CN103333644A - Adhesive agent for high-strength paper box and preparation method thereof - Google Patents
Adhesive agent for high-strength paper box and preparation method thereof Download PDFInfo
- Publication number
- CN103333644A CN103333644A CN2013102086924A CN201310208692A CN103333644A CN 103333644 A CN103333644 A CN 103333644A CN 2013102086924 A CN2013102086924 A CN 2013102086924A CN 201310208692 A CN201310208692 A CN 201310208692A CN 103333644 A CN103333644 A CN 103333644A
- Authority
- CN
- China
- Prior art keywords
- sweet potato
- potato starch
- constitutive material
- preparation
- acetate emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an adhesive agent for high-strength paper box and a preparation method thereof. The adhesive agent comprises following raw materials: polyvinyl acetate emulsion, sweet potato starch, calcium carbonate, high-abrasion-resistance carbon black, tert-butyl hydroperoxide, polytetrafluoroethylene wax, methyl triethoxysilane, brown sugar, sodium benzoate, polyvinyl alcohol, diacetone alcohol, and water. The method adopts polyvinyl acetate emulsion and sweet potato starch as the main materials, and through pre-treatment of sweet potato starch, the performances of the sweet potato starch are improved. Trough crosslink among brown sugar, polyvinyl alcohol, tert-butyl hydroperoxide in the ingredients, the adhesive ability of the sweet potato starch is improved, and the adhesive strength is increased. The preparation method has the advantages of simple preparation, low cost and suitability for mass production.
Description
Technical field
The invention belongs to the tackiness agent preparing technical field, be specifically related to the saturating carton of a kind of high strength and stick with glue agent and preparation method thereof.
Background technology
At present, the product of printing industry, material is a lot, quality in order to ensure wrapped product, prevent toxic substance, the application of wrapped product inferior, must get hold of the use of tackiness agent, starch adhesive more and more is subjected to the favor of carton production firm as environmentally friendly natural adhesive, but at present at the used starch adhesive of carton production industry, mainly be with starch, water, sodium hydroxide, starting material such as oxygenant are made, shortcoming is that rate of drying is slow, bonding strength is low, poor water resistance and storge quality instability etc., thus limited its application in the carton production industry to a certain extent.
Summary of the invention
The object of the present invention is to provide the saturating carton of a kind of high strength to stick with glue agent and preparation method thereof.
The present invention adopts following technical scheme:
The saturating carton of high strength sticks with glue agent, and the weight part of its constitutive material is: polyvinyl acetate emulsion 70-80, sweet potato starch 17-23, calcium carbonate 28-32, high wear-resistant carbon black 12-15, tertbutyl peroxide 0.5-1.0, tetrafluoroethylene wax 1.0-1.5, Union carbide A-162 3.0-5.0, brown sugar 15-20, Sodium Benzoate 0.5-0.8, polyvinyl alcohol 5.5-6.5, diacetone alcohol 1.8-2.5 and water 550-650.
The saturating carton of high strength sticks with glue agent, and the weight part of its constitutive material is: polyvinyl acetate emulsion 75, sweet potato starch 20, calcium carbonate 30, high wear-resistant carbon black 14, tertbutyl peroxide 0.8, tetrafluoroethylene wax 1.2, Union carbide A-162 4.0, brown sugar 18, Sodium Benzoate 0.7, polyvinyl alcohol 6.0, diacetone alcohol 2.2 and water 600.
The saturating carton of high strength sticks with glue the preparation method of agent, may further comprise the steps:
(1) processing of sweet potato starch: the weight part by constitutive material takes by weighing sweet potato starch, adds the water gelatinization then 20-30 minute, and the microwave oven of putting into 800-1000w heats 20-25s, uses ultrasonication 2-3h again after the taking-up cooling, takes out namely;
(2) weight part by constitutive material takes by weighing each constitutive material, sweet potato starch, polyvinyl acetate emulsion and remaining water after earlier above-mentioned steps (1) being handled mix, and stir, and add other constitutive material then successively, restir reaction 50-60min obtains.
