CN1454945A - Environmental-protection type gypsum-based putty powder for building - Google Patents
Environmental-protection type gypsum-based putty powder for building Download PDFInfo
- Publication number
- CN1454945A CN1454945A CN 03117999 CN03117999A CN1454945A CN 1454945 A CN1454945 A CN 1454945A CN 03117999 CN03117999 CN 03117999 CN 03117999 A CN03117999 A CN 03117999A CN 1454945 A CN1454945 A CN 1454945A
- Authority
- CN
- China
- Prior art keywords
- powder
- plaster
- friendly type
- paris
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to an environment-protecting gypsum base building putty powder, which uses building gupsum as main setting hardening component, and utilizes the composite retarding agent to resolve the problems of that the building gupsum can be quickly set and hardened and single retarding agent can be resulted into large strength loss. Said invention adopts inorganic mineral powder and cellulose ether composition to reduce material cost and improve water-holding property of putty, and adopts water-soluble adhesive powder to raise cohesional strength of building putty, and said environment-protecting type gypsum base building putty powder is a single component solid powder, has no harmful substance, and has good construction property, and said putty surface is fine and smooth.
Description
Technical field:
The invention belongs to material of construction, it is as inner wall of building putty.
Background technology:
Traditional architecture putty is filler with inorganic inert mineral mainly, is filmogen with the organic polymer material, and the putty completion of cure relies on polymer film forming.Such building putties cohesive strength is lower, shrinks greatlyyer, generally only is suitable for constructing on more smooth metope, if thickness is excessive, then easy to crack; Operating efficiency is low, and is dry slow, long construction period; Preparation is at the construction field (site) used inconvenient; Construction of the putty that has and toxic substance such as release formaldehyde between the usage period, construction environment is abominable, and environmental pollution is big.And traditional architecture putty usually adopts single water-holding agent technology, i.e. ether of cellulose water conservation, and its cost is higher.Consider that plaster of Paris has hydration activity, fast solidifying, cohesive strength height, good, the exquisite in texture of volume stability, satisfy the basic demand of building putties to wood property, and it is affine harmless to human body, be green building material, the contriver is under the subsidy of National Natural Science Foundation of China and Chongqing City Science ﹠. Technology Commision (subsidize item number is respectively 50078055,2000-6375), with the plaster of Paris is main raw material, is that research emphasis has been carried out experimental study with putty workability, water-retentivity, cohesiveness.Adopt the main setting and harden component of plaster of Paris as building putty powder, break through traditional architecture putty and relied on the technology mode that adds inorganic inert filler in the organic polymer filmogen, and on " New Building Materials " the 1st phase in 2002, delivered paper " prescription and the performance study of putty built in phosphogypsum capital construction ", this article has highlighted the part achievement of this research.
The production technique that the present invention adopts is a common process.
Summary of the invention:
The objective of the invention is to avoid above-mentioned the deficiencies in the prior art part and provide a kind of and do not contain Toxic matter, have good workability, short construction period, cohesive strength height, water-retentivity, the fine and smooth slick environment-friendly type gypsum-based construction putty powder in putty surface.
