CN103304891A - 一种塑料盖及其制备方法 - Google Patents
一种塑料盖及其制备方法 Download PDFInfo
- Publication number
- CN103304891A CN103304891A CN2012100695317A CN201210069531A CN103304891A CN 103304891 A CN103304891 A CN 103304891A CN 2012100695317 A CN2012100695317 A CN 2012100695317A CN 201210069531 A CN201210069531 A CN 201210069531A CN 103304891 A CN103304891 A CN 103304891A
- Authority
- CN
- China
- Prior art keywords
- plastic cover
- slipping agent
- raw material
- plastic
- injection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种塑料盖及其制备方法,该塑料盖的原材料包括注塑原料和爽滑剂,所述的爽滑剂的含量为注塑原料的2wt%-5wt%。在常温下,将注塑原料和爽滑剂混合均匀,然后在注塑机中注塑成型,即得产品。与现有技术相比,本发明具有使用范围广、安全可靠、节约成本等优点。
Description
技术领域
本发明涉及一种塑料盖,尤其是涉及一种塑料盖及其制备方法。
背景技术
目前,许多塑料防伪盖在组装后存在防伪环断裂问题,这是由于单一的塑料粒子注塑出来后防伪环韧性不足,容易裂开起不到防伪的作用,造成一定量原材料的浪费,若流入市场将会对企业的声誉造成很大的负面影响。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种使用范围广、安全可靠、节约成本的塑料盖及其制备方法。
本发明的目的可以通过以下技术方案来实现:一种塑料盖,其特征在于,该塑料盖的原材料包括注塑原料和爽滑剂,所述的爽滑剂的含量为注塑原料的2wt%-5wt%。
所述的注塑原料由塑料粒子和色母粒组成,以注塑原料的重量为100%计,塑料粒子的含量为90wt%-98wt%,色母粒的含量为2wt%-10wt%。
所述的塑料粒子为市售PPR 6288,PPR 7220,PPR 7225中的一种或几种。
所述的色母粒为市售色母料10076410。
所述的爽滑剂为市售爽滑剂6103。
一种塑料盖的制备方法,其特征在于,该方法包括以下步骤:在常温下,将注塑原料和爽滑剂混合均匀,然后在注塑机中注塑成型,即得产品。
本配方是在原有的原材料中添加一定比例的爽滑剂,均匀搅拌后再进行注塑,加入爽滑剂后会增加塑料粒子的柔韧性,从而改善防伪环断裂的问题。
本配方利用了有机塑料粒子之间能相溶的特性,在不改变原材料特性的情况下,增加了材料的柔韧性,降低了产品的报废率。
与现有技术相比,本发明具有以下优点:
一、使用范围广:对于需改善柔韧性的塑料件可推广;
二、安全可靠:对产品的外观、尺寸无影响;
三、节约成本:降低了报废率。
具体实施方式
下面结合具体实施例对本发明进行详细说明。
实施例1
一种塑料盖的制备包括以下步骤:
(1)以注塑原料的重量为100%计,将95wt%的市售塑料粒子PPR 7220,与5wt%的市售色母料10076410混合均匀得到注塑原料;
(2)在常温下,在步骤(1)得到的注塑原料中加入爽滑剂6103,爽滑剂6103的加入量为注塑原料的3wt%,混合均匀后放入注塑机中注塑成型,得到塑料盖。
实施例2
一种塑料盖的制备包括以下步骤:
(1)以注塑原料的重量为100%计,将90wt%的市售塑料粒子PPR 6288,与10wt%的市售色母料10076410混合均匀得到注塑原料;
(2)在常温下,在步骤(1)得到的注塑原料中加入爽滑剂6103,爽滑剂6103的加入量为注塑原料的5wt%,混合均匀后放入注塑机中注塑成型,得到塑料盖。
实施例3
一种塑料盖的制备包括以下步骤:
(1)以注塑原料的重量为100%计,将98wt%的市售塑料粒子PPR 7225,与2wt%的市售色母料10076410混合均匀得到注塑原料;
(2)在常温下,在步骤(1)得到的注塑原料中加入爽滑剂6103,爽滑剂6103的加入量为注塑原料的2wt%,混合均匀后放入注塑机中注塑成型,得到塑料盖。
本配方是在原有的原材料中添加一定比例的爽滑剂,均匀搅拌后再进行注塑,加入爽滑剂后会增加塑料粒子的柔韧性,从而改善防伪环断裂的问题。
本配方利用了有机塑料粒子之间能相溶的特性,在不改变原材料特性的情况下,增加了材料的柔韧性,降低了产品的报废率。
Claims (6)
1.一种塑料盖,其特征在于,该塑料盖的原材料包括注塑原料和爽滑剂,所述的爽滑剂的含量为注塑原料的2wt%-5wt%。
2.根据权利要求1所述的一种塑料盖,其特征在于,所述的注塑原料由塑料粒子和色母粒组成,以注塑原料的重量为100%计,塑料粒子的含量为90wt%-98wt%,色母粒的含量为2wt%-10wt%。
3.根据权利要求2所述的一种塑料盖,其特征在于,所述的塑料粒子为市售PPR 6288,PPR 7220,PPR 7225中的一种或几种。
4.根据权利要求2所述的一种塑料盖,其特征在于,所述的色母粒为市售色母料10076410。
5.根据权利要求1所述的一种塑料盖,其特征在于,所述的爽滑剂为市售爽滑剂6103。
6.一种如权利要求1所述的塑料盖的制备方法,其特征在于,该方法包括以下步骤:在常温下,将注塑原料和爽滑剂混合均匀,然后在注塑机中注塑成型,即得产品。