CN103286832A - Acacia mangium board mending agent and acacia mangium board mending method - Google Patents
Acacia mangium board mending agent and acacia mangium board mending method Download PDFInfo
- Publication number
- CN103286832A CN103286832A CN2013101899481A CN201310189948A CN103286832A CN 103286832 A CN103286832 A CN 103286832A CN 2013101899481 A CN2013101899481 A CN 2013101899481A CN 201310189948 A CN201310189948 A CN 201310189948A CN 103286832 A CN103286832 A CN 103286832A
- Authority
- CN
- China
- Prior art keywords
- healant
- yearning
- wood
- parts
- lovers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a floor scar mending agent and a floor scar mending method, in particular to an acacia mangium board mending agent and an acacia mangium board mending method. The acacia mangium board mending method includes the steps: according to parts by weight, preparing a first mending agent from 40-60 parts of wood flour, 10-20 parts of iron oxide powder and 25-40 parts of reduced iron powder, or preparing a second mending agent from 28-33 parts of putty, 25-28 parts of iron oxide powder and 13-16 parts of reduced iron powder; adding 5-20 parts of water into the first mending agent with uniform stirring, and standing so that first mixed liquor is obtained; adding 5-20 parts of water into the second mending agent with uniform stirring, and standing so that second mixed liquor is obtained; adding the first mixed liquor into an acacia mangium blank scar pit, and dripping glue water along the periphery or the middle of the scar pit; adding curing agent into the second mixed liquor with uniform stirring, and filling a uniformly stirred mixture into the scar pit within 0-30min; performing secondary sanding; performing roll coating of priming paint; sanding; and painting finishing paint. By the mending agent and the mending method for mending, original effect of acacia mangium scar mending can be achieved.
Description
Technical field
The present invention relates to a kind of floor scar healant and method for repairing and mending thereof, particularly a kind of yearning between lovers wood is mended plate healant and method for repairing and mending thereof.
Background technology
Domestic factory owner will use the true qualities wood chip to mend soil in conjunction with 502 glue and PE to carry out repairings that scab of yearning between lovers wood, but has serious hidden danger of quality, can produce after the repairing become phenomenons such as white or grey, and color naturally, does not cause a large amount of complaint and claims.CN102632528A (2012-8-15) discloses a kind of arithmetic for lumber surface defects' processing method, may further comprise the steps: (1) is partly cleared up arithmetic for lumber surface defects'; (2) use alcohol or water paint or adhesive wetting to spraying around the defect part; (3) to defect part with the coating of direct water paint/isocyanate glue or after filling out repairing putty earlier again use lacquer/isocyanate glue be coated with; (4) indoor natural surface drying carries out light weight sand to the surface and handles and can paint more than 3 hours or after the oven dry processing solidified it in 20-120 minute fully under 30 ℃ of-80 ℃ of temperature.Yet this method is not suitable for yearning between lovers wood and mends plate.
Summary of the invention
One of purpose of the present invention can not produce blushing, color nature after providing a kind of the repairing, can reach the yearning between lovers wood benefit plate healant that yearning between lovers wood scabs and repairs the original flavor effect.
Two of purpose of the present invention can not produce blushing, color nature after providing a kind of the repairing, can reach the yearning between lovers wood method for repairing and mending that yearning between lovers wood scabs and repairs the original flavor effect.
First technical purpose of the present invention is achieved by the following technical programs:
In order to solve technical problem of the present invention, reach technique effect of the present invention: the invention provides two kinds of yearning between lovers wood and make up healant, first kind is:
A kind of yearning between lovers wood is mended the plate healant, comprises wood powder 40-60 part, brown iron oxide 10-20 part, reduced iron powder 25-40 part of proportioning by weight.
Adopt healant of the present invention, be filled into the scar place of yearning between lovers plank, can reach the original flavor that the coffee bean look scabs and repairs, and coffee bean is the most approaching repairing original flavor effect that scabs; The scar place intensity height that adopts this healant to repair simultaneously can meet or exceed scar periphery yearning between lovers wood material intensity.
As preferably, described wood powder is yearning between lovers wood wood powder.
As preferably, described wood powder 48-52 part, brown iron oxide 13-16 part, reduced iron powder 30-35 part.
Umber of the present invention is all parts by weight.
More preferably, 50 parts of described wood powders, 15 parts of brown iron oxides, 30 parts of reduced iron powders.
As preferably, described yearning between lovers wood is mended the plate healant and is also comprised water 5-20 part.
