CN103305115B - 一种消除空气中甲醛的紫外光固化涂料配方及其制备工艺 - Google Patents
一种消除空气中甲醛的紫外光固化涂料配方及其制备工艺 Download PDFInfo
- Publication number
- CN103305115B CN103305115B CN201310236512.3A CN201310236512A CN103305115B CN 103305115 B CN103305115 B CN 103305115B CN 201310236512 A CN201310236512 A CN 201310236512A CN 103305115 B CN103305115 B CN 103305115B
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- ultraviolet
- curing paint
- powder
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及紫外光固化涂料技术领域,特别涉及一种消除空气中甲醛的紫外光固化涂料配方及其制备工艺。涂料由下述重量百分比含量的组分组成:聚氨酯丙烯酸酯20%~40%,1,6己二醇二丙烯酸酯10~30%,三羟甲基丙烷三丙烯酸酯1~10%,2-苯氧基乙基丙烯酸酯1~5%,分散剂1~5%,超细二氧化硅2~6%,超细氧化铝粉1~4%,哑粉1~12%,蜡粉1~4%,2-羟基-2-甲基-1-苯基-1-丙酮4~6%,表面助剂0.1~2%,除甲醛助剂1%~15%。涂料的制备工艺为依次投入各原料并搅拌,使其混合均匀;通过本配方及工艺制备的涂料能适用于工厂化流水线快速作业,也具备有良好的附着力、耐刮等保护功能。
Description
【技术领域】
本发明涉及紫外光固化涂料技术领域,特别涉及一种用于木制、塑胶和金属等装饰板材表面涂布的具有消除空气中甲醛功能的紫外光固化涂料。
【背景技术】
甲醛是一种挥发性有机化合物,无色、有特殊气味、略重于空气,易溶于水。甲醛对人体健康有重要影响,对眼睛、呼吸道、人体粘膜和皮肤有强烈的刺激作用;急性中毒可导致流泪、流涕、咳嗽等症状,引发多种呼吸道疾病;慢性吸入低浓度可导致持续头痛、无力、失眠等;长期皮肤接触会导致皮炎,对人体的呼吸系统、消化系统和中枢神经系统产生不良影响,造成肺和肝免疫功能异常。甲醛对人体危害如此严重,生产出能有效降解甲醛的建材产品引起了建筑行业的重视。
传统的消除甲醛涂料主要是由水、苯丙乳液以及除甲醛助剂配制而成,该涂料涂布于墙面后,能够消除空气中甲醛。但其使用方式为自然干燥,不适用于工厂化流水线快速作业。且对木材,塑料板材,铝板材等家庭装修板材不具备良好的附着力,也具备耐刮、耐划伤、耐冲击等基本涂料保护功能。
故有必要对现有除甲醛涂料的配方和制备工艺进行进一步地技术革新。
【发明内容】
本发明解决的技术问题是提供一种适于工厂流水线快速使用消除空气中甲醛的紫外光固化涂料;同时能保持装饰板材涂布漆膜后满足国标GB/T 9286、GB/T1768,美标ISO 2409、ASTM D 4060,欧标EN 438-2.6、EN 438-2.14要求的消除空气中甲醛的紫外光固化涂料配方及其制备工艺。