Beneficial effect of the present invention:
It is major ingredient that the present invention adopts polyvinyl acetate emulsion and sweet potato starch, by anticipating sweet potato starch, improved the performance of sweet potato starch, have brown sugar, polyvinyl alcohol, tertbutyl peroxide in the present invention's prescription by crosslinked, improved the bonding force with sweet potato starch, increased bonding strength, and preparation method of the present invention has been simple, cost is low, is fit to scale operation.
Embodiment
Embodiment 1: the saturating carton of high strength sticks with glue agent, and the weight part of its constitutive material (jin) is: polyvinyl acetate emulsion 75, sweet potato starch 20, calcium carbonate 30, high wear-resistant carbon black 14, tertbutyl peroxide 0.8, tetrafluoroethylene wax 1.2, Union carbide A-162 4.0, brown sugar 18, Sodium Benzoate 0.7, polyvinyl alcohol 6.0, diacetone alcohol 2.2 and water 600.
The saturating carton of high strength sticks with glue the preparation method of agent, may further comprise the steps:
(1) processing of sweet potato starch: the weight part by constitutive material takes by weighing sweet potato starch, adds the water gelatinization then 25 minutes, and the microwave oven of putting into 900w heats 22s, uses ultrasonication 2-3h again after the taking-up cooling, takes out namely;
(2) weight part by constitutive material takes by weighing each constitutive material, and sweet potato starch, polyvinyl acetate emulsion and remaining water after earlier above-mentioned steps (1) being handled mix, and stir, and add other constitutive material then successively, and restir reaction 55min obtains.
The tackiness agent that above-described embodiment 1 makes is used for carton performance data after testing:
Outward appearance: oyster white; Titre: 53-60 drips/minute; Time of drying 18-22min; Ultimate compression strength: 510-570Kgf; Pop strength: 4830Kpa/10min; Transfix intensity: 280Kgf.cm; Water tolerance: 〉=4.5h; Cost: 480 yuan/ton.
Claims (3)
1. the saturating carton of high strength sticks with glue agent, it is characterized in that the weight part of its constitutive material is: polyvinyl acetate emulsion 70-80, sweet potato starch 17-23, calcium carbonate 28-32, high wear-resistant carbon black 12-15, tertbutyl peroxide 0.5-1.0, tetrafluoroethylene wax 1.0-1.5, Union carbide A-162 3.0-5.0, brown sugar 15-20, Sodium Benzoate 0.5-0.8, polyvinyl alcohol 5.5-6.5, diacetone alcohol 1.8-2.5 and water 550-650.
2. the saturating carton of high strength according to claim 1 sticks with glue agent, it is characterized in that the weight part of its constitutive material is: polyvinyl acetate emulsion 75, sweet potato starch 20, calcium carbonate 30, high wear-resistant carbon black 14, tertbutyl peroxide 0.8, tetrafluoroethylene wax 1.2, Union carbide A-162 4.0, brown sugar 18, Sodium Benzoate 0.7, polyvinyl alcohol 6.0, diacetone alcohol 2.2 and water 600.
3. the saturating carton of high strength as claimed in claim 1 sticks with glue the preparation method of agent, it is characterized in that may further comprise the steps:
(1) processing of sweet potato starch: the weight part by constitutive material takes by weighing sweet potato starch, adds the water gelatinization then 20-30 minute, and the microwave oven of putting into 800-1000w heats 20-25s, uses ultrasonication 2-3h again after the taking-up cooling, takes out namely;
(2) weight part by constitutive material takes by weighing each constitutive material, sweet potato starch, polyvinyl acetate emulsion and remaining water after earlier above-mentioned steps (1) being handled mix, and stir, and add other constitutive material then successively, restir reaction 50-60min obtains.