CN103334201A - Environment-friendly multifunctional textile comprising collagen fiber and preparation method thereof - Google Patents
Environment-friendly multifunctional textile comprising collagen fiber and preparation method thereof Download PDFInfo
- Publication number
- CN103334201A CN103334201A CN2013102620644A CN201310262064A CN103334201A CN 103334201 A CN103334201 A CN 103334201A CN 2013102620644 A CN2013102620644 A CN 2013102620644A CN 201310262064 A CN201310262064 A CN 201310262064A CN 103334201 A CN103334201 A CN 103334201A
- Authority
- CN
- China
- Prior art keywords
- mins
- rev
- speed
- speeds
- collagen fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to environment-friendly multifunctional textile comprising collagen fiber and a preparation method thereof. The fabric comprises the following components in percentage by weight: 40-50% of collagen fiber, 20-30% of Leo bamboo fiber, 10-20% of Modal fiber and 10-20% of cotton fiber. The fabric is finally prepared by the following steps of: blowing, cotton carding, drawing, roving, spinning and the like step by step to prepare a multifunctional yarn with four-component fiber, and then, warping, sizing, denting and the like step by step.
Description
Technical field
The present invention relates to a kind of textiles and preparation method thereof, relate in particular to a kind of environment protection multifunctional textiles that contains collagen fabric and preparation method thereof.
Background technology
In recent years; along with the develop rapidly of global economy and science and technology, people's living standard improve constantly and to the attention of healthy and environmental protection, people the emphasis clothes attractive in appearance and comfortable in; health care consciousness strengthens day by day, and is also more and more higher to the textiles feature of environmental protection and functional requirement.The economic theme of 21 century is undoubtedly environmental protection, and the collagen product with multiple medical treatment and health-care effect is subject to people's attention day by day.
The international market is with many-sided market that is applied to of collagen technology success at present, and its Application Areas comprises medical material, cosmetics, food industry, research purposes etc.The application of collagen on textiles is the inexorable trend of textile articles for use development from now on.The daily employed textiles of people is mostly through chemicals processing processing, and collagen fabric is pure biologic product, to human body without any side effect, natural environmental-protective, compared with natural fabric, the fiber of collagen has better water imbibition and natural sense of touch, even chemical fibre also can have the hydrophily the same with natural fabric and moisture retention.
The present use of collagen fabric aspect textiles of China also is being in embryo.The present invention will produce more far-reaching influence to the development of China's collagen industry, will greatly promote the development of collagen product, and the collagen product is really walked with world's pace.
Common bamboo fibre or Modal and the cotton pure textiles that spins, more single in performance, though wear pleasant, attractive in appearance, functional and the health properties aspect still is weak.For adapting to current weaving Market Situation, satisfy people's uphold nature, pursue consumption concept healthy, environmental protection.
Summary of the invention
Also has multiple functional environment protection multifunctional textiles that contains collagen fabric and preparation method thereof when the purpose of this invention is to provide a kind of environmental protection.
For achieving the above object, the technical solution used in the present invention is: a kind of environment protection multifunctional textiles that contains collagen fabric is characterized in that: the shared percentage by weight of each component is in its fabric:
Collagen fabric 40～50%;
In bamboo fibre 20～30% difficult to understand;
Modal fiber 10～20%;
Cotton fiber 10～20%.
In this product, the shared percentage by weight of each component is in the described textiles:
Collagen fabric 50%;
In bamboo fibre 20% difficult to understand;
Modal fiber 15%;
Cotton fiber 15%.
In this product, the shared percentage by weight of each component is in the described textiles:
Collagen fabric 40%;
In bamboo fibre 30% difficult to understand;
Modal fiber 20%;
Cotton fiber 10%.
In this product, the shared percentage by weight of each component is in the described textiles:
Collagen fabric 50%;
In bamboo fibre 30% difficult to understand;
Modal fiber 10%;
Cotton fiber 10%.
A kind of preparation method who contains the environment protection multifunctional textiles of collagen fabric, it is characterized in that: carry out blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn etc. respectively and pursue the multi-functional yarn that operation is spun into four component fibers, finally be woven into fabric through warping, sizing, denting etc. by operation again.
Among this preparation method:
(1) in the cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step, 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer 0.30～0.35mm.
