CN103280265B - 一种海上风电用双云母亚胺烧结绕组线 - Google Patents

一种海上风电用双云母亚胺烧结绕组线 Download PDF

Info

Publication number
CN103280265B
CN103280265B CN201310236962.2A CN201310236962A CN103280265B CN 103280265 B CN103280265 B CN 103280265B CN 201310236962 A CN201310236962 A CN 201310236962A CN 103280265 B CN103280265 B CN 103280265B
Authority
CN
China
Prior art keywords
layer
polyester film
fluorine
mica
imines
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310236962.2A
Other languages
English (en)
Other versions
CN103280265A (zh
Inventor
谢云岩
匡美周
李荣海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gold electrician electromagnetic wire Co. Ltd.
Original Assignee
HUNAN XINXIN CABLE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN XINXIN CABLE CO Ltd filed Critical HUNAN XINXIN CABLE CO Ltd
Priority to CN201310236962.2A priority Critical patent/CN103280265B/zh
Publication of CN103280265A publication Critical patent/CN103280265A/zh
Application granted granted Critical
Publication of CN103280265B publication Critical patent/CN103280265B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种海上风电用双云母亚胺烧结绕组线，包括裸导体和包绕在裸导体外的三层绝缘层，所述的三层绝缘层，靠近裸导体的一层绝缘层为聚酰亚胺氟46复合薄膜层，聚酰亚胺氟46复合薄膜层外侧的两层绝缘层均为单面聚酯薄膜补强少胶粉云母带层。本发明耐高频脉冲，且可以满足风力发电机绕组耐潮湿、耐盐雾、耐霉菌、耐高压、耐辐射等要求，本发明还具有优良的电气性能和机械性能，良好的耐热性能，可满足F级绝缘要求；与国外相同性能的电缆相比，本发明价格低廉。

Description

一种海上风电用双云母亚胺烧结绕组线
技术领域
本发明涉及一种绕组线，尤其是涉及一种海上风电用双云母亚胺烧结绕组线。
背景技术
随着海上风力发电电机在国内的快速发展，目前，5MW海上风力发电机是国内输出功率最大的风力发电机，发电机的频率变化时，电压值最高达3.3KV。由于变压器连接过程中频率变化大，使得发电机中含有高频脉冲的尖峰过电压的波形很陡，造成电压在发电机绕制的电压值分布不均匀，除此之外发电机在海上运行中绝缘层必须能耐潮湿、耐盐雾、耐霉菌、耐高压、耐辐射等要求，现有的绕组线难以满足要求。
发明内容
为了解决上述技术问题，本发明提供了一种海上风电用双云母亚胺烧结绕组线，既可以满足风力发电机绕组耐潮湿、耐盐雾、耐霉菌、耐高压、耐辐射等要求，又可以满足耐高频脉冲的要求。
本发明采用的技术方案是：包括裸导体和包绕在裸导体外的三层绝缘层，所述的三层绝缘层，靠近裸导体的一层绝缘层为聚酰亚胺氟46复合薄膜层，聚酰亚胺氟46复合薄膜层外侧的两层绝缘层均为单面聚酯薄膜补强少胶粉云母带层；所述的聚酰亚胺氟46复合薄膜层由聚酰亚胺氟46复合薄膜绕包而成，所述的聚酰亚胺氟46复合薄膜由含有耐电晕材料的聚酰亚胺薄膜和氟46组成，氟46位于聚酰亚胺薄膜朝向裸导体的面上；所述的单面聚酯薄膜补强少胶粉云母带层由单面聚酯薄膜补强少胶粉云母带绕包而成，所述的单面聚酯薄膜补强少胶粉云母带依次由促进剂和胶粘剂混合层、云母纸层、促进剂和胶粘剂混合层、聚酯薄膜层、热熔胶层组成，所述的促进剂和胶粘剂混合层朝向聚酰亚胺氟46复合薄膜层；所述的单面聚酯薄膜补强少胶粉云母带厚度为0.06～0.08mm，两层单面聚酯薄膜补强少胶粉云母带层的单面聚酯薄膜补强少胶粉云母带绕包方向相同，且重叠的范围均为49～51%，最外层的单面聚酯薄膜补强少胶粉云母带层与中间层的单面聚酯薄膜补强少胶粉云母带层重叠位置应相互错开45～55%。
上述的海上风电用双云母亚胺烧结绕组线中，所述的三层绝缘层的总厚度为0.6～0.8mm。
上述的海上风电用双云母亚胺烧结绕组线中，所述的聚酰亚胺氟46复合薄膜厚度为0.03～0.05mm，绕包重叠范围为51%～66.67%。
上述的海上风电用双云母亚胺烧结绕组线中，所述的聚酰亚胺氟46复合薄膜层的绕包方向与两层单面聚酯薄膜补强少胶粉云母带层的绕包方向可以相同，也可以相反。
上述的海上风电用双云母亚胺烧结绕组线中，所述的裸导体可为铜扁线或铝扁线。
上述的海上风电用双云母亚胺烧结绕组线中，所述的耐电晕材料为Al2O3或TiO2、氟46主要成分为聚氟乙烯-丙烯。
本发明的有益效果是：本发明耐高频脉冲，且可以满足风力发电机绕组耐潮湿、耐盐雾、耐霉菌、耐高压、耐辐射等要求，本发明还具有优良的电气性能和机械性能，良好的耐热性能，可满足F级绝缘要求，击穿电压高达7000v以上；与国外相同性能的绕组线相比，本发明价格低廉。
附图说明
图1是本发明的截面图。
图2是本发明耐电晕的聚酰亚胺氟46复合薄膜层绕包的截面示意图。
图3是本发明耐电晕的聚酰亚胺氟46复合薄膜层绕包重叠立体示意图。
图4是本发明的两层单面聚酯薄膜补强少胶粉云母带层绕包结构示意图。
图5是本发明的两侧单面聚酯薄膜补强少胶粉云母带层绕包重叠立体示意图。
图6是本发明单面聚酯薄膜补强少胶粉云母带层和耐电晕的聚酰亚胺氟46复合薄膜层绕包方向相同时的绕包示意图。
图7是本发明单面聚酯薄膜补强少胶粉云母带层和耐电晕的聚酰亚胺氟46复合薄膜层绕包方向相反时的绕包示意图。
具体实施方式
下面结合附图对本发明做进一步说明。
如图1所示，本发明包括裸导体1及包绕在裸导体1外侧的三层绝缘层，靠近裸导体1的一层绝缘层为聚酰亚胺氟46复合薄膜层2，聚酰亚胺氟46复合薄膜层2外侧的两层绝缘层均为单面聚酯薄膜补强少胶粉云母带层3、4，所述的裸导体1为铜扁线或铝扁线，三层绝缘层的总厚度为0.6～0.8mm。
如图2、图3所示，所述的聚酰亚胺氟46复合薄膜层2由聚酰亚胺氟46复合薄膜21绕包而成，所述的聚酰亚胺氟46复合薄膜21由含有耐电晕的材料聚酰亚胺薄膜和氟46组成，其中耐电晕的材料为Al2O3或TiO2，氟46主要成分为聚氟乙烯-丙烯，氟46位于聚酰亚胺薄膜朝向裸导体的面上。所述的聚酰亚胺氟46复合薄膜21厚度为0.03～0.05mm；绕包重叠范围为51%～66.67%。
如图4、图5所示，所述的单面聚酯薄膜补强少胶粉云母带层3、4均由单面聚酯薄膜补强少胶粉云母带31绕包而成，所述的单面聚酯薄膜补强少胶粉云母带31依次由促进剂和胶粘剂混合层、云母纸层、促进剂和胶粘剂混合层、聚酯薄膜层、热熔胶层组成，所述的促进剂和胶粘剂混合层朝向聚酰亚胺氟46复合薄膜层2。所述的单面聚酯薄膜补强少胶粉云母带厚度为0.06～0.08mm，两层单面聚酯薄膜补强少胶粉云母带层3、4的单面聚酯薄膜补强少胶粉云母带31的绕包方向相同，且重叠的范围均为49～51%，最外层的单面聚酯薄膜补强少胶粉云母带层4的重叠处与中间层的单面聚酯薄膜补强少胶粉云母带层3重叠处应相互错开45～55%。
如图6、图7所示，所述的聚酰亚胺氟46复合薄膜层2的绕包方向与两层单面聚酯薄膜补强少胶粉云母带层3、4的绕包方向可以相同，也可以相反。

