CN103265767A - Pvc透明磨砂密封条及其制备方法 - Google Patents
Pvc透明磨砂密封条及其制备方法 Download PDFInfo
- Publication number
- CN103265767A CN103265767A CN2013101144049A CN201310114404A CN103265767A CN 103265767 A CN103265767 A CN 103265767A CN 2013101144049 A CN2013101144049 A CN 2013101144049A CN 201310114404 A CN201310114404 A CN 201310114404A CN 103265767 A CN103265767 A CN 103265767A
- Authority
- CN
- China
- Prior art keywords
- sealing strip
- frosted
- stearic acid
- soybean oil
- elastic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种密封条，尤其是一种PVC透明磨砂密封条及其制备方法；本发明的目的是提供一种有弹性、抗压缩变形、表面吸附力小的PVC透明磨砂密封条及其制备方法；它由磨砂料制备而成，磨砂料包括弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂；所述的弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂的重量比为45:28:0.2:0.2:4:0.55:5；由于这种物质表面具有磨砂效果，相互之间吸附力就比较小，同时它也适宜在潮湿的环境使用，我国南方多雨天气，室内会比较潮湿，因此更能受广大消费者欢迎。
Description
技术领域
本发明涉及一种密封条，尤其是一种PVC透明磨砂密封条及其制备方法。
背景技术
目前企业所生产的密封条包括特有的汽车密封条、机械密封条、门窗密封条、淋浴房密封条等产品。
但用于淋浴房玻璃门上的密封条，由于环境潮湿，温度变化较大，使得密封条很容易老化，使命寿命较短；且淋浴房玻璃门在开关过程中，密封条与密封条之间会相互吸附，吸附力大，容易在拉玻璃门时将玻璃门上的密封条拉下来或由于抗拉强度太大使玻璃门碎掉。
发明内容
本发明的目的在于为了解决上述技术的不足，而提供一种有弹性、抗压缩变形、表面吸附力小的PVC透明磨砂密封条及其制备方法。
为了达到上述目的，本发明所设计的PVC透明磨砂密封条，它由磨砂料制备而成，磨砂料包括弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂；弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂的重量比为45:28:0.2:0.2:4:0.55:5。
所述的PVC透明磨砂料的制备方法是：第一步，将弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂混合均匀，当温度达到90至100℃时，将混合好的物料放置到造粒机内造粒料；第二步，将制备好的粒料放入到挤出机内，按照所需密封条的形状、尺寸挤出成型。
本发明所得的PVC透明磨砂密封条，由于这种物质表面具有磨砂效果，相互之间吸附力就比较小，同时它也适宜在潮湿的环境使用，我国南方多雨天气，室内会比较潮湿，因此更能受广大消费者欢迎。
具体实施方式
实施例1：
本实施例描述的PVC透明磨砂密封条，它由磨砂料制备而成，磨砂料包括弹性树脂45kg、二辛脂25kg、硬脂酸0.2kg、石蜡0.2kg、大豆油4kg、稳定剂0.55kg、氯化甲脂5kg；弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂和氯化甲脂的物质均可在市场上买的。
所述的PVC透明磨砂料的制备方法是：第一步，将45kg的弹性树脂、58kg的二辛脂、0.2kg的硬脂酸、0.2kg的石蜡、4kg的大豆油、0.55kg的稳定剂、5kg的氯化甲脂混合均匀，当温度达到95℃时，将混合好的物料放置到造粒机内造粒料；第二步，将制备好的粒料放入到挤出机内，按照所需密封条的形状、尺寸挤出成型。该温度下产品质量最好。
实施例2：
与实施例1的区别是，所述的PVC透明磨砂料的制备方法是：第一步，将45kg的弹性树脂、58kg的二辛脂、0.2kg的硬脂酸、0.2kg的石蜡、4kg的大豆油、0.55kg的稳定剂、5kg的氯化甲脂混合均匀，当温度达到90℃时，将混合好的物料放置到造粒机内造粒料；第二步，将制备好的粒料放入到挤出机内，按照所需密封条的形状、尺寸挤出成型。
实施例3：
与实施例1的区别是，所述的PVC透明磨砂料的制备方法是：第一步，将45kg的弹性树脂、58kg的二辛脂、0.2kg的硬脂酸、0.2kg的石蜡、4kg的大豆油、0.55kg的稳定剂、5kg的氯化甲脂混合均匀，当温度达到100℃时，将混合好的物料放置到造粒机内造粒料；第二步，将制备好的粒料放入到挤出机内，按照所需密封条的形状、尺寸挤出成型。
Claims (3)
1.一种PVC透明磨砂密封条，其特征在于：它由磨砂料制备而成，磨砂料包括弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂；所述的弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂的重量比为45:28:0.2:0.2:4:0.55:5。
2.一种PVC透明磨砂密封条的制备方法，其特征在于：第一步，将弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂混合均匀，当温度达到90至100℃时，将混合好的物料放置到造粒机内造粒料；第二步，将制备好的粒料放入到挤出机内，按照所需密封条的形状、尺寸挤出成型。
3.根据权利要求2所述的一种PVC透明磨砂密封条的制备方法，其特征在于：第一步，将弹性树脂、二辛脂、硬脂酸、石蜡、大豆油、稳定剂、氯化甲脂混合均匀，当温度达到90℃时，将混合好的物料放置到造粒机内造粒料；第二步，将制备好的粒料放入到挤出机内，按照所需密封条的形状、尺寸挤出成型。