(3) in the rove operation, roving twist factor 75～90, back zone drafting multiple 1.2～1.45;
(4) in the spinning process, spun yarn twist factor 370～390,12000～14000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the warping process, the speed of a motor vehicle 450～550m/min;
(6) in the weaving process, warp let-off tension force 360～380kg, opening traverse 80～90mm, back rest height 80～100mm, warp stop frame height 20～40 mm, opening time 280～300
o, main jet air pressure 3.0～3.5kg/cm
2, auxilliary jet pressure 3.8～4.4kg/cm
2
Among this preparation method:
(1) in the cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 955 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
(2) in the carding step, 330 rev/mins of cylinder speeds, 18 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 80, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 380,12000 rev/mins of ingot speed, back zone drafting multiple 1.25;
(5) in the warping process, speed of a motor vehicle 500m/min;
(6) in the weaving process, warp let-off tension force 365kg, opening traverse 84mm, back rest height 80mm, warp stop frame height 20 mm, opening time 290
o, main jet air pressure 3.4kg/cm
2, auxilliary jet pressure 4.0kg/cm
2
Among this preparation method:
(1) in the cotton cleaning process, 465 rev/mins of opener hired roughneck speed, 930 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
(2) in the carding step, 310 rev/mins of cylinder speeds, 17 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 85, back zone drafting multiple 1.25;
(4) in the spinning process, spun yarn twist factor 370,12500 rev/mins of ingot speed, back zone drafting multiple 1.20;
(5) in the warping process, speed of a motor vehicle 450m/min;
(6) in the weaving process, warp let-off tension force 360kg, opening traverse 82mm, back rest height 90mm, warp stop frame height 30 mm, opening time 280
o, main jet air pressure 3.2kg/cm
2, auxilliary jet pressure 3.9kg/cm
2
Among this preparation method:
(1) in the cotton cleaning process, 485 rev/mins of opener hired roughneck speed, 985 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
(2) in the carding step, 340 rev/mins of cylinder speeds, 20 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 90, back zone drafting multiple 1.40;
(4) in the spinning process, spun yarn twist factor 390,13500 rev/mins of ingot speed, back zone drafting multiple 1.35;
(5) in the warping process, speed of a motor vehicle 520m/min;
(6) in the weaving process, warp let-off tension force 380kg, opening traverse 88mm, back rest height 95mm, warp stop frame height 35 mm, opening time 295
o, main jet air pressure 3.3kg/cm
2, auxilliary jet pressure 4.2kg/cm
2
Advantageous effect of the present invention is: because the present invention adopts collagen fabric, lining bamboo fibre difficult to understand, Modal fiber, cotton fiber blending, fabric combines the good characteristic of collagen fabric and other fiber blend, take full advantage of the excellent properties of various fibers, so remedied common bamboo fibre or Modal and the cotton pure textiles that spins, in problem functional, the more single shortcoming of health properties, so following advantage is arranged:
1, functional, product combines the good characteristic of collagen fabric and other fiber, has functions such as excellent moisture absorption is ventilative, close skin health care, bactericidal, anti-mite deodorization;
2, the natural rice that the feature of environmental protection, product are collagen fabric is brown, can not print and dye, and is a kind of environmental protection fabric, people is no longer stood pollute puzzlement, more can embody the standard of the high-quality healthy living of modern humans.
3, comfortableness is good, collagen fabric, lining bamboo fibre difficult to understand, Modal fiber, cotton fiber environment protection multifunctional textiles not only feel sliding glutinous, soft comfortable sense of touch arranged, and aspect comfortable and easy to wear, characteristic out of the ordinary is arranged more, be desirable fabric next to the skin, bedding and clothes decoration product.
4, outward appearance is luxurious, and collagen fabric, lining bamboo fibre difficult to understand, Modal fiber, cotton fiber environment protection multifunctional textiles have excellent visual effect, cloth cover smooth bright and clean, lines is clear, drapability is good.
The specific embodiment
A kind of environment protection multifunctional textiles that contains collagen fabric is characterized in that: the shared percentage by weight of each component is in its fabric:
Collagen fabric 40～50%;
In bamboo fibre 20～30% difficult to understand;
Modal fiber 10～20%;
Cotton fiber 10～20%.
The preparation method of this product is characterized in that: carry out blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn etc. respectively and pursue the multi-functional yarn that operation is spun into four component fibers, finally be woven into fabric through warping, sizing, denting etc. by operation again.
