously, obtaining white compound, the fineness of this white compound was 180 mesh sieves, tailed over 0.88%;
3) yellow material is first mixed with the white compound of about 7%, until becoming the mill base that color and luster is homogeneous, then putting in stock tank together with remaining white compound, camwood knag again, being uniformly mixed and obtain color slurry, then color slurry is crossed 180 mesh sieves;
4) by color slurry filter-press dehydration, the colored mud cake that moisture content is 26.8% is obtained;
5) colour mud cake is inserted in vacuum deairing machine together with Bravo, benzene isothiazolone, slightly practice, concise, make plastic colored porcelain mud.
Embodiment 8
Less than the 1150 DEG C colored porcelain mud burnt till provided by the invention, including following raw material and weight portion thereof:
Wherein, in described synthesis mineralizer grog, the weight ratio of lithium porcelain stone and albite is 7.9 2.1, and makes through 1052 DEG C of calcinings.In the present embodiment, Li in described lithium porcelain stone2O content is 1.75%.
The preparation method of described less than the 1150 DEG C colored porcelain mud burnt till comprises the following steps:
1) after lithium porcelain stone, albite being mixed, then it is placed under 1052 DEG C of conditions and calcines makes synthesis mineralizer grog;
2) by ball milling after Kaolin, porcelain stone, Anhydrite, quartz, synthesis mineralizer grog mix homogeneously, obtaining white compound, the fineness of this white compound was 180 mesh sieves, tailed over 0.95%;
3) black material is first mixed with the white compound of about 4%, until becoming the mill base that color and luster is homogeneous, then put in stock tank together with remaining white compound, polyvinyl butyral resin, sodium carboxymethyl cellulose, camwood knag again, it is uniformly mixed and obtains color slurry, then color slurry is crossed 180 mesh sieves;
4) by color slurry filter-press dehydration, the colored mud cake that moisture content is 25% is obtained;
5) by colour mud cake and match bacterium spirit, insert in vacuum deairing machine together with Bravo, slightly practice, concise, make plastic colored porcelain mud.
Then, above-mentioned plastic colored mud bar is rubbed into various shape, then pinches mud by intention is manual or is aided with model hand-pressing molding;The moulded pottery not yet put in a kiln to bake made by plastic molding by after cementing drying, directly executes unleaded high glaze clear frit glaze on moulded pottery not yet put in a kiln to bake, then by having executed the base substrate of glaze in oxidizing flame electrical kiln, is rapidly fired to prepare color mud product with 1100~1150 DEG C.Visible, colored porcelain mud provided by the invention can reduce firing temperature 30~50 DEG C further, for example, base substrate firing temperature in oxidizing flame electrical kiln can reduce to 1150 DEG C, 1145 DEG C, 1140 DEG C, 1138 DEG C, 1132 DEG C, it might even be possible to reduces to 1127 DEG C, 1122 DEG C, 1118 DEG C, 1115 DEG C, 1112 DEG C, 1110 DEG C etc. further, therefore, firing temperature can be effectively reduced, both having saved the energy and cost, goods glaze paint can be made again smoother, color and luster is more gorgeous.
It should be noted that, in color mud field, reduce temperature and cannot realize porcelain, but, the present invention is by adding synthesis mineralizer grog, lithium porcelain stone, albite are the mineral that silicate mineral firing temperature is relatively low, calcine at a certain temperature, through physical-chemical reaction, become the material of a kind of abundant sintering, but do not become frit, without influence on follow-up pulverizing.The addition of synthesis mineralizer grog not only can significantly reduce firing temperature and realize porcelain, moreover it is possible to ensureing that the color mud product color and luster after burning till is abundant, beautiful, intensity can be kept not decline simultaneously, yield rate is high so that it is is readily transported and stores.
Those of ordinary skill in the field are it is understood that the discussion of any of the above embodiment is exemplary only, it is not intended that hint the scope of the present disclosure (including claim) is limited to these examples;Under the thinking of the present invention, can also be combined between technical characteristic in above example or different embodiment, step can realize with random order, and there are other changes many of the different aspect of the present invention as above, for they not offers in details simple and clear.Therefore, all within the spirit and principles in the present invention, any omission of making, amendment, equivalent replacement, improvement etc., should be included within protection scope of the present invention.
Claims (10)
1. one kind less than the 1150 DEG C colored porcelain mud burnt till, it is characterised in that by weight, including:
1~10 part of mineralizer grog of synthesis;
80~100 parts of porcelain mud of white;
0.1~10 part of colorant;
Wherein, described synthesis mineralizer grog is by by after lithium porcelain stone, albite mixing, making then through calcining.
2. the weight ratio of less than the 1150 DEG C colored porcelain mud burnt till according to claim 1, it is characterised in that in described synthesis mineralizer grog, lithium porcelain stone and albite is 7 3~8 2.
3. less than the 1150 DEG C colored porcelain mud burnt till according to claim 1, it is characterised in that Li in described lithium porcelain stone2O content is 0.4~3%.
4. less than the 1150 DEG C colored porcelain mud burnt till according to claim 1, it is characterised in that the calcining heat of described synthesis mineralizer grog is 1050~1100 DEG C.
5. less than the 1150 DEG C colored porcelain mud burnt till according to claim 1, it is characterised in that described colored porcelain mud also includes:
Base substrate reinforcing agent 0.05~5.00 part;And/or
Preservative 0.05~0.5 part.
6. less than the 1150 DEG C colored porcelain mud burnt till according to claim 5, it is characterised in that described base substrate reinforcing agent at least one in organic base substrate reinforcing agent, inorganic base substrate reinforcing agent;
Described organic base substrate reinforcing agent at least one in sodium carboxymethyl cellulose, polysaccharide, polyvinyl butyral resin, methylcellulose;
Described inorganic base substrate reinforcing agent at least one in bentonite, ball clay, camwood knag;
Described preservative at least one in Bravo, match bacterium spirit, thiram, benzene isothiazolone and first Kui at tenth of the twelve Earthly Branches derivative formulations.
7. less than the 1150 DEG C colored porcelain mud burnt till according to claim 1, it is characterised in that described white porcelain mud drum is drawn together:
Kaolin 20.00~40.00 parts;
At least two in Anhydrite, quartz, Muscovitum, porcelain stone, wollastonite 60.00~80.00% parts.
8. the method for the colored porcelain mud that less than 1150 DEG C prepared as described in claim 1~7 burn till, it is characterised in that comprise the following steps:
By ball milling after white porcelain mud, synthesis mineralizer grog mixing, obtain white compound;
Colorant is mixed with partial white compound, until becoming the mill base that color and luster is homogeneous, then mixing with remaining white compound, base substrate reinforcing agent again, obtaining color slurry;
By color slurry filter-press dehydration, obtain colored mud cake;
Colour mud cake is inserted in vacuum deairing machine together with preservative slightly practice, concise, make colored porcelain mud.
9. the preparation method of less than the 1150 DEG C colored porcelain mud burnt till according to claim 8, it is characterised in that the moisture content of described colored mud cake is 25~30%.
10. the preparation method of less than the 1150 DEG C colored porcelain mud burnt till according to claim 8, it is characterized in that, by the white compound mixing of colorant and 3~8%, until becoming the mill base that color and luster is homogeneous, then mix with remaining white compound, base substrate reinforcing agent again, obtain color slurry.