In wood powder, brown iron oxide and the reduced iron powder of described weight proportion, add an amount of water, be after stirring and partly solidify shape, more be conducive to the effect that scar is repaired, improve the scar place intensity of repairing.
More preferably, described yearning between lovers wood benefit plate healant also comprises premetallized dye toner 0.5-5 part.
The premetallized dye toner adds the effect that helps scar to repair in the healant, can not produce blushing, and it is more natural that scar is repaired.
More preferably, described toner is for only being dissolved in the water-based coffee bean look toner of water.
It is more natural that this toner is repaired scar.
As preferably, described yearning between lovers wood is mended the plate healant and is also comprised glue.
In order to solve technical problem of the present invention, reach technique effect of the present invention: the invention provides two kinds of yearning between lovers wood and make up healant, second kind is:
A kind of yearning between lovers wood is mended the plate healant, comprises atom ash 28-33 part, brown iron oxide 25-28 part, reduced iron powder 13-16 part of proportioning by weight.
Two components that the main putty that described atom ash is formed through agitation grinding by material such as unsaturated resin, talcum powder, styrene and curing agent are formed are filled and led up material.The atom ash of described parts by weight, brown iron oxide and reduced iron powder mix the back and form a kind of special putty, fill it into the scar place of yearning between lovers plank, can reach the original flavor that the coffee bean look scabs and repairs, and coffee bean is the most approaching repairing original flavor effect that scabs; The scar place intensity height that adopts this healant to repair simultaneously can meet or exceed scar periphery yearning between lovers wood material intensity.
As preferably, described atom ash 29-31 part, brown iron oxide 26-27 part, reduced iron powder 14-15 part.
More preferably, 30 parts of described atom ashes, 26.5 parts of brown iron oxides, 14.5 parts of reduced iron powders.
As preferably, described yearning between lovers wood is mended the plate healant and is also comprised water 5-20 part.
In wood powder, brown iron oxide and the reduced iron powder of described weight proportion, add an amount of water, be after stirring and partly solidify shape, more be conducive to the effect that scar is repaired, improve the scar place intensity of repairing.
More preferably, described yearning between lovers wood benefit plate healant also comprises premetallized dye toner 0.5-5 part.
The premetallized dye toner adds the effect that helps scar to repair in the healant, can not produce blushing, and it is more natural that scar is repaired.
More preferably, described toner is for only being dissolved in the water-based coffee bean look toner of water.
It is more natural that this toner is repaired scar.
As preferably, described yearning between lovers wood is mended the plate healant and is also comprised curing agent 2-8 part.
More preferably, described curing agent is the mixture that 1.8-7.5 part polyamide curing agent and 0.2-0.5 part m-phenylene diamine (MPD) are formed.
Adopt curing agent of the present invention, can improve the scar place intensity of repairing simultaneously so that color is more natural.
Second technical purpose of the present invention is achieved by the following technical programs:
A kind of yearning between lovers wood method for repairing and mending, it comprises step successively:
(1) batching: proportioning first healant or second healant by weight, described first healant is wood powder 40-60 part, brown iron oxide 10-20 part, reduced iron powder 25-40 part; Described second healant is atom ash 28-33 part, brown iron oxide 25-28 part, reduced iron powder 13-16 part;
(2) mix: described first healant is added 5-20 part water, stir, leave standstill the mixed liquor of winning; Described second healant is added 5-20 part water, stir, leave standstill, get second mixed liquor;
(3) sandings: the yearning between lovers wood blank that pending scar is repaired carries out the sanding first time;
(4) repair:
A. described first mixed liquor is added in the yearning between lovers wood blank scar pit, the circumferential or middle part along the scar pit splashes into glue then, leaves standstill;
B. in described second mixed liquor, add curing agent, mix the back and in 0-30min, fill up the scar pit; Leave standstill;
(5) secondary sanding;
(6) priming paint roller coat;
(7) sand milling;
(8) go up finish paint.
The advantage of method for repairing and mending of the present invention is:
1. batching back gained is filled into the scar place of yearning between lovers plank, can reach the original flavor that the coffee bean look scabs and repairs, and coffee bean is the most approaching repairing original flavor effect that scabs; The scar place intensity height that adopts this healant to repair simultaneously can meet or exceed scar periphery yearning between lovers wood material intensity;
2. adopt two kinds of diverse ways to use described first healant or second healant, to reach the most approaching original flavor effect that scabs and repair, this may be because the viscosity of described first mixed liquor greater than the viscosity of described second mixed liquor, therefore needs to adopt method of the present invention could obtain required effect.
