CN103642297A - Polishing-free emulsion putty paste - Google Patents
Polishing-free emulsion putty paste Download PDFInfo
- Publication number
- CN103642297A CN103642297A CN201310716612.6A CN201310716612A CN103642297A CN 103642297 A CN103642297 A CN 103642297A CN 201310716612 A CN201310716612 A CN 201310716612A CN 103642297 A CN103642297 A CN 103642297A
- Authority
- CN
- China
- Prior art keywords
- putty
- parts
- water
- polishing
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polishing-free emulsion putty paste and relates to a surface filling material for pretreating a construction surface before paint construction. After adjusting the formula, putty construction on a flat wall surface is easy, silk marks do not exist, the coating demand of a dope can be met without polishing when a putty wall is brushed; the formula of the materials of the polishing-free emulsion putty paste comprises the following components in parts by weight: 15-20 parts of hydroxypropyl methyl (HPMC), 8-10 parts of re-dispersible emulsion powder, 1-2 parts of starch ether, 150-250 parts of sodium bentonite, 1-1.5 parts of ash calcium (polyacrylamide), 300-450 parts of lime powder, 650-500 parts of heavy calcium carbonate (white stone powder) and 400-500 parts of water. By adopting polishing-free putty, a lot of dust generated because of polishing is prevented from affecting the heath of constructors, a construction process is omitted, the human power is saved, and the human power cost is greatly saved under an existing condition of high human power salary.
Description
Technical field
the present invention relates to paint before class construction, construction surface is carried out to pretreated a kind of Surface filling material, i.e. a kind of finishing wallcovering claircolle and production method.
Background technology
the wall surface putty that existing market is generally used probably divides following 4 kinds:
one, water-fast dry-powder putty
its raw materials for production are: hydroxypropyl methyl fiber (HPMC), redispersible latex powder, water-ground limestone (white stone powder), grey calcium (lime powder), white cement.There is the outstanding problem in polishing in the putty that this formula is produced: as too hard, be just difficult for polishing, too soft metope after polishing has sand paper vestige, after japanning, can not cover, and makes metope attractive in appearance not, and difficulty of construction is large.
two, neutral dry-powder putty
its raw materials for production are: carboxymethyl cellulose (CMC), water-ground limestone (white stone powder).The dry-powder putty that this formula is produced is very not water-fast, whitewash coating at metope in moisture regain situation repeatedly, easily produce obscission, and because growing very soon mould containing metope in carboxymethyl cellulose (CMC) moisture regain situation repeatedly, metope is not only ugly, is also detrimental to health.
three, now join glue putty
on market, also use 107, 108, the on-the-spot adapted glue of white glue with vinyl and water-ground limestone (white stone powder) putty, glue putty existing problems: because of the way difference of different glue itself, if any glue use formol, some manufacturers are for reaching the harmful chemical industry additives such as adding acrylamide that reduces the cost, in construction, because the concentration of glue is high, make the too hard bad polishing of its putty of allotting, so add in a large number ripe rubber powder to improve its workability during construction, and in ripe rubber powder composition containing a large amount of organic starch, when metope gets damp again repeatedly, also easily produce and go mouldy, metope grows stain, to health, bring very large injury.
four, aqueous putty cream
raw materials for production are: carboxymethyl cellulose (CMC), sheet alkali, 108 glue, formaldehyde, water.Due to the interpolation of formaldehyde, directly cause affecting HUMAN HEALTH.
summary of the invention:
the present invention wants technical solution problem: a kind of latex putty cream of exempting to polish is provided, it is after adjusting formula, makes putty construction levelling metope easy, pays no attention to sleek, brushing putty metope need not be polished and just can be reached coating coating requirement, and has overcome existing putty all defect.
technical solution of the present invention: a kind of latex putty cream of exempting to polish, its parts by weight of raw materials compositing formula is: hydroxypropyl methyl fiber (HPMC) 15-20, redispersible latex powder 8-10, starch ethers 1-2, sodium bentonite 150-250, polyacrylamide 1-1.5, grey calcium (lime powder) 300-450, water-ground limestone (white stone powder) 650-500, water 400-500.
further described grey calcium (lime powder) can adopt lime putty to substitute, and consumption is pressed lime putty containing grey calcium amount conversion amount.
production stage: 1, take each pulvis raw material by above-mentioned weight part;
2, each dry powder raw material having weighed up is all added stirrer stir 15-25 minutes, stir;
3, will add in steeliness blender by the formula water yield, then add the dry mash being stirred, and stir to make for 30-50 minutes and exempt to polish latex putty cream;
beneficial effect of the present invention is:
1, the putty of exempting to polish has been avoided, because polishing produces a large amount of dusts, affect workmen healthy, has also avoided causing atmospheric pollution because of the dust of polishing.
