CN103788742A - High-temperature resistant environment-friendly glue powder - Google Patents
High-temperature resistant environment-friendly glue powder Download PDFInfo
- Publication number
- CN103788742A CN103788742A CN201310449123.9A CN201310449123A CN103788742A CN 103788742 A CN103788742 A CN 103788742A CN 201310449123 A CN201310449123 A CN 201310449123A CN 103788742 A CN103788742 A CN 103788742A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- glue
- glue powder
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-temperature resistant environment-friendly glue powder which consists of the following components in parts by weight: 40-60 parts of hydroxymethyl cellulose, 5-10 parts of corn starch, 1-5 parts of nano calcium carbonate, 5-10 parts of latex powder, 10-20 parts of shell powder, 15-20 parts of fly ash, 5-10 parts of viscose reinforcing agent and 3-5 parts of sodium benzoate. After the glue powder disclosed by the invention is dissolved in water, the high-molecular material and auxiliary thereof are adhered to the light calcium carbonate to form a high-performance glue binder; and the coating prepared from the glue powder has the advantages of convenience in construction, no urinary stream, good leveling property, no rolling and fast film formation and avoids the phenomena of rolling and falling in a high-temperature state.
Description
Technical field
The present invention relates to a kind of high temperature resistant environment-protective glue powder.
Background technology
The glue using in the middle of construction industry is different from common glue, and its requirement has higher adhesive ability, and keeps the time sufficiently long of viscosity.The building glue using on Vehicles Collected from Market has two kinds of modes of production, and a kind of is that manufacturer directly will put on market after the liquid packaging of the chemical materials such as polyvinyl alcohol, acrylamide production; After another kind is processed into building glue by manufacturer by high molecular polymer rubber powders such as PVA, EVA, CMC, packing is put on market.The packing material that these two kinds of modes of production need is large, energy-conservation not; Put storing cost on market high, economical not; The product of producing uses inconvenient; In the glue composition of its production, there are the toxic substances such as formaldehyde, ammonia, sanitas, not environmental protection; Product is in transportation, and cracky, can cause the wasting of resources; Glue quality is low, the putty poor adhesive force of modulation, easily rolls up skin, comes off etc.; Use the cement-based material of glue modulation for the base material such as exterior wall, because cement based kapillary water suction reason easily causes expansion, cracking, weathering, the problem such as pollute, go mouldy and cause peeling off when freeze-thaw cycle.At present a lot of producers have all carried out improving and upgrading for the feed composition of building glue, adopt the novel environment friendly building putties rubber powder of the raw material production such as latex powder, methylcellulose gum, defoamer, binding agent, white cement as Anhui Architectural Sci. Research & Design Inst., it is specifically designed to and replaces building glue configuration inner, external wall putty inferior.But the adhesive for building pigment (solid glue) of prior art, except its adhesive ability power differs, the shortcoming of ubiquity contaminate environment simultaneously, some Long contact time can cause damage to builder's health.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is, provide a kind of light calcium carbonate base material that adopts as carrier, by multiple macromolecular material, be aided with multifunctional assistant, scientific formula forms, have nontoxic, pollution-free, odorlessness, "dead", without alkaline feature, there is the high temperature resistant environment-protective glue powder of resistant to elevated temperatures feature.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of high temperature resistant environment-protective glue powder, is grouped into by the one-tenth of following weight part:
Walocel MT 20.000PV 40～60;
W-Gum 5～10;
Nano-calcium carbonate 1～5;
Latex powder 5～10;
Oyster shell whiting 10～20;
Flyash 15～20;
Viscosity-increasing agent 5～10;
Sodium Benzoate 3～5.
The advantage of high temperature resistant environment-protective glue powder of the present invention is: after the present invention is water-soluble, its macromolecular material and auxiliary agent depend on light calcium carbonate and form a kind of high performance glue disjunctor, with the coating of its preparation, easy construction, do not urinate line, good leveling property, does not roll up skin, film forming is fast, can not roll up skin obscission under the condition of high temperature.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details;
A kind of high temperature resistant environment-protective glue powder, is grouped into by the one-tenth of following weight part:
Walocel MT 20.000PV 40～60;
W-Gum 5～10;
Nano-calcium carbonate 1～5;
Latex powder 5～10;
Oyster shell whiting 10～20;
Flyash 15～20;
Viscosity-increasing agent 5～10;
Sodium Benzoate 3～5.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, variation, remodeling, interpolation or the replacement made, all should belong to protection scope of the present invention.
Claims (1)
1. a high temperature resistant environment-protective glue powder, is characterized in that, is grouped into by the one-tenth of following weight part:
Walocel MT 20.000PV 40～60;
W-Gum 5～10;
Nano-calcium carbonate 1～5;
Latex powder 5～10;
Oyster shell whiting 10～20;
Flyash 15～20;
Viscosity-increasing agent 5～10;
Sodium Benzoate 3～5.