CN103319973B - 一种无烟无味电油汀用粉末涂料 - Google Patents
一种无烟无味电油汀用粉末涂料 Download PDFInfo
- Publication number
- CN103319973B CN103319973B CN201310227117.9A CN201310227117A CN103319973B CN 103319973 B CN103319973 B CN 103319973B CN 201310227117 A CN201310227117 A CN 201310227117A CN 103319973 B CN103319973 B CN 103319973B
- Authority
- CN
- China
- Prior art keywords
- agent
- powder coating
- air release
- fland
- macromole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种无烟无味电油汀用粉末涂料,该粉末涂料由以下的原料制备得到:环氧树脂、聚酯树脂、反应性流平剂、大分子脱气剂、颜填料和其它助剂。本发明的流平剂选用液体涂料用带活性基团可反应型流平剂,流平剂在涂层固化时发生反应和涂层固化在一起,在后来的使用过程中就不会挥发出来造成烟雾和气味。安息香用一种大分子脱气剂代替,在油汀的使用温度下该脱气剂不会蒸发造成烟雾和气味。大分子脱气剂是聚合物型表面活性剂,具有很低的熔融粘度,帮助颜料的分散和促进流平,消除针孔。
Description
技术领域
本发明涉及粉末涂料领域。
背景技术
电油汀在使用时局部表面温度高达150℃,在这么高的温度下,表面粉末涂料涂层中的小分子物质如流平剂和脱气剂安息香会挥发出来,形成烟雾,产生不愉快气味。为了保暖和节约能源,电油汀通常在封闭很好的空间使用,因此这些烟雾和气味不易散去,长时间使用会影响使用者的心情和健康。
中国发明专利申请(申请号:200910027278.7申请日:2009-05-25)公开了一种电暖器用耐高温节约型静电粉末涂料及其制备方法,在这种粉末涂料的配方中,按重量百分比计算热固性树脂占53~57%、固化剂占3~7%、颜料占1~30%、填料占5~34%、助剂占2~5%。该粉末涂料采用预混合—→熔融挤出混合—→压片冷却破碎—→细粉碎和分级—→过筛分离—→产品的方法生产,使粉末涂料的平均粒度在25~30mm,满足涂膜厚度在50~60mm的节约型涂膜厚度要求。
发明内容
为了解决上述的技术问题,本发明的目的是提供一种无烟无味电油汀用粉末涂料,该涂料涂装的物体在油汀使用温度下不会生产烟雾和气味。
为了实现上述的目的,本发明采用了以下的技术方案:
一种无烟无味电油汀用粉末涂料,该粉末涂料按重量百分比由以下组分的原料制备得到:
作为优选,该粉末涂料按重量百分比由以下组分的原料制备得到:
作为优选,所述反应性流平剂是含反应性环氧基官能团的丙烯酸流平剂或含反应性羧基官能团的丙烯酸流平剂;优选,所述反应性流平剂为MF-A EX流平剂。
作为优选,所述的环氧树脂是环氧当量为0.12~0.125的环氧树脂。
作为优选,所述的聚酯树脂是5:5或6:4型的羧基聚酯树脂。
作为优选,所述的颜填料是选用钛白粉和硫酸钡中的一种或两种混合。
作为优选,所述其它助剂为增硬剂和增光剂中的一种或两种混合。
作为优选,所述其它助剂为1~2%的增光剂,0.3~0.8%的增硬剂。
作为优选,所述大分子脱气剂是具有低熔融粘度,能够帮助颜料的分散和促进流平,消除针的孔聚合物型表面活性剂。
作为优选,所述大分子脱气剂是氨基改性酚脲表面活性剂,优选为聚醚寡聚物消泡剂。
本发明的流平剂选用液体涂料用带活性基团可反应型流平剂,流平剂在涂层固化时发生反应和涂层固化在一起,在后来的使用过程中就不会挥发出来造成烟雾和气味。安息香用一种大分子脱气剂代替,在油汀的使用温度下该脱气剂不会蒸发造成烟雾和气味。大分子脱气剂是聚合物型表面活性剂,具有很低的熔融粘度,帮助颜料的分散和促进流平,消除针孔。
本发明的产品技术指标如下:
具体实施方式
下面通过实施例进一步说明本发明。
按表1实施例配方组成精确称量物料,置于高速混合机混合6~8分钟;物料混合后用挤出机在90~100℃的温度下挤出;挤出料冷却破碎后用粉碎机粉碎为平均粒径为38~42微米的粉末颗粒;再用180目筛网过筛,最后包装成成品。
为进一步说明本发明无烟无味电油汀用粉末涂料的独特性能,在表1中同时列出了两组对比配方:
表1无烟无味电油汀用粉末涂料实施例及对比例的配方(重量百分比)
按上述实施例所得无烟无味电油汀用粉末涂料,采用如下喷涂和测试工艺:成品经静电喷枪喷涂在3mm铁板上做检测,厚度为50~70微米,铁板在180℃电热烘箱固化15分钟后,将所得涂层在150℃下在密闭空间进行检测,测试结果见表2所示。
表2无烟无味电油汀用粉末涂料实施例及对比例的性能
从上表可以明显的看出,用反应性流平剂取代通用流平剂,用大分子脱气剂取代通用脱气剂安息香,能有效解决电油汀在使用时产生烟雾和异味的问题。
Claims (2)
1.一种无烟无味电油汀用粉末涂料,其特征在于该粉末涂料按重量百分比由以下组分的原料制备得到:
环氧树脂 24%~35%,
聚酯树脂 30%~35%,
反应性流平剂 0.5%~2%,
大分子脱气剂 0.3%~2%,
颜填料 30%~35%,
其他助剂1.5~2%;
所述的其他助剂为增光剂1~2%;增硬剂0.3~0.8%;
所述的环氧树脂是环氧当量为0.12~0.125的环氧树脂;所述的聚酯树脂是5:5或6:4型的羧基聚酯树脂;所述反应性流平剂为MODAREZ® MF-A EX流平剂;所述大分子脱气剂是聚醚寡聚物消泡剂;所述的颜填料是选用钛白粉和硫酸钡中的一种或两种混合;
上述的各组分置于高速混合机混合6~8分钟;物料混合后用挤出机在90~100℃的温度下挤出;挤出料冷却破碎后用粉碎机粉碎为平均粒径为38~42微米的粉末颗粒;再用180目筛网过筛,最后包装成成品。
2.根据权利要求1所述的一种无烟无味电油汀用粉末涂料,其特征在于该粉末涂料按重量百分比由以下组分的原料制备得到:
环氧树脂 24%~35%,
聚酯树脂 30%~35%,
反应性流平剂 0.5%~0.8%,
大分子脱气剂 0.3%~0.6%,
颜填料 30%~35%,
其他助剂1.5~2%。