CN103319112A - 以废弃聚苯乙烯泡沫制备堵漏剂的方法 - Google Patents
以废弃聚苯乙烯泡沫制备堵漏剂的方法 Download PDFInfo
- Publication number
- CN103319112A CN103319112A CN2013102741831A CN201310274183A CN103319112A CN 103319112 A CN103319112 A CN 103319112A CN 2013102741831 A CN2013102741831 A CN 2013102741831A CN 201310274183 A CN201310274183 A CN 201310274183A CN 103319112 A CN103319112 A CN 103319112A
- Authority
- CN
- China
- Prior art keywords
- waste
- polystyrene foam
- plugging agent
- waste polystyrene
- toluene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了以废弃聚苯乙烯泡沫制备堵漏剂的方法。主要工艺过程是将废弃聚苯乙烯泡沫加入甲苯,形成聚苯乙烯的甲苯溶液,加入废弃油脂及高岭土,搅拌均匀,即得堵漏剂。本方法制备的堵漏剂性能很好、成本低。本方法以废弃聚苯乙烯泡沫及废弃油脂为原料,这给废弃物综合利用拓展出一条新的道路。本方法制备的堵漏剂可用于城市建筑防水及水利工程的防渗漏等领域。
Description
技术领域
本发明涉及用于建筑或者水利工程堵漏剂的制备方法,特别指以废弃聚苯乙烯泡沫、废弃油脂、高岭土和甲苯为主要原料来制备堵漏剂的方法。
背景技术
本发明主要针对废弃聚苯乙烯泡沫造成的严重污染,而没有合理利用,废弃油脂已经成为公害,建筑防水及堵漏没有简易方法等方面的问题。利用废弃聚苯乙烯泡沫、废弃油脂、高岭土及甲苯制备堵漏剂。
由于本发明是利用废弃聚苯乙烯、废弃油脂、高岭土及甲苯为主要原料制备防水涂料,该方法成本低廉,目前还未见该方面的相关报道,而其独特的性能使其在建筑及水利工程堵漏方面将有广阔的应用前景。
发明内容
本发明要解决的技术问题是提供一种堵漏剂的制备方法,这种制备方法以废弃聚苯乙烯泡沫、废弃油脂、高岭土及甲苯为主要原料,经合理配比,通过一定的工艺过程而制得堵漏剂。
本发明要解决的技术问题是由如下方案解决的:以废弃聚苯乙烯泡沫制备堵漏剂的方法,其特征是:将废弃聚苯乙烯泡沫加入到甲苯中,形成聚苯乙烯的甲苯溶液,加入废弃油脂和高岭土,搅拌均匀后出料、包装即得堵漏剂,其中废弃聚苯乙烯泡沫、甲苯、废弃油脂及高岭土的质量比为1:5:0.1:1-6。
上述以废弃聚苯乙烯泡沫制备堵漏剂的方法中废弃聚苯乙烯泡沫是指:包装用的废弃聚苯乙烯泡沫及一次性餐盒用的废弃聚苯乙烯泡沫等。
本发明的优点是:1、用本方法制备堵漏剂的成本很低。2、可以有效利用城市产生的大量废弃聚苯乙烯泡沫和废弃油脂,合理利用资源并减轻废弃物造成的污染。
附图说明
图1以废弃聚苯乙烯泡沫制备堵漏剂的工艺流程图。
具体实施方式
实施例1:将10 g废弃聚苯乙烯泡沫加入到50g甲苯中,形成聚苯乙烯的甲苯溶液,加入1g废弃油脂及10 g高岭土,搅拌均匀后出料,包装即得产品。
实施例2:将10 g废弃聚苯乙烯泡沫加入到50g甲苯中,形成聚苯乙烯的甲苯溶液,加入1g废弃油脂及20g高岭土,搅拌均匀后出料,包装即得产品。
实施例3:将10 g废弃聚苯乙烯泡沫加入到50g甲苯中,形成聚苯乙烯的甲苯溶液,加入1g废弃油脂及30g高岭土,搅拌均匀后出料,包装即得产品。
实施例4:将10 g废弃聚苯乙烯泡沫加入到50g甲苯中,形成聚苯乙烯的甲苯溶液,加入1g废弃油脂及40g高岭土,搅拌均匀后出料,包装即得产品。
实施例5:将10 g废弃聚苯乙烯泡沫加入到50g甲苯中,形成聚苯乙烯的甲苯溶液,加入1g废弃油脂及50g高岭土,搅拌均匀后出料,包装即得产品。
实施例6:将10 g废弃聚苯乙烯泡沫加入到50 g甲苯中,形成聚苯乙烯的甲苯溶液,加入1g废弃油脂及60g高岭土,搅拌均匀后出料,包装即得产品。
Claims (2)
1.以废弃聚苯乙烯泡沫制备堵漏剂的方法,其特征是:将废弃聚苯乙烯泡沫加入到甲苯中,形成聚苯乙烯的甲苯溶液,加入废弃油脂和高岭土,搅拌均匀后出料、包装即得堵漏剂,其中废弃聚苯乙烯泡沫、甲苯、废弃油脂及高岭土的质量比为1:5:0.1:1-6。
2.权利要求1中的废弃聚苯乙烯泡沫是指:包装用的废弃聚苯乙烯泡沫及一次性餐盒用的废弃聚苯乙烯泡沫等。