In order to realize the foregoing invention purpose, technical scheme of the present invention is:
Prepared environment-friendly type gypsum-based construction putty powder, it comprises following component and weight percent:
Plaster of Paris 60-85
Compound retarder 0.15-0.5
Compound water retaining agent 3.05-10.2
Water-soluble gelatin powder 0.1-3
Filler 5-30
Wherein, plaster of Paris is a kind of in the following plaster of Paris: the plaster of Paris of the plaster of Paris of plaster of paris preparation, phosphogypsum preparation, the plaster of Paris of desulfurated plaster preparation; Water-soluble gelatin powder is a kind of in the following water-soluble gelatin powder: modified tapioca starch, polyvinyl alcohol rubber powder, ethene-vinyl acetate emulsion copolymer powder, polyacrylic ester latex powder; Filler is a kind of in the following filler: dry powder, talcum powder.Plaster of Paris has hydration activity, fast solidifying, cohesive strength height, good, the exquisite in texture, affine harmless to human body of volume stability, be green building material, can be used for preparing environment-friendly type building putty, add plaster of Paris, to improve the cohesive strength of this environment-friendly type gypsum-based construction putty powder.Add above-mentioned water-soluble solid powder rubber powder, to improve the cohesive strength of this building putty powder.Ethene-vinyl acetate emulsion copolymer powder, polyvinyl alcohol, modified tapioca starch, polyacrylic ester latex powder can effectively improve the cohesive strength of building putties.Mix 0.1%～0.5% ethene-vinyl acetate emulsion copolymer powder or 0.6%～1.0% polyvinyl alcohol rubber powder or 2%～3% modified tapioca starch glue, can satisfy of the requirement of this environment-friendly type gypsum-based construction putty powder cohesive strength.Add above-mentioned filler, to improve the application property of this environment-friendly type gypsum-based construction putty powder.In order to reduce the retardant volume, improve the putty application property, can mix a certain proportion of inorganic inert filler, increase with the filler volume, putty prolongs time of coagulation, and draw-off property, grinability turn for the better, but intensity, cohesiveness reduce.Talcum powder, dry powder etc. can effectively improve the workability of building putties.
Purpose of the present invention can reach by following measure:
Adopt compound retarder, its component and weight percent:
Citric acid 0.05-0.2
Gelatine 0.1-0.3
Add above-mentioned compound retarder, to regulate the plaster of Paris setting and harden time.Usually the plaster of Paris setting and harden is very fast, presetting period is 6～30 minutes, and operable time has only 4～10 minutes, can not satisfy the construction requirement of building putties, the working hour of building putties generally could satisfied construction requirement more than 2 hours, must adopt the slow setting technology for this reason.Retardant kind, volume difference are different to the prolongation of presetting period and final setting time.Common single slow setting technology exists retardant large usage quantity, defective that the hardenite loss of strength is very big.This putty adopts citric acid and the compound slow setting technology of gelatine, can effectively improve the defective that single slow setting technology exists.When the citric acid volume be 0.1%, when the gelatine volume is 0.2%, the presetting period of plaster of Paris was 172 minutes, final setting time can reach 213 minutes, and its folding strength can reach 2.11MPa, ultimate compression strength can reach 8.53MPa.
Adopt compound water retaining agent, its component and weight percent:
Methyl cellulose ether or TYLOSE 30000 or hydroxypropyl methyl cellulose ether 0.05-0.2
Wilkinite 3-10
Add above-mentioned compound water retaining agent, to improve the water-retentivity of this environment-friendly type gypsum-based construction putty powder.Water-retentivity is the important technology index of building putties, and good water-retentivity can be avoided building putties plastic cracking and surperficial efflorescence.Building putties adopts single water-holding agent technology usually, and ether of cellulose is the commodity water-holding agent of using always, different water-holding agent kind and volume, improve the water-retentivity difference of building putties, wherein methyl cellulose ether water conservation effect is best, but its volume is bigger, and cost is higher.Initiate component wilkinite has another name called otaylite or amargosite, with the montmorillonite be the essential mineral composition the particulate clay, often contain feldspar, quartz, visit stone, calcite and pyroclastics.Main chemical compositions is: SiO
2, Al
2O
3And small amount of Fe
2O
3, MgO, CaO, K
2O, Na
2O and TiO
2Deng.Generally be white in color, be pale green, light greenish blue, greyish white, pink isochrome when impure.Wilkinite has the intensive water-absorbent, and suction back volume expands 10-30 doubly, is to suspend and gelatinized in the aqueous solution, has the characteristic of cationic exchange, also has high cohesiveness and resistivity against fire.Wilkinite is a laminate structure, has water retention, can effectively reduce latter's volume with the compound use of methyl cellulose ether, reduces the material cost of putty preparation.When the methyl cellulose ether volume be 0.2%, when wilkinite is 3%～10%, the building putties percentage of water loss is 0.1042g/cm
2, over dry folding strength and ultimate compression strength are respectively 2.60MPa and 9.70MPa.
