CN103255646B - Bronzing pulp and preparation method thereof - Google Patents
Bronzing pulp and preparation method thereof Download PDFInfo
- Publication number
- CN103255646B CN103255646B CN201310177685.2A CN201310177685A CN103255646B CN 103255646 B CN103255646 B CN 103255646B CN 201310177685 A CN201310177685 A CN 201310177685A CN 103255646 B CN103255646 B CN 103255646B
- Authority
- CN
- China
- Prior art keywords
- agent
- gold stamping
- parts
- pulp
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses bronzing pulp. The bronzing pulp is prepared from the following raw materials in parts by weight: 60-80 parts of acrylic ester emulsion, 2-6 parts of deionized water, 3-10 parts of a solvent, 1-5 parts of a stabilizer, 10-20 parts of EVA (Ethylene-Vinyl Acetate) hot melt adhesive powder, 0.5-3 parts of silica, 0.2-0.5 part of a polyurethane defoaming agent, 0.1-0.5 part of a pH regulator, 0.1-0.2 part of a preservative, 0.3-1 part of an emulsion wetting agent and 0.4-2 parts of a thickener. The bronzing pulp has the beneficial effects that the bronzing pulp is water-based pulp, the raw materials are easy to obtain and environment-friendly, the production is convenient, the technology is mature, and substances harmful to the environment can not be produced; and the bronzing pulp is soft in handfeel, firm in fastness, outstanding in resistance to tension fracture and diversified in application mode, enriches the styles of textiles, and endows the textiles with the noble quality.
Description
Technical field
The present invention relates to printing in textiles Material Field, be specially a kind of gold stamping slurry and preparation method thereof.
Background technology
Prior art in garment printing, the gold stamping mark becoming fashion because it is bright and glittering.But all the time, all there is Boardy Feeling, wash water fastness difference and the bronzing effect not gold stamping defect such as glittering like that on such as plastics in costume bronzing.Along with consumer is to the favor of bronzing effect, these problems are also just more and more outstanding.Therefore client's these problems in the urgent need to address.
Summary of the invention
For the deficiency that above-mentioned prior art exists, the object of this invention is to provide a kind of soft, fastness is firm, and tension splits the gold stamping slurry of superior.
Another object of the present invention is to provide a kind of preparation method of above-mentioned gold stamping slurry.
To achieve these goals, the technical solution adopted in the present invention is: gold stamping slurry, is made up of the raw material comprising following parts by weight:
Acrylic acid ester emulsion 60-80,
Deionized water 2-6,
Solvent 3-10,
Stabilizing agent 1-5,
Hot-melt adhesive powder 10-20,
Silica 0.5-3,
Defoamer 0.2-0.5,
PH adjusting agent 0.1-0.5,
Preservative agent 0.1-0.2,
Emulsification wetting agent 0.3-1,
Thickener 0.4-2.
Described acrylic acid ester emulsion is the aqueous acrylic emulsion that Ahmedabad rich Industrial Co., Ltd. in Shuande, Foshan City produces, and its model is 1070HA.
Described solvent can be ethylene glycol.
Described stabilizing agent can be epoxidized soybean oil.
Described hot-melt adhesive powder is EVA hot-melt adhesive powder.
Described preservative agent can be isothiazolinone.
Described pH adjusting agent is ammoniacal liquor or NaOH.
Described emulsification wetting agent can be poly(ethylene oxide) phenolic ether, polyethylene glycol glycerol condensation polymer, and preferred German enlightening is high
dispers715W.
Described thickener can be PTF thickener.
Described defoamer is polyurethane defoamer or product type is the defoamer of BYK-025.
The preparation method of gold stamping slurry, its step is as follows: by the acrylic acid ester emulsion of the above parts by weight, deionized water input cylinder, EVA hot-melt adhesive powder and silica is slowly added under stirring state, add solvent, stabilizing agent, defoamer, pH adjusting agent, preservative agent and emulsification wetting agent again, then grind through grinder, filter and collect, dropping into thickener and carry out thickening.
Compared with prior art, the invention has the beneficial effects as follows: be water paste, raw material is easy to get, environmental protection is easy to make, does not produce environmental toxic harmful substances; Have soft, fastness is firm, and tension splits superior, and application mode variation, has enriched textiles style; The gold stamping excellent wash water fastness of textiles and glittering outward appearance can be given, embody the quality that weaving is noble.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
Gold stamping slurry, be made up of the raw material comprising following parts by weight:
Acrylic acid ester emulsion 61,
Deionized water 3,
Solvent 4,
Stabilizing agent 2,
Hot-melt adhesive powder 11,
Silica 0.6,
Defoamer 0.3,
PH adjusting agent 0.2,
Preservative agent 0.12,
Emulsification wetting agent 0.4;
Thickener 0.5.
