CN103255646A - Bronzing pulp and preparation method thereof - Google Patents
Bronzing pulp and preparation method thereof Download PDFInfo
- Publication number
- CN103255646A CN103255646A CN2013101776852A CN201310177685A CN103255646A CN 103255646 A CN103255646 A CN 103255646A CN 2013101776852 A CN2013101776852 A CN 2013101776852A CN 201310177685 A CN201310177685 A CN 201310177685A CN 103255646 A CN103255646 A CN 103255646A
- Authority
- CN
- China
- Prior art keywords
- agent
- gold stamping
- parts
- pulp
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses bronzing pulp. The bronzing pulp is prepared from the following raw materials in parts by weight: 60-80 parts of acrylic ester emulsion, 2-6 parts of deionized water, 3-10 parts of a solvent, 1-5 parts of a stabilizer, 10-20 parts of EVA (Ethylene-Vinyl Acetate) hot melt adhesive powder, 0.5-3 parts of silica, 0.2-0.5 part of a polyurethane defoaming agent, 0.1-0.5 part of a pH regulator, 0.1-0.2 part of a preservative, 0.3-1 part of an emulsion wetting agent and 0.4-2 parts of a thickener. The bronzing pulp has the beneficial effects that the bronzing pulp is water-based pulp, the raw materials are easy to obtain and environment-friendly, the production is convenient, the technology is mature, and substances harmful to the environment can not be produced; and the bronzing pulp is soft in handfeel, firm in fastness, outstanding in resistance to tension fracture and diversified in application mode, enriches the styles of textiles, and endows the textiles with the noble quality.
Description
Technical field
The present invention relates to printing in textiles material field, be specially a kind of gold stamping slurry and preparation method thereof.
Background technology
Prior art in the clothes stamp, the gold stamping sign that becomes fashion because it is bright and glittering.But all the time, all there is not gold stamping defective such as glittering like that on such as plastics of Boardy Feeling, wash water fastness difference and bronzing effect in costume bronzing.Along with the favor of consumer to bronzing effect, these problems are also just more and more outstanding.Therefore the client presses for and addresses these problems.
Summary of the invention
At the deficiency that above-mentioned prior art exists, the purpose of this invention is to provide a kind of softly, fastness is firm, the gold stamping slurry that the tension fragility can be outstanding.
Another object of the present invention provides a kind of preparation method of above-mentioned gold stamping slurry.
To achieve these goals, the technical solution adopted in the present invention is: gold stamping slurry, made by the raw material that comprises following parts by weight:
Acrylic acid ester emulsion 60-80,
Deionized water 2-6,
Solvent 3-10,
Stabilizing agent 1-5,
Hot-melt adhesive powder 10-20,
Silica 0.5-3,
Defoamer 0.2-0.5,
PH conditioning agent 0.1-0.5,
Preservative agent 0.1-0.2,
Emulsification wetting agent 0.3-1,
Thickener 0.4-2.
Described acrylic acid ester emulsion is the aqueous acrylic emulsion that Shuande, the Foshan City well-off industry of Ahmedabad Co., Ltd produces, and its model is 1070HA.
Described solvent can be ethylene glycol.
Described stabilizing agent can be epoxidized soybean oil.
Described hot-melt adhesive powder is the EVA hot-melt adhesive powder.
Described preservative agent can be isothiazolinone.
Described pH conditioning agent is ammoniacal liquor or NaOH.
Described emulsification wetting agent can be the poly(ethylene oxide) phenolic ether, polyethylene glycol glycerol condensation polymer, preferred German enlightening height
Dispers715W.
Described thickener can be the PTF thickener.
Described defoamer is that polyurethane defoamer or product type are the defoamer of BYK-025.
The preparation method of gold stamping slurry, its step is as follows: in the acrylic acid ester emulsion of the above parts by weight, deionized water input cylinder, slowly add EVA hot-melt adhesive powder and silica under the stirring state, add solvent, stabilizing agent, defoamer, pH conditioning agent, preservative agent and emulsification wetting agent again, grind through grinder then, filter and collect, drop into thickener and carry out thickening.
Compared with prior art, the invention has the beneficial effects as follows: be water paste, raw material is easy to get, and environmental protection is easy to make, does not produce the environment poisonous and harmful substances; Have softly, fastness is firm, and the tension fragility can be outstanding, and the textiles style has been enriched in the application mode variation; Can give the gold stamping good wash water fastness of textiles and glittering outward appearance, embody the noble quality of weaving.
The specific embodiment
The present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
Gold stamping slurry, made by the raw material that comprises following parts by weight:
Acrylic acid ester emulsion 61,
Deionized water 3,
Solvent 4,
Stabilizing agent 2,
Hot-melt adhesive powder 11,
Silica 0.6,
Defoamer 0.3,
PH conditioning agent 0.2,
Preservative agent 0.12,
Emulsification wetting agent 0.4;
Thickener 0.5.
