CN103304907A - 一种含有改性硅橡胶的氯化聚乙烯电缆料 - Google Patents

一种含有改性硅橡胶的氯化聚乙烯电缆料 Download PDF

Info

Publication number
CN103304907A
CN103304907A CN2013101777361A CN201310177736A CN103304907A CN 103304907 A CN103304907 A CN 103304907A CN 2013101777361 A CN2013101777361 A CN 2013101777361A CN 201310177736 A CN201310177736 A CN 201310177736A CN 103304907 A CN103304907 A CN 103304907A
Authority
CN
China
Prior art keywords
silicon rubber
parts
modified silicon
minute
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101777361A
Other languages
English (en)
Other versions
CN103304907B (zh
Inventor
周小刚
储刘生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI WANGDA COPPER INDUSTRY DEVELOPMENT Co Ltd
Original Assignee
ANHUI WANGDA COPPER INDUSTRY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI WANGDA COPPER INDUSTRY DEVELOPMENT Co Ltd filed Critical ANHUI WANGDA COPPER INDUSTRY DEVELOPMENT Co Ltd
Priority to CN201310177736.1A priority Critical patent/CN103304907B/zh
Publication of CN103304907A publication Critical patent/CN103304907A/zh
Application granted granted Critical
Publication of CN103304907B publication Critical patent/CN103304907B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有改性硅橡胶的氯化聚乙烯电缆料，其是由下述重量份的原料制得：氯化聚乙烯50-60、改性硅橡胶22-30，包膜煅烧重晶石粉30-50，抗氧剂2641-2,抗氧剂T5010.3-0.5、硬脂酸4-6、微晶蜡3-5，氧化铝2-4,过氧化二异丙苯2-4,明矾粉末2-4，硼酸锌4-6，环氧亚麻子油2-4，硅烷偶联剂DL602 1-2。

Description

一种含有改性硅橡胶的氯化聚乙烯电缆料
技术领域
本发明涉及电缆料领域，确切地说是一种含有改性硅橡胶的氯化聚乙烯电缆料。
背景技术
 电缆护套是电缆的最外层，如VV是聚氯乙烯绝缘，聚氯乙烯护套，外面穿的管叫保护管。电缆护套材料不仅需要有优良的物理性能，如拉伸强度、断裂伸长率等，同时还需要拥有良好的阻燃性能。
发明内容
本发明的目的在于提供一种含有改性硅橡胶的氯化聚乙烯电缆料。
上述目的通过以下方案实现：
一种含有改性硅橡胶的氯化聚乙烯电缆料，其特征在于：其是由下述重量份的原料制得：
氯化聚乙烯50-60、改性硅橡胶22-30，包膜煅烧重晶石粉 30-50，抗氧剂264 1-2,抗氧剂T501 0.3-0.5、硬脂酸 4-6、微晶蜡3-5，氧化铝 2-4,过氧化二异丙苯 2-4,明矾粉末 2-4，硼酸锌4-6，环氧亚麻子油2-4，硅烷偶联剂DL602  1-2； 
    所述的包膜煅烧重晶石粉的制备方法为：重晶石粉中加入相当于其重量2-4%的醇醚糖苷、1-2%的硅烷偶联剂a151 、7-10%的去离子水，超声震荡25-30分钟后，再于70-80℃恒温水浴中搅拌加热45-65分钟，得改性复混液；再在改性复混液中加入相当于其重量10-15%的浓度为24-27%的Al2(SO4)3溶液，同时加入适量氨水调节pH值为8-11，搅拌30-40min后，静置3-4小时后，经过滤、洗涤、干燥处理后，在500-550℃煅烧5-7小时，自然冷却至室温即得；
所述的改性硅橡胶的制备方法为：在硅橡胶中加入相当于其重量1-2%的邻苯二甲酸二异癸酯、3-5%的硅烷偶联剂KH580、1-2%的交联剂 TAC，放入密炼机上，温度控制在70-75℃，塑炼5-7分钟，即得。
所述的一种含有改性硅橡胶的氯化聚乙烯电缆料，其特征在于:制备方法包括以下步骤：
（1）将除包膜煅烧重晶石粉、硼酸锌外的原料按重量份放入密炼机，于95-105℃下合炼10-13分钟；
（2）再按重量份加入剩余原料，于80-90℃下混炼7-9分钟，再于80-85℃下混炼7-9分钟；
（3）双螺杆挤出机挤出造粒，即得。
本发明的有益效果为：改性硅橡胶通过复合改性，可以增加电缆护套材料的强度、弹性等物理性能以及阻燃效果。包膜煅烧重晶石粉可以增加本发明的强度和阻燃性能。
具体实施方式
一种含有改性硅橡胶的氯化聚乙烯电缆料，其是由下述重量份的原料制得：
氯化聚乙烯50、改性硅橡胶28，包膜煅烧重晶石粉 44，抗氧剂264 1,抗氧剂T501  0.5、硬脂酸 6、微晶蜡 5，氧化铝 2,过氧化二异丙苯 2,明矾粉末 2，硼酸锌 6，环氧亚麻子油4，硅烷偶联剂DL602 1.5； 
    所述的包膜煅烧重晶石粉的制备方法为：重晶石粉中加入相当于其重量3%的醇醚糖苷、1%的硅烷偶联剂a151 、10%的去离子水，超声震荡30分钟后，再于78℃恒温水浴中搅拌加热50分钟，得改性复混液；再在改性复混液中加入相当于其重量15%的浓度为25%的Al2(SO4)3溶液，同时加入适量氨水调节pH值为9，搅拌35min后，静置4小时后，经过滤、洗涤、干燥处理后，在550℃煅烧6小时，自然冷却至室温即得；
所述的改性硅橡胶的制备方法为：在硅橡胶中加入相当于其重量1.5%的邻苯二甲酸二异癸酯、3%的硅烷偶联剂KH580、1%的交联剂 TAC，放入密炼机上，温度控制在75℃，塑炼7分钟，即得。
所述的一种含有改性硅橡胶的氯化聚乙烯电缆料，制备方法包括以下步骤：
（1）将除包膜煅烧重晶石粉、硼酸锌外的原料按重量份放入密炼机，于105℃下合炼10分钟；
（2）再按重量份加入剩余原料，于90℃下混炼7分钟，再于85℃下混炼8分钟；
（3）双螺杆挤出机挤出造粒，即得。
测试本实施例材料性能，氧指数为44%，水平垂直燃烧测试中，水平燃烧达到FH-1等级，垂直燃烧达到FV-0等级。拉伸强度为14.8MPa，断裂伸长率＞387%。