Test shows, when proportioning is: plaster of Paris 68.96, citric acid 0.1, gelatine 0.2, methyl cellulose ether 0.1, wilkinite 4.0, ethene-vinyl acetate emulsion copolymer powder 0.25, dry powder 26.39, the performance of this environment-friendly type gypsum-based construction putty powder is: standard consistency 46%, surface drying time 2 hours 10 minutes, grinability 48%, whiteness 78, water retention 96%, over dry folding strength 2.8MPa, over dry ultimate compression strength 6.2MPa, cohesive strength 0.72MPa.
The present invention has following advantage compared to existing technology:
1. do not contain Toxic matter.
2. cohesive strength height, operating efficiency height, short construction period.
3. adopt wilkinite and ether of cellulose composite water conservation technology, not only reduced the material cost of putty, and improved water retention property.
4. have good workability, the putty surface is moist.
5. the present invention is a single component solid powdery product, need not on-the-spot prepare, and is easy to use.
Embodiment:
Specific embodiments of the invention are as follows, and each embodiment all represents with weight percent.
Embodiment 1:
Plaster of Paris 68.96
Citric acid 0.1
Gelatine 0.2
Methyl cellulose ether 0.1
Wilkinite 4
Ethene-vinyl acetate emulsion copolymer powder 0.25
Dry powder 26.39.
Embodiment 2:
Plaster of Paris 77.3
Citric acid 0.15
Gelatine 0.1
Hydroxypropyl methyl cellulose ether 0.2
Wilkinite 5.7
Polyvinyl alcohol rubber powder 0.85
Talcum powder 15.7.
Embodiment 3:
Plaster of Paris 85
Citric acid 0.1
Gelatine 0.2
TYLOSE 30000 0.1
Wilkinite 6.25
Ethene-vinyl acetate emulsion copolymer powder 0.25
Dry powder 8.1.
Embodiment 4:
Plaster of Paris 60
Citric acid 0.05
Gelatine 0.25
Methyl cellulose ether 0.05
Wilkinite 8
Modified tapioca starch 2.5
Talcum powder 29.15.
Embodiment 5:
Plaster of Paris 81.5
Citric acid 0.2
Gelatine 0.1
Hydroxypropyl methyl cellulose ether 0.2
Wilkinite 3
Modified tapioca starch 2.5
Dry powder 12.5.
Embodiment 6:
Plaster of Paris 65
Citric acid 0.1
Gelatine 0.1
Methyl cellulose ether 0.05
Wilkinite 10
Polyvinyl alcohol rubber powder 1
Talcum powder 23.75.
Embodiment 7:
Plaster of Paris 71.39
Citric acid 0.05
Gelatine 0.25
TYLOSE 30000 0.2
Wilkinite 7.45
Ethene-vinyl acetate latex powder 0.1
Talcum powder 20.56.Above-mentioned gypsum-based construction putty powder can once claim foot stirring simultaneously to form required starting material in proportion.
Claims (10)
1. environment-friendly type gypsum-based construction putty powder is characterized in that this environment-friendly type gypsum-based construction putty powder comprises following component and weight percent:
Plaster of Paris 60-85
Compound retarder 0.15-0.5
Compound water retaining agent 3.05-10.2
Water-soluble gelatin powder 0.1-3
Filler 5-30
Wherein, plaster of Paris is a kind of in the following plaster of Paris: the plaster of Paris of the plaster of Paris of plaster of paris preparation, phosphogypsum preparation, the plaster of Paris of desulfurated plaster preparation; Compound retarder is citric acid and gelatine; Compound water retaining agent is a kind of and wilkinite in methyl cellulose ether, TYLOSE 30000, the hydroxypropyl methyl cellulose ether; Water-soluble gelatin powder is a kind of in the following water-soluble gelatin powder: modified tapioca starch, ethene-vinyl acetate emulsion copolymer powder, polyvinyl alcohol rubber powder, polyacrylic ester latex powder; Filler is a kind of in the following filler: talcum powder, dry powder.
