CN102992720A - 一种外墙防水防开裂柔性腻子及其制备方法 - Google Patents
一种外墙防水防开裂柔性腻子及其制备方法 Download PDFInfo
- Publication number
- CN102992720A CN102992720A CN2012105428172A CN201210542817A CN102992720A CN 102992720 A CN102992720 A CN 102992720A CN 2012105428172 A CN2012105428172 A CN 2012105428172A CN 201210542817 A CN201210542817 A CN 201210542817A CN 102992720 A CN102992720 A CN 102992720A
- Authority
- CN
- China
- Prior art keywords
- powder
- cracking
- external wall
- flexible putty
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种外墙防水防开裂柔性腻子及其制备方法,柔性腻子含有硅酸盐水泥、重钙、石英粉、超细石英粉、可再分散弹性乳胶粉、羟丙基甲基纤维素、有机硅粉、触变剂、复合纤维和白云母粉。制备方法是按质量%按比例加入硅酸盐水泥、重钙、石英粉、复合纤维和白云母粉搅拌5min;再按质量%按比例加入可再分散弹性乳胶粉、羟丙基甲基纤维素、超细石英粉、可再分散弹性乳胶粉、有机硅粉和触变剂搅拌20min;最后计量包装。本柔性腻子可用于混凝土、混合砂浆,石膏板、埃特板及木板表面的各种墙面基层抹平。本柔性腻子与高反射隔热纳米复合外墙涂料系统配套使用,施工方便、可降低成本,并提高墙面整体防水、防裂和隔热等综合性能。
Description
技术领域
本发明涉及一种外墙防水防开裂柔性腻子及其制备方法,具体地说是一种用于与高反射隔热纳米复合外墙涂料配合使用的柔性腻子,属于建筑节能材料领域。
背景技术
在以往的施工中与反射隔热涂料配合使用的腻子通常采用普通腻子或加入胶水的水泥砂浆进行刮底,施工后经常出现整个墙面开裂现象,导致使高反射隔热涂料失去反射隔热效能,也会严重地影响建筑质量。这是因为保温层和腻子层有着不同的导热系数和传热速度,不同材料的变形差异导致裂缝的产生。为了提高反射隔热涂料的隔热性能,防水、防开裂,以利于反射隔热涂料具有更加优秀的综合性能,必须开发出于之相配套的防水防开裂的柔性腻子。
发明内容
本发明的目的是为了解决现有施工中使用的普通腻子易开裂的不足,而提供一种外墙防水防开裂柔性腻子及其制备方法, 提供的柔性腻子产品可以与高反射隔热纳米复合外墙涂料配合使用,提高反射隔热涂料与墙体的牢固程度,提高隔热保温性能,满足建筑业对节能材料的需求。
为了达到上述目的,本发明采取的措施是:提供一种外墙防水防开裂柔性腻子, 按质量%计含有白色或灰色硅酸盐水泥20~30、重钙25~35、石英粉24~34、超细石英粉8~12、可再分散弹性乳胶粉2.5~4.5、羟丙基甲基纤维素0.25~0.45、有机硅粉0.5~0.8、触变剂0.1~0.2、复合纤维0.2~0.4和白云母粉0.5~1.5。
所述的白色或灰色硅酸盐水泥标号为42.5, 重钙的粒径为0.045mm、石英粉的粒径为0.075mm、超细石英粉的粒径为≤15μ m、白云母粉的粒径为0.18mm。若原料的粒径达不到要求,需球磨机及气流粉碎机进行加工,直到达到要求才能保证本产品的质量要求。
本发明的柔性腻子所述的组分中可再分散弹性乳胶粉和羟丙基甲基纤维素虽加入量少,但可增加隔热保温层的保水率,能提高涂料的隔热保温性能。白云母粉和超细石英粉的加入能改善墙体腻子与高反射隔热涂料层的导热系数和传热速度,使腻子层和反射隔热层形成一个牢固的保温系统,起到优良的隔热保温性能,达到建筑节能减耗的目的。
本发明还提供一种制备上述外墙防水防开裂柔性腻子的方法,操作步骤为:
① 按质量%计将白色或灰色硅酸盐水泥20~30、重钙25~35、石英粉24~34、复合纤维0.2~0.4和白云母粉0.5~1. 5搅拌5min;
② 再按质量%计加入可再分散弹性乳胶粉2.5~4.5、羟丙基甲基纤维素0.25~0.45、超细石英粉8~12、有机硅粉0.5~0.8和触变剂0.1~0.2进行搅拌20 min;
③ 计量包装制得粉末状外墙防水防开裂柔性腻子产品。
本发明的方法制备的柔性腻子的性能指标:
初期干燥抗裂性(6h) 无裂纹; 吸水量/g/10min 1.4;
耐碱性(48h) 无异常; 耐水性(96h) 无异常;
干燥时间(表干)/h 2;
粘结强度标准状态/MPa 0.64; 冻融循环(5次)/MPa 0.42;
太阳反射比为91%;非金属固体材料的导热系数为0.069W/(m·K) 。