As preferably, also add 0.5-5 part premetallized dye toner during described step (2) mixing.
As preferably, described step (2) leaves standstill 2-48h.
As preferably, described step (4) A leaves standstill 6-48h.
As preferably, described step (4) B leaves standstill 1-5h.
As preferably, described step (7) is used UV lacquer or PU lacquer priming paint roller coat.
As preferably, described step (8) goes up 2-5 all over finish paint.
More preferably, described curing agent is the mixture that 1.8-7.5 part polyamide curing agent and 0.2-0.5 part m-phenylene diamine (MPD) are formed.
Adopt curing agent of the present invention, can improve the scar place intensity of repairing simultaneously so that color is more natural.
Description of drawings
Fig. 1 is the effect after prior art yearning between lovers wood scar is repaired;
Fig. 2 is to use yearning between lovers wood of the present invention to mend the repair efficiency of plate healant;
Among the figure, 1-has mend now; The new mend of 2-.
The specific embodiment
Embodiment one
Proportioning yearning between lovers wood is mended plate first healant by weight: 40 parts of former wood powders, 10 parts of brown iron oxides, 25 parts of reduced iron powders.Described first healant is added 5 parts of water, stir, leave standstill 2h, get thick mixed liquor; The yearning between lovers wood blank that pending scar is repaired carries out the sanding first time; Described mixed liquor is added in the yearning between lovers wood blank scar pit, and the circumferential or middle part along described scar pit splashes into 502 glue or floor special glue glue then, leaves standstill 6-48h to glue dries; Carry out the secondary sanding then; Yearning between lovers after secondary sanding wood blank is carried out one time or multipass UV lacquer or PU lacquer priming paint roller coat; Adopt automatic sand mill to carry out sand milling then; Go up at last the above finish paint of twice.Repair efficiency is seen the new mend 2 among Fig. 2, color nature, reaches yearning between lovers wood and scabs and repair the original flavor effect.
Embodiment two
With embodiment one, different is 60 parts of first healant yearning between lovers wood wood powders, 20 parts of brown iron oxides, 40 parts of reduced iron powders.Described first healant is added 20 parts of water, stir, leave standstill 48h.
Embodiment three
With embodiment one, different is 52 parts of the described wood powders of first healant, 16 parts of brown iron oxides, 35 parts of reduced iron powders.Described first healant is added 10 parts of water; , stir, leave standstill 20h.First healant also comprises 0.5 part of water-based coffee bean look toner.
Embodiment four
With embodiment one, different is 48 parts of the described wood powders of first healant, 13 parts of brown iron oxides, 30 parts of reduced iron powders; First healant also comprises 5 parts of water-based coffee bean look toners.
Embodiment five
With embodiment one, different is 50 parts of the described wood powders of first healant, 15 parts of brown iron oxides, 30 parts of reduced iron powders; First healant also comprises 2 parts of water-based coffee bean look toners.
Embodiment six
Proportioning yearning between lovers wood is mended plate second healant by weight: 28 parts of atom ashes, 25 parts of brown iron oxides, 13 parts of reduced iron powders.Described second healant is added 5-20 part water, stir, leave standstill, get second mixed liquor; Add that 1.8 parts of polyamide curing agents and 0.2 part of m-phenylene diamine (MPD) form in described second mixed liquor, mix and then in 0.2min, fill up the scar pit; Leave standstill 2h.Carry out the secondary sanding then; Yearning between lovers after secondary sanding wood blank is carried out one time or multipass UV lacquer or PU lacquer priming paint roller coat; Adopt automatic sand mill to carry out sand milling then; Go up at last the above finish paint of twice.Repair efficiency is seen the new mend 2 among Fig. 2, color nature, reaches yearning between lovers wood and scabs and repair the original flavor effect.
Embodiment seven
Proportioning yearning between lovers wood is mended plate second healant by weight: 33 parts of atom ashes, 28 parts of brown iron oxides, 16 parts of reduced iron powders.Described second healant is added 5-20 part water, stir, leave standstill, get second mixed liquor; In described second mixed liquor, add 7.5 parts of polyamide curing agents and 0.5 part of curing agent that m-phenylene diamine (MPD) is formed, mix the back and in 30min, fill up the scar pit; Leave standstill 1h.All the other are with embodiment six.
