CN104944904A - Novel human body bone china product and preparation method thereof - Google Patents
Novel human body bone china product and preparation method thereof Download PDFInfo
- Publication number
- CN104944904A CN104944904A CN201510308724.7A CN201510308724A CN104944904A CN 104944904 A CN104944904 A CN 104944904A CN 201510308724 A CN201510308724 A CN 201510308724A CN 104944904 A CN104944904 A CN 104944904A
- Authority
- CN
- China
- Prior art keywords
- powder
- bone
- kaolin
- clay
- feldspar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel human body bone china product and a preparation method thereof. The ceramic product comprises the following raw materials by weight percent: 45-50% of bone ash, 1-5% of clay, 8-15% of feldspar, 2-10% of quartz, 15-40% of kaolin, 5-10% of kibushi-clay, 1-3% of a plasticizer and 1-5% of sepiolite mineral nanofiber. The preparation method comprises the following steps: (1) preparing slurry agent; (2) forming; (3) firing; (4) coloring; (5) checking. Compared with the prior art, the ceramic product provided by the invention has the advantages of being good in bone-china texture, relatively high in plasticity in production process, not easy to deform, capable of being prepared into thinner bone-china products, relatively low in cost and relatively little in energy consumption, solving the problem that the land source is short at present, avoiding the problem that no place can be used for burying the dead in the future, and being a way of memorizing relatives.
Description
Technical field
The present invention relates to ceramic, particularly relate to a kind of novel human-body bone china goods and preparation method thereof.
Background technology
At present, State owned land is more in short supply, graveyard somewhat expensive, if select porcelain to bury, porcelain is buried and is made porcelain by bone ash, so both solves land resources in short supply, avoid occurring the problem that people after death can bury nowhere in the future, being made into porcelain simultaneously, being placed on family or carrying with, is also cherish the memory of mode to the one of relatives.
Bone China, i.e. bone china, be china again, originates from Britain, be a kind of with bone meal, clay, feldspar and quartz for basic raw material, through the porcelain that high temperature biscuiting and low temperature sinter are fired for twice, be the high-grade porcelain kind of generally acknowledging in the world.
Along with the raising of people's living standard, Bone China is as universally acknowledged high-grade porcelain kind, and what be more and more subject to people chases after rod, and its market scale expands gradually.But the quality of traditional Bone China is not good enough, and plasticity-is poor in process of production, is easily out of shape, and cause bone china product thicker, cost is high, and power consumption is large.
Summary of the invention
The present invention is to solve above-mentioned deficiency, provides a kind of novel human-body bone china goods and preparation method thereof.
Above-mentioned purpose of the present invention is realized by following technical scheme: a kind of novel human-body bone china goods, is characterized in that: by weight percentage, be made up of following raw material:
Bone meal 45-50%;
Clay 1-5%;
Feldspar 8-15%;
Quartz 2-10%;
Kaolin 15-40%;
Kieselguhr 5-10%;
Softening agent 1-3%;
Scpiolitc nanofiber 1-5%.
Described kaolin by weight percentage, is made up of following raw material: aluminum oxide 30%, silicon-dioxide 69.5%, ferric oxide 0.5%.
A making method for novel human-body bone china goods, is characterized in that: comprise the following steps:
(1) slurrying material: bone meal is dried, calcines, after having calcined, furnace cooling, ball milling washing post-drying, obtains the bone meal after ball milling; By clay, feldspar, quartz, kaolin and kieselguhr ball milling respectively, obtain clay powder, Feldspar Powder, silica powder, kaolin powder and the kieselguhr powder after ball milling respectively; Bone meal after ball milling, clay powder, Feldspar Powder, silica powder, kaolin powder and kieselguhr powder are mixed, adds the grinding of dispersion agent, softening agent and scpiolitc nanofiber, obtain Bone China slurry;
(2) shaping: to adopt slip casting, pour Bone China slurry into mould, the shaping rear demoulding, dry, and repaired biscuit is carried out to dried base substrate, obtain shaping base substrate;
(3) fire: after shaping, form burning with the highest temperature of 1250 DEG C; Carry out shape after forming burning to bend and the inspection of size, spray glaze with atomizer after lapped face, enter the glaze firing that kiln carries out 1150 DEG C;
(4) paint: on white quality finished product, paste colour painting, fire with 820 DEG C and form;
(5) check: every stroke all carries out narrow examination, and qualified product is just sent to next stroke, makes finished product and dispatches from the factory.
