CN103332917A - 防开裂建筑外墙材料及其制备方法 - Google Patents

防开裂建筑外墙材料及其制备方法 Download PDF

Info

Publication number
CN103332917A
CN103332917A CN2013102323116A CN201310232311A CN103332917A CN 103332917 A CN103332917 A CN 103332917A CN 2013102323116 A CN2013102323116 A CN 2013102323116A CN 201310232311 A CN201310232311 A CN 201310232311A CN 103332917 A CN103332917 A CN 103332917A
Authority
CN
China
Prior art keywords
kilogram
wall material
cracking
external wall
silicate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102323116A
Other languages
English (en)
Inventor
郑先平
段祥君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhenjiang Yinxin New Building Material Technology Co Ltd
Original Assignee
Zhenjiang Yinxin New Building Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhenjiang Yinxin New Building Material Technology Co Ltd filed Critical Zhenjiang Yinxin New Building Material Technology Co Ltd
Priority to CN2013102323116A priority Critical patent/CN103332917A/zh
Publication of CN103332917A publication Critical patent/CN103332917A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种防开裂建筑外墙材料，包括硅酸盐水泥，每100公斤硅酸盐水泥中主要混合有50-75公斤硫酸钙、50-75公斤硅酸铝、100-150公斤石英粉、10-20公斤甲基纤维素、20-30公斤硅灰、15-25公斤碳纤维和10-20公斤云母粉。甲基纤维素是一种分散剂，能使纤维材料分散均匀，从而更好的发挥纤维的增强、阻裂作用。本发明的防开裂建筑外墙材料，具有纤维材料和分散剂，分散剂能使纤维材料分散均匀，从而更好的发挥纤维的增强、阻裂作用，制成的混凝土制品具有较强的韧性，改善力学性能，显著提高界面抵抗变形的能力，减少墙壁上的裂纹，延长使用寿命。

Description

防开裂建筑外墙材料及其制备方法
 
技术领域
本发明涉及建筑材料技术领域，尤其是一种防开裂建筑外墙材料及其制备方法。
 
背景技术
建筑材料是建筑工程的物质基础，建筑物从主体结构到装饰装修施工中需要用到各种材料。混凝土作为应用最广泛的建筑材料，其主要成分包括水泥、掺合物和骨料，加水搅拌后硬化而成，具有工艺简单、防火性能等优点，但它是一种脆性材料，尤其是外墙在硬化后，时常会产生细小的裂纹，细小的裂纹时间长了会扩大形成裂缝，影响美观，更影响使用寿命。
发明内容
本发明要解决的技术问题是：克服现有技术中建筑外墙容易开裂的技术问题，提供一种防开裂建筑外墙材料，外墙硬化后较少开裂，延长使用寿命。
本发明解决其技术问题所采用的技术方案是：一种防开裂建筑外墙材料，包括硅酸盐水泥，每100公斤硅酸盐水泥中主要混合有50-75公斤硫酸钙、50-75公斤硅酸铝、100-150公斤石英粉、10-20公斤甲基纤维素、20-30公斤硅灰、15-25公斤碳纤维和10-20公斤云母粉。甲基纤维素是一种分散剂，能使纤维材料分散均匀，从而更好的发挥纤维的增强、阻裂作用。
进一步的，每100公斤硅酸盐水泥中还具有10-20公斤四氧化三铁。四氧化三铁提高外墙表面的结合强度和硬度。
进一步的，所述的石英粉的粒径为0.05-0.075mm。
进一步的，所述的云母粉的粒径为0.15-0.20mm。
一种制备上述防开裂建筑外墙材料的方法，具有如下步骤：将100公斤硅酸盐水泥投入搅拌装置中；开启搅拌装置，并投入50-75公斤硫酸钙、50-75公斤硅酸铝、100-150公斤石英粉和10-20公斤云母粉；将甲基纤维素10-20公斤、20-30公斤硅灰和15-25公斤碳纤维投入水中搅拌；将溶解后的溶液注入搅拌装置中，直至搅拌均匀呈砂浆状。
将10-20公斤四氧化三铁投入水中搅拌。
本发明的有益效果是，本发明的防开裂建筑外墙材料，具有纤维材料和分散剂，分散剂能使纤维材料分散均匀，从而更好的发挥纤维的增强、阻裂作用，制成的混凝土制品具有较强的韧性，改善力学性能，显著提高界面抵抗变形的能力，减少墙壁上的裂纹，延长使用寿命。
 
具体实施方式
本发明的防开裂建筑外墙材料，包括硅酸盐水泥，每100公斤硅酸盐水泥中主要混合有50-75公斤硫酸钙、50-75公斤硅酸铝、100-150公斤石英粉、10-20公斤甲基纤维素、20-30公斤硅灰、15-25公斤碳纤维和10-20公斤云母粉。甲基纤维素是一种分散剂，能使纤维材料分散均匀，从而更好的发挥纤维的增强、阻裂作用。
进一步的，每100公斤硅酸盐水泥中还具有10-20公斤四氧化三铁。提高外墙表面的结合强度和硬度。
进一步的，所述的石英粉的粒径为0.05-0.075mm。
进一步的，所述的云母粉的粒径为0.15-0.20mm。
一种制备上述防开裂建筑外墙材料的方法，具有如下步骤：将100公斤硅酸盐水泥投入搅拌装置中；开启搅拌装置，并投入50-75公斤硫酸钙、50-75公斤硅酸铝、100-150公斤石英粉和10-20公斤云母粉；将甲基纤维素10-20公斤、20-30公斤硅灰和15-25公斤碳纤维投入水中搅拌；将溶解后的溶液注入搅拌装置中，直至搅拌均匀呈砂浆状。
将10-20公斤四氧化三铁投入水中搅拌。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。

Claims (6)

1.一种防开裂建筑外墙材料，包括硅酸盐水泥，其特征是：每100公斤硅酸盐水泥中主要混合有50-75公斤硫酸钙、50-75公斤硅酸铝、100-150公斤石英粉、10-20公斤甲基纤维素、20-30公斤硅灰、15-25公斤碳纤维和10-20公斤云母粉。
2.如权利要求1所述的防开裂建筑外墙材料，其特征是：每100公斤硅酸盐水泥中还具有10-20公斤四氧化三铁。
3.如权利要求1或2所述的防开裂建筑外墙材料，其特征是：所述的石英粉的粒径为0.05-0.075mm。
4.如权利要求1或2所述的防开裂建筑外墙材料，其特征是：所述的云母粉的粒径为0.15-0.20mm。
5.一种制备权利要求1-4任一项所述的防开裂建筑外墙材料的方法，其特征是具有如下步骤：将100公斤硅酸盐水泥投入搅拌装置中；开启搅拌装置，并投入50-75公斤硫酸钙、50-75公斤硅酸铝、100-150公斤石英粉和10-20公斤云母粉；将甲基纤维素10-20公斤、20-30公斤硅灰和15-25公斤碳纤维投入水中搅拌；将溶解后的溶液注入搅拌装置中，直至搅拌均匀呈砂浆状。
6.如权利要求5所述的防开裂建筑外墙材料的制备方法，其特征是：将10-20公斤四氧化三铁投入水中搅拌。
CN2013102323116A 2013-06-13 2013-06-13 防开裂建筑外墙材料及其制备方法 Pending CN103332917A (zh)