CN103254519A - 电焊机电缆用耐寒阻燃护套橡皮 - Google Patents
电焊机电缆用耐寒阻燃护套橡皮 Download PDFInfo
- Publication number
- CN103254519A CN103254519A CN2013102089903A CN201310208990A CN103254519A CN 103254519 A CN103254519 A CN 103254519A CN 2013102089903 A CN2013102089903 A CN 2013102089903A CN 201310208990 A CN201310208990 A CN 201310208990A CN 103254519 A CN103254519 A CN 103254519A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- welding machine
- cold
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种电焊机电缆用耐寒阻燃护套橡皮,按配比由以下组分制成:氯化聚乙烯100份;活性剂8~15份;环保稳定剂3~5份;微晶蜡3~5份;环保三氧化二锑5~10份;补强填充剂60~100份;增塑剂15~30份;防老剂RD0.5~1.5份;抗氧剂10100.3~0.5份;偶联剂A-1720.6~1.2份;硫化剂DCP2~4份;硫化助剂TAIC2~4份;护套橡皮的含胶量为38~45%;含胶量为氯化聚乙烯的重量/总重量×100%。本发明性能满足GB/T5013.6-2008《额定电压450/750V及以下橡皮绝缘电缆 第6部分:电焊机电缆》的性能要求,长期使用温度为-40℃~90℃。
Description
技术领域
本发明涉及一种电缆用的护套橡皮,特别是涉及电焊机电缆用耐寒阻燃护套橡皮。
背景技术
电焊机电缆俗称焊把线,属于橡皮绝缘电缆类,最新执行标准为GB/T 5013.6-2008《额定电压450/750V及以下橡皮绝缘电缆》,包括两种型号:60245 IEC 81(YH)(高强度橡套电焊机电缆)和60245 IEC 81(YHF)(氯丁或其他相当合成弹性体橡套电焊机电缆),是用于电焊机二次侧接线及连接电焊钳、电焊机的专用电缆,其特点是电流大、电压低。
目前YH型电焊机电缆胶采用天然橡胶或天然橡胶与氯丁橡胶并用胶,其特点是耐油性护套差、不阻燃、价格高、长期工作温度为60℃。
目前YHF型电焊机电缆护套胶采用氯丁橡胶,其特点是加工性差、价格高、长期工作温度为60℃。
橡胶型氯化聚乙烯是一种价格低廉、综合性能优良、耐热氧臭氧老化、耐磨性、阻燃性良好的特种合成橡胶,长期工作温度可达90℃。
本发明选用氯化聚乙烯(CPE)为主材来开发电焊机电缆用耐寒阻燃护套橡皮。
发明内容
本发明的目的是解决上述不足,提供一种电焊机电缆用耐寒阻燃护套橡皮,性能满足GB/T 5013.6-2008《额定电压450/750V及以下橡皮绝缘电缆 第6部分:电焊机电缆》的性能要求,且长期使用温度为-40℃~90℃。
为了实现上述目的,本发明的技术方案是:
一种电焊机电缆用耐寒阻燃护套橡皮,按配比由以下组分制成:氯化聚乙烯100份;活性剂8~15份;环保稳定剂3~5份;微晶蜡3~5份;环保三氧化二锑5~10份;补强填充剂60~100份;增塑剂15~30份;防老剂RD 0.5~1.5份;抗氧剂1010 0.3~0.5份;偶联剂A-172 0.6~1.2份;硫化剂DCP 2~4份;硫化助剂TAIC 2~4份;护套橡皮的含胶量为38~45%;含胶量为氯化聚乙烯的重量/总重量×100%。
所述的活性剂为活性氧化镁。
所述的环保稳定剂为环保钙锌复合稳定剂。
所述的补强填充剂为纳米改性硅藻土、N550炭黑、6000目硅烷改性煅烧陶土和2500目滑石粉的混合物,在护套橡皮的补强填充剂总组分中纳米改性硅藻土30~60份,N550炭黑5~25份,6000目硅烷改性煅烧陶土30~60份,2500目滑石粉0~30份。
所述的纳米改性硅藻土为霍夫曼HOFFMANN诺易堡硅土(矽丽粉)Aktisil VM56。(备注:HOFFMANN为厂商名称)
所述的增塑剂为癸二酸二辛酯(DOS)和偏苯三酸三辛酯(TOTM)的混合物,在护套橡皮的增塑剂总组分中癸二酸二辛酯(DOS)5~15份,偏苯三酸三辛酯(TOTM)5~15份。
