CN102677260A - Blended fabric containing platinum fiber and production process thereof - Google Patents
Blended fabric containing platinum fiber and production process thereof Download PDFInfo
- Publication number
- CN102677260A CN102677260A CN2012101485528A CN201210148552A CN102677260A CN 102677260 A CN102677260 A CN 102677260A CN 2012101485528 A CN2012101485528 A CN 2012101485528A CN 201210148552 A CN201210148552 A CN 201210148552A CN 102677260 A CN102677260 A CN 102677260A
- Authority
- CN
- China
- Prior art keywords
- mins
- rev
- fiber
- speeds
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a blended fabric containing platinum fiber. The blended fabric comprises the following components in percentage by weight: 30-40% of platinum fiber, 10-20% of VILOFT, 10-20% of spun silk, and 30-40% of cotton fiber. A production process of the lending fabric containing platinum fiber is that the hatchet man speed of an opener is 460-500 turns/min; the cylinder speed is 300-350 turns/min, and the doffer speed is 17-21 turns/min in a hackling process; a head way broken draft times is 1.68-1.72 in a drawing process, and a rear way broken draft times is 1.28-1.32; spun yarn twist multiplier is 370-390 in a spun yarn process, the spindle speed is 10000-13000 turns/min, and the broken draft times is 1.2-1.45; and the serous fluid concentration is 11.5-12.5% in a sizing process. The blending fabric provided by the invention has an excellent visual effect, has soft comfortable tactile impression, and simultaneously has a health care function.
Description
Technical field
The present invention relates to a kind of blended yarn woven fabric and production technology thereof, relate in particular to a kind of platinum fiber, VILOFT, spun silk, cotton fiber blended yarn woven fabric and production technology thereof.
Background technology
In recent years, along with the develop rapidly of global economy with science and technology, people's living standard improve constantly and to attention healthy and environmental protection, people the emphasis clothes attractive in appearance and comfortable in, also increasingly high to textiles taking and functional requirement.
Common VILOFT or spun silk and cotton PURE YARN FABRIC, more single on performance, though wear pleasant, attractive in appearance, wrinkle resistance and the health properties aspect still is weak.For adapting to current weaving Market Situation, satisfy people's uphold nature, pursue consumption concept healthy, environmental protection, the present invention adopts platinum fiber and other three kinds of fiber blends, to reach taking and functional diversification is perfect.Chinese patent is not seen lining and the production technology thereof that platinum fiber and VILOFT and other fiber blends are arranged as yet.
The platinum fiber with the terylene is carrier, and nano level ceramic powder is mixing in polyster fibre, produces the specialty fibers with heat accumulation thermal activation blood health-care effect; The VILOFT fiber is a regenerated celulose fibre, has good warmth retention property, has good wicking, moisture regulatory function concurrently; Contain 18 seed amino acids in the silk flock, human body skin is had various health-care.Cotton fiber is as natural fabric, has softness, ventilative, good hygroscopicity, characteristics comfortable and easy to wear.
Summary of the invention
The object of the invention provides a kind of multiple characteristics such as comfortable and easy to wear, attractive in appearance that have simultaneously, also have multiple functions such as heat accumulation thermal, anti-inflammation, skin-protection and health-care, be the lining and the production technology thereof of raw material blending with tencels such as platinum fiber, VILOFT, spun silk, cotton fibers.
For realizing above-mentioned purpose, the technical scheme that the present invention adopts is:
A kind of blended yarn woven fabric that contains the platinum fiber is characterized in that: lining forms with platinum fiber, VILOFT, spun silk, cotton fiber blending, and the shared percentage by weight of each component is in its lining:
Platinum fiber 30～40%;
VILOFT 10～20%；
Spun silk 10～20%;
Cotton fiber 30～40%.
Above-mentioned a kind of blended yarn woven fabric that contains the platinum fiber is characterized in that: the shared percentage by weight of each component is in the described lining:
Platinum fiber 40%;
VILOFT 20%；
Spun silk 10%;
Cotton fiber 30%.
Above-mentioned a kind of blended yarn woven fabric that contains the platinum fiber is characterized in that: the shared percentage by weight of each component is in the described lining:
Platinum fiber 35%;
VILOFT 20%；
Spun silk 15%;
Cotton fiber 30%.