Embodiment eight
Proportioning yearning between lovers wood is mended plate second healant by weight: 29 parts of atom ashes, 26 parts of brown iron oxides, 14 parts of reduced iron powders.Described second healant is added 5-20 part water, stir, leave standstill, get second mixed liquor; In described second mixed liquor, add 4 parts of polyamide curing agents and 0.3 part of curing agent that m-phenylene diamine (MPD) is formed, mix the back and in 20min, fill up the scar pit; Leave standstill 5h.All the other are with embodiment six.
Embodiment nine
Proportioning yearning between lovers wood is mended plate second healant by weight: 31 parts of atom ashes, 27 parts of brown iron oxides, 15 parts of reduced iron powders.
Embodiment ten
Proportioning yearning between lovers wood is mended plate second healant by weight: 30 parts of atom ashes, 26.5 parts of brown iron oxides, 14.5 parts of reduced iron powders.
The comparative example one
Yearning between lovers wood scar method for repairing and mending is: the timber sanding, and--PE mends soil, and-----face is repaiied look (carrying out in case of necessity) in PU two degree priming paint sprayings twice--sand milling (320# sand paper)--in sanding, there is serious hidden danger of quality after the repairing, repair color variable color behind paint, become white or lime look etc. and cause a large amount of complaint and claims, repair efficiency is seen Fig. 1, and variable color place after this technical method is repaired is adopted in existing mend 1 expression.
This specific embodiment only is explanation of the invention; it is not limitation of the present invention; those skilled in the art can make the modification that does not have creative contribution to present embodiment as required after reading this specification, but as long as all are subjected to the protection of Patent Law in claim scope of the present invention.
Claims (10)
1. a yearning between lovers wood is mended the plate healant, it is characterized in that: comprise wood powder 40-60 part, brown iron oxide 10-20 part, reduced iron powder 25-40 part of proportioning by weight.
2. a kind of yearning between lovers wood according to claim 1 is mended the plate healant, it is characterized in that: described wood powder is yearning between lovers wood wood powder.
3. a kind of yearning between lovers wood according to claim 1 is mended the plate healant, it is characterized in that: described wood powder 48-52 part, brown iron oxide 13-16 part, reduced iron powder 30-35 part.
4. a kind of yearning between lovers wood according to claim 3 is mended the plate healant, it is characterized in that: 50 parts of described wood powders, 15 parts of brown iron oxides, 30 parts of reduced iron powders.
5. mend the plate healant according to each described a kind of yearning between lovers wood of claim 1-4, it is characterized in that: described yearning between lovers wood is mended the plate healant and is also comprised water 5-20 part.
6. a kind of yearning between lovers wood according to claim 5 is mended the plate healant, it is characterized in that: described yearning between lovers wood is mended the plate healant and is also comprised premetallized dye toner 0.5-5 part.
7. a kind of yearning between lovers wood according to claim 6 is mended the plate healant, it is characterized in that: described toner is for only being dissolved in the water-based coffee bean look toner of water.
8. a yearning between lovers wood is mended the plate healant, it is characterized in that: comprise atom ash 28-33 part, brown iron oxide 25-28 part, reduced iron powder 13-16 part of proportioning by weight.
9. a kind of yearning between lovers wood according to claim 8 is mended the plate healant, it is characterized in that: described atom ash 29-31 part, brown iron oxide 26-27 part, reduced iron powder 14-15 part.
10. a right to use requires 1 or 8 described a kind of yearning between lovers wood to mend the yearning between lovers wood method for repairing and mending of plate healant, and it comprises step successively:
(1) batching: proportioning first healant or second healant by weight, described first healant is wood powder 40-60 part, brown iron oxide 10-20 part, reduced iron powder 25-40 part; Described second healant is atom ash 28-33 part, brown iron oxide 25-28 part, reduced iron powder 13-16 part;
(2) mix: described first healant is added 5-20 part water, stir, leave standstill the mixed liquor of winning; Described second healant is added 5-20 part water, stir, leave standstill, get second mixed liquor;
(3) sandings: the yearning between lovers wood blank that pending scar is repaired carries out the sanding first time;
(4) repair:
A. described first mixed liquor is added in the yearning between lovers wood blank scar pit, the circumferential or middle part along the scar pit splashes into glue then, leaves standstill;
B. in described second mixed liquor, add curing agent, mix the back and in 0-30min, fill up the scar pit; Leave standstill;
(5) secondary sanding;
(6) priming paint roller coat;
(7) sand milling;
(8) go up finish paint.