2. environment-friendly type gypsum-based construction putty powder as claimed in claim 1 is characterized in that the component and the weight percent of compound retarder:
Citric acid 0.05-0.2
Gelatine 0.1-0.3.
3. environment-friendly type gypsum-based construction putty powder as claimed in claim 1 is characterized in that the component and the weight percent of compound water retaining agent: methyl cellulose ether or TYLOSE 30000 or hydroxypropyl methyl cellulose ether 0.05-0.2
Wilkinite 3-10.
4. as claim 1 or claim 2 or the described environment-friendly type gypsum-based construction of claim 3 putty powder, it is characterized in that the concrete component and the weight percent of this environment-friendly type gypsum-based construction putty powder:
Plaster of Paris 68.96
Citric acid 0.1
Gelatine 0.2
Methyl cellulose ether 0.1
Wilkinite 4
Ethene-vinyl acetate emulsion copolymer powder 0.25
Dry powder 26.39.
5. as claim 1 or claim 2 or the described environment-friendly type gypsum-based construction of claim 3 putty powder, it is characterized in that the concrete component and the weight percent of this environment-friendly type gypsum-based construction putty powder:
Plaster of Paris 77.3
Citric acid 0.15
Gelatine 0.1
Hydroxypropyl methyl cellulose ether 0.2
Wilkinite 5.7
Polyvinyl alcohol rubber powder 0.85
Talcum powder 15.7.
6. as claim 1 or claim 2 or the described environment-friendly type gypsum-based construction of claim 3 putty powder, it is characterized in that the concrete component and the weight percent of this environment-friendly type gypsum-based construction putty powder:
Plaster of Paris 85
Citric acid 0.1
Gelatine 0.2
TYLOSE 30000 0.1
Wilkinite 6.25
Ethene-vinyl acetate emulsion copolymer powder 0.25
Dry powder 8.1.
7. as claim 1 or claim 2 or the described environment-friendly type gypsum-based construction of claim 3 putty powder, it is characterized in that the concrete component and the weight percent of this environment-friendly type gypsum-based construction putty powder:
Plaster of Paris 60
Citric acid 0.05
Gelatine 0.25
Wilkinite 8
Methyl cellulose ether 0.05
Modified tapioca starch 2.5
Talcum powder 29.15.
8. as claim 1 or claim 2 or the described environment-friendly type gypsum-based construction of claim 3 putty powder, it is characterized in that the concrete component and the weight percent of this environment-friendly type gypsum-based construction putty powder:
Plaster of Paris 81.5
Citric acid 0.2
Gelatine 0.1
Hydroxypropyl methyl cellulose ether 0.2
Wilkinite 3
Modified tapioca starch 2.5
Dry powder 12.5.
9. as claim 1 or claim 2 or the described environment-friendly type gypsum-based construction of claim 3 putty powder, it is characterized in that the concrete component and the weight percent of this environment-friendly type gypsum-based construction putty powder:
Plaster of Paris 65
Citric acid 0.1
Gelatine 0.1
Methyl cellulose ether 0.05
Wilkinite 10
Polyvinyl alcohol rubber powder 1
Talcum powder 23.75.
10. as claim 1 or claim 2 or the described environment-friendly type gypsum-based construction of claim 3 putty powder, it is characterized in that the concrete component and the weight percent of this environment-friendly type gypsum-based construction putty powder:
Plaster of Paris 71.39
Citric acid 0.05
Gelatine 0.25
TYLOSE 30000 0.2
Wilkinite 7.45
Ethene-vinyl acetate latex powder 0.1
Talcum powder 20.56.