为了解决上述技术问题,本发明采用的技术方案是:一种消除空气中甲醛的紫外光固化涂料配方,所述涂料由下述重量百分比含量的组分组成:聚氨酯丙烯酸酯20%~40%,1,6己二醇二丙烯酸酯10~30%,三羟甲基丙烷三丙烯酸酯1~10%,2-苯氧基乙基丙烯酸酯1~5%,分散剂1~5%,超细二氧化硅2~6%,超细氧化铝粉1~4%,哑粉1~12%,蜡粉1~4%,2-羟基-2-甲基-1-苯基-1-丙酮4~6%,表面助剂0.1~2%,除甲醛助剂1%~15%。
进一步地,所述分散剂为丙烯酸共聚物。
进一步地,所述表面助剂为有机硅共聚物。
进一步地,所述除甲醛助剂为甲壳素衍生物。
为了解决上述技术问题,本发明采用的技术方案是:包括如下步骤:
a、将聚氨酯丙烯酸酯、1,6己二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯、2-苯氧基乙基丙烯酸酯和分散剂依次加入搅拌罐中并搅拌,使各种原料充分混合均匀;
b、在步骤a的溶液中依次投入超细二氧化硅、超细氧化铝粉、哑粉、蜡粉和除甲醛助剂并搅拌,使各种原料充分混合均匀,使溶液的原料达到35微米以下即可停止搅拌;
c、在步骤b的溶液中依次投入2-羟基-2-甲基-1-苯基-1-丙酮和表面助剂并搅拌,搅拌10分钟即可涂料。
进一步地,所述搅拌是在每个步骤投料的同时进行搅拌。
进一步地,所述搅拌是在每个步骤投料之后再进行搅拌。
本发明与现有技术相比的有益效果是:
1、通过紫外光来固化涂料,能够适用于工厂化流水线快速作业;
2、该涂料对木材、塑料板材、铝板材等家庭装修板材具备良好的附着力;
3、该涂料具有耐刮、耐划伤、耐冲击等保护功能。
【具体实施方式】
下面将结合附图以及具体实施例来详细说明本发明,其中的示意性实施例以及说明仅用来解释本发明,但并不作为对本发明的限定。
实例1:
配备100kg本发明消除空气中甲醛的紫外光固化涂料,由以下重量的组分配制而成:
聚氨酯丙烯酸酯20kg,1,6己二醇二丙烯酸酯20kg,三羟甲基丙烷三丙烯酸酯5kg,2-苯氧基乙基丙烯酸酯1kg,分散剂5kg,超细二氧化硅6kg,超细氧化铝粉4kg,哑粉12kg,蜡粉4kg,2-羟基-2-甲基-1-苯基-1-丙酮6kg,表面助剂2kg,除甲醛助剂15kg。所述分散剂为丙烯酸共聚物;所述表面助剂为有机硅共聚物;所述除甲醛助剂为甲壳素衍生物。
配备100kg本发明消除空气中甲醛的紫外光固化涂料,通过以下制备工艺实现:包括如下步骤:
a、将聚氨酯丙烯酸酯20kg,1,6己二醇二丙烯酸酯20kg,三羟甲基丙烷三丙烯酸酯5kg,2-苯氧基乙基丙烯酸酯1kg和分散剂5kg依次加入搅拌罐中并搅拌,使各种原料充分混合均匀;
b、在步骤a的溶液中依次投入超细二氧化硅6kg,超细氧化铝粉4kg,哑粉12kg,蜡粉4kg和除甲醛助剂15kg并搅拌,使各种原料充分混合均匀,使溶液的原料达到35微米以下即可停止搅拌;
c、在步骤b的溶液中依次投入2-羟基-2-甲基-1-苯基-1-丙酮6kg和表面助剂2kg,并搅拌,搅拌10分钟即可涂料。
实例2:
配备100kg本发明消除空气中甲醛的紫外光固化涂料,由以下重量的组分配制而成:
聚氨酯丙烯酸酯20kg,1,6己二醇二丙烯酸酯30kg,三羟甲基丙烷三丙烯酸酯3kg,2-苯氧基乙基丙烯酸酯4kg,分散剂2kg,超细二氧化硅5kg,超细氧化铝粉4kg,哑粉6kg,蜡粉4kg,2-羟基-2-甲基-1-苯基-1-丙酮5kg,表面助剂2kg,除甲醛助剂15kg。所述分散剂为丙烯酸共聚物;所述表面助剂为有机硅共聚物;所述除甲醛助剂为甲壳素衍生物。
配备100kg本发明消除空气中甲醛的紫外光固化涂料,通过以下制备工艺实现:包括如下步骤:
