CN103289570A - 一种环保型pu木器漆擦色剂及其制备方法 - Google Patents
一种环保型pu木器漆擦色剂及其制备方法 Download PDFInfo
- Publication number
- CN103289570A CN103289570A CN2013101244456A CN201310124445A CN103289570A CN 103289570 A CN103289570 A CN 103289570A CN 2013101244456 A CN2013101244456 A CN 2013101244456A CN 201310124445 A CN201310124445 A CN 201310124445A CN 103289570 A CN103289570 A CN 103289570A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- wiping stain
- wood lacquer
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用在PU涂层上的擦色剂,特别涉及一种环保型PU木器漆擦色剂及其制备方法;所述环保型PU木器漆擦色剂,包括以下重量份的组分:蓖麻油40~60份,白炭黑1~4份,流平剂0.5~3份,DBE35~58份,色精0.5~20份;本发明可以直接刷涂在干燥好的透明PU涂层上,不需要打磨,平面和立面均具有良好的施工性,擦色剂待干时间可以灵活掌握,10分钟至24小时内,都可以轻松擦掉涂层表面的擦色剂,得到着色均匀涂层,操作方便,解决现有的施工难题。
Description
技术领域
本发明涉及一种用在PU涂层上的擦色剂,特别涉及一种环保型PU木器漆擦色剂。
背景技术
在家庭装修时,喷涂色漆的熟练油漆工很少,特别在施工透明有色面,很难做到均匀一致,达不到需要的装修效果,使用户和油工都不愿选用透明有色面漆、装修风格比较单一,缺少个性。
发明内容
本发明目的是可以直接刷涂在干燥好的透明PU涂层上,不需要打磨,平面和立面均具有良好的施工性,操作方便,解决现有的施工难题的一种环保型PU木器漆擦色剂及其制备方法。
为实现本发明的目的采用的技术方案是:一种环保型PU木器漆擦色剂,其特征在于:包括以下重量份的组分:
蓖麻油 40~60份
白炭黑 1~4份
流平剂 0.5~3份
DBE 35~58份
色精 0.5~20份。
所述色精最佳采用溶剂型金属络合物。
所述DBE(高沸点溶剂混合二元酸酯)最佳采用混二酸二甲酯。
所述流平剂最佳采用聚硅氧烷-聚醚共聚物。
所述白炭黑最佳采用气相二氧化硅,选自德固赛的R-972。
所述环保型PU木器漆擦色剂的制备方法,包括以下步骤组成:
A.将蓖麻油、白炭黑、流平剂、DBE依次按顺序加入容器中;
B.将搅拌机调到低速为200-500转/分钟搅拌,边分散边加入色精;
C.根据用户需要的颜色确定色精的品种和添加量,送检合格后包装。
所述其最佳的重量份如下:
蓖麻油 50份
白炭黑 2份
流平剂 1份
DBE 45份
色精 12份。
本发明的优点如下:
1.直接刷涂在干燥好的透明PU涂层上,不需要打磨;
2.平面和立面均具有良好的施工性;
3.擦色剂待干时间可以灵活掌握,10分钟至24小时内,都可以轻松擦掉涂层表面的擦色剂,得到着色均匀涂层;
4.操作方便,解决现有的施工难题;
5.选用溶剂环保无毒、气味小。
具体实施方式
下面结合具体实施例来对本发明进行详细的说明。
实施例1:
一种环保型PU木器漆擦色剂,包括以下重量份的组分:
蓖麻油 40份
白炭黑 4份
流平剂 2份
DBE 36份
色精 18份。
所述环保型PU木器漆擦色剂的制备方法包括以下步骤组成:
A.将蓖麻油、白炭黑、流平剂、DBE依次按顺序加入容器中;
B.将搅拌机调到低速为200-500转/分钟搅拌,边分散边加入色精;
C.根据用户需要的颜色确定色精的品种和添加量,送检合格后包装。
实施例2:
一种环保型PU木器漆擦色剂,包括以下重量份的组分:
蓖麻油 50份
白炭黑 2份
流平剂 1份
DBE 45份
色精 12份。
所述环保型PU木器漆擦色剂的制备方法包括以下步骤组成:
A.将蓖麻油、白炭黑、流平剂、DBE依次按顺序加入容器中;
B.将搅拌机调到低速为200-500转/分钟搅拌,边分散边加入色精;
C.根据用户需要的颜色确定色精的品种和添加量,送检合格后包装。
实施例3:
一种环保型PU木器漆擦色剂,包括以下重量份的组分:
蓖麻油 60份
白炭黑 1份
流平剂 0.5份
DBE 35份
色精 3.5份。
所述环保型PU木器漆擦色剂的制备方法包括以下步骤组成:
A.将蓖麻油、白炭黑、流平剂、DBE依次按顺序加入容器中;
B.将搅拌机调到低速为200-500转/分钟搅拌,边分散边加入色精;
C.根据用户需要的颜色确定色精的品种和添加量,送检合格后包装。
本发明最佳的实施例:
一种环保型PU木器漆擦色剂,包括以下重量份的组分:
蓖麻油 50份
白炭黑 2份
流平剂 1份
DBE 45份
色精 12份。
所述环保型PU木器漆擦色剂的制备方法包括以下步骤组成:
A.将蓖麻油、白炭黑、流平剂、DBE依次按顺序加入容器中;
B.将搅拌机调到低速为200-500转/分钟搅拌,边分散边加入色精;
C.根据用户需要的颜色确定色精的品种和添加量,送检合格后包装。
Claims (7)
1.一种环保型PU木器漆擦色剂,其特征在于:包括以下重量份的组分:
蓖麻油 40~60份
白炭黑 1~4份
流平剂 0.5~3份
DBE 35~58份
色精 0.5~20份。
2.根据权利要求1所述的环保型PU木器漆擦色剂,其特征在于:所述色精最佳采用溶剂型金属络合物。
3.根据权利要求1所述的环保型PU木器漆擦色剂,其特征在于:所述DBE最佳采用混二酸二甲酯。
4.根据权利要求1所述的环保型PU木器漆擦色剂,其特征在于:所述流平剂最佳采用聚硅氧烷-聚醚共聚物。
5.根据权利要求1所述的环保型PU木器漆擦色剂,其特征在于:所述白炭黑最佳采用气相二氧化硅。
6.根据权利要求1所述的环保型PU木器漆擦色剂,其特征在于:其最佳的重量份如下:
蓖麻油 50份
白炭黑 2份
流平剂 1份
DBE 45份
色精 12份。
7.一种制备权利要求1所述的环保型PU木器漆擦色剂方法,其特征在于:所述该方法包括以下步骤组成:
A.将蓖麻油、白炭黑、流平剂、DBE依次按顺序加入容器中;
B.将搅拌机调到低速为200-500转/分钟搅拌,边分散边加入色精;
C.根据用户需要的颜色确定色精的品种和添加量,送检合格后包装。