Embodiment 1(most preferred embodiment)
The shared percentage by weight of each component is in collagen fabric, lining bamboo fibre difficult to understand, Modal fiber, the cotton fiber environment protection multifunctional textiles:
Collagen fabric 50%;
In bamboo fibre 30% difficult to understand;
Modal fiber 10%;
Cotton fiber 10%.
Embodiment 2
The shared percentage by weight of each component is in collagen fabric, lining bamboo fibre difficult to understand, Modal fiber, the cotton fiber environment protection multifunctional textiles:
Collagen fabric 50%;
In bamboo fibre 20% difficult to understand;
Modal fiber 15%;
Cotton fiber 15%.
Embodiment 3
The shared percentage by weight of each component is in collagen fabric, lining bamboo fibre difficult to understand, Modal fiber, the cotton fiber environment protection multifunctional textiles:
Collagen fabric 40%;
In bamboo fibre 30% difficult to understand;
Modal fiber 20%;
Cotton fiber 10%.
The present invention produces the technology of collagen fabric, lining bamboo fibre difficult to understand, Modal fiber, cotton fiber environment protection multifunctional textiles:
(1) in the cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step, 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer 0.30～0.35mm.
(3) in the rove operation, roving twist factor 75～90, back zone drafting multiple 1.2～1.45;
(4) in the spinning process, spun yarn twist factor 370～390,12000～14000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the warping process, the speed of a motor vehicle 450～550m/min;
(6) in the weaving process, warp let-off tension force 360～380kg, opening traverse 80～90mm, back rest height 80～100mm, warp stop frame height 20～40 mm, opening time 280～300
o, main jet air pressure 3.0～3.5kg/cm
2, auxilliary jet pressure 3.8～4.4kg/cm
2
Embodiment 4(optimised process embodiment)
(1) in the cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 955 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
(2) in the carding step, 330 rev/mins of cylinder speeds, 18 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 80, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 380,12000 rev/mins of ingot speed, back zone drafting multiple 1.25;
(5) in the warping process, speed of a motor vehicle 500m/min;
(6) in the weaving process, warp let-off tension force 365kg, opening traverse 84mm, back rest height 80mm, warp stop frame height 20 mm, opening time 290
o, main jet air pressure 3.4kg/cm
2, auxilliary jet pressure 4.0kg/cm
2
Embodiment 5
(1) in the cotton cleaning process, 465 rev/mins of opener hired roughneck speed, 930 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
(2) in the carding step, 310 rev/mins of cylinder speeds, 17 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 85, back zone drafting multiple 1.25;
(4) in the spinning process, spun yarn twist factor 370,12500 rev/mins of ingot speed, back zone drafting multiple 1.20;
(5) in the warping process, speed of a motor vehicle 450m/min;
(6) in the weaving process, warp let-off tension force 360kg, opening traverse 82mm, back rest height 90mm, warp stop frame height 30 mm, opening time 280
o, main jet air pressure 3.2kg/cm
2, auxilliary jet pressure 3.9kg/cm
2
Embodiment 6
(1) in the cotton cleaning process, 485 rev/mins of opener hired roughneck speed, 985 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
(2) in the carding step, 340 rev/mins of cylinder speeds, 20 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 90, back zone drafting multiple 1.40;
(4) in the spinning process, spun yarn twist factor 390,13500 rev/mins of ingot speed, back zone drafting multiple 1.35;
(5) in the warping process, speed of a motor vehicle 520m/min;
(6) in the weaving process, warp let-off tension force 380kg, opening traverse 88mm, back rest height 95mm, warp stop frame height 35 mm, opening time 295
o, main jet air pressure 3.3kg/cm
2, auxilliary jet pressure 4.2kg/cm
2
The present invention adopts collagen fabric and other three kinds of fiber blends, to reach taking, functional and the health diversification is perfect.
Collagen fabric is a kind of synthetic fiber of animal protein modification, its raw material is animal protein and hydroxyl, cyano group high polymer, can promote the health blood circulation, and the skin of human body is had close skin and health-care function, it is brown that fiber itself is natural rice, is a kind of degradable environmental protection fiber.
Claims (9)
1. environment protection multifunctional textiles that contains collagen fabric, it is characterized in that: the shared percentage by weight of each component is in its fabric:
Collagen fabric 40～50%;
In bamboo fibre 20～30% difficult to understand;
Modal fiber 10～20%;
Cotton fiber 10～20%.