, the selected raw material of putty of exempting to polish is all to the nontoxic environmental protection raw material of human body, uses the metope of the putty finishing of exempting to polish can again not discharge objectionable impurities, therefore safe and reliable.
, owing to exempting from polishing, saved working procedure one, save manpower, for existing high manpower wage situation, significantly saved human cost.
4, this putty meets GB18582-2008 national standard through check, not containing free formaldehyde, benzene, toluene, ethylbenzene, dimethylbenzene objectionable constituent.
Specific embodiment
embodiment mono-
parts by weight of raw materials compositing formula is: hydroxypropyl methyl fiber (HPMC) 15, redispersible latex powder 8, starch ethers 1, sodium bentonite 150, polyacrylamide 1.5, grey calcium (lime powder) 300, water-ground limestone (white stone powder) 650, water 400.
production stage: 1, take each pulvis raw material by above-mentioned weight part;
2, each dry powder raw material having weighed up is all added stirrer stir 15 minutes, stir;
3, will add in steeliness blender by the formula water yield, then add the dry mash being stirred, and stir to make for 50 minutes and exempt to polish latex putty cream;
embodiment bis-
parts by weight of raw materials compositing formula is: hydroxypropyl methyl fiber (HPMC) 18, redispersible latex powder 9, starch ethers 1.5, sodium bentonite 190, polyacrylamide 1, grey calcium (lime powder) 400, water-ground limestone (white stone powder) 600, water 450.
production stage: 1, take each pulvis raw material by above-mentioned weight part;
2, each dry powder raw material having weighed up is all added stirrer stir 20 minutes, stir;
3, will add in steeliness blender by the formula water yield, then add the dry mash being stirred, and stir to make for 40 minutes and exempt to polish latex putty cream.
embodiment tri-
parts by weight of raw materials compositing formula is: hydroxypropyl methyl fiber (HPMC) 20, redispersible latex powder 10, starch ethers 2, sodium bentonite 250, polyacrylamide 1.3, grey calcium (lime powder) 450, water-ground limestone (white stone powder) 500, water 500.
production stage: 1, take each pulvis raw material by above-mentioned weight part;
2, each dry powder raw material having weighed up is all added stirrer stir 25 minutes, stir;
3, will add in steeliness blender by the formula water yield, then add the dry mash being stirred, and stir to make for 30 minutes and exempt to polish latex putty cream.
Claims (6)
1. exempt from the glue putty of polishing, it is characterized in that: its parts by weight of raw materials compositing formula is: hydroxypropyl methyl fiber 15-20, redispersible latex powder 8-10, starch ethers 1-2, sodium bentonite 150-250, polyacrylamide 1-1.5, grey calcium 300-450, water-ground limestone 650-500, water 400-500.
2. putty according to claim 1, is characterized in that:
parts by weight of raw materials compositing formula is: hydroxypropyl methyl fiber 15, redispersible latex powder 8, starch ethers 1, sodium bentonite 250, polyacrylamide 1.5, grey calcium 300, water-ground limestone 650, water 400.
3. putty according to claim 1, is characterized in that:
parts by weight of raw materials compositing formula is: hydroxypropyl methyl fiber 18, redispersible latex powder 9, starch ethers 1.5, sodium bentonite 190, polyacrylamide 1, grey calcium 400, water-ground limestone 600, water 450.
4. putty according to claim 1, is characterized in that:
parts by weight of raw materials compositing formula is: hydroxypropyl methyl fiber 20, redispersible latex powder 10, starch ethers 2, sodium bentonite 250, polyacrylamide 1.3, grey Ca45 0, water-ground limestone 500, water 500.
5. according to the putty one of claim 1-4 Suo Shu, it is characterized in that:
described grey calcium (lime powder) adopts lime putty to substitute, and consumption is pressed lime putty containing grey calcium amount conversion amount.
6. according to the production method of the putty one of claim 1-4 Suo Shu, it is characterized in that: comprise following steps:
1), by above-mentioned weight part, take each pulvis raw material;
2), all add stirrer to stir 15-25 minutes each dry powder raw material having weighed up, stir;
3), the dry mash being stirred is added in steeliness blender, and add the water yield by formula, stir to make for 30-50 minutes and exempt from the putty of polishing.
?
?