CN103254689A - Gravure ink for aluminium foil and preparation method of gravure ink - Google Patents
Gravure ink for aluminium foil and preparation method of gravure ink Download PDFInfo
- Publication number
- CN103254689A CN103254689A CN2013102109362A CN201310210936A CN103254689A CN 103254689 A CN103254689 A CN 103254689A CN 2013102109362 A CN2013102109362 A CN 2013102109362A CN 201310210936 A CN201310210936 A CN 201310210936A CN 103254689 A CN103254689 A CN 103254689A
- Authority
- CN
- China
- Prior art keywords
- gravure ink
- aluminium foil
- parts
- softening agent
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a gravure ink for an aluminium foil. The gravure ink for the aluminium foil comprises the following composition ingredients in parts by mass: 10-12 parts of organic pigments, 8-12 parts of light calcium carbonate, 12-18 parts of chlorinated rubber, 1-2 parts of thermoplastic acrylic resin, 2.5-3.0 parts of plasticizer, 2.0-7.5 parts of polyethylene microcrystalline wax, 5-62 parts of methylbenzene, 1-2 parts of a stabilizer, 5-8 parts of terpilenol, and 15-17.5 parts of modified phenolic resin. According to the gravure ink for the aluminium foil and the preparation method of the gravure ink provided by the invention, the ink is heat-resistant, transfer-resistant, fireproof and set-off-proof, has a viscosity of 20-40 s, can be completely dry in 1 second, and can be widely applied and continuously replace the existing products.
Description
Technical field
The present invention relates to a kind of printing ink and preparation method thereof, relate in particular to a kind of aluminium foil base gravure ink and preparation method thereof.
Background technology
The intaglio process paper printing ink of China at first gets up at the publication and printing industry development.Because print speed significantly improves, started the new stage of China's intaglio process paper printing ink development.The current improved technological line of intaglio process paper printing ink is main binder with nitro-cotton still, is solvent with alcohols, ester class etc., and the rate of drying of printing ink is brought up to 150 meters/minute.This China ink has that scumming not, levelling are good, the characteristics of transfer printing excellent property, the dense profit of color and luster.Mainly print non-overlay paper in the past, now based on printed coating paper.In order to improve the printing property made of seal paper printing ink, to level version printing development, domestic printing ink manufacturing enterprise has developed four look printing inks of standard now, to adapt to the needs of printing enterprise.At present, the kind of intaglio process paper printing ink still is in the stage that increase, quality still are in rising, development along with social cityization, technicalization, hommization, printing has obtained vigorous growth, increasing gravure printing machine is not as huge numbers of families, and the consequent is the increase of gravure printing ink usage quantity and the gravure printing ink thermotolerance is weak, not anti-migration, the waterproof of not setting fire and dryly wait showing of problem slowly.
Intaglio printing is that image is from the recessed plate-making technology of surface engraving.In general, adopt copper or zine plate as engraved surface, recessed part can be utilized burn into engraving, copperplate etching or mezzotint metallograph graphic arts process, and Collographs may be according to the gravure printing.Print gravure, the surface is covered with printing ink, wipes printing ink with tarlatan or newspaper from the surface then, only stays recessed part.Wet paper is overlayed on forme top, forme and paper pressurize by printing press, printing ink is sent on the paper from the recessed part of forme, and popularizing along with humanity concept, and the formation of novel harmonious society, the aluminium foil that designs a kind of heat-resisting, anti-migration, the anti-set-off of fire-proof and water-proof is very important with base gravure ink.
Summary of the invention
The technical problem that solves:At a little less than the above-mentioned printing ink thermotolerance, not anti-migration, the waterproof of not setting fire and drying wait shortcoming slowly, provides a kind of aluminium foil with base gravure ink and preparation method thereof.
Technical scheme:A kind of aluminium foil base gravure ink, its composition with the mass fraction representation is:
Pigment dyestuff 10-12;
Light calcium carbonate 8-12;
Chlorinated rubber 12-18;
Thermoplastic acrylic resin 1-2;
Softening agent 2.5-3.0;
Polyethylene Microcrystalline Wax 2.0-7.5;
Toluene 5-62;
Stablizer 1-2;
Terpineol 350 5-8;
Modified phenolic resins 15-17.5.
As a kind of optimal technical scheme of the present invention: described softening agent adopts epoxy soybean oil.
As a kind of optimal technical scheme of the present invention: described stablizer adopts barium sulfate.
As a kind of optimal technical scheme of the present invention: described aluminium foil is as follows with preparation method's step of base gravure ink:
The first step: toluene, Terpineol 350, softening agent and the chlorinated rubber of 2/3rds mass parts are packed in the reactor, have reflux exchanger on the reactor, begin to stir after opening the reflux exchanger water coolant, slowly add thermoplastic acrylic resin and modified phenolic resins then, stop heating after being warming up to 60~70 ℃, continue to stir, cool the temperature to 35~38 ℃ behind insulation 4.5~5h;
Second step: then add pigment dyestuff, stablizer and light calcium carbonate and stir;
The 3rd step: add remaining toluene, Terpineol 350, softening agent and chlorinated rubber at last, and add after the polyethylene Microcrystalline Wax stirs, filter and namely get the aluminium foil base gravure ink.
Beneficial effect:Aluminium foil provided by the invention is prevented set-off with base gravure ink and preparation method thereof, the heat-resisting anti-migration of printing ink, fire prevention, and is absolutely dry in the viscosity 20-40s, 1S, and the not division of history into periods of can being used widely is for currently available products.
Embodiment
Set forth content of the present invention by the following examples in further detail.