本发明的一种外墙防水防开裂柔性腻子及其制备方法具有如下优点:
1、本发明的柔性腻子产品与高反射隔热纳米复合外墙涂料配合使用,经测试,太阳反射比为91%,非金属固体材料的导热系数为0.069W/(m·K),隔热保温效果好。
2、本发明制备方法简单,只需要搅拌机将硅酸盐水泥、重钙和石英粉等原料按规定的比例配方, 按原料的粒径要求在搅拌机内搅拌即可制得。
3、本发明的产品为粉末状,方便保管和运输,也方便施工,使用时用净水将粉末状柔性腻子产品按水灰比例为1:3.5调成稠浆,搅拌均匀即可使用。
具体实施方式
以下结合实施例对本发明作进一步描述。
实施例1:制备一种外墙防水防开裂柔性腻子,按质量%计称取下述各种原料:
白色硅酸盐水泥(标号为42.5):25; 重钙(粒径0.045mm): 25;
石英粉(粒径0.075mm): 34; 超细石英粉(≤15μ m): 8.5;
白云母粉(0.18mm): 1.5 ; 可再分散弹性乳胶粉: 4.5;
羟丙基甲基纤维素: 0. 4; 有机硅粉: 0.8;
触变剂: 0.1 ; 复合纤维: 0 .2。
上述原料按比例称量后,先将白色硅酸盐水泥、重钙、石英粉、复合纤维、白云母粉在搅拌机上搅拌5min,再加入可再分散弹性乳胶粉、羟丙基甲基纤维素、超细石英粉、有机硅粉、触变剂在搅拌机上分散搅拌20min搅拌均匀后计量包装。现场使用时按水灰比例为1:3.5调成稠浆,搅拌均匀即可使用。
实施例2:制备一种外墙防水防开裂柔性腻子,按质量%计称取下述各种原料:
灰色硅酸盐水泥(标号为42.5):20; 重钙(粒径0.045mm): 35;
石英粉(粒径0.075mm): 31 ; 超细石英粉(≤15μ m): 8.0;
白云母粉(0.18mm): 1.15; 可再分散弹性乳胶粉: 3. 45;
羟丙基甲基纤维素: 0. 3; 有机硅粉: 0.6;
触变剂: 0.2 ; 复合纤维: 0 .3。
将上述原料按比例称量后,先将灰色硅酸盐水泥、重钙、石英粉、复合纤维和白云母粉在搅拌机上搅拌5min,再加入可再分散弹性乳胶粉、羟丙基甲基纤维素、超细石英粉、有机硅粉和触变剂在搅拌机上搅拌20min搅拌均匀后计量包装。现场使用时按水灰比例为1:3.5调成稠浆,搅拌均匀即可使用。
实施例3:制备一种外墙防水防开裂柔性腻子,按质量%计称取下述各种原料:
白色硅酸盐水泥(标号为42.5):30; 重钙(粒径0.045mm): 28;
石英粉(粒径0.075mm): 26; 超细石英粉(≤15μ m): 11.7;
白云母粉(0.18mm): 0.5; 可再分散弹性乳胶粉: 2. 5;
羟丙基甲基纤维素: 0. 25; 有机硅粉: 0.5;
触变剂: 0.15 ; 复合纤维: 0 .4。
将上述原料按比例称量后,先将白色硅酸盐水泥、重钙、石英粉、复合纤维、白云母粉在搅拌机上搅拌5min,再加入可再分散弹性乳胶粉、羟丙基甲基纤维素、超细石英粉、有机硅粉和触变剂在搅拌机上搅拌20min,搅拌均匀后计量包装。现场使用时按水灰比例为1:3.5调成稠浆,搅拌均匀即可使用。施工时要求基层平整无油污、无杂质、粉化,起皮的基层在施工前应清理干净。使用前用先进行小面积试刮。使用时采用钢刮板批刮,施工中力求不露底、不漏刮、不留接缝痕迹。腻子刮两遍成活。腻子层总厚度一般不小于5mm。二遍腻子批刮时间不宜太长,第二遍腻子需在第一遍腻子干燥后进行批刮。腻子干固后即可打磨。
本发明柔性腻子适用于在外墙施工,可用于混凝土表面、蒸压加气混凝土表面、水泥混合砂浆表面、石膏板表面、硅酸钙板表面、埃特板表面、三合板表面、木板等各种墙面基层抹平;本发明柔性腻子与高反射隔热纳米复合外墙涂料系统配套施工,可提高反射隔热纳米复合外墙涂料在墙体上的防水、防开裂性能,从而提高墙面整体防水、隔热等综合性能。
Claims (3)
1.一种外墙防水防开裂柔性腻子,其特征在于:按质量%计含有白色或灰色硅酸盐水泥20~30、重钙25~35、石英粉24~34、超细石英粉8~12、可再分散弹性乳胶粉2.5~4.5、羟丙基甲基纤维素0.25~0.45、有机硅粉0.5~0.8、触变剂0.1~0.2、复合纤维0.2~0.4和白云母粉0.5~1.5。
2.根据权利要求1所述的外墙防水防开裂柔性腻子,其特征在于:所述的白色或灰色硅酸盐水泥标号为42.5,重钙的粒径为0.045mm、石英粉的粒径为0.075mm、超细石英粉的粒径为≤15μ m、白云母粉的粒径为0.18mm。
3.一种制备权利要求1所述的外墙防水防开裂柔性腻子的方法,其特征在于:操作步骤为:
① 按质量%计将白色或灰色硅酸盐水泥20~30、重钙25~35、石英粉24~34、复合纤维0.2~0.4和白云母粉0.5~1. 5混合搅拌5min;
② 再按质量%计加入可再分散弹性乳胶粉2.5~4.5、羟丙基甲基纤维素0.25~0.45、超细石英粉8~12、有机硅粉0.5~0.8和触变剂0.1~0.2进行搅拌20 min;
③ 计量包装制得粉末状外墙防水防开裂柔性腻子产品。