Above-mentioned a kind of blended yarn woven fabric that contains the platinum fiber is characterized in that: the shared percentage by weight of each component is in the described lining:
Platinum fiber 35%;
VILOFT 15%；
Spun silk 15%;
Cotton fiber 35%.
A kind of production technology that contains the blended yarn woven fabric of platinum fiber is characterized in that:
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step; The mixing lap of VILOFT, spun silk, cotton fiber; 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer: 0.13～0.20mm, spacing between licker-in and feed plate: 0.25～0.35mm;
The lap of platinum fiber is in carding step; 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer: 0.30～0.36mm, spacing between licker-in and feed plate: 0.25～0.35mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.68～1.72, extreme trace back zone drafting multiple 1.28～1.32; In the rove operation, roving twist factor: 75～90, back zone drafting multiple 1.2～1.45;
(4) in the spinning process, spun yarn twist factor 370～390,10000～13000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the sizing operation, concentration of slurry 11.5～12.5%, the rate of sizing 12～13%, percentage elongation is controlled in 1%;
(6) in the weaving process, back rest height 70～90mm, warp stop frame height 20～40mm, opening time 290～310
o, heald frame height 155～170mm, main jet air pressure 3.2～3.8kg/cm
2, auxilliary jet pressure 3.6～4.2kg/cm
2
The production technology of the above-mentioned blended yarn woven fabric that contains the platinum fiber is characterized in that:
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
(2) in the carding step; The mixing lap of VILOFT, spun silk, cotton fiber; 330 rev/mins of cylinder speeds, 19 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.20mm, 0.17 mm, 0.17 mm, 0.17 mm, 0.20mm, spacing between licker-in and feed plate: 0.30mm;
The lap of platinum fiber is in carding step; 330 rev/mins of cylinder speeds, 19 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.35mm, 0.30 mm, 0.30 mm, 0.30 mm, 0.35 mm, spacing between licker-in and feed plate: 0.30mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.7, extreme trace back zone drafting multiple 1.3; In the rove operation, roving twist factor: 78, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 383,13000 rev/mins of ingot speed, back zone drafting multiple 1.30;
(5) in the sizing operation, concentration of slurry 12%, the rate of sizing 13%, percentage elongation is controlled at 0.8%;
(6) in the weaving process, back rest height 80mm; Warp stop frame height 20mm; Opening time 290
o, heald frame height 160mm; Main jet air pressure 3.5kg/cm
2, auxilliary jet pressure 3.8kg/cm
2
The production technology of the above-mentioned blended yarn woven fabric that contains the platinum fiber is characterized in that:
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 465 rev/mins of opener hired roughneck speed, 910 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 465 rev/mins of opener hired roughneck speed, 910 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
(2) in the carding step; The mixing lap of VILOFT, spun silk, cotton fiber; 310 rev/mins of cylinder speeds; 17 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds. 5 space between cylinder and cover plate: 0.20mm, 0.17 mm, 0.17 mm, 0.17 mm, 0.20mm, spacing between licker-in and feed plate: 0.25mm
The lap of platinum fiber is in carding step; 310 rev/mins of cylinder speeds; 17 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds. 5 space between cylinder and cover plate: 0.35mm, 0.30 mm, 0.30 mm, 0.30 mm, 0.35 mm, spacing between licker-in and feed plate: 0.25mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.68, extreme trace back zone drafting multiple 1.28; In the rove operation, roving twist factor: 77.Back zone drafting multiple 1.25;
(4) in the spinning process, spun yarn twist factor 375,10000 rev/mins of ingot speed, back zone drafting multiple 1.25;
(5) in the sizing operation, concentration of slurry 11.5%, the rate of sizing 12%, percentage elongation is controlled at 0.9%;
(6) in the weaving process, back rest height 70mm; Warp stop frame height 30mm; Opening time 300
