CN103289440A - 一种包覆水玻璃的氧化铁黑颗粒的制备方法 - Google Patents

一种包覆水玻璃的氧化铁黑颗粒的制备方法 Download PDF

Info

Publication number
CN103289440A
CN103289440A CN2013101946478A CN201310194647A CN103289440A CN 103289440 A CN103289440 A CN 103289440A CN 2013101946478 A CN2013101946478 A CN 2013101946478A CN 201310194647 A CN201310194647 A CN 201310194647A CN 103289440 A CN103289440 A CN 103289440A
Authority
CN
China
Prior art keywords
iron oxide
oxide black
preparation
water glass
viscous liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101946478A
Other languages
English (en)
Other versions
CN103289440B (zh
Inventor
姚佐胜
孙晓庆
章志海
曹阳
黄忠达
杜松松
刘凡
缪志剑
沃承立
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING RELY TECHNOLOGY Co Ltd
Original Assignee
TONGLING RELY TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING RELY TECHNOLOGY Co Ltd filed Critical TONGLING RELY TECHNOLOGY Co Ltd
Priority to CN201310194647.8A priority Critical patent/CN103289440B/zh
Publication of CN103289440A publication Critical patent/CN103289440A/zh
Application granted granted Critical
Publication of CN103289440B publication Critical patent/CN103289440B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种包覆水玻璃的氧化铁黑颗粒的制备方法，具体步骤如下：按一定重量比将海藻酸钠、羟乙基纤维素和吐温-60溶解于去离子水中，得粘性液体；再在上述制得的粘性液体中加入偏硅酸钠和半补强炭黑进行改性；取氧化铁黑加入造粒机中进行造粒，同时将改性粘性液体均匀地喷淋到氧化铁黑粉料上，形成氧化铁黑小颗粒，烘干，过筛，即得成品。偏硅酸钠具有较好的水溶性，与粘结性，可以与水性溶剂或油性酯类物质进行反应或联接，提高氧化铁黑颜料的粘结强度，同时也提高了氧化铁黑颜料的流动性和分散性。

Description

一种包覆水玻璃的氧化铁黑颗粒的制备方法
技术领域
本发明涉及一种氧化铁黑的制备方法，具体涉及一种包覆水玻璃的氧化铁黑颗粒的制备方法。
背景技术
    氧化铁黑，分子式为Fe3O4，为黑色粉末，是Fe2O3和FeO的加成物，不溶于水，具有磁性，着色力和遮盖力很高。氧化铁黑作为铁系颜料中的一种，由于其无毒、无嗅、无污染等特点，广泛用于建筑行业中酚醛防锈漆填料、重防腐涂料底漆等；在用于橡胶、塑料的着色时，有补强老化的作用，同时保护有机物被紫外光降解的特点；此外，也用于人造大理石、陶瓷及水泥地面的着色。但是氧化铁黑在较高温度下会发生褪色、变色等现象，耐热稳定性差，从而限制了氧化铁黑的使用范围。
发明内容
本发明的目的在于提供一种包覆水玻璃的氧化铁黑颗粒的制备方法，提高氧化铁黑的高温稳定性。
本发明采用的技术方案如下：
    一种包覆水玻璃的氧化铁黑颗粒的制备方法，包括以下步骤：
    （1）按重量比3-5:2-4:1称取海藻酸钠、羟乙基纤维素和吐温-60加入10-15倍去离子水中，水浴加热至50-60℃，超声分散30-40分钟，得粘性液体；
    （2）在上述制得的粘性液体中加入3-5%的偏硅酸钠和1-3%的半补强炭黑，2000-3000rpm高速剪切分散15-20分钟，得偏硅酸钠和半补强炭黑改性的粘性液体；
    （3）按重量份取100-150份氧化铁黑加入造粒机中进行造粒，同时将40-60份步骤（2）制得的改性粘性液体均匀地喷淋到氧化铁黑粉料上，形成氧化铁黑小颗粒；
    （4）将步骤（3）制得的氧化铁黑颗粒于80-90℃下烘干，然后过40-50目筛，即得成品。
    步骤（1）中所述的超声功率为600-800W，超声频率为20-30KHz。
    步骤（3）中所述的造粒机的转速为1500-2500rpm。
本发明有益效果：
本发明将氧化铁黑粉末制造成表面覆盖有含有炭黑、偏硅酸钠、海藻酸钠等组分的颗粒状颜料，偏硅酸钠具有较好的水溶性，与粘结性，可以与水性溶剂或油性酯类物质进行反应或联接，提高氧化铁黑颜料的粘结强度，同时也提高了氧化铁黑颜料的流动性和分散性；本发明所生产的氧化铁黑具有优越的耐温性能，良好的耐酸、耐碱性能以及吸光性强、着色力高、相容性好、分散性好等特点，具有巨大的市场前景。
具体实施方式
    一种包覆水玻璃的氧化铁黑颗粒的制备方法，包括以下步骤：
    （1）按重量比4:3:1称取海藻酸钠、羟乙基纤维素和吐温-60加入12倍去离子水中，水浴加热至55℃，超声分散30分钟，得粘性液体；
    （2）在上述制得的粘性液体中加入4%的偏硅酸钠和2%的半补强炭黑，2000rpm高速剪切分散20分钟，得偏硅酸钠和半补强炭黑改性的粘性液体；
    （3）按重量份取120份氧化铁黑加入造粒机中进行造粒，同时将50份步骤（2）制得的改性粘性液体均匀地喷淋到氧化铁黑粉料上，形成氧化铁黑小颗粒；
    （4）将步骤（3）制得的氧化铁黑颗粒于85℃下烘干，然后过50目筛，即得成品。
    步骤（1）中所述的超声功率为800W，超声频率为20KHz。
    步骤（3）中所述的造粒机的转速为2000rpm。
本实施例生产出来的氧化铁黑产品性能分析数据如下表：
项目 指标 检测结果
水溶物（%） ≤1.0  0.76
105℃挥发物（%） ≤1.0 0.83
吸油量（%） 15-25 22.9
着色强度（%） 95-105 99.6
耐200℃/30min （△E） ≤1.0 0.82

Claims (3)

1.一种包覆水玻璃的氧化铁黑颗粒的制备方法，其特征在于包括以下步骤：
（1）按重量比3-5:2-4:1称取海藻酸钠、羟乙基纤维素和吐温-60加入10-15倍去离子水中，水浴加热至50-60℃，超声分散30-40分钟，得粘性液体；
（2）在上述制得的粘性液体中加入3-5%的偏硅酸钠和1-3%的半补强炭黑，2000-3000rpm高速剪切分散15-20分钟，得偏硅酸钠和半补强炭黑改性的粘性液体；
（3）按重量份取100-150份氧化铁黑加入造粒机中进行造粒，同时将40-60份步骤（2）制得的改性粘性液体均匀地喷淋到氧化铁黑粉料上，形成氧化铁黑小颗粒；
（4）将步骤（3）制得的氧化铁黑颗粒于80-90℃下烘干，然后过40-50目筛，即得成品。
2.根据权利要求1所述的一种包覆水玻璃的氧化铁黑颗粒的制备方法，其特征在于，步骤（1）中所述的超声功率为600-800W，超声频率为20-30KHz。
3.根据权利要求1所述的一种包覆水玻璃的氧化铁黑颗粒的制备方法，其特征在于，步骤（3）中所述的造粒机的转速为1500-2500rpm。
CN201310194647.8A 2013-05-23 2013-05-23 一种包覆水玻璃的氧化铁黑颗粒的制备方法 Active CN103289440B (zh)