Embodiment 2
Gold stamping slurry, be made up of the raw material comprising following parts by weight:
Acrylic acid ester emulsion 79,
Deionized water 5,
Solvent 9,
Stabilizing agent 4,
Hot-melt adhesive powder 19,
Silica 2.9,
Defoamer 0.45,
PH adjusting agent 0.45,
Preservative agent 0.19,
Emulsification wetting agent 0.9
Thickener 1.9.
Embodiment 3
Gold stamping slurry, be made up of the raw material comprising following parts by weight:
Acrylic acid ester emulsion 67,
Deionized water 3,
Solvent 7,
Stabilizing agent 2,
Hot-melt adhesive powder 18,
Silica 1,
Defoamer 0.4,
PH adjusting agent 0.3,
Preservative agent 0.15,
Emulsification wetting agent 0.6,
Thickener 0.8.
Embodiment 4
Gold stamping slurry, be made up of the raw material comprising following parts by weight:
Acrylic acid ester emulsion 70,
Deionized water 4,
Solvent 6,
Stabilizing agent 3,
Hot-melt adhesive powder 15,
Silica 2,
Defoamer 0.4,
PH adjusting agent 0.3,
Preservative agent 0.15,
Emulsification wetting agent 0.7,
Thickener 1.2.
Described acrylic acid ester emulsion is the aqueous acrylic emulsion that Ahmedabad rich Industrial Co., Ltd. in Shuande, Foshan City produces, and its model is 1070HA.Described solvent can be ethylene glycol.Described stabilizing agent can be epoxidized soybean oil.Described hot-melt adhesive powder is EVA hot-melt adhesive powder.Described preservative agent can be isothiazolinone.Described pH adjusting agent is ammoniacal liquor or NaOH.Described emulsification wetting agent can be poly(ethylene oxide) phenolic ether, polyethylene glycol glycerol condensation polymer, and preferred German enlightening is high
dispers715W.Described thickener can be PTF thickener.Described defoamer is polyurethane defoamer or product type is the defoamer of BYK-025.
The preparation method of gold stamping slurry, its step is as follows: by the acrylic acid ester emulsion of the above parts by weight, deionized water input cylinder, EVA hot-melt adhesive powder and silica is slowly added under stirring state, add solvent, stabilizing agent, defoamer, pH adjusting agent, preservative agent and emulsification wetting agent again, then grind through grinder, filter and collect, dropping into thickener and carry out thickening.Wherein, EVA hot-melt adhesive powder and silica slowly add hot-melt adhesive powder and silica while stirring under 400-800rpm/min rotating speed, grinder ground 800-1000 order net, drops into thickener, be thickened to viscosity 37000-57000 centipoise.
After testing, the present invention has soft, and fastness is firm, and it is well a lot of that tension splits the current existing product of Performance Ratio, and can give the gold stamping excellent wash water fastness of textiles and glittering outward appearance, embodies the quality that weaving is noble.
Above-described embodiment is the present invention's preferably embodiment; but be not merely restricted to the described embodiments; change, the modification done under other any does not deviate from Spirit Essence of the present invention and principle, substitute, combine, simplify; all should be the substitute mode of equivalence, be all included within protection scope of the present invention.
Claims (8)
1. gold stamping slurry, is characterized in that, is made up of the raw material comprising following parts by weight:
Acrylic acid ester emulsion 60-80,
Deionized water 2-6,
Solvent 3-10,
Stabilizing agent 1-5,
Hot-melt adhesive powder 10-20,
Silica 0.5-3,
Defoamer 0.2-0.5,
PH adjusting agent 0.1-0.5,
Preservative agent 0.1-0.2,
Emulsification wetting agent 0.3-1,
Thickener 0.4-2.
2. gold stamping slurry according to claim 1, is characterized in that: described acrylic acid ester emulsion is the aqueous acrylic emulsion that Ahmedabad rich Industrial Co., Ltd. in Shuande, Foshan City produces.
3. gold stamping slurry according to claim 1, is characterized in that: described solvent is ethylene glycol; Described stabilizing agent is epoxidized soybean oil.
4. gold stamping slurry according to claim 1, is characterized in that: described hot-melt adhesive powder is EVA hot-melt adhesive powder.
5. gold stamping slurry according to claim 1, is characterized in that: described preservative agent is isothiazolinone; Described pH adjusting agent is ammoniacal liquor or NaOH.
6. gold stamping slurry according to claim 1, is characterized in that: described emulsification wetting agent is poly(ethylene oxide) phenolic ether, polyethylene glycol glycerol condensation polymer.
7. gold stamping slurry according to claim 1, is characterized in that: described defoamer is polyurethane defoamer or product type is the defoamer of BYK-025.
8. according to the preparation method of any described gold stamping slurry of claim 1-7, it is characterized in that: its step is as follows: by the acrylic acid ester emulsion of the above parts by weight, deionized water input cylinder, EVA hot-melt adhesive powder and silica is slowly added under stirring state, add solvent, stabilizing agent, defoamer, pH adjusting agent, preservative agent and emulsification wetting agent again, then grind through grinder, filter and collect, dropping into thickener and carry out thickening.