a、将聚氨酯丙烯酸酯20kg,1,6己二醇二丙烯酸酯30kg,三羟甲基丙烷三丙烯酸酯3kg,2-苯氧基乙基丙烯酸酯4kg和分散剂2kg,依次加入搅拌罐中并搅拌,使各种原料充分混合均匀;
b、在步骤a的溶液中依次投入超细二氧化硅5kg,超细氧化铝粉4kg,哑粉6kg,蜡粉4kg和除甲醛助剂15kg并搅拌,使各种原料充分混合均匀,使溶液的原料达到35微米以下即可停止搅拌;
c、在步骤b的溶液中依次投入2-羟基-2-甲基-1-苯基-1-丙酮5kg和表面助剂2kg,并搅拌,搅拌10分钟即可涂料。
实例3:
配备100kg本发明消除空气中甲醛的紫外光固化涂料,由以下重量的组分配制而成:
聚氨酯丙烯酸酯35kg,1,6己二醇二丙烯酸酯16kg,三羟甲基丙烷三丙烯酸酯10kg,2-苯氧基乙基丙烯酸酯4kg,分散剂3kg,超细二氧化硅4kg,超细氧化铝粉2kg,哑粉6kg,蜡粉4kg,2-羟基-2-甲基-1-苯基-1-丙酮5kg,表面助剂1kg,除甲醛助剂10kg。所述分散剂为丙烯酸共聚物;所述表面助剂为有机硅共聚物;所述除甲醛助剂为甲壳素衍生物。
配备100kg本发明消除空气中甲醛的紫外光固化涂料,通过以下制备工艺实现:包括如下步骤:
a、将聚氨酯丙烯酸酯35kg,1,6己二醇二丙烯酸酯16kg,三羟甲基丙烷三丙烯酸酯10kg,2-苯氧基乙基丙烯酸酯4kg和分散剂3kg,依次加入搅拌罐中并搅拌,使各种原料充分混合均匀;
b、在步骤a的溶液中依次投入超细二氧化硅4kg,超细氧化铝粉2kg,哑粉6kg,蜡粉4kg和除甲醛助剂10kg并搅拌,使各种原料充分混合均匀,使溶液的原料达到35微米以下即可停止搅拌;
c、在步骤b的溶液中依次投入2-羟基-2-甲基-1-苯基-1-丙酮5kg和表面助剂1kg并搅拌,搅拌10分钟即可涂料。
以上所述仅是本发明的较佳实施方式,故凡依本发明专利申请范围所述的构造、特征及原理所做的等效变化或修饰,均包括于本发明专利申请范围内。
Claims (5)
1.一种消除空气中甲醛的紫外光固化涂料,其特征在于,所述涂料由下述重量百分比含量的组分组成:
聚氨酯丙烯酸酯20%~40%,
1,6己二醇二丙烯酸酯10~30%,
三羟甲基丙烷三丙烯酸酯1~10%,
2-苯氧基乙基丙烯酸酯1~5%,
分散剂1~5%,
超细二氧化硅2~6%,
超细氧化铝粉1~4%,
哑粉1~12%,
蜡粉1~4%,
2-羟基-2-甲基-1-苯基-1-丙酮4~6%,
表面助剂0.1~2%,
除甲醛助剂1%~15%。
2.根据权利要求1所述的一种消除空气中甲醛的紫外光固化涂料,其特征在于,所述分散剂为丙烯酸共聚物。
3.根据权利要求1所述的一种消除空气中甲醛的紫外光固化涂料,其特征在于,所述表面助剂为有机硅共聚物。
4.根据权利要求1所述的一种消除空气中甲醛的紫外光固化涂料,其特征在于,所述除甲醛助剂为甲壳素衍生物。
5.根据权利要求1所述的一种消除空气中甲醛的紫外光固化涂料的制备工艺,其特征在于,包括如下步骤:
a、将聚氨酯丙烯酸酯、1,6己二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯、2-苯氧基乙基丙烯酸酯和分散剂依次加入搅拌罐中并搅拌,使各种原料充分混合均匀;
b、在步骤a的溶液中依次投入超细二氧化硅、超细氧化铝粉、哑粉、蜡粉和除甲醛助剂并搅拌,使各种原料充分混合均匀,使溶液的原料达到35微米以下即可停止搅拌;
c、在步骤b的溶液中依次投入2-羟基-2-甲基-1-苯基-1-丙酮和表面助剂并搅拌,搅拌10分钟即可涂料。