The present invention's advantage is compared with prior art: the quality of bone china of the present invention is good, and plasticity-is comparatively strong in process of production, and not yielding, can obtain thinner Bone China product, cost is lower, consumes energy less; And solve current land resources in short supply, avoiding occurring the problem that people after death can bury nowhere in the future, meanwhile, is also cherish the memory of mode to the one of relatives.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1: a kind of novel human-body bone china goods, by weight percentage, are made up of following raw material: bone meal 45%; Clay 5%; Feldspar 10%; Quartz 5%; Kaolin 20%; Kieselguhr 10%; Softening agent 2%; Scpiolitc nanofiber 3%.Described kaolin by weight percentage, is made up of following raw material: aluminum oxide 30%, silicon-dioxide 69.5%, ferric oxide 0.5%.
Embodiment 2: a kind of novel human-body bone china goods, by weight percentage, are made up of following raw material: bone meal 48%; Clay 2%; Feldspar 10%; Quartz 10%; Kaolin 20%; Kieselguhr 5%; Softening agent 3%; Scpiolitc nanofiber 2%.Described kaolin by weight percentage, is made up of following raw material: aluminum oxide 30%, silicon-dioxide 69.5%, ferric oxide 0.5%.
Embodiment 3: a kind of novel human-body bone china goods, by weight percentage, are made up of following raw material: bone meal 50%; Clay 2%; Feldspar 10%; Quartz 10%; Kaolin 15%; Kieselguhr 8%; Softening agent 2%; Scpiolitc nanofiber 3%.Described kaolin by weight percentage, is made up of following raw material: aluminum oxide 30%, silicon-dioxide 69.5%, ferric oxide 0.5%.
The making method of a kind of novel human-body bone china goods of the present invention, comprises the following steps:
(1) slurrying material: bone meal is dried, calcines, after having calcined, furnace cooling, ball milling washing post-drying, obtains the bone meal after ball milling; By clay, feldspar, quartz, kaolin and kieselguhr ball milling respectively, obtain clay powder, Feldspar Powder, silica powder, kaolin powder and the kieselguhr powder after ball milling respectively; Bone meal after ball milling, clay powder, Feldspar Powder, silica powder, kaolin powder and kieselguhr powder are mixed, adds the grinding of dispersion agent, softening agent and scpiolitc nanofiber, obtain Bone China slurry;
(2) shaping: to adopt slip casting, pour Bone China slurry into mould, the shaping rear demoulding, dry, and repaired biscuit is carried out to dried base substrate, obtain shaping base substrate;
(3) fire: after shaping, form burning with the highest temperature of 1250 DEG C; Carry out shape after forming burning to bend and the inspection of size, spray glaze with atomizer after lapped face, enter the glaze firing that kiln carries out 1150 DEG C;
(4) paint: on white quality finished product, paste colour painting, fire with 820 DEG C and form;
(5) check: every stroke all carries out narrow examination, and qualified product is just sent to next stroke, makes finished product and dispatches from the factory.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. novel human-body bone china goods, is characterized in that: by weight percentage, are made up of following raw material:
Bone meal 45-50%;
Clay 1-5%;
Feldspar 8-15%;
Quartz 2-10%;
Kaolin 15-40%;
Kieselguhr 5-10%;
Softening agent 1-3%;
Scpiolitc nanofiber 1-5%.
2. a kind of novel human-body bone china goods according to claim 1, is characterized in that: described kaolin by weight percentage, is made up of following raw material: aluminum oxide 30%, silicon-dioxide 69.5%, ferric oxide 0.5%.
3. a making method for novel human-body bone china goods, is characterized in that: comprise the following steps:
(1) slurrying material: bone meal is dried, calcines, after having calcined, furnace cooling, ball milling washing post-drying, obtains the bone meal after ball milling; By clay, feldspar, quartz, kaolin and kieselguhr ball milling respectively, obtain clay powder, Feldspar Powder, silica powder, kaolin powder and the kieselguhr powder after ball milling respectively; Bone meal after ball milling, clay powder, Feldspar Powder, silica powder, kaolin powder and kieselguhr powder are mixed, adds the grinding of dispersion agent, softening agent and scpiolitc nanofiber, obtain Bone China slurry;
(2) shaping: to adopt slip casting, pour Bone China slurry into mould, the shaping rear demoulding, dry, and repaired biscuit is carried out to dried base substrate, obtain shaping base substrate;
(3) fire: after shaping, form burning with the highest temperature of 1250 DEG C; Carry out shape after forming burning to bend and the inspection of size, spray glaze with atomizer after lapped face, enter the glaze firing that kiln carries out 1150 DEG C;
(4) paint: on white quality finished product, paste colour painting, fire with 820 DEG C and form;
(5) check: every stroke all carries out narrow examination, and qualified product is just sent to next stroke, makes finished product and dispatches from the factory.