Claims (6)

1.一种海上风电用双云母亚胺烧结绕组线，其特征是：包括裸导体和包绕在裸导体外的三层绝缘层，所述的三层绝缘层，靠近裸导体的一层绝缘层为聚酰亚胺氟46复合薄膜层，聚酰亚胺氟46复合薄膜层外侧的两层绝缘层均为单面聚酯薄膜补强少胶粉云母带层；所述的聚酰亚胺氟46复合薄膜层由聚酰亚胺氟46复合薄膜绕包而成，所述的聚酰亚胺氟46复合薄膜由含有耐电晕材料的聚酰亚胺薄膜和氟46组成，氟46位于聚酰亚胺薄膜朝向裸导体的面上；所述的单面聚酯薄膜补强少胶粉云母带层由单面聚酯薄膜补强少胶粉云母带绕包而成，所述的单面聚酯薄膜补强少胶粉云母带依次由促进剂和胶粘剂混合层、云母纸层、促进剂和胶粘剂混合层、聚酯薄膜层、热熔胶层组成，所述的促进剂和胶粘剂混合层朝向聚酰亚胺氟46复合薄膜层；所述的单面聚酯薄膜补强少胶粉云母带厚度为0.06～0.08mm，两层单面聚酯薄膜补强少胶粉云母带层的单面聚酯薄膜补强少胶粉云母带绕包方向相同，且重叠的范围均为49～51%，最外层的单面聚酯薄膜补强少胶粉云母带层与中间层的单面聚酯薄膜补强少胶粉云母带层重叠位置应相互错开45～55%。
2.如权利要求1所述的海上风电用双云母亚胺烧结绕组线，其特征是：所述的三层绝缘层的总厚度为0.6～0.8mm。
3.如权利要求1所述的海上风电用双云母亚胺烧结绕组线，其特征是：所述的裸导体可为铜扁线或铝扁线。
4.如权利要求2所述的海上风电用双云母亚胺烧结绕组线，其特征是：所述的聚酰亚胺氟46复合薄膜厚度为0.03～0.05mm，绕包重叠范围为51%～66.67%。
5.如权利要求2所述的海上风电用双云母亚胺烧结绕组线，其特征是：所述的耐电晕材料为Al2O3或TiO2、氟46主要成分为聚氟乙烯-丙烯。
6.如权利要求1所述的海上风电用双云母亚胺烧结绕组线，其特征是：所述的聚酰亚胺氟46复合薄膜层的绕包方向与两层单面聚酯薄膜补强少胶粉云母带层的绕包方向相同或相反。
CN201310236962.2A 2013-06-17 2013-06-17 一种海上风电用双云母亚胺烧结绕组线 Active CN103280265B (zh)