o, heald frame height 155mm; Main jet air pressure 3.3kg/cm
2, auxilliary jet pressure 3.7kg/cm
2
Production technology according to the above-mentioned blended yarn woven fabric that contains the platinum fiber is characterized in that:
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 490 rev/mins of opener hired roughneck speed, 980 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 490 rev/mins of opener hired roughneck speed, 980 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
(2) in the carding step; The mixing lap of VILOFT, spun silk, cotton fiber; 340 rev/mins of cylinder speeds, 21 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.20mm, 0.17 mm, 0.17 mm, 0.17 mm, 0.20mm, spacing between licker-in and feed plate: 0.35mm;
The lap of platinum fiber is in carding step; 340 rev/mins of cylinder speeds, 21 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.35mm, 0.30 mm, 0.30 mm, 0.30 mm, 0.35 mm, spacing between licker-in and feed plate: 0.35mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.72, extreme trace back zone drafting multiple 1.32; In the rove operation, roving twist factor: 79.Back zone drafting multiple 1.40;
(4) in the spinning process, spun yarn twist factor 390,12000 rev/mins of ingot speed, back zone drafting multiple 1.40;
(5) in the sizing operation, concentration of slurry 12.5%, the rate of sizing 13%, percentage elongation is controlled at 1.0%;
(6) in the weaving process, back rest height 90mm; Warp stop frame height 40mm; Opening time 310
o, heald frame height 165mm; Main jet air pressure 3.7kg/cm
2, auxilliary jet pressure 4.1kg/cm
2
The present invention adopts platinum fiber, VILOFT, spun silk, cotton fiber blending; Lining combines the good characteristic of platinum fiber and other fiber blend; Make full use of the excellent properties of various fibers; Common VILOFT or spun silk and cotton-spinning fabric have been remedied, the problem of more single shortcoming on, the health properties poor in wrinkle resistance.
Blended yarn woven fabric of the present invention has following characteristics:
1, health care property, VILOFT, spun silk and human body skin compatibility are good, and contain multiple necessary for human body amino acid.Not only have nature and environmental protection characteristic, multiple functions such as far infrared, anion, heat accumulation thermal are more arranged.
2, comfortableness is good, platinum fiber, VILOFT, spun silk, cotton blended spinning face fabric not only feel sliding glutinous, soft comfortable sense of touch is arranged, and aspect comfortable and easy to wear, characteristic out of the ordinary is arranged more.
3, outward appearance is luxurious, and platinum fiber, VILOFT, spun silk, cotton blended spinning face fabric have excellent visual effect, cloth cover smooth bright and clean, lines is clear, drapability is good.
The specific embodiment
Below in conjunction with specific embodiment the present invention is described further:
The present invention pursues the multi-function health-care yarn that operation is spun into four component fibers with platinum fiber, VILOF, spun silk, cotton blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the spun yarn etc. of carrying out respectively, finally is woven into fabric through warping, sizing, denting etc. by operation again.It is characterized in that: the shared percentage by weight of each component is in its lining:
Platinum fiber 30～40%;
VILOFT 10～20%；
Spun silk 10～20%;
Cotton fiber 30～40%.
Embodiment 1 (most preferred embodiment)
The shared percentage by weight of each component is in platinum fiber, VILOFT, spun silk, the cotton fiber blended yarn woven fabric:
Platinum fiber 40%;
VILOFT 20%；
Spun silk 10%;
Cotton fiber 30%.
Embodiment 2
The shared percentage by weight of each component is in platinum fiber, VILOFT, spun silk, the cotton fiber blended yarn woven fabric:
Platinum fiber 35%;
VILOFT 20%；
Spun silk 15%;
Cotton fiber 30%.
Embodiment 3
The shared percentage by weight of each component is in platinum fiber, VILOFT, spun silk, the cotton fiber blended yarn woven fabric:
Platinum fiber 35%;
VILOFT 15%；
Spun silk 15%;
Cotton fiber 35%.