Embodiment 1:
The first step: take by weighing various raw materials according to ratio of quality and the number of copies hereinafter described
Pigment dyestuff 12;
Light calcium carbonate 12;
Chlorinated rubber 18;
Thermoplastic acrylic resin 2;
Epoxy soybean oil 3.0;
Polyethylene Microcrystalline Wax 3;
Toluene 62;
Barium sulfate 1;
Terpineol 350 6;
Modified phenolic resins 17.5.
Second step: toluene, Terpineol 350, softening agent and the chlorinated rubber of 2/3rds mass parts are packed in the reactor, have reflux exchanger on the reactor, begin to stir after opening the reflux exchanger water coolant, slowly add thermoplastic acrylic resin and modified phenolic resins then, stop heating after being warming up to 65 ℃, continue to stir, cool the temperature to 35 ℃ behind the insulation 4.5h;
The 3rd step: then add pigment dyestuff, stablizer and light calcium carbonate and stir;
The 4th step: add remaining toluene, Terpineol 350, softening agent and chlorinated rubber at last, and add after the polyethylene Microcrystalline Wax stirs, filter and namely get the aluminium foil base gravure ink.
Embodiment 2:
The first step: take by weighing various raw materials according to ratio of quality and the number of copies hereinafter described
Pigment dyestuff 10;
Light calcium carbonate 8;
Chlorinated rubber 12;
Thermoplastic acrylic resin 1;
Epoxy soybean oil 2.5;
Polyethylene Microcrystalline Wax 2.0;
Toluene 5;
Barium sulfate 1;
Terpineol 350 5;
Modified phenolic resins 15.
Second step: toluene, Terpineol 350, softening agent and the chlorinated rubber of 2/3rds mass parts are packed in the reactor, have reflux exchanger on the reactor, begin to stir after opening the reflux exchanger water coolant, slowly add thermoplastic acrylic resin and modified phenolic resins then, stop heating after being warming up to 60 ℃, continue to stir, cool the temperature to 35 ℃ behind the insulation 4.5h;
The 3rd step: then add pigment dyestuff, stablizer and light calcium carbonate and stir;
The 4th step: add remaining toluene, Terpineol 350, softening agent and chlorinated rubber at last, and add after the polyethylene Microcrystalline Wax stirs, filter and namely get the aluminium foil base gravure ink.
Embodiment 3:
The first step: take by weighing various raw materials according to ratio of quality and the number of copies hereinafter described
Pigment dyestuff 11;
Light calcium carbonate 10;
Chlorinated rubber 15;
Thermoplastic acrylic resin 1.5;
Epoxy soybean oil 3.0;
Polyethylene Microcrystalline Wax 7.5;
Toluene 30;
Barium sulfate 1.5;
Terpineol 350 8;
Modified phenolic resins 16.
Second step: toluene, Terpineol 350, softening agent and the chlorinated rubber of 2/3rds mass parts are packed in the reactor, have reflux exchanger on the reactor, begin to stir after opening the reflux exchanger water coolant, slowly add thermoplastic acrylic resin and modified phenolic resins then, stop heating after being warming up to 70 ℃, continue to stir, cool the temperature to 38 ℃ behind the insulation 5h;
The 3rd step: then add pigment dyestuff, stablizer and light calcium carbonate and stir;
The 4th step: add remaining toluene, Terpineol 350, softening agent and chlorinated rubber at last, and add after the polyethylene Microcrystalline Wax stirs, filter and namely get the aluminium foil base gravure ink.
Composition all components in above embodiment and the Comparative Examples all can commercially be bought.
Test performance:
Embodiment 1 ~ 3 is carried out viscosity and test time of drying, the results are shown in Table one:
Epoxy soybean oil | Thermoplastic acrylic resin | Toluene | Chlorinated rubber | Viscosity/s | Time of drying/s | |
Embodiment 1 | 3 | 2 | 62 | 18 | 3.0 | 0.4 |
Embodiment 2 | 2.5 | 1 | 5 | 12 | 2.0 | 0.6 |
Embodiment 3 | 3 | 1.5 | 30 | 15 | 4.0 | 0.8 |
Table one
Above-described embodiment just is used for content of the present invention is set forth, rather than restriction, therefore in the implication suitable with claims of the present invention and any change in the scope, all should think to be included in the scope of claims.
Claims (4)
1. aluminium foil base gravure ink, it is characterized in that: its composition with the mass fraction representation is:
Pigment dyestuff 10-12;
Light calcium carbonate 8-12;
Chlorinated rubber 12-18;
Thermoplastic acrylic resin 1-2;
Softening agent 2.5-3.0;
Polyethylene Microcrystalline Wax 2.0-7.5;
Toluene 5-62;
Stablizer 1-2;
Terpineol 350 5-8;
Modified phenolic resins 15-17.5.
2. aluminium foil base gravure ink according to claim 1 is characterized in that: described softening agent employing epoxy soybean oil.
3. aluminium foil base gravure ink according to claim 1 is characterized in that: described stablizer employing barium sulfate.
4. one kind prepares the method that the described aluminium foil of claim 1 is used base gravure ink, it is characterized in that the preparation process of this method is as follows:
The first step: toluene, Terpineol 350, softening agent and the chlorinated rubber of 2/3rds mass parts are packed in the reactor, have reflux exchanger on the reactor, begin to stir after opening the reflux exchanger water coolant, slowly add thermoplastic acrylic resin and modified phenolic resins then, stop heating after being warming up to 60~70 ℃, continue to stir, cool the temperature to 35~38 ℃ behind insulation 4.5~5h;
Second step: then add pigment dyestuff, stablizer and light calcium carbonate and stir;
The 3rd step: add remaining toluene, Terpineol 350, softening agent and chlorinated rubber at last, and add after the polyethylene Microcrystalline Wax stirs, filter and namely get the aluminium foil base gravure ink.