2. the environment protection multifunctional textiles that contains collagen fabric according to claim 1, it is characterized in that: the shared percentage by weight of each component is in the described textiles:
Collagen fabric 50%;
In bamboo fibre 20% difficult to understand;
Modal fiber 15%;
Cotton fiber 15%.
3. the environment protection multifunctional textiles that contains collagen fabric according to claim 2, it is characterized in that: the shared percentage by weight of each component is in the described textiles:
Collagen fabric 40%;
In bamboo fibre 30% difficult to understand;
Modal fiber 20%;
Cotton fiber 10%.
4. the environment protection multifunctional textiles that contains collagen fabric according to claim 3, it is characterized in that: the shared percentage by weight of each component is in the described textiles:
Collagen fabric 50%;
In bamboo fibre 30% difficult to understand;
Modal fiber 10%;
Cotton fiber 10%.
5. preparation method who contains the environment protection multifunctional textiles of collagen fabric, it is characterized in that: carry out blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn etc. respectively and pursue the multi-functional yarn that operation is spun into four component fibers, finally be woven into fabric through warping, sizing, denting etc. by operation again.
6. the preparation method who contains the environment protection multifunctional textiles of collagen fabric according to claim 5 is characterized in that:
(1) in the cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step, 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer 0.30～0.35mm;
(3) in the rove operation, roving twist factor 75～90, back zone drafting multiple 1.2～1.45;
(4) in the spinning process, spun yarn twist factor 370～390,12000～14000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the warping process, the speed of a motor vehicle 450～550m/min;
(6) in the weaving process, warp let-off tension force 360～380kg, opening traverse 80～90mm, back rest height 80～100mm, warp stop frame height 20～40 mm, opening time 280～300
o, main jet air pressure 3.0～3.5kg/cm
2, auxilliary jet pressure 3.8～4.4kg/cm
2
7. the preparation method who contains the environment protection multifunctional textiles of collagen fabric according to claim 6 is characterized in that:
(1) in the cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 955 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
(2) in the carding step, 330 rev/mins of cylinder speeds, 18 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 80, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 380,12000 rev/mins of ingot speed, back zone drafting multiple 1.25;
(5) in the warping process, speed of a motor vehicle 500m/min;
(6) in the weaving process, warp let-off tension force 365kg, opening traverse 84mm, back rest height 80mm, warp stop frame height 20 mm, opening time 290
o, main jet air pressure 3.4kg/cm
2, auxilliary jet pressure 4.0kg/cm
2
8. the preparation method who contains the environment protection multifunctional textiles of collagen fabric according to claim 7 is characterized in that:
(1) in the cotton cleaning process, 465 rev/mins of opener hired roughneck speed, 930 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
(2) in the carding step, 310 rev/mins of cylinder speeds, 17 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 85, back zone drafting multiple 1.25;
(4) in the spinning process, spun yarn twist factor 370,12500 rev/mins of ingot speed, back zone drafting multiple 1.20;
(5) in the warping process, speed of a motor vehicle 450m/min;
(6) in the weaving process, warp let-off tension force 360kg, opening traverse 82mm, back rest height 90mm, warp stop frame height 30 mm, opening time 280
o, main jet air pressure 3.2kg/cm
2, auxilliary jet pressure 3.9kg/cm
2
9. the preparation method who contains the environment protection multifunctional textiles of collagen fabric according to claim 8 is characterized in that:
(1) in the cotton cleaning process, 485 rev/mins of opener hired roughneck speed, 985 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
(2) in the carding step, 340 rev/mins of cylinder speeds, 20 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds; 5 0.35mm that space, 0.30mm, 0.30mm, 0.30mm, 0.35mm. between cylinder and cover plate
(3) in the rove operation, roving twist factor 90, back zone drafting multiple 1.40;
(4) in the spinning process, spun yarn twist factor 390,13500 rev/mins of ingot speed, back zone drafting multiple 1.35;
(5) in the warping process, speed of a motor vehicle 520m/min;
(6) in the weaving process, warp let-off tension force 380kg, opening traverse 88mm, back rest height 95mm, warp stop frame height 35 mm, opening time 295
o, main jet air pressure 3.3kg/cm
2, auxilliary jet pressure 4.2kg/cm
2