CN103305069B - 一种以废弃聚苯乙烯泡沫为原料制备涂料的方法 - Google Patents
一种以废弃聚苯乙烯泡沫为原料制备涂料的方法 Download PDFInfo
- Publication number
- CN103305069B CN103305069B CN201310275003.1A CN201310275003A CN103305069B CN 103305069 B CN103305069 B CN 103305069B CN 201310275003 A CN201310275003 A CN 201310275003A CN 103305069 B CN103305069 B CN 103305069B
- Authority
- CN
- China
- Prior art keywords
- polystyrene foam
- waste polystyrene
- coating
- toluene
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种以废弃聚苯乙烯泡沫、甲苯及其他原料制备涂料的方法。主要工艺过程是将废弃聚苯乙烯泡沫加入甲苯,形成聚苯乙烯的甲苯溶液,加入涂料和颜料,搅拌均匀,高速搅拌后即得涂料。本方法制备的涂料性能很好。本方法以废弃聚苯乙烯泡沫为原料,这给废弃物综合利用拓展出一条新的道路。本方法制备的涂料可用于城市建筑防外墙涂料等领域。
Description
技术领域
本发明涉及一种涂料的制备方法,特别指以废弃聚苯乙烯泡沫和甲苯为主要原料,添加其他辅料和填料来制备涂料的方法。
背景技术
本发明主要针对废弃聚苯乙烯泡沫造成的严重公害而没有合理利用,而涂料在建筑外墙等领域有非常广泛的用途,因此产品容易推广和应用。
由于本发明是利用废弃聚苯乙烯及甲苯为主要原料,制备成本低廉,目前还未见该方面的相关报道,而其独特的性能使其在建筑外墙涂料方面将有广阔的应用前景。
发明内容
本发明要解决的技术问题是提供一种涂料的制备方法,这种制备方法以废弃聚苯乙烯泡沫和甲苯为主要原料,经合理配比,通过一定的工艺过程而制得涂料。
本发明要解决的技术问题是由如下方案解决的:一种以废弃聚苯乙烯泡沫为原料制备涂料的方法,其特征是:将废弃聚苯乙烯泡沫加入到甲苯中,形成聚苯乙烯的甲苯溶液,加入加入钛白粉,滑石粉,有机土,分散剂,沉淀硫酸钡,硅油,在高速搅拌下搅拌均匀后出料,包装即得产品,其中甲苯、废弃聚苯乙烯泡沫、钛白粉、滑石粉、有机土、分散剂、沉淀硫酸钡及硅油的质量比为1:0.1667-0.2708:0.10:0.0375:0.0125:0.005:0.0125:0.0025。
上述一种以废弃聚苯乙烯泡沫为原料制备涂料的方法中废弃聚苯乙烯泡沫是指:包装用的废弃聚苯乙烯泡沫及一次性餐盒用的废弃聚苯乙烯泡沫等。
本发明的优点是:1、用本方法制备涂料的成本很低。2、可以有效利用城市产生的大量废弃聚苯乙烯泡沫,合理利用资源并减轻废弃物造成的污染。
附图说明
图1以废弃聚苯乙烯泡沫为原料制备涂料的工艺流程图。
具体实施方式
实施例1:在240g甲苯中加入65g废弃聚苯乙烯泡沫,形成聚苯乙烯的甲苯溶液,加入24g钛白粉,9g滑石粉,3g有机土,1.2g分散剂,3g沉淀硫酸钡,0.6g硅油,搅拌均匀,在高速搅拌下搅拌均匀后出料,包装即得产品。
实施例2:在240g甲苯中加入60g废弃聚苯乙烯泡沫,形成聚苯乙烯的甲苯溶液,加入24g钛白粉,9g滑石粉,3g有机土,1.2g分散剂,3g沉淀硫酸钡,0.6g硅油,搅拌均匀,在高速搅拌下搅拌均匀后出料,包装即得产品。
实施例3:在240g甲苯中加入55g废弃聚苯乙烯泡沫,形成聚苯乙烯的甲苯溶液,加入24g钛白粉,9g滑石粉,3g有机土,1.2g分散剂,3g沉淀硫酸钡,0.6g硅油,搅拌均匀,在高速搅拌下搅拌均匀后出料,包装即得产品。
实施例4:在240g甲苯中加入50g废弃聚苯乙烯泡沫,形成聚苯乙烯的甲苯溶液,加入24g钛白粉,9g滑石粉,3g有机土,1.2g分散剂,3g沉淀硫酸钡,0.6g硅油,搅拌均匀,在高速搅拌下搅拌均匀后出料,包装即得产品。
实施例5:在240g甲苯中加入45g废弃聚苯乙烯泡沫,形成聚苯乙烯的甲苯溶液,加入24g钛白粉,9g滑石粉,3g有机土,1.2g分散剂,3g沉淀硫酸钡,0.6g硅油,搅拌均匀,在高速搅拌下搅拌均匀后出料,包装即得产品。
实施例6:在240g甲苯中加入40g废弃聚苯乙烯泡沫,形成聚苯乙烯的甲苯溶液,加入24g钛白粉,9g滑石粉,3g有机土,1.2g分散剂,3g沉淀硫酸钡,0.6g硅油,搅拌均匀,在高速搅拌下搅拌均匀后出料,包装即得产品。
Claims (2)
1.一种以废弃聚苯乙烯泡沫为原料制备涂料的方法,其特征是:将废弃聚苯乙烯泡沫加入到甲苯中,形成聚苯乙烯的甲苯溶液,加入钛白粉,滑石粉,有机土,分散剂,沉淀硫酸钡,硅油,在高速搅拌下搅拌均匀后出料,包装即得产品,其中甲苯、废弃聚苯乙烯泡沫、钛白粉、滑石粉、有机土、分散剂、沉淀硫酸钡及硅油的质量比为1:0.1667-0.2708:0.10:0.0375:0.0125:0.005:0.0125:0.0025。
2.根据权利要求1所述的以废弃聚苯乙烯泡沫为原料制备涂料的方法,其中所述废弃聚苯乙烯泡沫为包装用的废弃聚苯乙烯泡沫及一次性餐盒用的废弃聚苯乙烯泡沫。