A kind of high resistance to compression carton sticks with glue agent and preparation method thereof
Technical field
The invention belongs to the tackiness agent preparing technical field, be specifically related to a kind of high resistance to compression carton and stick with glue agent and preparation method thereof.
Background technology
At present, the product of printing industry, material is a lot, quality in order to ensure wrapped product, prevent toxic substance, the application of wrapped product inferior, must get hold of the use of tackiness agent, starch adhesive more and more is subjected to the favor of carton production firm as environmentally friendly natural adhesive, but at present at the used starch adhesive of carton production industry, mainly be with starch, water, sodium hydroxide, starting material such as oxygenant are made, shortcoming is that rate of drying is slow, bonding strength is low, poor water resistance and storge quality instability etc., thus limited its application in the carton production industry to a certain extent.
Summary of the invention
The object of the present invention is to provide a kind of high resistance to compression carton to stick with glue agent and preparation method thereof.
The present invention adopts following technical scheme:
A kind of high resistance to compression carton sticks with glue agent, it is characterized in that the weight part of its constitutive material is: benzene emulsion 75-85, W-Gum 13-18, Nano titanium dioxide 23-28, zirconium white 8.0-10.0, epoxy chloropropane 1.0-1.2, polydimethylsiloxane 2.3-2.8, phenyl triethoxysilane 5.0-5.5, triethylene tetramine 15-17,12 rare basic Succinic Acid 0.7-0.9, sodium methyl silicate 11-13, methoxybutanol 2.8-3.5 and water 600-650.
Described high resistance to compression carton sticks with glue agent, it is characterized in that the weight part of its constitutive material is: benzene emulsion 80, W-Gum 15, Nano titanium dioxide 25, zirconium white 9.0, epoxy chloropropane 1.1, polydimethylsiloxane 2.5, phenyl triethoxysilane 5.2, triethylene tetramine 16,12 rare basic Succinic Acid 0.8, sodium methyl silicate 12, methoxybutanol 3.2 and water 620.
Described high resistance to compression carton sticks with glue the preparation method of agent, it is characterized in that may further comprise the steps:
(1) processing of W-Gum: the weight part by constitutive material took by weighing W-Gum, is added to the water, and is heated to 90-100 ℃, is incubated 10-20 minute, by ozone bubbling 30-40 minute;
(2) weight part by constitutive material takes by weighing other each constitutive material, with above-mentioned steps (1) mixing of materials, stirs, and is heated to 80-90 ℃, and restir reaction 1.0-1.5h obtains.
Beneficial effect of the present invention:
It is major ingredient that the present invention adopts benzene emulsion and W-Gum, by the ozone Oxidation Treatment to W-Gum, has improved the premium properties of W-Gum, improved the ultimate compression strength of product greatly, and preparation method of the present invention is simple, and cost is low, is fit to scale operation.
Embodiment
Embodiment 1: high resistance to compression carton sticks with glue agent, and the weight part of its constitutive material (jin) is: benzene emulsion 80, W-Gum 15, Nano titanium dioxide 25, zirconium white 9.0, epoxy chloropropane 1.1, polydimethylsiloxane 2.5, phenyl triethoxysilane 5.2, triethylene tetramine 16,12 rare basic Succinic Acid 0.8, sodium methyl silicate 12, methoxybutanol 3.2 and water 620.
High resistance to compression carton sticks with glue the preparation method of agent, may further comprise the steps:
(1) processing of W-Gum: the weight part by constitutive material took by weighing W-Gum, is added to the water, and is heated to 90-100 ℃, is incubated 10-20 minute, by ozone bubbling 30-40 minute;
(2) weight part by constitutive material takes by weighing other each constitutive material, with above-mentioned steps (1) mixing of materials, stirs, and is heated to 80-90 ℃, and restir reaction 1.0-1.5h obtains.
The tackiness agent that above-described embodiment 1 makes is used for carton performance data after testing:
Outward appearance: oyster white; Titre: 55-63 drips/minute; Time of drying 20-23min; Ultimate compression strength: 570-630Kgf; Pop strength: 4820Kpa/10min; Transfix intensity: 220Kgf.cm; Water tolerance: 〉=3.5h; Cost: 440 yuan/ton.