The production technology that contains the blended yarn woven fabric of platinum fiber according to the invention:
(1) in cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step, the mixing lap of VILOFT, spun silk, cotton fiber, 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds.Cylinder and cover plate spacer: 0.13～0.20mm, spacing between licker-in and feed plate: 0.25～0.35mm;
The lap of platinum fiber is in carding step; 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer: 0.30～0.36mm, spacing between licker-in and feed plate: 0.25～0.35mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.68～1.72, extreme trace back zone drafting multiple 1.28～1.32; In the rove operation, roving twist factor: 75～90, the back zone roller gauge is amplified, and adopts less back zone drafting multiple, back zone drafting multiple 1.2～1.45;
(4) in the spinning process, spun yarn twist factor 370～390,10000～13000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the sizing operation, concentration of slurry 11.5～12.5%, the rate of sizing 12～13%, percentage elongation is controlled in 1%;
(6) in the weaving process, back rest height 70～90mm, warp stop frame height 20～40mm, opening time 290～310
o, heald frame height 155～170mm, main jet air pressure 3.2～3.8kg/cm
2, auxilliary jet pressure 3.6～4.2kg/cm
2
Embodiment 4 (optimised process embodiment)
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
(2) in the carding step, the mixing lap of VILOFT, spun silk, cotton fiber, 330 rev/mins of cylinder speeds, 19 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.20mm, 0.17 mm, 0.17mm, 0.17mm, 0.20mm, spacing between licker-in and feed plate: 0.30mm;
The lap of platinum fiber is in carding step; 330 rev/mins of cylinder speeds, 19 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; Cylinder and cover plate spacer: 0.35mm, 0.30mm, 0.30mm, 0.30mm, 0.35mm, spacing between licker-in and feed plate: 0.30mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.7, extreme trace back zone drafting multiple 1.3; In the rove operation, roving twist factor: 78, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 383,13000 rev/mins of ingot speed, back zone drafting multiple 1.30;
(5) in the sizing operation, concentration of slurry 12%, the rate of sizing 13%, percentage elongation is controlled at 0.8%;
(6) in the weaving process, back rest height 80mm; Warp stop frame height 20mm; Opening time 290
o, heald frame height 160mm; Main jet air pressure 3.5kg/cm
2, auxilliary jet pressure 3.8kg/cm
2
Embodiment 5
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 465 rev/mins of opener hired roughneck speed, 910 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 465 rev/mins of opener hired roughneck speed, 910 rev/mins of single beater scutcher hired roughneck speed, 10 rev/mins of lap roller speed;
(2) in the carding step; The mixing lap of VILOFT, spun silk, cotton fiber; 310 rev/mins of cylinder speeds, 17 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.20mm, 0.17 mm, 0.17 mm, 0.17 mm, 0.20mm, spacing between licker-in and feed plate: 0.25mm;
The lap of platinum fiber is in carding step; 310 rev/mins of cylinder speeds; 17 rev/mins of doffer speeds, 750 rev/mins of licker-in speeds. 5 space between cylinder and cover plate: 0.35mm, 0.30 mm, 0.30 mm, 0.30 mm, 0.35 mm, spacing between licker-in and feed plate: 0.25mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.68, extreme trace back zone drafting multiple 1.28; In the rove operation, roving twist factor: 77, back zone drafting multiple 1.25;
(4) in the spinning process, spun yarn twist factor 375,10000 rev/mins of ingot speed, back zone drafting multiple 1.25;
(5) in the sizing operation, concentration of slurry 11.5%, the rate of sizing 12%, percentage elongation is controlled at 0.9%;
(6) in the weaving process, back rest height 70mm; Warp stop frame height 30mm; Opening time 300
o, heald frame height 155mm; Main jet air pressure 3.3kg/cm
2, auxilliary jet pressure 3.7kg/cm
2
Embodiment 6
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 490 rev/mins of opener hired roughneck speed, 980 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 490 rev/mins of opener hired roughneck speed, 980 rev/mins of single beater scutcher hired roughneck speed, 12 rev/mins of lap roller speed;
(2) in the carding step; The mixing lap of VILOFT, spun silk, cotton fiber; 340 rev/mins of cylinder speeds; 21 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds. 5 space between cylinder and cover plate: 0.20mm, 0.17 mm, 0.17 mm, 0.17 mm, 0.20mm, spacing between licker-in and feed plate: 0.35mm;
The lap of platinum fiber is in carding step; 340 rev/mins of cylinder speeds, 21 rev/mins of doffer speeds, 850 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.35mm, 0.30 mm, 0.30 mm, 0.30 mm, 0.35 mm, spacing between licker-in and feed plate: 0.35mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.72, extreme trace back zone drafting multiple 1.32; In the rove operation, roving twist factor: 79, back zone drafting multiple 1.40;
(4) in the spinning process, spun yarn twist factor 390,12000 rev/mins of ingot speed, back zone drafting multiple 1.40;
(5) in the sizing operation, concentration of slurry 12.5%, the rate of sizing 13%, percentage elongation is controlled at 1.0%;
(6) in the weaving process, back rest height 90mm; Warp stop frame height 40mm; Opening time 310
o, heald frame height 165mm; Main jet air pressure 3.7kg/cm
2, auxilliary jet pressure 4.1kg/cm
2
Embodiment recited above describes preferred implementation of the present invention; Be not that design of the present invention and protection domain are limited; Under the prerequisite that does not break away from design concept of the present invention; Common engineers and technicians make technical scheme of the present invention in this area various modification and improvement all should fall into protection scope of the present invention.