Embodiment 2
Gold stamping slurry, made by the raw material that comprises following parts by weight:
Acrylic acid ester emulsion 79,
Deionized water 5,
Solvent 9,
Stabilizing agent 4,
Hot-melt adhesive powder 19,
Silica 2.9,
Defoamer 0.45,
PH conditioning agent 0.45,
Preservative agent 0.19,
Emulsification wetting agent 0.9
Thickener 1.9.
Embodiment 3
Gold stamping slurry, made by the raw material that comprises following parts by weight:
Acrylic acid ester emulsion 67,
Deionized water 3,
Solvent 7,
Stabilizing agent 2,
Hot-melt adhesive powder 18,
Silica 1,
Defoamer 0.4,
PH conditioning agent 0.3,
Preservative agent 0.15,
Emulsification wetting agent 0.6,
Thickener 0.8.
Embodiment 4
Gold stamping slurry, made by the raw material that comprises following parts by weight:
Acrylic acid ester emulsion 70,
Deionized water 4,
Solvent 6,
Stabilizing agent 3,
Hot-melt adhesive powder 15,
Silica 2,
Defoamer 0.4,
PH conditioning agent 0.3,
Preservative agent 0.15,
Emulsification wetting agent 0.7,
Thickener 1.2.
Described acrylic acid ester emulsion is the aqueous acrylic emulsion that Shuande, the Foshan City well-off industry of Ahmedabad Co., Ltd produces, and its model is 1070HA.Described solvent can be ethylene glycol.Described stabilizing agent can be epoxidized soybean oil.Described hot-melt adhesive powder is the EVA hot-melt adhesive powder.Described preservative agent can be isothiazolinone.Described pH conditioning agent is ammoniacal liquor or NaOH.Described emulsification wetting agent can be the poly(ethylene oxide) phenolic ether, polyethylene glycol glycerol condensation polymer, preferred German enlightening height
Dispers715W.Described thickener can be the PTF thickener.Described defoamer is that polyurethane defoamer or product type are the defoamer of BYK-025.
The preparation method of gold stamping slurry, its step is as follows: in the acrylic acid ester emulsion of the above parts by weight, deionized water input cylinder, slowly add EVA hot-melt adhesive powder and silica under the stirring state, add solvent, stabilizing agent, defoamer, pH conditioning agent, preservative agent and emulsification wetting agent again, grind through grinder then, filter and collect, drop into thickener and carry out thickening.Wherein, EVA hot-melt adhesive powder and silica are slowly to add hot-melt adhesive powder and silica under the 400-800rpm/min rotating speed while stirring, and grinder ground 800-1000 order net, drop into thickener, are thickened to viscosity 37000-57000 centipoise.
After testing, the present invention has soft, and fastness is firm, and the tension fragility can will be got well much than present existing product, and can give the gold stamping good wash water fastness of textiles and glittering outward appearance, embodies the noble quality of weaving.
Above-described embodiment is preferred implementation of the present invention; but not merely be restricted to the described embodiments; other any do not deviate from change, the modification done under spiritual essence of the present invention and the principle, substitutes, combination, simplify; all should be the substitute mode of equivalence, all be included within protection scope of the present invention.
Claims (8)
1. gold stamping slurry is characterized in that, is made by the raw material that comprises following parts by weight:
Acrylic acid ester emulsion 60-80,
Deionized water 2-6,
Solvent 3-10,
Stabilizing agent 1-5,
Hot-melt adhesive powder 10-20,
Silica 0.5-3,
Defoamer 0.2-0.5,
PH conditioning agent 0.1-0.5,
Preservative agent 0.1-0.2,
Emulsification wetting agent 0.3-1,
Thickener 0.4-2.
2. gold stamping slurry according to claim 1 is characterized in that: described acrylic acid ester emulsion is the aqueous acrylic emulsion that Shuande, the Foshan City well-off industry of Ahmedabad Co., Ltd produces.
3. gold stamping slurry according to claim 1, it is characterized in that: described solvent is ethylene glycol; Described stabilizing agent is epoxidized soybean oil.
4. gold stamping slurry according to claim 1, it is characterized in that: described hot-melt adhesive powder is the EVA hot-melt adhesive powder.
5. gold stamping slurry according to claim 1, it is characterized in that: described preservative agent is isothiazolinone; Described pH conditioning agent is ammoniacal liquor or NaOH.
6. gold stamping slurry according to claim 1, it is characterized in that: described emulsification wetting agent is the poly(ethylene oxide) phenolic ether, the polyethylene glycol glycerol condensation polymer.
7. gold stamping slurry according to claim 1, it is characterized in that: described defoamer is that polyurethane defoamer or product type are the defoamer of BYK-025.
8. according to any preparation method of described gold stamping slurry of claim 1-7, it is characterized in that: its step is as follows: in the acrylic acid ester emulsion of the above parts by weight, deionized water input cylinder, slowly add EVA hot-melt adhesive powder and silica under the stirring state, add solvent, stabilizing agent, defoamer, pH conditioning agent, preservative agent and emulsification wetting agent again, grind through grinder then, filter and collect, drop into thickener and carry out thickening.