Claims (2)

1.一种含有改性硅橡胶的氯化聚乙烯电缆料，其特征在于：其是由下述重量份的原料制得：
氯化聚乙烯50-60、改性硅橡胶22-30，包膜煅烧重晶石粉 30-50，抗氧剂264 1-2,抗氧剂T501 0.3-0.5、硬脂酸 4-6、微晶蜡3-5，氧化铝 2-4,过氧化二异丙苯 2-4,明矾粉末 2-4，硼酸锌4-6，环氧亚麻子油2-4，硅烷偶联剂DL602  1-2； 
    所述的包膜煅烧重晶石粉的制备方法为：重晶石粉中加入相当于其重量2-4%的醇醚糖苷、1-2%的硅烷偶联剂a151 、7-10%的去离子水，超声震荡25-30分钟后，再于70-80℃恒温水浴中搅拌加热45-65分钟，得改性复混液；再在改性复混液中加入相当于其重量10-15%的浓度为24-27%的Al2(SO4)3溶液，同时加入适量氨水调节pH值为8-11，搅拌30-40min后，静置3-4小时后，经过滤、洗涤、干燥处理后，在500-550℃煅烧5-7小时，自然冷却至室温即得；
所述的改性硅橡胶的制备方法为：在硅橡胶中加入相当于其重量1-2%的邻苯二甲酸二异癸酯、3-5%的硅烷偶联剂KH580、1-2%的交联剂 TAC，放入密炼机上，温度控制在70-75℃，塑炼5-7分钟，即得。
2.根据权利要求1所述的一种含有改性硅橡胶的氯化聚乙烯电缆料，其特征在于:制备方法包括以下步骤：
（1）将除包膜煅烧重晶石粉、硼酸锌外的原料按重量份放入密炼机，于95-105℃下合炼10-13分钟；
（2）再按重量份加入剩余原料，于80-90℃下混炼7-9分钟，再于80-85℃下混炼7-9分钟；
（3）双螺杆挤出机挤出造粒，即得。
CN201310177736.1A 2013-05-14 2013-05-14 一种含有改性硅橡胶的氯化聚乙烯电缆料 Expired - Fee Related CN103304907B (zh)