CN103305058A - 一种复合树脂涂料 - Google Patents
一种复合树脂涂料 Download PDFInfo
- Publication number
- CN103305058A CN103305058A CN2013102657901A CN201310265790A CN103305058A CN 103305058 A CN103305058 A CN 103305058A CN 2013102657901 A CN2013102657901 A CN 2013102657901A CN 201310265790 A CN201310265790 A CN 201310265790A CN 103305058 A CN103305058 A CN 103305058A
- Authority
- CN
- China
- Prior art keywords
- parts
- resol
- rosin
- based resins
- alcohol based
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种复合树脂涂料，包括以下重量配比的组分：包括以下重量配比的组分：松香改进酚醛树脂8-10份，改性醇酸树脂6-8份，填料5-8份，颜料8-12份，分散剂0.5-0.7份，溶剂55-65份。本发明制备得到的树脂涂料能耐乳化、稳定性、固着性、干燥性均较好，且对颜料有较强的湿润性、发色性。
Description
技术领域
本发明涉及一种树脂涂料，具体涉及一种油墨用复合型树脂涂料。
背景技术
印刷油墨是传递信息及装饰文化世界的精细化工产品。油墨工业和印刷工业都随着国家经济的繁荣、文化教育事业的发展而发展。油墨的技术进步及产量在某种程度上是该地区文化发达程度的标志之一。
传统采用植物油作为连接料制备油墨，随着工业技术的进步，各种类型的树脂逐步取代植物油引入了油墨连接料领域。但目前油墨多采用毒性较大的苯类、酮类、醚类等作为溶剂，危害较大，且影响环境。
发明内容
本发明的目的是为了解决现有技术中存在的缺陷，提供一种毒性较小的油墨。
为了达到上述目的，本发明提供了一种复合树脂涂料，包括以下重量配比的组分：松香改进酚醛树脂8-10份，改性醇酸树脂6-8份，填料5-8份，颜料8-12份，分散剂0.5-0.7份，溶剂55-65份，可选自乙醇、异丙醇、正丁醇或其混合物，优选乙醇和异丙醇体积比为4:1的混合溶液。
其中，松香改进酚醛树脂软化点为150-170℃，酸值为15-20。通过以下步骤制备：取对-辛基酚2100份溶解，加入25%苛性钠液90份，37%甲醛160份，于55℃反应8h，得酚醛树脂初期缩合物；取松香750份、马来酸酐30份，酚醛树脂初期缩合物250份于反应釜中，在氮气流保护下，在180-200℃下搅拌反应3h后，加入季戊四醇106份、甘油16份，于200-270℃反应至酸值达到15-20，即得松香改进酚醛树脂。
改性醇酸树脂酸价为16左右，粘度11泊（75%石脑油溶液），通过以下步骤制备：取亚麻仁油70份、甘油11.5份进行酯交换反应后，加入间苯二酸24.6份进行酯化反应，即得。
填料可采用氢氧化铝、碳酸钠、高岭土或硫酸钡，优选高岭土。
本发明相比现有技术具有以下优点：本发明采用松香改进酚醛树脂和改性醇酸树脂复配作为连接料，醇类溶液作为溶剂，制备得到的树脂涂料能耐乳化、稳定性、固着性、干燥性均较好，且对颜料有较强的湿润性、发色性，转印性很好，转印字符边缘整齐，且具有很好的柔软性，热烫印过程中转印率不低于95%。
具体实施方式
下面结合具体实施例对本发明醇基树脂涂料进行详细说明。
实施例1
松香改进酚醛树脂：取对-辛基酚2100份溶解，加入25%苛性钠液90份，37%甲醛160份，于55℃反应8h，得酚醛树脂初期缩合物；取松香750份、马来酸酐30份，酚醛树脂初期缩合物250份于反应釜中，在氮气流保护下，在180-200℃下搅拌反应3h后，加入季戊四醇106份、甘油16份，于200-270℃反应至酸值达到15-20，即得松香改进酚醛树脂。
改性醇酸树脂：取亚麻仁油70份、甘油11.5份进行酯交换反应后，加入间苯二酸24.6份进行酯化反应，即得。
醇基树脂涂料：取松香改进酚醛树脂9份，改性醇酸树脂7份，高岭土7份，碳黑10份，分散剂0.6份（如毕克K-163），乙醇48份，异丙醇12份。先将松香改进酚醛树脂和改性醇酸树脂加热溶解在乙醇和异丙醇的混合溶液中，再按顺序加入其它组分，通过研磨机使体系分散均匀，粒径在10μm以下即可。
实施例2
醇基树脂涂料：取松香改进酚醛树脂8份，改性醇酸树脂6份，碳酸钠5份，颜料8份，分散剂0.5份，乙醇65份。先将松香改进酚醛树脂和改性醇酸树脂加热溶解在乙醇中，再按顺序加入其它组分，通过研磨机使体系分散均匀，粒径在10μm以下即可。
实施例3
醇基树脂涂料：松香改进酚醛树脂10份，改性醇酸树脂8份，硫酸钡8份，颜料12份，分散剂0.7份，正丁醇55份。先将松香改进酚醛树脂和改性醇酸树脂加热溶解在正丁醇中，再按顺序加入其它组分，通过研磨机使体系分散均匀，粒径在10μm以下即可。
Claims (6)
1.一种复合树脂涂料，其特征在于：所述涂料包括以下重量配比的组分：松香改进酚醛树脂8-10份，改性醇酸树脂6-8份，填料5-8份，颜料8-12份，分散剂0.5-0.7份，溶剂55-65份；所述溶剂为醇类溶剂。
2.根据权利要求1所述的醇基树脂涂料，其特征在于：所述松香改进酚醛树脂软化点为150-170℃，酸值为15-20。
3.根据权利要求2所述的醇基树脂涂料，其特征在于：所述松香改进酚醛树脂通过以下步骤制备：取对-辛基酚2100份溶解，加入25%苛性钠液90份，37%甲醛160份，于55℃反应8h，得酚醛树脂初期缩合物；取松香750份、马来酸酐30份，酚醛树脂初期缩合物250份于反应釜中，在氮气流保护下，在180-200℃下搅拌反应3h后，加入季戊四醇106份、甘油16份，于200-270℃反应至酸值达到15-20，即得所述松香改进酚醛树脂。
4.根据权利要求1所述的醇基树脂涂料，其特征在于：所述改性醇酸树脂通过以下步骤制备：取亚麻仁油70份、甘油11.5份进行酯交换反应后，加入间苯二酸24.6份进行酯化反应，即得所述改改性醇酸树脂。
5.根据权利要求1、3或4所述的醇基树脂涂料，其特征在于：所述溶剂选自乙醇、异丙醇、正丁醇或其混合物。
6.根据权利要求1或3所述的醇基树脂涂料，其特征在于：所述填料采用高岭土。