采用上述方案后,本发明具有以下的有益效果:⑴、采用CPE为主体来降低成本:氯化聚乙烯(CPE)价格比氯丁橡胶(CR)、氯磺化聚乙烯(CSM)和天然橡胶(NR)的价格低很多,以氯化聚乙烯(CPE)为主体,符合低成本要求;⑵、通过补强填充剂适宜组合,尤其是通过6000目改性煅烧陶土来提高电绝缘性能、通过纳米改性硅藻土来提高耐磨性能和柔软性能;⑶、通过阻燃剂来提高阻燃性能;⑷、通过抗氧剂、增塑剂、稳定剂和防老剂的适宜组合来提高耐热性能、耐候性能;⑸、通过增塑剂的适宜组合来提高低温柔软性;⑹、该护套橡皮能满足GB/T 5013.6-2008《额定电压450/750V及以下橡皮绝缘电缆 第6部分:电焊机电缆》的性能要求,长期使用温度为-40℃~90℃,且制备工艺简单,可操作性强。
具体实施方式
下面进一步阐述本发明。
氯化聚乙烯橡胶具有良好的机械性能、阻燃性能、耐热性能、耐油性能且加工性能优良,但电绝缘性能一般,只能作为低压电缆绝缘。
在电焊机电缆用耐寒阻燃护套橡皮,用氯化聚乙烯作为基料,通过阻燃剂三氧化二锑提高其阻燃性能,在护套橡皮中通过添加补强剂填充剂炭黑、硅藻土和滑石粉提高其机械性能同时还具备良好的柔软性,通过添加偶联剂和煅烧陶土提高其绝缘电阻和降低吸水率,通过添加增塑剂提高耐低温性能和低温柔软性,通过添加防老剂和抗氧剂提高其耐候性和耐热性能。
具体实施例:
电焊机电缆用耐寒阻燃护套橡皮的组成、配比份数及型号见表一。
表一
按照表一比例称重后进行混合、出片、挤出成型、蒸汽硫化后取得成品电缆60245 IEC82(YHF) 16mm2。
具体加工制备方法如下:
⑴、按照配方组分和橡胶及配合剂品种、类别和用量进行称量和配合。称量配合操作必须做到精密、准确、不漏、不错;
⑵、将氯化聚乙烯胶料和增塑剂投入密炼机中常压混合1~2分钟,然后加入除硫化剂和硫化助剂外所有配合剂,压力下混合6~8分钟,下料温度控制110~120℃,卸料,过滤,出片冷却;
⑶、密炼机加入硫化剂和硫化助剂,压力下混合1~2分钟,下料温度控制75~85℃,出片冷却,静置16~24小时;
⑷、在∮90连硫挤橡机挤出硫化,开机速度15~25m/min,蒸汽压力1.2~1.3Mpa。
电缆铜导体线芯表面光亮,护套表面光滑,护套断面结实,电缆柔软,各项性能均能符合GB/T 5013.6-2008标准的要求,具体性能见详见表二。
表二
以上所述的具体实施例,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所理解的是,以上所述为本发明的具体提实施例而已,并不用于限制本发明,凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均包含在本发明的保护范围之内。
Claims (6)
1.一种电焊机电缆用耐寒阻燃护套橡皮,其特征在于:按配比由以下组分制成:氯化聚乙烯100份;活性剂8~15份;环保稳定剂3~5份;微晶蜡3~5份;环保三氧化二锑5~10份;补强填充剂60~100份;增塑剂15~30份;防老剂RD 0.5~1.5份;抗氧剂1010 0.3~0.5份;偶联剂A-172 0.6~1.2份;硫化剂DCP 2~4份;硫化助剂TAIC 2~4份;护套橡皮的含胶量为38~45%;含胶量为氯化聚乙烯的重量/总重量×100%。
2.根据权利要求1所述的一种电焊机电缆用耐寒阻燃护套橡皮,其特征在于:所述的活性剂为活性氧化镁。
3.根据权利要求1所述的电焊机电缆用耐寒阻燃护套橡皮,其特征在于:所述的环保稳定剂为环保钙锌复合稳定剂。
4.根据权利要求1所述的电焊机电缆用耐寒阻燃护套橡皮,其特征在于:所述的补强填充剂为纳米改性硅藻土、N550炭黑、6000目硅烷改性煅烧陶土和2500目滑石粉的混合物,在护套橡皮的补强填充剂总组分中纳米改性硅藻土30~60份,N550炭黑5~25份,6000目硅烷改性煅烧陶土30~60份,2500目滑石粉0~30份。
5.根据权利要求4所述的电焊机电缆用耐寒阻燃护套橡皮,其特征在于:所述的纳米改性硅藻土为霍夫曼HOFFMANN诺易堡硅土Aktisil VM56。
6.根据权利要求1所述的电焊机电缆用耐寒阻燃护套橡皮,其特征在于:所述的增塑剂为癸二酸二辛酯和偏苯三酸三辛酯的混合物,在护套橡皮的增塑剂总组分中癸二酸二辛酯5~15份,偏苯三酸三辛酯5~15份。