Claims (4)
1. blended yarn woven fabric that contains the platinum fiber, it is characterized in that: lining forms with platinum fiber, VILOFT, spun silk, cotton fiber blending, and the shared percentage by weight of each component is in its lining:
Platinum fiber 30～40%;
VILOFT 10～20%；
Spun silk 10～20%;
Cotton fiber 30～40%.
2. a kind of blended yarn woven fabric that contains the platinum fiber according to claim 1 is characterized in that: the shared percentage by weight of each component is in the described lining:
Platinum fiber 40%;
VILOFT 20%；
Spun silk 10%;
Cotton fiber 30%.
3. production technology that contains the blended yarn woven fabric of platinum fiber is characterized in that:
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 460～500 rev/mins of opener hired roughneck speed, 900～1000 rev/mins of single beater scutcher hired roughneck speed, 10～12 rev/mins of lap roller speed;
(2) in the carding step; The mixing lap of VILOFT, spun silk, cotton fiber; 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer: 0.13～0.20mm, spacing between licker-in and feed plate: 0.25～0.35mm;
The lap of platinum fiber is in carding step; 300～350 rev/mins of cylinder speeds, 17～21 rev/mins of doffer speeds, 750～850 rev/mins of licker-in speeds; Cylinder and cover plate spacer: 0.30～0.36mm, spacing between licker-in and feed plate: 0.25～0.35mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.68～1.72, extreme trace back zone drafting multiple 1.28～1.32; In the rove operation, roving twist factor: 75～90, back zone drafting multiple 1.2～1.45;
(4) in the spinning process, spun yarn twist factor 370～390,10000～13000 rev/mins of ingot speed, back zone drafting multiple 1.2～1.45;
(5) in the sizing operation, concentration of slurry 11.5～12.5%, the rate of sizing 12～13%, percentage elongation is controlled in 1%;
(6) in the weaving process, back rest height 70～90mm, warp stop frame height 20～40mm, opening time 290～310
o, heald frame height 155～170mm, main jet air pressure 3.2～3.8kg/cm
2, auxilliary jet pressure 3.6～4.2kg/cm
2
4. a kind of production technology that contains the blended yarn woven fabric of platinum fiber according to claim 3 is characterized in that:
(1) in the cotton cleaning process, VILOFT, spun silk and cotton fiber wrap and blend together volume, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
The platinum fiber is in the independent rolling of cotton cleaning process, 480 rev/mins of opener hired roughneck speed, 950 rev/mins of single beater scutcher hired roughneck speed, 11 rev/mins of lap roller speed;
(2) in the carding step; The mixing lap of VILOFT, spun silk, cotton fiber; 330 rev/mins of cylinder speeds, 19 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.20mm, 0.17 mm, 0.17 mm, 0.17 mm, 0.20mm, spacing between licker-in and feed plate: 0.30mm;
The lap of platinum fiber is in carding step; 330 rev/mins of cylinder speeds, 19 rev/mins of doffer speeds, 800 rev/mins of licker-in speeds; 5 space between cylinder and cover plate: 0.35mm, 0.30 mm, 0.30 mm, 0.30 mm, 0.35 mm, spacing between licker-in and feed plate: 0.30mm;
(3) in the mixing in doubling step, two kinds of slivers are carried out bar mix slubbing back zone drafting multiple 1.7, extreme trace back zone drafting multiple 1.3; In the rove operation, roving twist factor: 78, back zone drafting multiple 1.30;
(4) in the spinning process, spun yarn twist factor 383,13000 rev/mins of ingot speed, back zone drafting multiple 1.30;
(5) in the sizing operation, concentration of slurry 12%, the rate of sizing 13%, percentage elongation is controlled at 0.8%;
(6) in the weaving process, back rest height 80mm; Warp stop frame height 20mm; Opening time 290
o, heald frame height 160mm; Main jet air pressure 3.5kg/cm
2, auxilliary jet pressure 3.8kg/cm
2