CN103252378A - 一种连续挤压冷轧生产高精度无氧银铜带的方法 - Google Patents

一种连续挤压冷轧生产高精度无氧银铜带的方法 Download PDF

Info

Publication number
CN103252378A
CN103252378A CN2012100355762A CN201210035576A CN103252378A CN 103252378 A CN103252378 A CN 103252378A CN 2012100355762 A CN2012100355762 A CN 2012100355762A CN 201210035576 A CN201210035576 A CN 201210035576A CN 103252378 A CN103252378 A CN 103252378A
Authority
CN
China
Prior art keywords
copper strips
free silver
oxygen
silver copper
cold rolling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100355762A
Other languages
English (en)
Inventor
黄四龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGXI GUANGXIN COPPER INDUSTRY Co Ltd
Original Assignee
JIANGXI GUANGXIN COPPER INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGXI GUANGXIN COPPER INDUSTRY Co Ltd filed Critical JIANGXI GUANGXIN COPPER INDUSTRY Co Ltd
Priority to CN2012100355762A priority Critical patent/CN103252378A/zh
Publication of CN103252378A publication Critical patent/CN103252378A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种连续挤压冷轧生产高精度无氧银铜带的方法，采用的原料为Ф20mm的无氧银铜合金杆，把无氧银铜合金杆放在挤压机中进行挤压，再把挤出的铜带通过四辊冷轧机进行粗轧、精轧至成品厚度。本发明与传统方法相比，不需要进行热轧，其内部组织通过挤压变形由铸造组织变为热加工组织，大大提高了产品的综合力学性能；通过挤压出来的铜带坯料，表面光洁，与传统方法相比，省去了坯料的洗面工序，从而使成材率提高了5%-10%。本发明的方法可广泛适用于高精度无氧银铜带的生产。

Description

一种连续挤压冷轧生产高精度无氧银铜带的方法
技术领域
本发明涉及一种无氧银铜带的生产方法。
背景技术
现有无氧银铜带生产方法需通过热轧方法进行，不仅能耗高，而且要通过洗面和退火等工序，加工程序复杂，生产成本高，设备投入量大。
发明内容
本发明的目的就是针对上述情况提供一种工艺简单，能耗低的无氧银铜带的生产方法。本发明的目的可通过以下方案来实现：本发明采用的原料为Ф20mm的无氧银铜合金杆，把无氧银铜合金杆放在挤压机中进行挤压，挤压的温度控制在450—500℃，挤压程度控制在8转/分钟，无氧银铜合金杆在挤压轮的驱动下，通过摩擦产生热量，使铜合金杆从挤压模具中连续挤出合适厚度的铜带，再把挤出的铜带通过四辊冷轧机进行粗轧、精轧至成品厚度。
本发明与传统方法相比，不需要进行热轧，其内部组织通过挤压变形由铸造组织变为热加工组织，大大提高了产品的综合力学性能；通过挤压出来的铜带坯料，表面光洁，与传统方法相比，省去了坯料的洗面工序，从而使成材率提高了5%-10%。本发明的方法可广泛适用于高精度无氧银铜带的生产。

Claims (1)

1.一种连续挤压冷轧生产高精度无氧银铜带的方法，其特征是采用的原料为Ф20mm的无氧银铜合金杆，把无氧银铜合金杆放在挤压机中进行挤压，挤压的温度控制在450—500℃，挤压程度控制在8转/分钟，无氧银铜合金杆在挤压轮的驱动下，通过摩擦产生热量，使铜合金杆从挤压模具中连续挤出合适厚度的铜带，再把挤出的铜带通过四辊冷轧机进行粗轧、精轧至成品厚度。
CN2012100355762A 2012-02-17 2012-02-17 一种连续挤压冷轧生产高精度无氧银铜带的方法 Pending CN103252378A (zh)